WO2021037313A1 - Procédé de production de noyaux et de moules en fonte au sable - Google Patents

Procédé de production de noyaux et de moules en fonte au sable Download PDF

Info

Publication number
WO2021037313A1
WO2021037313A1 PCT/DE2020/100761 DE2020100761W WO2021037313A1 WO 2021037313 A1 WO2021037313 A1 WO 2021037313A1 DE 2020100761 W DE2020100761 W DE 2020100761W WO 2021037313 A1 WO2021037313 A1 WO 2021037313A1
Authority
WO
WIPO (PCT)
Prior art keywords
molding material
binder
component
sand
catalysts
Prior art date
Application number
PCT/DE2020/100761
Other languages
German (de)
English (en)
Inventor
Sandra ESCHRICH
Daniel HOLSTEIN
Thomas GALLERT
Tina HERTEL
Jörg GEBEL
Robin GOLDACKER
Original Assignee
Bindur Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bindur Gmbh filed Critical Bindur Gmbh
Priority to EP20771195.3A priority Critical patent/EP4021662A1/fr
Publication of WO2021037313A1 publication Critical patent/WO2021037313A1/fr

Abstract

L'invention concerne un procédé de production de noyaux et de moules en fonte au sable, comprenant au moins les étapes suivantes : A) la fourniture d'un outil de moulage ayant une cavité reproduisant la partie moulée, B) le mélange du matériau de moulage thermodurcissable, le matériau de moulage étant au moins composé des constituants suivants : un liant à deux constituants, exempt de phénol et de formaldéhyde, à base de polyuréthane, contenant un constituant de résine sous forme de mélange d'au moins deux composés qui ont une activité hydrogène par rapport à des isocyanates contenant des groupes hydroxyle et/ou mercapto et/ou amino et/ou carbamide ayant une fonctionnalité OH, SH et NH de 1,5 à 8 et des poids équivalents de 9 à 2 000 g/val des constituants individuels et une fonctionnalité H moyenne de 1,8 à 4,0 et un poids équivalent moyen de 90 à 200 g/val des constituants de résine et un constituant durcisseur contenant un ou plusieurs diisocyanates ou polyisocyanates, un ou plusieurs catalyseurs activables thermiquement ayant des températures d'activation comprises entre 50 et 170 °C et contenant des bases de Brönsted favorisant la réaction de polyuréthane et/ou des acides de Lewis et leurs agents de blocage associés, et un ou plusieurs matériaux de charge coulants résistants au feu, C) l'introduction du matériau de moulage dans l'outil de moulage, D) le durcissement du matériau de moulage thermodurcissable dans l'outil de moulage à l'aide d'un procédé en boîte chaude ou d'un procédé à l'air chaud avec l'outil de moulage chauffant ou l'air chaud à des températures comprises entre 90 et 170 °C, de préférence entre 100 et 130 °C, et E) le retrait de la pièce moulée produite de l'outil de moulage.
PCT/DE2020/100761 2019-08-30 2020-08-27 Procédé de production de noyaux et de moules en fonte au sable WO2021037313A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP20771195.3A EP4021662A1 (fr) 2019-08-30 2020-08-27 Procédé de production de noyaux et de moules en fonte au sable

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102019123374.7A DE102019123374A1 (de) 2019-08-30 2019-08-30 Verfahren zur Herstellung von Kernen und Formen im Sandformverfahren
DE102019123374.7 2019-08-30

Publications (1)

Publication Number Publication Date
WO2021037313A1 true WO2021037313A1 (fr) 2021-03-04

Family

ID=72470133

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/DE2020/100761 WO2021037313A1 (fr) 2019-08-30 2020-08-27 Procédé de production de noyaux et de moules en fonte au sable

Country Status (3)

Country Link
EP (1) EP4021662A1 (fr)
DE (1) DE102019123374A1 (fr)
WO (1) WO2021037313A1 (fr)

Citations (40)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2800487A (en) 1952-12-31 1957-07-23 Universal Oil Prod Co Polyoxyalkylene substituted heterocyclic amines and their ammonium salt derivatives
US2891025A (en) 1954-08-30 1959-06-16 American Cyanamid Co Copolymer of acrylonitrile and a quaternary imidazolium compound, method of making same, and a spinning solution thereof
GB876493A (en) 1957-05-03 1961-09-06 Leicester Lovell & Company Ltd Improvements in or relating to the preparation of sand for moulding
US3010963A (en) 1959-05-21 1961-11-28 Houdry Process Corp Quaternary hydroxyalkyl tertiary heterocyclic amine bases and salts
US3409579A (en) 1966-08-01 1968-11-05 Ashland Oil Inc Foundry binder composition comprising benzylic ether resin, polyisocyanate, and tertiary amine
DE1570203A1 (de) 1965-04-24 1969-08-07 Albertuswerke Gmbh Giessereisandbindemittel
DE1928475A1 (de) 1968-06-04 1969-12-11 Bridgestone Tire Co Ltd Verfahren zum Verbinden eines Polyester-Fasermaterials mit einem Kautschuk oder Gummi
DE1959023A1 (de) 1969-11-25 1971-05-27 Cobomat Apparatebau Gmbh Verfahren und Vorrichtung zur Zufuehrung des Katalysators bei der Herstellung von Kernen nach dem Cold-box-Verfahren
DE2162137A1 (de) 1971-12-15 1973-06-20 Michel Horst Werner Verfahren und geraet zum aushaerten von sandformen und kernen fuer giessereizwecke
DE1569023C3 (de) 1965-02-13 1981-08-20 Hüttenes-Albertus Chemische Werke GmbH, 4000 Düsseldorf Bindemittel für das Hot-Box-Verfahren
DE2404739C2 (de) 1974-02-01 1982-04-22 Bayer Ag, 5090 Leverkusen Verfahren zur Herstellung von Filmen und Überzügen
DE3032592C2 (de) 1980-08-28 1982-12-16 Hüttenes-Albertus Chemische Werke GmbH, 4000 Düsseldorf Inhibitor für Formstoffmischungen, dessen Herstellung und dessen Verwendung
US4678020A (en) 1984-12-22 1987-07-07 Bcira Curing foundry moulds and cores
WO1988008763A1 (fr) 1987-05-08 1988-11-17 Ashland Oil, Inc. Procede de boite a noyau chauffe permettant de preparer des formes de fonderie
DE3738902A1 (de) 1987-11-17 1989-05-24 Ruetgerswerke Ag Hitzehaertendes bindemittel und seine verwendung
EP0423780A2 (fr) 1989-10-20 1991-04-24 GVT- GIESSEREI VERFAHRENS-TECHNIK GmbH Nouvelle liant résineux organique durcissant à chaud pour sable de fonderie
WO1995029007A1 (fr) 1994-04-20 1995-11-02 Ashland Inc. Utilisation d'un systeme de catalyseur a base d'etain bloque
WO1995032824A1 (fr) 1994-05-27 1995-12-07 Eos Gmbh Electro Optical Systems Procede s'utilisant en fonderie
DE10031954A1 (de) 2000-06-30 2002-02-21 Ashland Suedchemie Kernfest Heiss härtendes Bindemittelsystem auf der Basis nachwachsender Rohstoffe
DE69331286T2 (de) * 1992-09-08 2002-07-18 Ashland Oil Inc Giessereimischung mit polyetherpolyol und ihre verwendung
DE10256953A1 (de) 2002-12-05 2004-06-24 Ashland-Südchemie-Kernfest GmbH Heißhärtendes Bindemittel auf Polyurethanbasis
DE69921284T2 (de) 1999-01-05 2005-02-24 General Electric Co. Verfahren zur Herstellung von Polyurethanschaumstoffen
DE69533438T2 (de) 1994-03-25 2005-09-15 Ashland Inc., Columbus Wärmehärtbare Gießereibindemittelsysteme
DE69926577T2 (de) 1998-09-21 2006-06-08 Tosoh Corp., Shinnanyo Katalysator für Polyurethanherstellung
US7125914B2 (en) 2003-09-18 2006-10-24 Ashland Licensing And Intellectual Property Llc Heat-cured furan binder system
DE202006018044U1 (de) 2006-11-28 2007-01-18 Hydro Aluminium Mandl&Berger Ges. M.B.H. Einrichtung zum Beheizen eines Gasstroms und Vorrichtung zum Herstellen von Gießkernen oder Gießformteilen
EP1990387A1 (fr) 2007-05-11 2008-11-12 Sika Technology AG Corps de couche composite lié par de la matière collante transdermique tout comme procédé de collage de plastifiants comprenant du plastique
DE102007027577A1 (de) 2007-06-12 2008-12-18 Minelco Gmbh Formstoffmischung, Formling für Gießereizwecke und Verfahren zur Herstellung eines Formlings
WO2009080738A1 (fr) 2007-12-21 2009-07-02 Sika Technology Ag Compositions durcissables à dégagement gazeux réduit
DE102008021980A1 (de) * 2008-05-02 2009-11-05 Bayer Materialscience Ag Neue Katalysatoren und deren Einsatz bei der Herstellung von Polyurethanen
DE202007019185U1 (de) 2006-10-19 2011-03-31 Ashland-Südchemie-Kernfest GmbH Phosphorhaltige Formstoffmischung zur Herstellung von Giessformen für die Metallverarbeitung
WO2011095440A1 (fr) 2010-02-02 2011-08-11 Bayer Materialscience Ag Produits de polyaddition de polyisocyanate, procédé pour leur production et leur utilisation
WO2012080226A1 (fr) 2010-12-16 2012-06-21 Bayer Materialscience Ag Produits de polyaddition de polyisocyanate, leur procédé de fabrication et leur utilisation
WO2014040922A1 (fr) 2012-09-11 2014-03-20 Sika Technology Ag Composition de polyuréthane bicomposants
DE102014110189A1 (de) 2014-07-18 2016-01-21 Ask Chemicals Gmbh CO-Katalysatoren für Polyurethan-Coldbox-Bindemittel
DE102015118428A1 (de) 2015-10-28 2017-05-04 Purinvent System Gmbh Phenol-Formaldehydharz-freie Bindemittel für Gießerei-Formsande
WO2017149031A1 (fr) 2016-03-04 2017-09-08 Covestro Deutschland Ag Procédé pour la fabrication de composants composites fibreux
DE112016006377T5 (de) 2016-03-07 2018-10-18 Suzhou Mingzhi Technology Co., Ltd Kernfertigungsmaschine mit integrierter Mikrowellen-Aushärtungsfunktion
EP2864435B1 (fr) 2012-06-21 2019-04-10 PRC-Desoto International, Inc. Compositions de polymère contenant du soufre, catalysées par une amine, durcissables à l'humidité
WO2019081581A1 (fr) 2017-10-24 2019-05-02 Sika Technology Ag Composition de résine époxyde thermodurcissable à haute stabilité au stockage

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4370463A (en) * 1978-06-14 1983-01-25 Ashland Oil, Inc. Process for no-bake foundry application utilizing polyurethanes based on amine polyols
DE69412231T2 (de) * 1993-09-22 1998-12-10 Ashland Oil Inc Polyurethan-reaktionssystem mit blockierter katalysatorkombination

Patent Citations (41)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2800487A (en) 1952-12-31 1957-07-23 Universal Oil Prod Co Polyoxyalkylene substituted heterocyclic amines and their ammonium salt derivatives
US2891025A (en) 1954-08-30 1959-06-16 American Cyanamid Co Copolymer of acrylonitrile and a quaternary imidazolium compound, method of making same, and a spinning solution thereof
GB876493A (en) 1957-05-03 1961-09-06 Leicester Lovell & Company Ltd Improvements in or relating to the preparation of sand for moulding
US3010963A (en) 1959-05-21 1961-11-28 Houdry Process Corp Quaternary hydroxyalkyl tertiary heterocyclic amine bases and salts
DE1569023C3 (de) 1965-02-13 1981-08-20 Hüttenes-Albertus Chemische Werke GmbH, 4000 Düsseldorf Bindemittel für das Hot-Box-Verfahren
DE1570203A1 (de) 1965-04-24 1969-08-07 Albertuswerke Gmbh Giessereisandbindemittel
US3409579A (en) 1966-08-01 1968-11-05 Ashland Oil Inc Foundry binder composition comprising benzylic ether resin, polyisocyanate, and tertiary amine
DE1928475A1 (de) 1968-06-04 1969-12-11 Bridgestone Tire Co Ltd Verfahren zum Verbinden eines Polyester-Fasermaterials mit einem Kautschuk oder Gummi
DE1959023A1 (de) 1969-11-25 1971-05-27 Cobomat Apparatebau Gmbh Verfahren und Vorrichtung zur Zufuehrung des Katalysators bei der Herstellung von Kernen nach dem Cold-box-Verfahren
DE2162137A1 (de) 1971-12-15 1973-06-20 Michel Horst Werner Verfahren und geraet zum aushaerten von sandformen und kernen fuer giessereizwecke
DE2404739C2 (de) 1974-02-01 1982-04-22 Bayer Ag, 5090 Leverkusen Verfahren zur Herstellung von Filmen und Überzügen
DE3032592C2 (de) 1980-08-28 1982-12-16 Hüttenes-Albertus Chemische Werke GmbH, 4000 Düsseldorf Inhibitor für Formstoffmischungen, dessen Herstellung und dessen Verwendung
US4678020A (en) 1984-12-22 1987-07-07 Bcira Curing foundry moulds and cores
WO1988008763A1 (fr) 1987-05-08 1988-11-17 Ashland Oil, Inc. Procede de boite a noyau chauffe permettant de preparer des formes de fonderie
DE3738902A1 (de) 1987-11-17 1989-05-24 Ruetgerswerke Ag Hitzehaertendes bindemittel und seine verwendung
EP0423780A2 (fr) 1989-10-20 1991-04-24 GVT- GIESSEREI VERFAHRENS-TECHNIK GmbH Nouvelle liant résineux organique durcissant à chaud pour sable de fonderie
DE69331286T2 (de) * 1992-09-08 2002-07-18 Ashland Oil Inc Giessereimischung mit polyetherpolyol und ihre verwendung
DE69533438T2 (de) 1994-03-25 2005-09-15 Ashland Inc., Columbus Wärmehärtbare Gießereibindemittelsysteme
WO1995029007A1 (fr) 1994-04-20 1995-11-02 Ashland Inc. Utilisation d'un systeme de catalyseur a base d'etain bloque
WO1995032824A1 (fr) 1994-05-27 1995-12-07 Eos Gmbh Electro Optical Systems Procede s'utilisant en fonderie
DE69926577T2 (de) 1998-09-21 2006-06-08 Tosoh Corp., Shinnanyo Katalysator für Polyurethanherstellung
DE69921284T2 (de) 1999-01-05 2005-02-24 General Electric Co. Verfahren zur Herstellung von Polyurethanschaumstoffen
DE10031954A1 (de) 2000-06-30 2002-02-21 Ashland Suedchemie Kernfest Heiss härtendes Bindemittelsystem auf der Basis nachwachsender Rohstoffe
DE10256953A1 (de) 2002-12-05 2004-06-24 Ashland-Südchemie-Kernfest GmbH Heißhärtendes Bindemittel auf Polyurethanbasis
US7125914B2 (en) 2003-09-18 2006-10-24 Ashland Licensing And Intellectual Property Llc Heat-cured furan binder system
DE202007019185U1 (de) 2006-10-19 2011-03-31 Ashland-Südchemie-Kernfest GmbH Phosphorhaltige Formstoffmischung zur Herstellung von Giessformen für die Metallverarbeitung
DE202006018044U1 (de) 2006-11-28 2007-01-18 Hydro Aluminium Mandl&Berger Ges. M.B.H. Einrichtung zum Beheizen eines Gasstroms und Vorrichtung zum Herstellen von Gießkernen oder Gießformteilen
EP1990387A1 (fr) 2007-05-11 2008-11-12 Sika Technology AG Corps de couche composite lié par de la matière collante transdermique tout comme procédé de collage de plastifiants comprenant du plastique
DE102007027577A1 (de) 2007-06-12 2008-12-18 Minelco Gmbh Formstoffmischung, Formling für Gießereizwecke und Verfahren zur Herstellung eines Formlings
WO2009080738A1 (fr) 2007-12-21 2009-07-02 Sika Technology Ag Compositions durcissables à dégagement gazeux réduit
EP2274092B1 (fr) 2008-05-02 2012-09-05 Bayer MaterialScience AG Nouveaux catalyseurs et leur utilisation dans la préparation de polyuréthanes
DE102008021980A1 (de) * 2008-05-02 2009-11-05 Bayer Materialscience Ag Neue Katalysatoren und deren Einsatz bei der Herstellung von Polyurethanen
WO2011095440A1 (fr) 2010-02-02 2011-08-11 Bayer Materialscience Ag Produits de polyaddition de polyisocyanate, procédé pour leur production et leur utilisation
WO2012080226A1 (fr) 2010-12-16 2012-06-21 Bayer Materialscience Ag Produits de polyaddition de polyisocyanate, leur procédé de fabrication et leur utilisation
EP2864435B1 (fr) 2012-06-21 2019-04-10 PRC-Desoto International, Inc. Compositions de polymère contenant du soufre, catalysées par une amine, durcissables à l'humidité
WO2014040922A1 (fr) 2012-09-11 2014-03-20 Sika Technology Ag Composition de polyuréthane bicomposants
DE102014110189A1 (de) 2014-07-18 2016-01-21 Ask Chemicals Gmbh CO-Katalysatoren für Polyurethan-Coldbox-Bindemittel
DE102015118428A1 (de) 2015-10-28 2017-05-04 Purinvent System Gmbh Phenol-Formaldehydharz-freie Bindemittel für Gießerei-Formsande
WO2017149031A1 (fr) 2016-03-04 2017-09-08 Covestro Deutschland Ag Procédé pour la fabrication de composants composites fibreux
DE112016006377T5 (de) 2016-03-07 2018-10-18 Suzhou Mingzhi Technology Co., Ltd Kernfertigungsmaschine mit integrierter Mikrowellen-Aushärtungsfunktion
WO2019081581A1 (fr) 2017-10-24 2019-05-02 Sika Technology Ag Composition de résine époxyde thermodurcissable à haute stabilité au stockage

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
ANONYMOUS: "Additives for Polyurethane Case Applications - EMEA", 1 February 2019 (2019-02-01), XP055738255, Retrieved from the Internet <URL:https://coatings.evonik.com/product/coatings/downloads/evonik_en_case%20brochure_web.pdf> [retrieved on 20201009] *

Also Published As

Publication number Publication date
EP4021662A1 (fr) 2022-07-06
DE102019123374A1 (de) 2021-03-04

Similar Documents

Publication Publication Date Title
KR950015154B1 (ko) 접착제 조성물, 이를 사용한 성형용 조립체와 그 제조방법
EP2485859B1 (fr) Résines à base de lignite-uréthane pour performance améliorée d&#39;un sable de fonderie
CA2355055C (fr) Liants melanges pmdi/resol pour produire des articles en bois composites
AU748344B2 (en) Process for production of wood composites using a mixed PMDI/solid novolac resin binder
US6509392B1 (en) Foundry binder and process
EP1567576A1 (fr) Procede de production de corps moules, notamment de noyaux, de moules et de masselottes pour la fonderie
US4358570A (en) Binder composition for foundry sand molds
FI90020B (fi) Gjuteriharts
CN104220188B (zh) 铸模用聚氨酯固化型有机粘结剂以及使用其得到的型砂组合物和铸模
EP3368233A1 (fr) Liant exempt de résine de phénol - formaldéhyde pour des sables de moulage de fonderie
CN103314026A (zh) 供用于制造模具和型芯的造型材料混合物的包含磺酸的粘合剂
JP2736377B2 (ja) 鋳型材料および鋳型の製作法
WO2021037313A1 (fr) Procédé de production de noyaux et de moules en fonte au sable
EP4021661A1 (fr) Matière à mouler thermodurcissable conçue pour produire des noyaux et des moules dans le cadre de procédés de moulage en sable
US4448907A (en) Process for casting lightweight metals
US20200108552A1 (en) Method for the layerwise construction of molded bodies with a novolac-polyurethane-based binder system
US4370463A (en) Process for no-bake foundry application utilizing polyurethanes based on amine polyols
US4724892A (en) Mold assembly and fabrication thereof with a self-setting urethane adhesive paste system
KR102659527B1 (ko) 바인더 시스템
WO2022008001A1 (fr) Matière à mouler pour fabriquer des noyaux et procédé pour durcir la matière à mouler
US3796583A (en) Process for making foundry molds
EP1375028B1 (fr) Systemes de liants de fonderie
MXPA01006020A (en) Process for production of wood composites using a mixed pmdi/solid novolac resin binder

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20771195

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020771195

Country of ref document: EP

Effective date: 20220330