WO2021131987A1 - 化粧料 - Google Patents

化粧料 Download PDF

Info

Publication number
WO2021131987A1
WO2021131987A1 PCT/JP2020/047045 JP2020047045W WO2021131987A1 WO 2021131987 A1 WO2021131987 A1 WO 2021131987A1 JP 2020047045 W JP2020047045 W JP 2020047045W WO 2021131987 A1 WO2021131987 A1 WO 2021131987A1
Authority
WO
WIPO (PCT)
Prior art keywords
iron oxide
cosmetic
color
oil
present
Prior art date
Application number
PCT/JP2020/047045
Other languages
English (en)
French (fr)
Inventor
祐輔 中野
Original Assignee
株式会社 資生堂
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社 資生堂 filed Critical 株式会社 資生堂
Priority to US17/789,164 priority Critical patent/US20230068215A1/en
Priority to EP20908009.2A priority patent/EP4082618A4/en
Priority to CN202080090188.7A priority patent/CN114901239A/zh
Publication of WO2021131987A1 publication Critical patent/WO2021131987A1/ja

Abstract

本発明は、高彩度でありながら、退色性にも優れた化粧料を提供することを目的とする。本発明はアルミニウムを１５モル％以上４０モル％以下含むα－酸化鉄（ＩＩＩ）を含有する化粧料に関する。

Description

化粧料
　本発明は、色材を含む化粧料に関する。さらに詳しくは、高彩度で退色しにくい化粧料に関する。
　色材は、化粧料において彩色したり被覆力を付与する目的で配合され、皮膚や毛髪に好みの色彩を与え、健康で魅力的な容貌をつくる役割を担う。
　化粧料に配合される色材には、主に有機合成色素（タール色素）、無機顔料、天然色素が含まれる。無機顔料としては、金属の酸化物、水酸化物、硫化物、ケイ酸塩等が用いられている。
　有機合成色素は、一般的に鮮やかな発色性が期待できるが、光、熱、水分等によって分解し退色しやすいという欠点がある。一方、無機顔料は一般的に耐光性、耐熱性が良好であり、溶媒やその他の薬品類と接しても性質が変わらないものが多いことから、退色性に優れている反面、鮮やかさの点で有機合成色素に劣るとされている（非特許文献１）。
　したがって、鮮やかな発色性と優れた退色性を兼ね備えた化粧料の開発が望まれていた。
　ここで、アルミニウムを固溶した酸化鉄系赤色顔料が開発されている（特許文献１、特許文献２、非特許文献２）。
日本国特開２００４－４３２０８号公報 国際公開第２０１９／２４５０４６号
「新化粧品学（第２版）」、光井武夫編、南山堂、２００１年 橋本英樹，"超高彩度酸化鉄系赤色顔料"，［ｏｎｌｉｎｅ］，平成３０年１２月４日，新技術説明会［令和１年１１月１９日検索］，インターネット<URL:https://shingi.jst.go.jp/var/rev0/0000/7855/2018_kogakuin_2.pdf>
　特許文献１、特許文献２および非特許文献２には、アルミニウムを固溶した酸化鉄系赤色顔料が化粧料の色材として有用である旨の記載はない。
　本発明は、高彩度でありながら、退色性にも優れた化粧料を提供することを目的とする。
　本発明者等は、前記の課題を解決すべく鋭意検討を重ねた結果、赤色を呈する無機顔料として知られているベンガラ（α－酸化鉄（ＩＩＩ））において、特定量のアルミニウムを含む酸化鉄を用いることで、従来のベンガラにはない色鮮やかさを呈することができることを見出し、本発明を完成するに至った。
　すなわち本発明は、下記化粧料に関する。
［１］アルミニウムを１５モル％以上４０モル％以下含むα－酸化鉄（ＩＩＩ）を含有する化粧料。
［２］前記α－酸化鉄（ＩＩＩ）が疎水処理されている、［１］に記載の化粧料。
［３］前記α－酸化鉄（ＩＩＩ）を単一色材として配合したとき、明度（Ｌ）が３９．５以上である、［１］または［２］に記載の化粧料。
　本発明によれば、退色性に優れ、かつ、鮮やかな発色性を実現できる化粧料を提供できる。
（色材）
　本発明に係る化粧料は、色材として、アルミニウムを１５モル％以上４０モル％以下含むα－酸化鉄（ＩＩＩ）（以下、「本発明における酸化鉄」とも記載する。）を含有する。
　酸化鉄がアルミニウムを１５モル％以上含むことで、無機顔料が有する優れた退色性を保持したまま、従来のα－酸化鉄（ＩＩＩ）よりも鮮やかな発色が可能となる。その理由としては、ヘマタイト１次粒子の凝集空間が広がり、光の反射波長が変化したことであることが推測される。また、アルミニウムは酸化鉄結晶構造中に適度に分散してドープされていると推測される。
　アルミニウムの含有量は、高彩度の観点から好ましくは１５モル％以上、より好ましくは２０モル％以上であり、また、結晶形状維持の観点から好ましくは５０モル％以下、より好ましくは４０モル％以下である。
　また、本発明における酸化鉄は、平均粒径が好ましくは０．３μｍ～５μｍであり、平均厚さが好ましくは０．１５μｍ～２．５μｍであり、結晶構造が好ましくはコイン状構造である。なおコイン状構造とは、円柱状であり、直径が厚みより大きい形状を意味する。
　酸化鉄の結晶構造がコイン状構造であることで分散性に優れ、例えばファンデーションに配合された場合に色じまが発生しにくい。
　本発明における化粧料における酸化鉄の含有量としては、外観色発現の観点から好ましくは０．０５質量％以上、より好ましくは０．０７５質量％以上であり、また、隠ぺい力の観点から好ましくは２５質量％以下、より好ましくは２０質量％以下である。
　本発明における酸化鉄としては、例えば、橋本英樹，“超高彩度酸化鉄系赤色顔料”，［ｏｎｌｉｎｅ］，平成３０年１２月４日，新技術説明会（非特許文献２）および国際公開第２０１９／２４５０４６号（特許文献２）等に記載されているものを使用できる。
　本発明における酸化鉄はさらに、油性基材に配合する際は疎水処理（表面処理）がなされていることが好ましい。かかる処理をすることで、油性基材中の分散性が上昇し、彩度がさらに向上する。
　疎水処理としては疎水性を保つ処理であればよく、例えばパーフルオロオクチルトリエトキシシラン処理、メチコン処理、ジメチコン処理、ハイドロゲンジメチコン処理、（アクリル酸アルキル／ジメチコン）コポリマー処理、トリエトキシカプリリルシラン処理（ＯＴＳ処理）、ステアリン酸マグネシウム処理などがある。
　本発明の化粧料には、上記必須成分に加えて、化粧料に通常配合される他の成分を、発明の効果を阻害しない範囲で配合することができる。
　他の成分には、上記特定の酸化鉄以外の他の色材、油性成分、油性基材を構成する成分、及びその他の任意成分が含まれる。
（他の色材）
　他の色材としては、化粧料の用途に応じて化粧品用色材として公知の他の色材を含有することができる。
　他の色材としては、染料、レーキ及び有機顔料から選択される有機合成色素、天然色素、ならびに、体質顔料、着色顔料（ただし上記特定の酸化鉄は除く。）、及び白色顔料から選択される無機顔料等、が挙げられ、これらの中から１種以上を組み合わせて用いることができる。
（油性成分）
　本発明の化粧料は、化粧料に通常配合される油性成分を含有することができる。配合可能な油分として以下の固形油分及び液状油分が例示できるが、これらに限定されるものではない。
　固形油分としては、固体油脂、ロウ類、炭化水素、高級アルコールが挙げられる。例えば、モクロウ、カカオ脂、硬化ヒマシ油等の固体油脂；カルナウバロウ、ミツロウ、キャンデリラロウ、ホホバ（ｊｏｊｏｂａ）ロウ等のロウ類：ポリエチレンワックス、パラフィンワックス、セレシン、マイクロクリスタリンワックス等の炭化水素系ワックス類；ベヘニルアルコール、セタノール、バチルアルコール等の高級アルコール；シリコンワックス等が挙げられる。
　液状油分としては、オリーブ油、アボカド油、ツバキ油、マカデミアナッツ油、月見草油、ホホバ油、ナタネ油、卵黄油、ゴマ油、ヒマシ油、サフラワー油、綿実油、大豆油、茶実油、コメヌカ油、胚芽油等の液体油脂類；スクワラン、流動パラフィン等の炭化水素油；イソステアリン酸イソセチル、トリイソステアリン酸ポリグリセリル－２、２－エチルヘキサン酸セチル、２ヘプチルウンデシルパルミテート、アジピン酸ジイソブチル、セバシン酸２－ヘキシルデシル、イソプロピルミリステート、２－オクチルドデシルオレエート、リンゴ酸ジイソステアリル、ジ－２－エチルヘキサン酸エチレングリコール、トリ－２－ヘプチルウンデカン酸グリセライド、グリセリルジイソステアレート、グリセリルトリイソステアレート、トリオクタン酸グリセリン、トリイソパルミチン酸グリセリン、トリ－２－エチルヘキサン酸トリメチロールプロパン、トリ－２－エチルヘキサン酸グリセリル、テトラ－２－エチルヘキサン酸ペンタエリスリトール等のエステル油類；ジメチルポリシロキサン、メチルフェニルポリシロキサン（ジフェニルシロキシフェニルトリメチコン）等の鎖状シリコーン油；オクタメチルシクロテトラシロキサン、デカメチルシクロペンタシロキサン等の環状シリコーン油；トリグリセリン、フッ素変性油等が挙げられる。
（油性基材を構成する成分）
　油性基材を構成する成分として、油分増粘剤又はゲル化剤を挙げることができる。
　油分増粘剤（ゲル化剤）としては、デキストリン脂肪酸エステル、グリセリン脂肪酸エステル、有機変性粘土鉱物等が例示できる。デキストリン脂肪酸エステルには、例えば、ミリスチン酸デキストリン、パルミチン酸デキストリン、（パルミチン酸／２－エチルヘキサン酸）デキストリン等が含まれる。グリセリン脂肪酸エステルには、例えば、ベヘン酸グリセリル、オクタステアリン酸グリセリル、エイコ酸グリセリル等が含まれる。
（他の任意成分）
　他の任意成分には水、紫外線吸収剤、界面活性剤、酸化防止剤、香料、防腐剤、多価アルコール、低級アルコール、揮発油、無機粉末、有機粉末、及び各種活性成分等が含まれる。
　本発明の化粧料は、従来の化粧料に汎用されている方法に従って製造することができる。即ち、上記特定の酸化鉄と任意成分とを混合し、加熱しながらホモミキサー等を用いて攪拌混合し、型に流し込んで冷却することにより製造できる。
　本発明の化粧料は、上記したように、アルミニウムを多く含む特有の酸化鉄（ＩＩＩ）を色材として含むことで高彩度を実現できる。
　色の数値化指標としては、明度をＬ＊、色度をａ＊、ｂ＊で示したＬ＊ａ＊ｂ＊色空間（ＪＩＳ　Ｚ８７２９－１９９４）が知られており、明度Ｌ＊が大きいほど色鮮やかであるとされる。
　本発明の化粧料は、本発明における特定の酸化鉄を単一色材として配合した際の明度Ｌ＊が好ましくは３９．５以上、より好ましくは４０以上である。
　本発明の化粧料は、特定の酸化鉄を含むことで鮮やかな発色性と優れた退色性を兼ね備えたものである。よって、本発明の化粧料は、彩色を目的とするメーキャップ化粧料に特に適しており、メーキャップ化粧料としては、例えば口紅、グロス等の口唇化粧料、アイシャドウ、チーク（頬紅）等のポイントメーキャップ化粧料、ファンデーション、コンシーラー、日焼け止めクリーム等のベースメーキャップ化粧料等が挙げられる。
　以下に実施例を挙げて本発明を更に具体的に説明するが、本発明はこれらによって限定されるものではない。なお、特に断りのない限り、配合量は全量に対する質量％を表す。
（口紅化粧料の製造）
　下記の表１に掲げた組成で口紅を製造した。
　各例の口紅の外観色について、ベンチトップ積分球分光色測計（Ｘ－ｒｉｔｅ社）を用いて明度（Ｌ）、色度（ａ）、（ｂ）を測定した。
　また、各例の口紅をパネラーの腕に塗布し、塗布色の発色を目視で確認した。なお、アルミニウムを１５モル％以上４０モル％以下含むα－酸化鉄（ＩＩＩ）の中で、最も塗布色が鮮やかだった３０モル％のアルミニウムを配合したα－酸化鉄（ＩＩＩ）を単独で含む実施例３を塗布色評価の基準として、その他の実施例を評価した。
　口紅の退色性について、（１）３０℃の雰囲気下で、各口紅にキセノンを５０時間照射し、照射前後での色差、（２）２５℃の雰囲気で、各口紅に蛍光灯を３００時間照射し、照射前後での色差、（３）４０℃、湿度９０％の雰囲気下に各口紅を静置し、４週間後の色差によりそれぞれ評価した。
Figure JPOXMLDOC01-appb-T000001
　外観色評価の結果から、特定量のアルミニウムを含む酸化鉄を含む実施例１～４の口紅は、明度（Ｌ）が４０以上であり、発色性に優れていることが分かる。
　また、塗布色評価の結果から、アルミニウムを含有しない従来のベンガラを配合した比較例１の口紅や、アルミニウム含有量が小さい酸化鉄を色材として用いた比較例２の口紅が赤褐色を呈しているのに対し、特定量のアルミニウムを含む酸化鉄を配合した実施例１～４の口紅は、有機色材を用いた比較例３～５の口紅と同程度の鮮やかな橙色を呈した。
　また、退色性については、有機色材を用いた比較例３～５の口紅では色差ΔＥがいずれの試験においても大きく変化したが、α－酸化鉄を用いた実施例１～４の口紅は色差の変化は小さかった。
（処方例）
　ファンデーション、コンシーラーの処方例を下記に示す。
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。本出願は２０１９年１２月２７日出願の日本特許出願（特願２０１９－２３９１００）に基づくものであり、その内容はここに参照として取り込まれる。

Claims (3)

  1. 　アルミニウムを１５モル％以上４０モル％以下含むα－酸化鉄（ＩＩＩ）を含有する化粧料。
  2. 　前記α－酸化鉄（ＩＩＩ）が疎水処理されている、請求項１に記載の化粧料。
  3. 　前記α－酸化鉄（ＩＩＩ）を単一色材として配合したとき、明度（Ｌ）が３９．５以上である、請求項１または２に記載の化粧料。
PCT/JP2020/047045 2019-12-27 2020-12-16 化粧料 WO2021131987A1 (ja)