WO2021166968A1 - Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batteries rechargeables tout-solide et procédé de production de batterie rechargeable tout-solide - Google Patents

Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batteries rechargeables tout-solide et procédé de production de batterie rechargeable tout-solide Download PDF

Info

Publication number
WO2021166968A1
WO2021166968A1 PCT/JP2021/005973 JP2021005973W WO2021166968A1 WO 2021166968 A1 WO2021166968 A1 WO 2021166968A1 JP 2021005973 W JP2021005973 W JP 2021005973W WO 2021166968 A1 WO2021166968 A1 WO 2021166968A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
solid electrolyte
polymer
solid
secondary battery
Prior art date
Application number
PCT/JP2021/005973
Other languages
English (en)
Japanese (ja)
Inventor
陽 串田
安田　浩司
宏顕 望月
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2022501941A priority Critical patent/JPWO2021166968A1/ja
Publication of WO2021166968A1 publication Critical patent/WO2021166968A1/fr

Abstract

La présente invention concerne : une composition contenant un électrolyte solide inorganique qui contient un électrolyte solide inorganique, un liant polymère et un milieu de dispersion, le liant polymère étant composé d'un polymère qui est configuré à partir d'atomes qui ne sont pas substitués par des atomes de fluor, tout en ayant une chaîne principale contenant une liaison spécifique telle qu'une liaison uréthane et contenant un constituant qui a au moins un groupe fonctionnel spécifique tel qu'un groupe hydroxyle ; une feuille pour batteries rechargeables tout-solide, ladite feuille utilisant cette composition contenant un électrolyte solide inorganique ; une batterie rechargeable tout-solide ; un procédé de production d'une feuille pour batteries rechargeables tout-solide ; et un procédé de production d'une batterie rechargeable tout-solide.
PCT/JP2021/005973 2020-02-20 2021-02-17 Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batteries rechargeables tout-solide et procédé de production de batterie rechargeable tout-solide WO2021166968A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022501941A JPWO2021166968A1 (fr) 2020-02-20 2021-02-17

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-027191 2020-02-20
JP2020027191 2020-02-20

Publications (1)

Publication Number Publication Date
WO2021166968A1 true WO2021166968A1 (fr) 2021-08-26

Family

ID=77391272

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/005973 WO2021166968A1 (fr) 2020-02-20 2021-02-17 Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batteries rechargeables tout-solide et procédé de production de batterie rechargeable tout-solide

Country Status (2)

Country Link
JP (1) JPWO2021166968A1 (fr)
WO (1) WO2021166968A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023058543A1 (fr) * 2021-10-05 2023-04-13 株式会社クレハ Solution de polymère de fluorure de vinylidène
WO2024071056A1 (fr) * 2022-09-30 2024-04-04 富士フイルム株式会社 Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille pour batteries secondaires entièrement solides et procédé de production de batterie secondaire entièrement solide

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015088480A (ja) * 2013-09-25 2015-05-07 富士フイルム株式会社 固体電解質組成物および全固体二次電池用のバインダー、ならびにこれらを用いた電池用電極シートおよび全固体二次電池
JP2015167126A (ja) * 2014-02-17 2015-09-24 富士フイルム株式会社 固体電解質組成物、これを用いた電池用電極シートおよび全固体二次電池、ならびにそれらの製造方法
JP2016181448A (ja) * 2015-03-24 2016-10-13 富士フイルム株式会社 硫化物系固体電解質組成物、電池用電極シートおよびその製造方法、並びに、全固体二次電池およびその製造方法
WO2018151161A1 (fr) * 2017-02-17 2018-08-23 富士フイルム株式会社 Composition d'électrolyte solide, feuille contenant un électrolyte solide et son procédé de production, batterie secondaire entièrement solide et son procédé de production, et polymère et dispersion non aqueuse de solvant correspondante

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015088480A (ja) * 2013-09-25 2015-05-07 富士フイルム株式会社 固体電解質組成物および全固体二次電池用のバインダー、ならびにこれらを用いた電池用電極シートおよび全固体二次電池
JP2015167126A (ja) * 2014-02-17 2015-09-24 富士フイルム株式会社 固体電解質組成物、これを用いた電池用電極シートおよび全固体二次電池、ならびにそれらの製造方法
JP2016181448A (ja) * 2015-03-24 2016-10-13 富士フイルム株式会社 硫化物系固体電解質組成物、電池用電極シートおよびその製造方法、並びに、全固体二次電池およびその製造方法
WO2018151161A1 (fr) * 2017-02-17 2018-08-23 富士フイルム株式会社 Composition d'électrolyte solide, feuille contenant un électrolyte solide et son procédé de production, batterie secondaire entièrement solide et son procédé de production, et polymère et dispersion non aqueuse de solvant correspondante

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023058543A1 (fr) * 2021-10-05 2023-04-13 株式会社クレハ Solution de polymère de fluorure de vinylidène
WO2024071056A1 (fr) * 2022-09-30 2024-04-04 富士フイルム株式会社 Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille pour batteries secondaires entièrement solides et procédé de production de batterie secondaire entièrement solide

Also Published As

Publication number Publication date
JPWO2021166968A1 (fr) 2021-08-26

Similar Documents

Publication Publication Date Title
WO2021039950A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires à semi-conducteur, batterie secondaire à semi-conducteur et procédés de production de batterie secondaire à semi-conducteur et feuille pour batteries secondaires à semi-conducteur
WO2021039948A1 (fr) Procédé de production de composition d'électrode, procédé de fabrication de feuille d'électrode pour une batterie secondaire tout solide et procédé de fabrication de batterie secondaire tout solide
WO2021100362A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille pour batteries secondaires entièrement solides et procédé de production de batterie secondaire entièrement solide
WO2021039468A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, méthode de fabrication de feuille pour batteries secondaires entièrement solides, et méthode de fabrication de batterie secondaire entièrement solide
JP7234400B2 (ja) 無機固体電解質含有組成物、全固体二次電池用シート及び全固体二次電池、並びに、無機固体電解質含有組成物、全固体二次電池用シート及び全固体二次電池の製造方法
WO2021060541A1 (fr) Composition comprenant un électrolyte solide inorganique, feuille pour batterie secondaire entièrement solide ainsi que procédé de fabrication de celle-ci, feuille d'électrode pour batterie secondaire entièrement solide, et batterie secondaire entièrement solide ainsi que procédé de fabrication de celle-ci
WO2021014852A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, feuille d'électrode pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille pour batteries secondaires entièrement solides et procédé de production de batterie secondaire entièrement solide
CN112470316A (zh) 固体电解质组合物、含固体电解质的片材、全固态二次电池用电极片及全固态二次电池、含固体电解质的片材及全固态二次电池的制造方法以及粒子状粘合剂的制造方法
WO2021166968A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batteries rechargeables tout-solide et procédé de production de batterie rechargeable tout-solide
WO2021157278A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batterie secondaire entièrement solide, batterie secondaire entièrement solide, et procédés de fabrication de feuille pour batterie secondaire entièrement solide et batterie secondaire entièrement solide
WO2021200497A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries rechargeables tout-solide, batterie rechargeable tout-solide, procédé de production de feuille pour batterie rechargeable tout-solide et procédé de production de batterie rechargeable tout-solide
WO2021039947A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille pour batteries secondaires entièrement solides et procédé de production de batterie secondaire entièrement solide
WO2020129802A1 (fr) Composition d'électrolyte solide, feuille contenant l'électrolyte solide, batterie secondaire entièrement solide, procédé de production de feuille contenant l'électrolyte solide, et procédé de production de batterie secondaire entièrement solide
WO2020067108A1 (fr) Composition pour électrodes négatives de batteries secondaires entièrement solides, feuille d'électrode négative pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, procédé de production de feuille d'électrode négative pour batteries secondaires entièrement solides, et procédé de production de batterie secondaire entièrement solide
WO2023054425A1 (fr) Composition d'électrode, feuille d'électrode pour batterie secondaire tout solide, batterie secondaire tout solide, et procédés de fabrication de composition d'électrode, de feuille d'électrode pour batterie secondaire tout solide, et de batterie secondaire tout solide
WO2021039946A1 (fr) Composition contenant un électrolyte solide inorganique, feuille de batterie tout solide secondaire, batteries tout solide secondaires, procédés de production de feuilles de batterie tout solide secondaire et batterie tout solide secondaire, et particules polymères composites
WO2021020031A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires entièrement solides, batterie secondaire entièrement solide, et procédé de production de feuille pour batteries secondaires entièrement solides ou batterie secondaire entièrement solide
WO2021193826A1 (fr) Composition contenant un électrolyte solide inorganique, feuille de batterie secondaire entièrement solide, batterie secondaire entièrement solide, et procédé de fabrication d'une feuille de batterie secondaire entièrement solide et d'une batterie secondaire entièrement solide
JP7266152B2 (ja) 無機固体電解質含有組成物、全固体二次電池用シート及び全固体二次電池、並びに、全固体二次電池用シート及び全固体二次電池の製造方法
WO2022202495A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour une batterie secondaire entièrement solide, batterie secondaire entièrement solide, procédé de production d'une feuille pour une batterie secondaire entièrement solide et procédé de production d'une batterie secondaire entièrement solide
WO2021060542A1 (fr) Composition comprenant un électrolyte solide inorganique, feuille pour batterie secondaire entièrement solide ainsi que procédé de fabrication de celle-ci, feuille d'électrode pour batterie secondaire entièrement solide, et batterie secondaire entièrement solide ainsi que procédé de fabrication de celle-ci
WO2023054455A1 (fr) Feuille pour électrode, batterie secondaire entièrement solide, et procédés de production de feuille pour électrode, feuille d'électrode et batterie secondaire entièrement solide
WO2022138752A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batterie secondaire entièrement solide, batterie secondaire entièrement solide, et méthode de production de feuille pour batterie secondaire entièrement solide et méthode de production de batterie secondaire entièrement solide
WO2022065477A1 (fr) Composition contenant un électrolyte solide inorganique, feuille pour batteries secondaires à l'état solide, batterie secondaire à l'état solide, et procédés de production de feuille pour batteries secondaires à l'état solide ou batterie secondaire à l'état solide
JP7096367B2 (ja) 固体電解質組成物、全固体二次電池用シート及び全固体二次電池、並びに、全固体二次電池用シート若しくは全固体二次電池の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21756319

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022501941

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21756319

Country of ref document: EP

Kind code of ref document: A1