WO2021134768A1 - Dispositif de formage - Google Patents

Dispositif de formage Download PDF

Info

Publication number
WO2021134768A1
WO2021134768A1 PCT/CN2020/070184 CN2020070184W WO2021134768A1 WO 2021134768 A1 WO2021134768 A1 WO 2021134768A1 CN 2020070184 W CN2020070184 W CN 2020070184W WO 2021134768 A1 WO2021134768 A1 WO 2021134768A1
Authority
WO
WIPO (PCT)
Prior art keywords
molding
nozzle
molding material
device system
printing
Prior art date
Application number
PCT/CN2020/070184
Other languages
English (en)
Chinese (zh)
Inventor
荆剑
李遂林
陶国强
Original Assignee
泰州鑫宇精工股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 泰州鑫宇精工股份有限公司 filed Critical 泰州鑫宇精工股份有限公司
Priority to CN202080086996.6A priority Critical patent/CN114829118A/zh
Priority to PCT/CN2020/070184 priority patent/WO2021134768A1/fr
Publication of WO2021134768A1 publication Critical patent/WO2021134768A1/fr

Abstract

La présente invention concerne un dispositif de formage. Le dispositif de formage comprend : un module de formage (110) pour déposer un matériau de formage afin de former une forme prédéfinie ; et un module de commande (140) pour commander le module de formage (110) afin d'effectuer une pose selon une trajectoire prédéfinie correspondant à la forme prédéfinie. Un premier matériau de formage appliqué à une région de formage solide (210) comprend une résine de pétrole et un matériau de base et la résine de pétrole peut améliorer la ténacité du premier matériau de formage.
PCT/CN2020/070184 2020-01-03 2020-01-03 Dispositif de formage WO2021134768A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202080086996.6A CN114829118A (zh) 2020-01-03 2020-01-03 一种成型装置
PCT/CN2020/070184 WO2021134768A1 (fr) 2020-01-03 2020-01-03 Dispositif de formage

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2020/070184 WO2021134768A1 (fr) 2020-01-03 2020-01-03 Dispositif de formage

Publications (1)

Publication Number Publication Date
WO2021134768A1 true WO2021134768A1 (fr) 2021-07-08

Family

ID=76686261

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/070184 WO2021134768A1 (fr) 2020-01-03 2020-01-03 Dispositif de formage

Country Status (2)

Country Link
CN (1) CN114829118A (fr)
WO (1) WO2021134768A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113968022A (zh) * 2021-11-22 2022-01-25 宁波大学科学技术学院 一种三维打印机的混合供料装置

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1799821A (zh) * 2006-01-16 2006-07-12 南京师范大学 采用逐层喷涂方式制作三维物体的方法
CN101561674A (zh) * 2009-05-22 2009-10-21 南京师范大学 多相材料零件的成型方法
CN103909655A (zh) * 2013-01-06 2014-07-09 北京国视国电科技有限公司 3d快速成型立体三维打印装置和工艺
CN105062090A (zh) * 2015-07-20 2015-11-18 福建省蓝天阳信息科技有限公司 一种3d打印机专用蜡线及其配方和制作工艺
WO2016154849A1 (fr) * 2015-03-30 2016-10-06 北京大学口腔医院 Tête de pulvérisation d'impression, imprimante en trois dimensions et procédé de commande
CN106915084A (zh) * 2017-03-07 2017-07-04 杭州杭景模型有限公司 3d打印机及其打印平台
CN107513428A (zh) * 2016-06-17 2017-12-26 中国石油化工股份有限公司 一种3d打印用蜡的生产方法
WO2018157148A1 (fr) * 2017-02-27 2018-08-30 Voxel8, Inc. Dispositifs d'impression 3d comprenant des buses de mélange
CN109070200A (zh) * 2016-03-03 2018-12-21 德仕托金属有限公司 使用金属构建材料的增材制造
CN209794572U (zh) * 2019-04-23 2019-12-17 锐力斯传动系统（苏州）有限公司 3d打印机用不粘喷嘴

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1799821A (zh) * 2006-01-16 2006-07-12 南京师范大学 采用逐层喷涂方式制作三维物体的方法
CN101561674A (zh) * 2009-05-22 2009-10-21 南京师范大学 多相材料零件的成型方法
CN103909655A (zh) * 2013-01-06 2014-07-09 北京国视国电科技有限公司 3d快速成型立体三维打印装置和工艺
WO2016154849A1 (fr) * 2015-03-30 2016-10-06 北京大学口腔医院 Tête de pulvérisation d'impression, imprimante en trois dimensions et procédé de commande
CN105062090A (zh) * 2015-07-20 2015-11-18 福建省蓝天阳信息科技有限公司 一种3d打印机专用蜡线及其配方和制作工艺
CN109070200A (zh) * 2016-03-03 2018-12-21 德仕托金属有限公司 使用金属构建材料的增材制造
CN107513428A (zh) * 2016-06-17 2017-12-26 中国石油化工股份有限公司 一种3d打印用蜡的生产方法
WO2018157148A1 (fr) * 2017-02-27 2018-08-30 Voxel8, Inc. Dispositifs d'impression 3d comprenant des buses de mélange
CN106915084A (zh) * 2017-03-07 2017-07-04 杭州杭景模型有限公司 3d打印机及其打印平台
CN209794572U (zh) * 2019-04-23 2019-12-17 锐力斯传动系统（苏州）有限公司 3d打印机用不粘喷嘴

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113968022A (zh) * 2021-11-22 2022-01-25 宁波大学科学技术学院 一种三维打印机的混合供料装置

Also Published As

Publication number Publication date
CN114829118A (zh) 2022-07-29

Similar Documents

Publication Publication Date Title
CN101158040B (zh) 同轴送粉装置
WO2021134768A1 (fr) Dispositif de formage
TWI596000B (zh) 立體列印裝置以及列印頭模組
CN104629161A (zh) 一种低熔点3d打印材料及其制备方法
CN103568154B (zh) 3d打印机的供料喉管及供料结构
WO2018228450A1 (fr) Procédé d'impression 3d
CN204109390U (zh) 一种3d打印机
CN110355993A (zh) 一种基于复合材料喷雾式3d打印装置及方法
CN106064477A (zh) 一种可快速更换3d打印喷头
CN101010182A (zh) 多层挤压件用挤压设备和用该设备制造多层挤压件的方法
CN106671455A (zh) 免丝印导光板在线生产工艺与生产设备
CN204604710U (zh) 塑料薄膜流延设备的风刀调节装置
CN115302768A (zh) 一种基于复合粘土支撑的3d打印方法及设备
CN202318887U (zh) 塑料管材定径套
CN102441976A (zh) 塑料管材挤出成型装置
CN210552909U (zh) 环形出片模具
CN206357646U (zh) 一种增材制造中收粉设备
CN203381193U (zh) 丝材熔接装置
CN108748772A (zh) 一种冷切粒系统
CN206751930U (zh) 用于激光熔覆的全方位同轴送粉嘴
CN102398037A (zh) 控制硬质合金喇叭状材料烧结变形的异形舟皿
CN204504221U (zh) 一种基于激光熔融的打印喷头装置
CN105538698A (zh) 一种3d打印机
CN113210568A (zh) 一种混合进料的双喷头3d打印机
CN109435241A (zh) 一种3d打印装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20910439

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20910439

Country of ref document: EP

Kind code of ref document: A1