WO2021130091A1 - Composition de résine de polyuréthane et produit moulé en résine de polyuréthane - Google Patents

Composition de résine de polyuréthane et produit moulé en résine de polyuréthane Download PDF

Info

Publication number
WO2021130091A1
WO2021130091A1 PCT/EP2020/086604 EP2020086604W WO2021130091A1 WO 2021130091 A1 WO2021130091 A1 WO 2021130091A1 EP 2020086604 W EP2020086604 W EP 2020086604W WO 2021130091 A1 WO2021130091 A1 WO 2021130091A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
polyurethane resin
group
resin composition
polyol component
Prior art date
Application number
PCT/EP2020/086604
Other languages
English (en)
Inventor
Tohru Matsumura
Shoko Aoki
Original Assignee
Covestro Intellectual Property Gmbh & Co. Kg
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2019232568A external-priority patent/JP2021100995A/ja
Application filed by Covestro Intellectual Property Gmbh & Co. Kg filed Critical Covestro Intellectual Property Gmbh & Co. Kg
Priority to EP20830163.0A priority Critical patent/EP4081566A1/fr
Publication of WO2021130091A1 publication Critical patent/WO2021130091A1/fr

Abstract

Le but de l'invention est de fournir une composition capable de former une mousse de polyuréthane présentant d'excellentes propriétés de remplissage, ainsi que de remarquables propriétés de surface et une très grande résistance. L'invention concerne une composition de résine de polyuréthane contenant un composant polyol et un composant polyisocyanate, la composition de résine de polyuréthane contenant un composé (A) en tant que composant polyol ou que composant autre que le composant polyol, le composé (A) présente un poids moléculaire égal ou inférieur à 220, comporte au moins deux groupes réactifs capables de réagir avec un isocyanate dans une molécule, ainsi qu'un groupe réactif présentant une activité réactionnelle avec un groupe isocyanate qui est supérieure à l'activité réactionnelle avec un groupe isocyanate des autres groupes réactifs du composé (A), et le rapport entre l'indice d'hydroxyle du composé (A) et l'indice d'hydroxyle du composant polyol est égal ou supérieur à 1,2, à condition que lorsque le composé (A) fait partie du composant polyol, la proposition « l'indice d'hydroxyle du composant polyol » se réfère à l'indice d'hydroxyle du composant polyol autre que le composé (A).
PCT/EP2020/086604 2019-12-24 2020-12-17 Composition de résine de polyuréthane et produit moulé en résine de polyuréthane WO2021130091A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP20830163.0A EP4081566A1 (fr) 2019-12-24 2020-12-17 Composition de résine de polyuréthane et produit moulé en résine de polyuréthane

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2019232568A JP2021100995A (ja) 2019-12-24 2019-12-24 ポリウレタン樹脂組成物及びポリウレタン樹脂成形物
JP2019-232568 2019-12-24
EP20161049.0 2020-03-04
EP20161049 2020-03-04

Publications (1)

Publication Number Publication Date
WO2021130091A1 true WO2021130091A1 (fr) 2021-07-01

Family

ID=74104096

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2020/086604 WO2021130091A1 (fr) 2019-12-24 2020-12-17 Composition de résine de polyuréthane et produit moulé en résine de polyuréthane

Country Status (2)

Country Link
EP (1) EP4081566A1 (fr)
WO (1) WO2021130091A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4085140A (en) * 1976-09-22 1978-04-18 Imperial Chemical Industries Limited Carbodiimides
JPH0597954A (ja) 1991-05-10 1993-04-20 Kao Corp 硬質ポリウレタンフオームの製造方法
JPH06322099A (ja) 1993-04-22 1994-11-22 Nisso Maruzen Chem Kk 低粘度ポリエーテル
JP2009067995A (ja) 2007-08-21 2009-04-02 Asahi Glass Co Ltd 硬質発泡合成樹脂の製造方法
US8541478B2 (en) * 2009-05-21 2013-09-24 Huntsman International Llc Rigid polyurethane foam and system and method for making the same
EP3545016A1 (fr) * 2016-11-25 2019-10-02 Covestro Deutschland AG Procédé de production d'une mousse de polyuréthanne rigide à alvéoles ouverts
US20190367667A1 (en) * 2017-02-22 2019-12-05 Mitsui Chemicals Inc. Polyurethane elastomer foam material, polyurethane elastomer foam, and method for producing polyurethane elastomer foam

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4085140A (en) * 1976-09-22 1978-04-18 Imperial Chemical Industries Limited Carbodiimides
JPH0597954A (ja) 1991-05-10 1993-04-20 Kao Corp 硬質ポリウレタンフオームの製造方法
JPH06322099A (ja) 1993-04-22 1994-11-22 Nisso Maruzen Chem Kk 低粘度ポリエーテル
JP2009067995A (ja) 2007-08-21 2009-04-02 Asahi Glass Co Ltd 硬質発泡合成樹脂の製造方法
US8541478B2 (en) * 2009-05-21 2013-09-24 Huntsman International Llc Rigid polyurethane foam and system and method for making the same
EP3545016A1 (fr) * 2016-11-25 2019-10-02 Covestro Deutschland AG Procédé de production d'une mousse de polyuréthanne rigide à alvéoles ouverts
US20190367667A1 (en) * 2017-02-22 2019-12-05 Mitsui Chemicals Inc. Polyurethane elastomer foam material, polyurethane elastomer foam, and method for producing polyurethane elastomer foam

Also Published As

Publication number Publication date
EP4081566A1 (fr) 2022-11-02

Similar Documents

Publication Publication Date Title
US10450402B2 (en) Polyester polyol-containing polyurethane systems having improved hydrolytic stability
EP2820057B1 (fr) Polyéther-ester-polyols et leur utilisation pour la fabrication de mousses rigides de polyuréthane
KR20070085327A (ko) 경질 폴리우레탄 발포체의 제조 방법
CA3003315C (fr) Polyetheresters et leur utilisation pour produire des mousses dures de polyurethane
US20110319572A1 (en) Polyols from hppo and polyurethane products made therefrom
JP3948014B2 (ja) 硬質ポリイソシアヌレートフォームの製造方法
WO2022122360A1 (fr) Production de mousse de polyuréthane
US11124595B2 (en) Polyol blends useful for producing viscoelastic foam
WO2021130091A1 (fr) Composition de résine de polyuréthane et produit moulé en résine de polyuréthane
EP3906267A1 (fr) Composition permettant de former une mousse de polyuréthane
WO2022184543A1 (fr) Production de mousse de polyuréthane
JP2021100995A (ja) ポリウレタン樹脂組成物及びポリウレタン樹脂成形物
US11738487B2 (en) Processes for making molded flexible foams and flexible foams produced thereby
US20220235168A1 (en) Processes for making molded flexible foams and flexible foams produced thereby
US20220315693A1 (en) Formulated polyol compositons
JP2023039017A (ja) 制振性の良好なポリウレタン形成原料組成物
WO2023232528A1 (fr) Composition de matières premières pour mousse d&#39;isocyanurate rigide, mousse d&#39;isocyanurate rigide et matériau absorbant le son
JP2023540151A (ja) ポリウレタンフォーム形成用組成物
JP2024056519A (ja) ポリイソシアヌレートフォーム原料用組成物及びポリイソシアヌレートフォーム
WO2021130092A1 (fr) Composition pour former une mousse de polyuréthane rigide ayant une perméabilité à l&#39;air et mousse de polyuréthane rigide
JP2021098813A (ja) ポリウレタンフォーム形成用組成物
EP3957669A1 (fr) Production de mousse de polyuréthane
JP5648468B2 (ja) ポリオール組成物、及びそのポリオール組成物を用いた硬質ポリウレタンフォームの製造方法
JP2023038106A (ja) ポリウレタンフォーム用組成物及びその使用
JP2008260841A (ja) 独立気泡を有する硬質ポリウレタンフォーム製造用ポリイソシアネート組成物および該組成物を用いた独立気泡を有する硬質ポリウレタンフォームの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20830163

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2020830163

Country of ref document: EP

Effective date: 20220725

NENP Non-entry into the national phase