WO2020166595A1 - ダイバーティングエージェント及びこれを用いた坑井の亀裂の閉塞方法 - Google Patents

ダイバーティングエージェント及びこれを用いた坑井の亀裂の閉塞方法 Download PDF

Info

Publication number
WO2020166595A1
WO2020166595A1 PCT/JP2020/005300 JP2020005300W WO2020166595A1 WO 2020166595 A1 WO2020166595 A1 WO 2020166595A1 JP 2020005300 W JP2020005300 W JP 2020005300W WO 2020166595 A1 WO2020166595 A1 WO 2020166595A1
Authority
WO
WIPO (PCT)
Prior art keywords
diverting agent
based resin
pva
formula
slope
Prior art date
Application number
PCT/JP2020/005300
Other languages
English (en)
French (fr)
Inventor
万代　修作
泰広 平野
亮輔 谷口
千津子 風呂
健二 古井
賢司 篠原
顕 佐藤
Original Assignee
三菱ケミカル株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱ケミカル株式会社 filed Critical 三菱ケミカル株式会社
Priority to JP2020572265A priority Critical patent/JPWO2020166595A1/ja
Priority to EP20755810.7A priority patent/EP3925983A4/en
Priority to CN202080013465.4A priority patent/CN113412285A/zh
Publication of WO2020166595A1 publication Critical patent/WO2020166595A1/ja
Priority to US17/397,244 priority patent/US11674073B2/en

Abstract

本発明のダイバーティングエージェントは、ポリビニルアルコール系樹脂を含有し、グアーガムの０．４８質量％水溶液にダイバーティングエージェントを加えて濃度が１２質量％の混合液を調製し、混合液を３０℃で６０分間分散させて得た分散液を、２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、横軸に時間の平方根ｘを、縦軸に積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により式（Ａ）：ｙ＝ａｘ＋ｂ（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが条件（Ｂ）：ａ≦８０を満たす。

Description

ダイバーティングエージェント及びこれを用いた坑井の亀裂の閉塞方法
　本発明は、ダイバーティングエージェント（Diverting Agent）及びこれを用いた坑井の亀裂の閉塞方法に関し、更に詳しくは、水圧破砕法を用いる掘削工法の施工時に用いられるダイバーティングエージェント、及び該ダイバーティングエージェントを用いて坑井の亀裂を閉塞する方法に関する。
　石油やその他の地下資源の採取のために、地下の頁岩（シェール）層に高圧の水を注入して亀裂を生じさせる水圧破砕法が広く採用されている。水圧破砕法では、まず、ドリルで垂直に地下数千メートルの縦孔（垂直坑井）を掘削し、頁岩層に達したところで水平に直径十から数十センチメートルの横孔（水平坑井）を掘削する。垂直坑井と水平坑井内を流体で満たし、この流体を加圧することにより、坑井から亀裂（フラクチャ、fracture）を生成させ、かかる亀裂から頁岩層にある天然ガスや石油（シェールガス・オイル）等が流出してくるので、それを回収する。このような手法によれば、亀裂の生成により、坑井の資源流入断面が増大し、効率よく地下資源の採取を行うことができる。
　上記の水圧破砕法においては、流体加圧による亀裂の生成に先立って、水平坑井中でパーフォレーション（Perforation）と呼ばれる予備爆破が行われる。このような予備爆破により、坑井から生産層に穿孔を開ける。この後、この坑井内にフラクチュアリング流体を圧入することにより、これら穿孔に流体が流入し、これら穿孔に負荷が加えられることにより、これら穿孔に亀裂が生じ、資源の採取に好適な大きさの亀裂に成長していくこととなる。
　水圧破砕法では、既に生成している亀裂をより大きく成長させたり、さらに多くの亀裂を生成させるために、既に生成している亀裂の一部をダイバーティングエージェントと呼ばれる添加剤を用いて一時的に塞ぐことがなされる。亀裂の一部をダイバーティングエージェントで一時的に閉塞し、この状態で坑井内に充填されたフラクチュアリング流体を加圧することにより、他の亀裂内に流体が浸入していき、これにより、他の亀裂を大きく成長させるあるいは新たな亀裂を発生させることができる。
　ダイバーティングエージェントは、上記したように亀裂を一時的に閉塞するために用いられるものであるので、一定期間はその形状を維持でき、天然ガスや石油等を採取する際には加水分解して消失するものが使用される。例えば、ポリグリコール酸やポリ乳酸等の加水分解性樹脂をダイバーティングエージェントとして使用する技術が種々提案されている。
　特許文献１では、生分解性脂肪族ポリエステル系樹脂の中でも生分解性の高いポリグリコール酸を含有する坑井掘削用一時目止め剤が提案されている。
　また、特許文献２では、生分解性樹脂であるポリ乳酸の粒子からなり、目開き５００μｍの篩にかけた際にパスしない粒子が５０質量％以上、且つ、５１度以上の安息角を有する粉体が提案されている。
　そして、特許文献３では、ポリ乳酸中に該ポリ乳酸の加水分解性を調整するための生分解性の高いポリオキサレートの微細粒子が分布している分散構造を有している加水分解性粒子であって、平均粒径（Ｄ５０）が３００～１０００μｍの範囲にあり、短径／長径比が０．８以上の真円度を有する加水分解性粒子が提案されている。
　そしてまた、特許文献４では、平均粒径（Ｄ５０）が３００～１０００μｍの範囲にあり、短径／長径比が０．８以上の真円度を有しているポリオキサレート粒子が提案されている。
国際公開第２０１５／０７２３１７号 日本国特開２０１６－５６２７２号公報 日本国特開２０１６－１４７９７１号公報 日本国特開２０１６－１４７９７２号公報
　従来用いられているポリグリコール酸やポリ乳酸等は非水溶性樹脂であり、これらは除去されるまでにかなりの時間を要する。
　また、水圧破砕法で亀裂を大きく成長させたり新たな亀裂を発生させるには、既に生成している亀裂を十分に閉塞することが必要である。従来のダイバーティングエージェントは亀裂の閉塞維持時間が不十分であり、フラクチュアリング流体を加圧した際に当該流体が亀裂に浸入してしまい、他の亀裂を大きく成長させる、新たな亀裂を発生させるといったことが十分になされず、作業効率が低下することがあった。
　そこで、本発明は上記課題を解決するためになされたものであり、水圧破砕法を用いる掘削工法において、坑井の亀裂の閉塞時間の持続性を向上させつつ、かつ閉塞する必要が無くなった後には水に溶けて容易に除去できるダイバーティングエージェントを提供することを課題とする。
　本発明者らは、鋭意検討を重ねた結果、特定の加圧脱水試験を行い、加圧時間の平方根に対する積算脱水量をプロットし、最小二乗法によって回帰直線ｙ＝ａｘ＋ｂを引いたときの傾きａが特定値以下となるダイバーティングエージェントを用いることで上記課題を解決できることを見出し、本発明を完成するに至った。
　すなわち本発明は、以下の（１）～（５）を特徴とする。
（１）ポリビニルアルコール系樹脂を含有するダイバーティングエージェントであって、グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすダイバーティングエージェント。
　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
　　ａ≦８０　・・・（Ｂ）
（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
（２）前記ポリビニルアルコール系樹脂は、粒子状であり、且つ、平均粒子径の異なる２種類以上の樹脂粒子を含む、前記（１）に記載のダイバーティングエージェント。
（３）前記ポリビニルアルコール系樹脂が、変性ポリビニルアルコール系樹脂を含む、前記（１）又は（２）に記載のダイバーティングエージェント。
（４）坑井に生成された亀裂を一時的に閉塞するためのダイバーティングエージェントの作製方法であって、ポリビニルアルコール系樹脂を含有させ、グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすものとするダイバーティングエージェントの作製方法。
　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
　　ａ≦８０　・・・（Ｂ）
（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
（５）坑井に生成された亀裂を一時的に閉塞する方法であって、前記（１）～（３）のいずれか１つに記載のダイバーティングエージェントを、坑井内の流体の流れにより亀裂に流入させる坑井の亀裂の閉塞方法。
　本発明のダイバーティングエージェントは、水溶性のポリビニルアルコール系樹脂を含有し、また当該ダイバーティングエージェントは上記特定の加圧脱水試験を行って算出された式（Ａ）で表わされる回帰直線の傾きａが８０以下であることを特徴とする。この傾きが小さいほど水が流れにくい状態が継続することが示され、値が８０以下であると亀裂が閉塞される時間の持続性を有するといえる。よって、本発明のダイバーティングエージェントは、坑井の亀裂に対して十分な閉塞性を有しつつ、閉塞時間の持続性も有し、さらにポリビニルアルコール系樹脂は水溶性であるため、閉塞後は水に溶解し容易に除去される。
　したがって、本発明のダイバーティングエージェントは、天然ガスや石油等の掘削作業で行われる水圧破砕法に好適に用いることができる。
　以下、本発明について詳述するが、これらは望ましい実施形態の一例を示すものであり、本発明はこれらの内容に特定されるものではない。
　なお、用語「ポリビニルアルコール」は、単に「ＰＶＡ」ということがある。
　また、本明細書において、（メタ）アリルとはアリル又はメタリル、（メタ）アクリルとはアクリル又はメタクリル、（メタ）アクリレートとはアクリレート又はメタクリレートをそれぞれ意味する。
　また、本明細書において、「質量」は「重量」と同義である。
　本発明のダイバーティングエージェントは、ポリビニルアルコール（ＰＶＡ）系樹脂を含有し、グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすものである。
　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
　　ａ≦８０　・・・（Ｂ）
（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
　式（Ａ）は、上記特定の加圧脱水試験を行い、時間（分）の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法によって得られる回帰直線である。式（Ａ）中、０＜ｘ≦２のとき、すなわち加圧を開始してから４分の間において、傾きａは８０以下である。傾きａが８０以下であると脱水量が少ないことが示され、水が流れにくい状態であると言えるので、亀裂に対する一定時間（ＰＶＡ系樹脂が溶解し始めるまでの期間）の閉塞性があり、加えて亀裂の閉塞時間の持続性を有する。傾きａは７５以下であることが好ましく、７０以下がより好ましい。下限値は特に限定されないが、通常０より大きくなる。
　また、式（Ａ）中、切片ｂは傾きａにより定まる変数である。加圧した瞬間にある程度の脱水が起こり、これによりダイバーティングエージェントが最適配置となって加圧脱水装置のスリットを閉塞することができる。前記を踏まえたうえで、切片ｂとなる加圧開始０分における脱水量は、特に限定はされないが、５０ｇ以下であることが好ましく、３０ｇ以下がより好ましい。
　以下、本発明で用いるＰＶＡ系樹脂について説明する。
〔ＰＶＡ系樹脂〕
　本発明で用いられるＰＶＡ系樹脂は、ビニルエステル系モノマーを重合して得られるポリビニルエステル系樹脂をケン化して得られる、ビニルアルコール構造単位を主体とする樹脂であり、ケン化度相当のビニルアルコール構造単位と未ケン化部分の酢酸ビニル構造単位を有するものである。
　本発明では、ＰＶＡ系樹脂として、未変性ＰＶＡ系樹脂の他に、ポリビニルエステル系樹脂の製造時に各種モノマーを共重合させ、これをケン化して得られる変性ＰＶＡ系樹脂や、未変性ＰＶＡ系樹脂に後変性によって各種官能基を導入した各種の後変性ＰＶＡ系樹脂等を用いることができる。かかる変性は、ＰＶＡ系樹脂の水溶性が失われない範囲で行うことができる。また、場合によっては、変性ＰＶＡ系樹脂を更に後変性させてもよい。
　本発明で用いられるＰＶＡ系樹脂の平均重合度（ＪＩＳ　Ｋ　６７２６：１９９４に準拠して測定）は、１００～３５００であることが好ましい。平均重合度は、小さすぎると溶解しやすくなり閉塞性が発揮できず、平均重合度が大きすぎると溶解速度が遅く一定時間経過後の溶解が難しくなるため、閉塞性の持続と一定時間経過後の溶解性の観点から、２００～２５００であることがより好ましく、３００～２０００がさらに好ましい。
　ＰＶＡ系樹脂のケン化度（ＪＩＳ　Ｋ　６７２６：１９９４に準拠して測定）は、６０～１００モル％であることが好ましい。かかるケン化度が低すぎると水溶性が低下する傾向がある。ケン化度は、亀裂等の隙間に対する閉塞性の観点から、９０モル％以上であることがより好ましく、９５モル％以上がさらに好ましい。また、上限は９９．８モル％以下であることがより好ましく、さらに好ましくは９９．５モル％以下である。
　ＰＶＡ系樹脂の融点は、１４０～２５０℃であることが好ましく、より好ましくは１５０～２４５℃、更に好ましくは１６０～２４０℃、特に好ましくは１７０～２３０℃である。
　なお、融点は、示差走査熱量計（ＤＳＣ）で昇降温速度１０℃／ｍｉｎで測定した値である。
　ＰＶＡ系樹脂の４質量％水溶液粘度は、２～８５ｍＰａ・ｓであることが好ましく、より好ましくは２．５～８０ｍＰａ・ｓ、更に好ましく３～７５ｍＰａ・ｓ、特に好ましくは３．５～７０ｍＰａ・ｓである。かかる粘度が低すぎると本願の効果がでにくくなる傾向があり、高すぎると製造しにくくなる傾向がある。
　なお、ＰＶＡ系樹脂の４質量％水溶液粘度は、ＰＶＡ系樹脂の４質量％水溶液を調製し、ＪＩＳ　Ｋ６７２６：１９９４に準拠して測定した２０℃における粘度である。
　本発明において、ＰＶＡ系樹脂は、官能基が導入された変性ＰＶＡ系樹脂を用いてもよい。例えば、側鎖に一級水酸基を有するＰＶＡ系樹脂や、エチレン変性ＰＶＡ系樹脂が好ましく、特に、溶融成形性に優れる点で、側鎖に一級水酸基を有するＰＶＡ系樹脂が好ましい。側鎖に一級水酸基を有するＰＶＡ系樹脂における一級水酸基の数は、１～５個であることが好ましく、より好ましくは１～２個であり、特に好ましくは１個である。また、一級水酸基以外にも二級水酸基を有することが好ましい。
　このような側鎖に一級水酸基を有するＰＶＡ系樹脂としては、例えば、側鎖に１，２－ジオール構造単位を有する変性ＰＶＡ系樹脂、側鎖にヒドロキシアルキル基構造単位を有する変性ＰＶＡ系樹脂等が挙げられる。中でも、特に下記一般式（１）で表される、側鎖に１，２－ジオール構造単位を含有する変性ＰＶＡ系樹脂（以下、「側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂」と称することがある。）を用いることが好ましい。
　なお、１，２－ジオール構造単位以外の部分は、通常のＰＶＡ系樹脂と同様、ビニルアルコール構造単位と未ケン化部分のビニルエステル構造単位である。
Figure JPOXMLDOC01-appb-C000001
（式（１）中、Ｒ１～Ｒ４はそれぞれ独立して水素原子又は炭素数１～４のアルキル基を表し、Ｘは単結合又は結合鎖を表す。）
　上記一般式（１）において、Ｒ１～Ｒ４はそれぞれ独立して水素原子又は炭素数１～４のアルキル基を表す。Ｒ１～Ｒ４は、すべて水素原子であることが望ましいが、樹脂特性を大幅に損なわない程度の量であれば炭素数１～４のアルキル基であってもよい。当該アルキル基としては特に限定しないが、例えば、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｔｅｒｔ－ブチル基等が好ましく、当該アルキル基は必要に応じてハロゲノ基、水酸基、エステル基、カルボン酸基、スルホン酸基等の置換基を有していてもよい。
　上記一般式（１）中、Ｘは単結合又は結合鎖であり、熱安定性の点や高温下や酸性条件下での安定性の点で、単結合であることが好ましいが、本発明の効果を阻害しない範囲であれば結合鎖であってもよい。
　かかる結合鎖としては、特に限定されず、例えば、アルキレン基、アルケニレン基、アルキニレン基、フェニレン基、ナフチレン基等の炭化水素基（これらの炭化水素基は、フッ素原子、塩素原子、臭素原子等のハロゲン原子等で置換されていてもよい。）の他、－Ｏ－、－（ＣＨ２Ｏ）ｍ－、－（ＯＣＨ２）ｍ－、－（ＣＨ２Ｏ）ｍＣＨ２－、－ＣＯ－、－ＣＯＣＯ－、－ＣＯ（ＣＨ２）ｍＣＯ－、－ＣＯ（Ｃ６Ｈ４）ＣＯ－、－Ｓ－、－ＣＳ－、－ＳＯ－、－ＳＯ２－、－ＮＲ－、－ＣＯＮＲ－、－ＮＲＣＯ－、－ＣＳＮＲ－、－ＮＲＣＳ－、－ＮＲＮＲ－、－ＨＰＯ４－、－Ｓｉ（ＯＲ）２－、－ＯＳｉ（ＯＲ）２－、－ＯＳｉ（ＯＲ）２Ｏ－、－Ｔｉ（ＯＲ）２－、－ＯＴｉ（ＯＲ）２－、－ＯＴｉ（ＯＲ）２Ｏ－、－Ａｌ（ＯＲ）－、－ＯＡｌ（ＯＲ）－、－ＯＡｌ（ＯＲ）Ｏ－等が挙げられる。Ｒは各々独立して水素原子又は任意の置換基であり、水素原子又はアルキル基（特に炭素数１～４のアルキル基）が好ましい。また、ｍは自然数であり、好ましくは１～１０、特に好ましくは１～５である。結合鎖は、これらのなかでも、製造時の粘度安定性や耐熱性等の点で、炭素数６以下のアルキレン基、特にメチレン基、あるいは－ＣＨ２ＯＣＨ２－が好ましい。
　上記一般式（１）で表される１，２－ジオール構造単位における特に好ましい構造は、Ｒ１～Ｒ４がすべて水素原子であり、Ｘが単結合である。
　ＰＶＡ系樹脂が変性ＰＶＡ系樹脂である場合、かかる変性ＰＶＡ系樹脂中の変性率、すなわち共重合体中の各種モノマーに由来する構造単位、あるいは後反応によって導入された官能基の含有量は、官能基の種類によって特性が大きく異なるため一概には言えないが、０．１～２０モル％であることが好ましい。
　例えば、ＰＶＡ系樹脂が側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂である場合の変性率は、０．１～２０モル％であることが好ましく、より好ましくは０．５～１０モル％、更に好ましくは１～８モル％、特に好ましくは１～３モル％である。かかる変性率が高すぎると、坑井の亀裂を一時的に閉塞できなくなり、低すぎると一定期間後の溶解性が悪化する傾向がある。
　なお、ＰＶＡ系樹脂中の１，２－ジオール構造単位の含有率（変性率）は、ケン化度１００モル％のＰＶＡ系樹脂の１Ｈ－ＮＭＲスペクトル（溶媒：ＤＭＳＯ－ｄ６、内部標準：テトラメチルシラン）から求めることができる。具体的には１，２－ジオール構造単位中の水酸基プロトン、メチンプロトン、およびメチレンプロトン、主鎖のメチレンプロトン、主鎖に連結する水酸基のプロトンなどに由来するピーク面積から算出することができる。
　ＰＶＡ系樹脂がエチレン変性ＰＶＡ系樹脂である場合の変性率は、０．１～１５モル％であることが好ましく、より好ましくは０．５～１０モル％、更に好ましくは１～１０モル％、特に好ましくは５～９モル％である。かかる変性率が高すぎると水溶性が低下する傾向があり、低すぎると溶融成形が困難となる傾向がある。
　本発明で用いられるＰＶＡ系樹脂の製造方法としては、例えば、ビニルエステル系モノマーを重合し、得られたポリビニルエステル重合体をケン化して製造する方法が挙げられる。
　ビニルエステル系モノマーとしては、例えば、酢酸ビニル、プロピオン酸ビニル、酪酸ビニル、カプロン酸ビニル、カプリル酸ビニル、カプリン酸ビニル、ラウリン酸ビニル、ミリスチン酸ビニル、パルミチン酸ビニル、ステアリン酸ビニル、シクロヘキサンカルボン酸ビニル、ピバリン酸ビニル、オクチル酸ビニル、モノクロロ酢酸ビニル、アジピン酸ビニル、メタクリル酸ビニル、クロトン酸ビニル、ソルビン酸ビニル、安息香酸ビニル、桂皮酸ビニル、トリフロロ酢酸ビニル等が挙げられ、価格や入手の容易さの観点で、酢酸ビニルが好ましく用いられる。
　ビニルエステル系樹脂の製造時にビニルエステル系モノマーとの共重合に用いられるモノマーとしては、例えば、エチレン、プロピレン、イソブチレン、α－オクテン、α－ドデセン、α－オクタデセン等のオレフィン類；アクリル酸、メタクリル酸、クロトン酸、マレイン酸、無水マレイン酸、イタコン酸等の不飽和酸類あるいはその塩、そのモノ又はジアルキルエステル等；アクリロニトリル、メタクリロニトリル等のニトリル類；アクリルアミド、メタクリルアミド等のアミド類；エチレンスルホン酸、アリルスルホン酸、メタアリルスルホン酸等のオレフィンスルホン酸あるいはその塩；アルキルビニルエーテル類；Ｎ－アクリルアミドメチルトリメチルアンモニウムクロライド；アリルトリメチルアンモニウムクロライド；ジメチルアリルビニルケトン；Ｎ－ビニルピロリドン；塩化ビニル；塩化ビニリデン；ポリオキシエチレン（メタ）アリルエーテル、ポリオキシプロピレン（メタ）アリルエーテル等のポリオキシアルキレン（メタ）アリルエーテル；ポリオキシエチレン（メタ）アクリレート、ポリオキシプロピレン（メタ）アクリレート等のポリオキシアルキレン（メタ）アクリレート；ポリオキシエチレン（メタ）アクリルアミド、ポリオキシプロピレン（メタ）アクリルアミド等のポリオキシアルキレン（メタ）アクリルアミド；ポリオキシエチレン［１－（メタ）アクリルアミド－１，１－ジメチルプロピル］エステル；ポリオキシエチレンビニルエーテル、ポリオキシプロピレンビニルエーテル等のポリオキシアルキレンビニルエーテル；ポリオキシエチレンアリルアミン、ポリオキシプロピレンアリルアミン等のポリオキシアルキレンアリルアミン；ポリオキシエチレンビニルアミン、ポリオキシプロピレンビニルアミン等のポリオキシアルキレンビニルアミン；３－ブテン－１－オール、４－ペンテン－１－オール、５－ヘキセン－１－オール等のヒドロキシ基含有α－オレフィン類あるいはそのアシル化物等の誘導体を挙げることができる。
　また、３，４－ジヒドロキシ－１－ブテン、３，４－ジアシロキシ－１－ブテン、３－アシロキシ－４－ヒドロキシ－１－ブテン、４－アシロキシ－３－ヒドロキシ－１－ブテン、３，４－ジアシロキシ－２－メチル－１－ブテン、４，５－ジヒドロキシ－１－ペンテン、４，５－ジアシロキシ－１－ペンテン、４，５－ジヒドロキシ－３－メチル－１－ペンテン、４，５－ジアシロキシ－３－メチル－１－ペンテン、５，６－ジヒドロキシ－１－ヘキセン、５，６－ジアシロキシ－１－ヘキセン、グリセリンモノアリルエーテル、２，３－ジアセトキシ－１－アリルオキシプロパン、２－アセトキシ－１－アリルオキシ－３－ヒドロキシプロパン、３－アセトキシ－１－アリルオキシ－２－ヒドロキシプロパン、グリセリンモノビニルエーテル、グリセリンモノイソプロペニルエーテル、ビニルエチレンカーボネート、２，２－ジメチル－４－ビニル－１，３－ジオキソラン等のジオールを有する化合物などが挙げられる。
　ビニルエステル系モノマーの重合又はビニルエステル系モノマーと共重合モノマーとの重合は、公知の任意の重合法、例えば、溶液重合、懸濁重合、エマルジョン重合などにより行うことができる。なかでも、反応熱を効率的に除去できる溶液重合を還流下で行うことが好ましい。
　かかる重合で用いられる溶媒としては、例えば、メタノール、エタノール、イソプロピルアルコール、ｎ－プロパノール、ブタノール等の炭素数１～４の脂肪族アルコールやアセトン、メチルエチルケトン等のケトン類等が挙げられ、好ましくは炭素数１～３の低級アルコールが用いられる。
　得られた重合体のケン化についても、従来より行われている公知のケン化方法を採用することができる。すなわち、重合体をアルコール又は水／アルコール溶媒に溶解させた状態で、アルカリ触媒又は酸触媒を用いて行うことができる。
　前記アルカリ触媒としては、例えば、水酸化カリウム、水酸化ナトリウム、ナトリウムメチラート、ナトリウムエチラート、カリウムメチラート、リチウムメチラート等のアルカリ金属の水酸化物やアルコラートを用いることができる。
　中でも、無水アルコール系溶媒下、アルカリ触媒を用いたエステル交換反応が反応速度の点や脂肪酸塩等の不純物を低減できるなどの点で好適に用いられる。
　ケン化反応の反応温度は、２０～６０℃であることが好ましい。反応温度が低すぎると、反応速度が小さくなり反応効率が低下する傾向があり、高すぎると反応溶媒の沸点以上となる場合があり、製造面における安全性が低下する傾向がある。なお、耐圧性の高い塔式連続ケン化塔などを用いて高圧下でケン化する場合には、より高温、例えば、８０～１５０℃でケン化することが可能であり、少量のケン化触媒でも短時間で、高ケン化度のＰＶＡ系樹脂を得ることが可能である。
　また、側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂は、公知の製造方法により製造することができる。例えば、日本国特開２００２－２８４８１８号公報、日本国特開２００４－２８５１４３号公報、日本国特開２００６－９５８２５号公報に記載されている方法により製造することができる。すなわち、（ｉ）ビニルエステル系モノマーと下記一般式（２）で示される化合物との共重合体をケン化する方法、（ｉｉ）ビニルエステル系モノマーと下記一般式（３）で示されるビニルエチレンカーボネートとの共重合体をケン化及び脱炭酸する方法、（ｉｉｉ）ビニルエステル系モノマーと下記一般式（４）で示される２，２－ジアルキル－４－ビニル－１，３－ジオキソランとの共重合体をケン化及び脱ケタール化する方法などにより、製造することができる。
Figure JPOXMLDOC01-appb-C000002
（式（２）中、Ｒ１～Ｒ４はそれぞれ独立して水素原子又は炭素数１～４のアルキル基を表し、Ｘは単結合又は結合鎖を表し、Ｒ７及びＲ８は、それぞれ独立して水素原子又はＲ９－ＣＯ－（式中、Ｒ９は炭素数１～４のアルキル基である。）を表す。）
Figure JPOXMLDOC01-appb-C000003
（式（３）中、Ｒ１～Ｒ４はそれぞれ独立して水素原子又は炭素数１～４のアルキル基を表し、Ｘは単結合又は結合鎖を表す。）
Figure JPOXMLDOC01-appb-C000004
（式（４）中、Ｒ１～Ｒ４はそれぞれ独立して水素原子又は炭素数１～４のアルキル基を表し、Ｘは単結合又は結合鎖を表し、Ｒ１０及びＲ１１は、それぞれ独立して、水素原子又は炭素数１～４のアルキル基を表す。）
　式（２）～式（４）中のＲ１～Ｒ４及びＸの具体例、好ましい例示は、上記式（１）の場合と同様であり、また、Ｒ７～Ｒ１１の炭素数１～４のアルキル基の具体例、好ましい例示も式（１）の場合と同様である。
　上記方法（ｉ）～（ｉｉｉ）のうち、共重合反応性及び工業的な取扱いにおいて優れるという点で、（ｉ）の方法が好ましく、特に、上記一般式（２）で示される化合物は、Ｒ１～Ｒ４が水素原子、Ｘが単結合、Ｒ７、Ｒ８がＲ９－ＣＯ－であり、Ｒ９が炭素数１～４のアルキル基である３，４－ジアシロキシ－１－ブテンが好ましく、その中でも特にＲ９がメチル基である３，４－ジアセトキシ－１－ブテンが好ましく用いられる。
　ＰＶＡ系樹脂は粒子状で用いられることが好ましく、その形状は、特に限定されないが、例えば、球状、粉末状、楕円球状、ペレット成形体（円柱状、板状、立方体状、直方体状、角柱状、多角面体状等）等が挙げられる。
　ＰＶＡ系樹脂粒子の粒子径は、坑井内の亀裂の大きさ、粒子の形状等を考慮して適宜調整すればよいが、０．１～５ｍｍの範囲とすることが好ましい。
　具体的に、ＰＶＡ系樹脂粒子が円柱状粒子（ペレット成形体）の場合、その平均粒子径は、軸方向と直交する断面の直径が０．５～５．０ｍｍであることが好ましく、より好ましくは１．０～４．５ｍｍ、更に好ましくは１．５～４．０ｍｍであり、厚み（軸方向の長さ）が０．５～５．０ｍｍであることが好ましく、より好ましくは１．０～４．５ｍｍ、更に好ましくは１．５～４．０ｍｍである。
　ＰＶＡ系樹脂粒子が球状粒子の場合、粉末状とすることが好ましく、その平均粒子径は、２００～２０００μｍであり、好ましくは４００～１５００μｍである。
　かかる平均粒子径は、乾式ふるい分け試験方法（ＪＩＳ　Ｚ　８８１５：１９９４参考）の方法により測定することができる。本明細書において、粒子径とは、乾式ふるい分け試験方法で粒径別の体積分布を測定し、積算値（累積分布）が５０％になる粒子径のことである。
　かかる大きさ（直径、長さ、平均粒子径）が大きすぎると水溶解性が低下する傾向があり、小さすぎると目止効果が低下する傾向がある。
　本発明で用いられるＰＶＡ系樹脂は、１種類であっても、２種類以上の混合物であってもよい。ＰＶＡ系樹脂を２種類以上用いる場合としては、例えば、ケン化度、平均重合度、融点などが異なる２種以上の未変性ＰＶＡ系樹脂の組み合わせ；未変性ＰＶＡ系樹脂と変性ＰＶＡ系樹脂との組み合わせ；ケン化度、平均重合度、融点、官能基の種類や変性率などが異なる２種以上の変性ＰＶＡ系樹脂の組み合わせ；溶融成形により製造したＰＶＡ系樹脂と溶融成形せずに得られたＰＶＡ系樹脂の組み合わせ、形状や平均粒子径などが異なるＰＶＡ系樹脂の組み合わせ等が挙げられる。
　中でも、ＰＶＡ系樹脂は平均粒子径の異なる２種類以上のＰＶＡ系樹脂粒子の混合物であることが好ましい。平均粒子径の異なる粒子を組み合わせることで、平均粒子径の大きいＰＶＡ系樹脂粒子が亀裂内での足場となり、その隙間を平均粒子径の小さいＰＶＡ系樹脂粒子が埋めていくこととなるので、亀裂内でのダイバーティングエージェントの密度が高くなり、閉塞性が向上する。
　なお、平均粒子径の大きいＰＶＡ系樹脂粒子と平均粒子径の小さいＰＶＡ系樹脂粒子を組み合わせて用いる場合、平均粒子径の大きいＰＶＡ系樹脂粒子の含有量が多すぎると、当該粒子同士の隙間を平均粒子径の小さいＰＶＡ系樹脂粒子で十分に埋めることが出来なくなる場合があるので、前者：後者の比（質量比）で６０：４０～５：９５であることが好ましく、５０：５０～１０：９０であることがより好ましい。
　さらに３種類以上の平均粒子径の異なるＰＶＡ系樹脂粒子を任意の割合で混合してもよい。
　ＰＶＡ系樹脂は水に分散した際に水を吸収して膨潤し、その後徐々に溶解していく。本発明のＰＶＡ系樹脂は、１～５日で溶解し始め、２～１５日、より好ましくは３～１０日で完全溶解することが好ましい。
　なお、ＰＶＡ系樹脂の溶解時間は、ＰＶＡ系樹脂のケン化度、変性率、平均重合度、平均粒子径、熱処理度等を調整することにより調整できる。
〔ダイバーティングエージェント〕
　本発明のダイバーティングエージェントは、上記したＰＶＡ系樹脂を含有する。ＰＶＡ系樹脂の含有量は、ダイバーティングエージェント全体に対して、５０～１００質量％であることが好ましく、より好ましくは８０～１００質量％、更に好ましくは９０～１００質量％である。かかる含有量が少なすぎると、本発明の効果が得られにくくなる傾向がある。
　本発明のダイバーティングエージェントには、本発明の効果を阻害しない範囲で、ＰＶＡ系樹脂以外に、例えば、砂、鉄、セラミック、その他の生分解性樹脂などの添加材（剤）を配合することができる。
　かかる添加材（剤）の配合量は、ダイバーティングエージェント全体に対して、５０質量％以下であることが好ましく、より好ましくは２０質量％以下、更に好ましくは１０質量％以下である。
　ダイバーティングエージェントは、本発明のＰＶＡ系樹脂と必要により他の添加材（剤）とを均一に混合することにより作製することができる。
　本発明のダイバーティングエージェントは、上記したように、グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすものである。
　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
　　ａ≦８０　・・・（Ｂ）
（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
　加圧脱水装置としては、例えば、Ｆａｎｎ　Ｉｎｓｔｒｕｍｅｎｔ社の「ＨＰＨＴ　Ｆｉｌｔｅｒ　Ｐｒｅｓｓ　５００ＣＴ」（商品名）等が挙げられる。
　上記式（Ａ）において、ｘは加圧開始から経過した時間（分）の平方根であり、ｙは積算脱水量（ｇ）である。ａ及びｂは回帰直線の傾きと切片である。傾きａはダイバーティングエージェント分散液中の水の流れやすさを表し、切片ｂは傾きａにより定まる変数であって、加圧開始０分における脱水量の目安となる値である。
　０＜ｘ≦２において、傾きａが８０以下であると、脱水量が少なく一定時間（ＰＶＡ系樹脂が溶解し始めるまでの期間）の閉塞性があり、加えて亀裂の閉塞時間の持続性を有することができる。
　式（Ａ）におけるａを８０以下とするためには、例えば、用いるＰＶＡ系樹脂の物性を調整する方法や、ＰＶＡ系樹脂の組み合わせを調整する方法、ＰＶＡ系樹脂と他の添加材（剤）との組み合わせを調整する方法等が挙げられる。ＰＶＡ系樹脂の物性を調整する方法としては、例えば、ケン化度、変性率、平均重合度、平均粒子径、熱処理度等を調整することが挙げられる。
　これらを調整することにより、上記の特定の加圧脱水試験をした際に式（Ａ）及び式（Ｂ）を満たすダイバーティングエージェントを作製することができる。
　本発明のダイバーティングエージェントは、石油や天然ガスなどの掘削において、水圧破砕法を用いる場合に、坑井に生成された亀裂や割れ目の中に入り、その亀裂や割れ目を一時的に閉塞することができる。本発明のダイバーティングエージェントは、上記した加圧脱水試験に基づき式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが８０以下であるので、亀裂や割れ目における閉塞性に優れ、閉塞時間の持続性も有する。よって、本発明のダイバーティングエージェントにより一時的に亀裂を塞いだ状態で、新たな亀裂や割れ目を形成することができる。亀裂や割れ目の閉塞方法としては、本発明のダイバーティングエージェントを坑井内の流体の流れにより亀裂に流入させればよい。これにより、閉塞したい亀裂の一時目止めを行うことができる。
　また、本発明のダイバーティングエージェントは水溶性で、かつ生分解性であるため、使用後は速やかに水に溶解し除去され、その後生分解されるため、環境負荷が小さく、非常に有用である。
　以下、実施例及び比較例を挙げて本発明を更に具体的に説明するが、本発明はこれらの実施例に限定されるものではない。なお、以下の実施例及び比較例において「部」及び「％」は、特に断りのない限り質量を基準とする。
（製造例１：ＰＶＡ系樹脂粒子（ＰＶＡ１）の製造）
　還流冷却器、滴下装置、撹拌機を備えた反応缶に、酢酸ビニル２０部（全体の２０％を初期仕込み）、メタノール３２．５部、及び３，４－ジアセトキシ－１－ブテン０．４０部（全体の２０％を初期仕込み）を仕込み、撹拌しながら窒素気流下で温度を上昇させ、沸点に到達した後、アセチルパーオキサイドを０．０９３部投入し、重合を開始した。さらに、重合開始から０．４時間後に酢酸ビニル８０部と３，４－ジアセトキシ－１－ブテン１．６０部を１１時間かけて等速滴下した。酢酸ビニルの重合率が９２％となった時点で、ヒドロキノンモノメチルエーテルを所定量添加して重合を終了し、続いて、メタノール蒸気を吹き込みつつ蒸留することで未反応の酢酸ビニルモノマーを系外に除去し共重合体のメタノール溶液を得た。
　ついで、上記溶液をメタノールで希釈し、固形分濃度を５５％に調整して、溶液温度を４５℃に保ちながら、水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を共重合体中の酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して１２ミリモルとなる割合で加えてケン化を行った。ケン化が進行すると共にケン化物が析出し、ケーキ状となった時点で粉砕した。その後、中和用の酢酸を水酸化ナトリウム１当量あたり０．３当量添加し、濾別し、メタノールでよく洗浄して熱風乾燥機中で乾燥し、側鎖１，２－ジオール構造単位を含有する変性ＰＶＡ系樹脂粒子（側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子）（ＰＶＡ１）を得た。
　得られたＰＶＡ１は粉末状であり、乾式ふるい分け試験方法でふるい分けし、積算値が５０％になる粒子径を算出した。ＰＶＡ１の平均粒子径は、７５０μｍであった。
　また、ＰＶＡ１のケン化度は、樹脂中の残存酢酸ビニルおよび３，４－ジアセトキシ－１－ブテンの構造単位の加水分解に要するアルカリ消費量にて分析したところ、９９．３モル％であった。また、平均重合度は、ＪＩＳ　Ｋ６７２６：１９９４に準じて分析を行ったところ、４５０であった。
　また、ＰＶＡ１中の前記式（１）で表される１，２－ジオール構造単位の含有量（変性率）は、１Ｈ－ＮＭＲ（３００ＭＨｚ　プロトンＮＭＲ、ｄ６－ＤＭＳＯ溶液、内部標準物質；テトラメチルシラン、５０℃）にて測定した積分値より算出したところ、１．０モル％であった。
（製造例２：ＰＶＡ系樹脂粒子（ＰＶＡ２）の製造）
　水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して１０ミリモルとなる割合で加えてケン化した以外は製造例１と同様の方法により側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ２）を得た。
　得られたＰＶＡ２は粉末状であり、平均粒子径７５０μｍ、ケン化度９８．９モル％、平均重合度４５０、変性率１．０モル％であった。
（製造例３：ＰＶＡ系樹脂粒子（ＰＶＡ３）の製造）
　水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して８ミリモルとなる割合で加えてケン化した以外は製造例１と同様の方法により側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ３）を得た。
　得られたＰＶＡ３は粉末状であり、平均粒子径７５０μｍ、ケン化度９８．５モル％、平均重合度４５０、変性率１．０モル％であった。
（製造例４：ＰＶＡ系樹脂粒子（ＰＶＡ４）の製造）
　上記製造例１において、仕込みの酢酸ビニルを１００部、メタノールを１８部、及び３，４－ジアセトキシ－１－ブテンを３部とし、重合反応において酢酸ビニルの重合率が９６％となった時点で重合を終了し、また、水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して１３ミリモルとなる割合で加えてケン化を行った以外は製造例１と同様にして、側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ４）を得た。
　得られたＰＶＡ４は粉末状であり、平均粒子径１１７０μｍ、ケン化度９９．５モル％、平均重合度６００、変性率１．５モル％であった。
（製造例５：ＰＶＡ系樹脂粒子（ＰＶＡ５）の製造）
　水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して１０ミリモルとなる割合で加えてケン化した以外は製造例４と同様の方法により側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ５）を得た。
　得られたＰＶＡ５は粉末状であり、平均粒子径１１７０μｍ、ケン化度９９．２モル％、平均重合度６００、変性率１．５モル％であった。
（製造例６：ＰＶＡ系樹脂粒子（ＰＶＡ６）の製造）
　上記製造例１において、仕込みの酢酸ビニルを１００部、メタノールを１８部、及び３，４－ジアセトキシ－１－ブテンを３部とし、重合反応において酢酸ビニルの重合率が９６％となった時点で重合を終了し、また、水酸化ナトリウム２％メタノール溶液（ナトリウム換算）を酢酸ビニル構造単位及び３，４－ジアセトキシ－１－ブテン構造単位の合計量１モルに対して１３．５ミリモルとなる割合で加えてケン化を行った以外は製造例１と同様にして、側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ６）を得た。
　得られたＰＶＡ６は粉末状であり、平均粒子径６８０μｍ、ケン化度９９．２モル％、平均重合度６００、変性率１．５モル％であった。
（製造例７：ＰＶＡ系樹脂粒子（ＰＶＡ７）の製造）
　上記製造例１において、仕込みの酢酸ビニルを１００部、メタノールを３２．５部、及び３，４－ジアセトキシ－１－ブテンを４部とし、重合反応において酢酸ビニルの重合率が９１％となった時点で重合を終了した以外は製造例１と同様の方法により側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子を得た。
　得られた側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子のケン化度は９９．０モル％、平均重合度５３０、変性率２．０モル％であった。
　上記で得られた側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子を押出機に投入し、さらにステアリン酸マグネシウム５００ｐｐｍと１２－ヒドロキシステアリン酸マグネシウム５００ｐｐｍを混合し下記の条件で溶融混練し、空冷させることにより凝固させた後、カッターを用いてカッティングした（ストランドカッティング方式）。その後、乾燥し、直径２．６ｍｍ、軸方向長さ３ｍｍの円柱状の側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ７）を得た。
　（溶融混練条件）
　押出機：テクノベル社製　１５ｍｍφ　Ｌ／Ｄ＝６０
　回転数：２００ｒｐｍ
　吐出量：１．２～１．５ｋｇ／ｈ
　押出温度：Ｃ１／Ｃ２／Ｃ３／Ｃ４／Ｃ５／Ｃ６／Ｃ７／Ｃ８／Ｄ＝９０／１７０／２００／２１５／２１５／２２０／２２５／２２５／２２５℃
（製造例８：ＰＶＡ系樹脂（ＰＶＡ８）の製造）
　上記製造例７において、カッティングの大きさを直径２．６ｍｍ、軸方向長さ１．８ｍｍにした以外は製造例７と同様にして、円柱状の側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ８）を得た。
（製造例９：ＰＶＡ系樹脂（ＰＶＡ９）の製造）
　上記製造例７において、カッティングの大きさを直径２．６ｍｍ、軸方向長さ１．１ｍｍにした以外は製造例７と同様にして、円柱状の側鎖１，２－ジオール構造単位含有変性ＰＶＡ系樹脂粒子（ＰＶＡ９）を得た。
　製造例１～９で作製したＰＶＡ１～ＰＶＡ９のケン化度、変性率、重合度、粒子の大きさ（粒子径）を表１に纏めて示す。
Figure JPOXMLDOC01-appb-T000005
（実施例１）
　ＰＶＡ１を９０％、ＰＶＡ７を１０％の割合で均一に混合して粒子混合物を得た。
（実施例２）
　ＰＶＡ１を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（実施例３）
　ＰＶＡ１を７０％、ＰＶＡ７を３０％の割合で均一に混合して粒子混合物を得た。
（実施例４）
　ＰＶＡ１を５０％、ＰＶＡ７を５０％の割合で均一に混合して粒子混合物を得た。
（実施例５）
　ＰＶＡ２を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（実施例６）
　ＰＶＡ３を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（実施例７）
　ＰＶＡ４を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（実施例８）
　ＰＶＡ５を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（実施例９）
　ＰＶＡ１を８０％、ＰＶＡ８を２０％の割合で均一に混合して粒子混合物を得た。
（実施例１０）
　ＰＶＡ１を８０％、ＰＶＡ９を２０％の割合で均一に混合して粒子混合物を得た。
（実施例１１）
　ＰＶＡ１を８０％、ＰＶＡ７を１０％、ＰＶＡ８を１０％の割合で均一に混合して粒子混合物を得た。
（実施例１２）
　ＰＶＡ１を８０％、ＰＶＡ７を１０％、ＰＶＡ９を１０％の割合で均一に混合して粒子混合物を得た。
（比較例１）
　ＰＶＡ６を８０％、ＰＶＡ７を２０％の割合で均一に混合して粒子混合物を得た。
（参考例１）
　ポリ乳酸（ＰＬＡ、ネイチャーワークス社製「Ｉｎｇｅｏ４０３２Ｄ」）を用いた。
＜加圧脱水試験＞
　各例の粒子を分散させた分散液の脱水量を、Ｆａｎｎ　Ｉｎｓｔｒｕｍｅｎｔ社の加圧脱水装置「ＨＰＨＴ　Ｆｉｌｔｅｒ　Ｐｒｅｓｓ　５００ＣＴ」を用いて測定した。
　グアーガムの０．４８質量％水溶液に粒子混合物を加えて、前記粒子混合物の濃度が１２質量％となる混合液を調製した。この混合液を２３℃で６０分間撹拌し分散させて分散液を得た。
　次に、上記加圧脱水装置の排水部のスリットを２ｍｍ幅に設定し、１ＭＰａの圧力を加えて加圧脱水した。
　加圧開始（０分）から５分後までの０．５分毎の脱水量を測定し、時間の平方根ｘに対する積算脱水量ｙを求めた。横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から、最小二乗法によって下記式（Ａ）で表わされる回帰直線を算出した。式（Ａ）において、ａが８０以下であるものは閉塞時間の持続性があると評価できる。各例の結果を表２に示す。
　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
（式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
Figure JPOXMLDOC01-appb-T000006
　表２の結果より、実施例１～１２は式（Ａ）における傾きａが８０以下であった。よって、実施例１～１２は加圧時に水が流れにくく、また閉塞初期だけでなく閉塞の持続性があることがわかった。よって、坑井の亀裂を閉塞した際に、十分な閉塞性と閉塞時間の持続性を発揮できることがわかった。
　本発明を詳細にまた特定の実施形態を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。本出願は、２０１９年２月１３日出願の日本特許出願（特願２０１９－０２３９４７）に基づくものであり、その内容はここに参照として取り込まれる。

Claims (5)

  1. 　ポリビニルアルコール系樹脂を含有するダイバーティングエージェントであって、
    　グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすダイバーティングエージェント。
    　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
    　　ａ≦８０　・・・（Ｂ）
    （式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
  2. 　前記ポリビニルアルコール系樹脂は、粒子状であり、且つ、平均粒子径の異なる２種類以上の樹脂粒子を含む、請求項１に記載のダイバーティングエージェント。
  3. 　前記ポリビニルアルコール系樹脂が、変性ポリビニルアルコール系樹脂を含む、請求項１又は２に記載のダイバーティングエージェント。
  4. 　坑井に生成された亀裂を一時的に閉塞するためのダイバーティングエージェントの作製方法であって、
    　ポリビニルアルコール系樹脂を含有させ、
    　グアーガムの０．４８質量％水溶液に前記ダイバーティングエージェントを加えてダイバーティングエージェントの濃度が１２質量％の混合液を調製し、前記混合液を３０℃で６０分間分散させて分散液を得て、前記分散液を２ｍｍ幅のスリットを有する排水部を備えた加圧脱水装置を用いて１ＭＰａの圧力で加圧脱水し、時間の平方根ｘに対する積算脱水量ｙを求め、横軸に前記時間の平方根ｘを、縦軸に前記積算脱水量ｙをとったグラフにプロットした散布図から最小二乗法により下記式（Ａ）で表わされる回帰直線を算出したとき、式（Ａ）の傾きａが下記条件（Ｂ）を満たすものとするダイバーティングエージェントの作製方法。
    　　ｙ＝ａｘ＋ｂ　・・・（Ａ）
    　　ａ≦８０　・・・（Ｂ）
    （式（Ａ）中、ｙは積算脱水量（ｇ）、ｘは加圧開始から経過した時間（分）の平方根、ａ及びｂは回帰直線の傾きと切片を表わし、０＜ｘ≦２である。）
  5. 　坑井に生成された亀裂を一時的に閉塞する方法であって、
    　請求項１～３のいずれか１項に記載のダイバーティングエージェントを、坑井内の流体の流れにより亀裂に流入させる坑井の亀裂の閉塞方法。
PCT/JP2020/005300 2019-02-13 2020-02-12 ダイバーティングエージェント及びこれを用いた坑井の亀裂の閉塞方法 WO2020166595A1 (ja)