WO2021024639A1 - Stratifié - Google Patents

Stratifié Download PDF

Info

Publication number
WO2021024639A1
WO2021024639A1 PCT/JP2020/024985 JP2020024985W WO2021024639A1 WO 2021024639 A1 WO2021024639 A1 WO 2021024639A1 JP 2020024985 W JP2020024985 W JP 2020024985W WO 2021024639 A1 WO2021024639 A1 WO 2021024639A1
Authority
WO
WIPO (PCT)
Prior art keywords
sensitive adhesive
pressure
layer
laminate
laminated body
Prior art date
Application number
PCT/JP2020/024985
Other languages
English (en)
Japanese (ja)
Inventor
昇祐 李
正熙 金
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to KR1020227000749A priority Critical patent/KR20220040455A/ko
Priority to CN202080054590.XA priority patent/CN114174874A/zh
Publication of WO2021024639A1 publication Critical patent/WO2021024639A1/fr

Abstract

L'objectif de la présente invention est fournir un stratifié ayant une durabilité améliorée dans un environment humide et chaude. Un stratifié selon la présente invention comprend : une plaque avant ; une plaque de polarisation circulaire ; et une couche adhésive sensible à la pression interposée entre la plaque avant et la plaque de polarisation circulaire, la relation de 0,6 ≤ B/A ≤ 2 étant satisfaite, où a (µm) représente l'épaisseur du stratifié, et B (%) représente le taux de restauration de compression du stratifié, et B (%) est la proportion (%), par rapport à la plus grande profondeur d'un évidement formé par pression de l'indenteur sphérique ayant un diamètre de 0,4 mm à partir de la surface du côté de la plaque avant du stratifié vers l'intérieur du stratifié par une force de 100 mN pendant 60 secondes, de la profondeur de l'évidement à restaurer lorsqu'un indenteur sphérique est retiré du stratifié.
PCT/JP2020/024985 2019-08-05 2020-06-25 Stratifié WO2021024639A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020227000749A KR20220040455A (ko) 2019-08-05 2020-06-25 적층체
CN202080054590.XA CN114174874A (zh) 2019-08-05 2020-06-25 层叠体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019143621A JP2021026109A (ja) 2019-08-05 2019-08-05 積層体
JP2019-143621 2019-08-05

Publications (1)

Publication Number Publication Date
WO2021024639A1 true WO2021024639A1 (fr) 2021-02-11

Family

ID=74502925

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/024985 WO2021024639A1 (fr) 2019-08-05 2020-06-25 Stratifié

Country Status (5)

Country Link
JP (1) JP2021026109A (fr)
KR (1) KR20220040455A (fr)
CN (1) CN114174874A (fr)
TW (1) TW202106839A (fr)
WO (1) WO2021024639A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20170120848A (ko) * 2016-04-22 2017-11-01 삼성에스디아이 주식회사 점착필름, 이를 포함하는 광학부재 및 이를 포함하는 광학표시장치
JP2018027995A (ja) * 2016-08-15 2018-02-22 日東電工株式会社 フレキシブル画像表示装置用粘着剤組成物、フレキシブル画像表示装置用粘着剤層、フレキシブル画像表示装置用積層体、及び、フレキシブル画像表示装置
KR20180099210A (ko) * 2017-02-28 2018-09-05 동우 화인켐 주식회사 윈도우 필름, 이를 포함하는 윈도우 필름 적층체 및 화상 표시 장치
WO2018208049A1 (fr) * 2017-05-10 2018-11-15 동우 화인켐 주식회사 Stratifié optique et dispositif d'affichage souple l'utilisant
US20190023860A1 (en) * 2016-01-22 2019-01-24 Samsung Sdi Co., Ltd. Composition for window film, flexible window film formed therefrom, and display device comprising same
WO2019026760A1 (fr) * 2017-07-31 2019-02-07 日東電工株式会社 Corps stratifié pour dispositif d'affichage d'image souple, et dispositif d'affichage d'image souple
JP2020131565A (ja) * 2019-02-20 2020-08-31 住友化学株式会社 積層体、粘着剤層および粘着シート

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101659239B1 (ko) 2014-11-01 2016-09-23 삼성에스디아이 주식회사 플렉시블 디스플레이 장치
KR102451081B1 (ko) 2016-02-05 2022-10-06 삼성전자주식회사 다양한 점착제를 사용하는 디스플레이 및 그것을 포함하는 전자 장치

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190023860A1 (en) * 2016-01-22 2019-01-24 Samsung Sdi Co., Ltd. Composition for window film, flexible window film formed therefrom, and display device comprising same
KR20170120848A (ko) * 2016-04-22 2017-11-01 삼성에스디아이 주식회사 점착필름, 이를 포함하는 광학부재 및 이를 포함하는 광학표시장치
JP2018027995A (ja) * 2016-08-15 2018-02-22 日東電工株式会社 フレキシブル画像表示装置用粘着剤組成物、フレキシブル画像表示装置用粘着剤層、フレキシブル画像表示装置用積層体、及び、フレキシブル画像表示装置
KR20180099210A (ko) * 2017-02-28 2018-09-05 동우 화인켐 주식회사 윈도우 필름, 이를 포함하는 윈도우 필름 적층체 및 화상 표시 장치
WO2018208049A1 (fr) * 2017-05-10 2018-11-15 동우 화인켐 주식회사 Stratifié optique et dispositif d'affichage souple l'utilisant
WO2019026760A1 (fr) * 2017-07-31 2019-02-07 日東電工株式会社 Corps stratifié pour dispositif d'affichage d'image souple, et dispositif d'affichage d'image souple
JP2020131565A (ja) * 2019-02-20 2020-08-31 住友化学株式会社 積層体、粘着剤層および粘着シート

Also Published As

Publication number Publication date
JP2021026109A (ja) 2021-02-22
TW202106839A (zh) 2021-02-16
CN114174874A (zh) 2022-03-11
KR20220040455A (ko) 2022-03-30

Similar Documents

Publication Publication Date Title
JP6792657B2 (ja) 積層体、粘着剤組成物および粘着シート
JP6911166B2 (ja) 積層体
JP2021184091A (ja) 積層体及び表示装置
JP2021181226A (ja) フレキシブル積層体
JP7039508B2 (ja) フレキシブル積層体
JP6771056B2 (ja) フレキシブル積層体
JP2021179615A (ja) 積層体及び表示装置
JP7039507B2 (ja) 積層体
JP7039509B2 (ja) 積層体
WO2021024639A1 (fr) Stratifié
JP2020138543A (ja) 積層体
JP2020140008A (ja) フレキシブル積層体
JP6938701B2 (ja) 積層体およびそれを含む表示装置
JP6935530B2 (ja) 積層体およびそれを含む表示装置
JP6771055B2 (ja) 積層体、粘着剤組成物および粘着シート
JP2020166167A (ja) 積層体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20849966

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20849966

Country of ref document: EP

Kind code of ref document: A1