WO2020138070A1 - Composition adhésive pour fixer un composant mobile, composant optique, composant électronique et module électronique - Google Patents

Composition adhésive pour fixer un composant mobile, composant optique, composant électronique et module électronique Download PDF

Info

Publication number
WO2020138070A1
WO2020138070A1 PCT/JP2019/050585 JP2019050585W WO2020138070A1 WO 2020138070 A1 WO2020138070 A1 WO 2020138070A1 JP 2019050585 W JP2019050585 W JP 2019050585W WO 2020138070 A1 WO2020138070 A1 WO 2020138070A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
adhesive composition
fixing
examples
compound
Prior art date
Application number
PCT/JP2019/050585
Other languages
English (en)
Japanese (ja)
Inventor
秀幸 林
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to JP2020504248A priority Critical patent/JP7431720B2/ja
Publication of WO2020138070A1 publication Critical patent/WO2020138070A1/fr

Abstract

Un but de la présente invention est de fournir une composition adhésive pour fixer des composants mobiles qui présente une excellente adhésivité tant pour les métaux que pour les non-métaux, peut être durcie à basses températures, et peut empêcher les composants mobiles de se déplacer à partir des positions d'origine. Un autre but de la présente invention est de fournir un composant optique, un composant électronique et un module électronique, tous obtenus à l'aide de la composition adhésive pour fixer des composants mobiles. La composition adhésive pour fixer des composants mobiles de la présente invention comprend une résine de poly(acétal de vinyle), un composé ayant un groupe époxy et/ou un groupe (méth)acryloyle, et un durcisseur polymérisable et donne des objets durcis ayant un module de conservation à 25 °C de 1,0 GPa ou plus.
PCT/JP2019/050585 2018-12-26 2019-12-24 Composition adhésive pour fixer un composant mobile, composant optique, composant électronique et module électronique WO2020138070A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020504248A JP7431720B2 (ja) 2018-12-26 2019-12-24 可動部品固定用接着剤組成物、光学部品、電子部品、及び、電子モジュール

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-243464 2018-12-26
JP2018243464 2018-12-26

Publications (1)

Publication Number Publication Date
WO2020138070A1 true WO2020138070A1 (fr) 2020-07-02

Family

ID=71125712

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/050585 WO2020138070A1 (fr) 2018-12-26 2019-12-24 Composition adhésive pour fixer un composant mobile, composant optique, composant électronique et module électronique

Country Status (3)

Country Link
JP (1) JP7431720B2 (fr)
TW (1) TW202035624A (fr)
WO (1) WO2020138070A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10501898A (ja) * 1994-05-27 1998-02-17 ジ・ユニバーシティ・オブ・アクロン 非複屈折光学接着剤及び薄膜
JP2012067221A (ja) * 2010-09-24 2012-04-05 Sekisui Chem Co Ltd 絶縁シート及び積層構造体
JP2016125042A (ja) * 2015-01-08 2016-07-11 横浜ゴム株式会社 接着剤組成物、これを用いる光制御パネル、その製造方法、光学結像装置
JP2017110128A (ja) * 2015-12-17 2017-06-22 Dic株式会社 熱硬化性接着シート、物品及び物品の製造方法
JP2017137376A (ja) * 2016-02-01 2017-08-10 積水化学工業株式会社 高弾性接着剤及びキーシート接合用接着剤

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008035791A1 (fr) 2006-09-22 2008-03-27 Henkel Corporation Procédé de collage et composition de résine adhésive
JP6376058B2 (ja) 2015-07-06 2018-08-22 トヨタ自動車株式会社 車両用表示装置
TW202113012A (zh) 2019-05-31 2021-04-01 日商積水化學工業股份有限公司 接著劑組成物、光學零件、電子零件及電子模組
JP2020196881A (ja) 2019-05-31 2020-12-10 積水化学工業株式会社 接着剤組成物、光学部品、電子部品、及び、電子モジュール

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10501898A (ja) * 1994-05-27 1998-02-17 ジ・ユニバーシティ・オブ・アクロン 非複屈折光学接着剤及び薄膜
JP2012067221A (ja) * 2010-09-24 2012-04-05 Sekisui Chem Co Ltd 絶縁シート及び積層構造体
JP2016125042A (ja) * 2015-01-08 2016-07-11 横浜ゴム株式会社 接着剤組成物、これを用いる光制御パネル、その製造方法、光学結像装置
JP2017110128A (ja) * 2015-12-17 2017-06-22 Dic株式会社 熱硬化性接着シート、物品及び物品の製造方法
JP2017137376A (ja) * 2016-02-01 2017-08-10 積水化学工業株式会社 高弾性接着剤及びキーシート接合用接着剤

Also Published As

Publication number Publication date
JPWO2020138070A1 (ja) 2021-11-11
JP7431720B2 (ja) 2024-02-15
TW202035624A (zh) 2020-10-01

Similar Documents

Publication Publication Date Title
CN102985461B (zh) 固化性树脂组合物
CN102958974B (zh) 固化性树脂组合物
KR101170529B1 (ko) 액상 실리콘 변성 아크릴레이트 수지를 포함하는 광경화형 점착 조성물 및 이를 이용한 점착테이프
KR20150024708A (ko) 벤조트리아졸계 (메트)아크릴레이트 공중합체 및 이를 포함하는 접착제 조성물
KR101841894B1 (ko) 경화성 수지 조성물
JPWO2019182009A1 (ja) ダイボンディングフィルム、ダイシングダイボンディングシート、及び半導体チップの製造方法
JP7431720B2 (ja) 可動部品固定用接着剤組成物、光学部品、電子部品、及び、電子モジュール
JP7291075B2 (ja) エポキシ樹脂組成物
CN113853413B (zh) 粘接剂组合物、光学部件、电子部件及电子模块
WO2023276889A1 (fr) Film adhésif pour circuit de connexion, structure de connexion de circuit et son procédé de fabrication
US11551987B2 (en) Power module comprising a primer layer
JP6936052B2 (ja) 硬化性樹脂組成物
KR101841893B1 (ko) 경화성 수지 조성물
EP3960828A1 (fr) Composition de résine et produit durci correspondant
JP2020200451A (ja) 可動部品固定用接着剤組成物、光学部品、電子部品、及び、電子モジュール
WO2017078036A1 (fr) Film de résine durcissable et première feuille de formation de film protecteur
WO2017061364A1 (fr) Film de résine thermodurcissable et feuille destinée à former un premier film de protection
JP7044486B2 (ja) 硬化性樹脂組成物
WO2017078039A1 (fr) Film de résine thermodurcissable, feuille formant un premier film protecteur, et procédé de formation d'un premier film protecteur
JP2020196881A (ja) 接着剤組成物、光学部品、電子部品、及び、電子モジュール
WO2016114268A1 (fr) Composition de résine durcissable
JP2020132863A (ja) エポキシ接着剤組成物
CN108350320B (zh) 粘接剂组合物和结构体
JP7402048B2 (ja) エポキシ樹脂組成物
WO2011040438A1 (fr) Composition adhésive

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2020504248

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19905325

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19905325

Country of ref document: EP

Kind code of ref document: A1