WO2019189411A1 - Metal chloride generator, and method for manufacturing metal powder - Google Patents
Metal chloride generator, and method for manufacturing metal powder Download PDFInfo
- Publication number
- WO2019189411A1 WO2019189411A1 PCT/JP2019/013277 JP2019013277W WO2019189411A1 WO 2019189411 A1 WO2019189411 A1 WO 2019189411A1 JP 2019013277 W JP2019013277 W JP 2019013277W WO 2019189411 A1 WO2019189411 A1 WO 2019189411A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- heating furnace
- metal
- gas
- furnace
- chloride
- Prior art date
Abstract
Description
本発明の実施形態の一つに係る金属塩化物生成装置110、およびこれを含む金属粉体製造システム(以下、単にシステムと記す)100を説明する。 (First embodiment)
A metal
図1にシステム100の構成の概要を示す。システム100は、主な構成として、金属塩化物生成装置110と還元炉200を備える。図示しないが、システム100はさらに、還元炉200に接続される分離装置300や、還元炉200または分離装置300に接続されるバグフィルターなどの回収装置を備えてもよい。金属塩化物生成装置110と還元炉200は第1の輸送管112によって連結され、還元炉200と分離装置300は第2の輸送管202によって連結される。 1. Overall Configuration FIG. 1 shows an outline of the configuration of the
金属塩化物生成装置110の断面模式図を図2に示す。金属塩化物生成装置110は、主な構成として、塩化炉120、塩化炉120を囲むように設けられ、塩化炉120を加熱するための第1のヒータ160と第2のヒータ162を有する。第1のヒータ160と第2のヒータ162は、それぞれ独立に制御することが可能である。 2. Metal Chloride Generating Device A schematic cross-sectional view of the metal
本実施形態のシステム100の金属塩化物生成装置110では、金属導入口128や第3のガス導入口130を介して塩素を含むガスが導入される。このガスは、金属を塩化するため、および生成した塩化物の蒸気を第2の加熱炉124に輸送するための陽圧を与えるために導入される。 3. Contribution of Chlorine In the
金属塩化物生成装置110は、図2や図3に示した構成に限られない。例えば図4に示すように、塩化炉120は、化学的手段として機能する塩素を含むガスを供給するガス導入口を複数備えてもよい。塩素ガスは不活性ガスとともに供給されてよい。図4に示した例では、第2の加熱炉124に塩素を含むガスを導入するためのガス導入口(第2のガス導入口)142がさらに設けられている。第2のガス導入口142は、排出口134よりも上に配置することができる。すなわち、第1の加熱炉122から排出口134までの距離が、第1の加熱炉122から第2のガス導入口142までの距離よりも大きくなるように第2のガス導入口142を設けることができる。第2のガス導入口142は図示しない塩素源と連結され、塩素を含むガスの供給はバルブ144によって制御される。 4). Modification The metal chloride production |
本実施形態では、システム100を用いる金属粉体の製造方法について述べる。ここでは、図2に示した金属塩化物生成装置110を備えるシステム100を用いて金属粉体を製造する方法を例として説明する。第1実施形態で述べた構成と同様、あるいは類似する構成については説明を割愛することがある。 (Second Embodiment)
In this embodiment, a method for producing metal powder using the
本実施形態では、金属塩化物生成装置110と構造が異なる金属塩化物生成装置116の構造を説明する。第1実施形態で述べた構成と同一、あるいは類似する構成については説明を割愛することがある。 (Third embodiment)
In the present embodiment, the structure of the
本実施例では、図2に示した構造を基本構造として有する金属塩化物生成装置110を備えたシステム100を用いて銅粉体を製造した例を説明する。具体的には、第1の加熱炉122に銅のペレットを配置し、第2の加熱炉124に石英のペレットを配置した。この状態で第1のヒータ160と第2のヒータ162を用い、第1の加熱炉122と第2の加熱炉124がそれぞれ900℃、1150℃になるよう加熱を行った。金属導入口128と第1のガス導入口136からそれぞれ窒素と塩素を含む混合ガスを導入した。混合ガスの塩素濃度は表1に示すとおりである。表1には第1のガス導入口136から導入される混合ガスの流量を1.0とした場合の金属導入口128から導入される混合ガスの流量比(すなわち、第1のガス導入口136から導入される混合ガスに対する金属導入口128から導入される混合ガスの流量比)も記載した。反応時間は10時間とした。 Example 1
In this embodiment, an example will be described in which copper powder is manufactured using a
本実施例では、図4に示した構造を基本構造として有する金属塩化物生成装置110を備えるシステム100を用いて銅粉体を製造した例を説明する。具体的には、第1の加熱炉122に銅のペレットを配置し、第2の加熱炉124に石英のペレットを配置した。この状態で第1のヒータ160と第2のヒータ162を用い、第1の加熱炉122と第2の加熱炉124がそれぞれ900℃、1150℃になるよう加熱を行った。金属導入口128、第1のガス導入口136、および第2のガス導入口142からともに窒素と塩素を含む混合ガスを導入した。反応は二段階で行った。第1のガス導入口136から導入される混合ガスの流量を1.0とした際の、第2のガス導入口142および金属導入口128から導入される混合ガスの流量、およびそれぞれの混合ガス中の塩素濃度は表2に示すとおりである。第1のガス導入口136と第2のガス導入口142は同一の混合ガス源に接続されており、これらのガス導入口から導入される混合ガスの各成分の濃度は同一である。第1段階と第2段階の反応時間はそれぞれ9時間、8時間であった。 (Example 2)
In this embodiment, an example in which copper powder is manufactured using a
本実施例では、図2に示した構造を基本構造として有する金属塩化物生成装置110を備えるシステム100を用い、第1のガス導入口136から導入される混合ガスの塩素濃度の影響を検討した結果を示す。具体的には、第1の加熱炉122に銅のペレットを配置し、第2の加熱炉124に石英のペレットを配置した。この状態で第1のヒータ160と第2のヒータ162を用い、第1の加熱炉122と第2の加熱炉124がそれぞれ900℃、1150℃になるよう加熱を行った。金属導入口128と第1のガス導入口136からともに窒素と塩素を含む混合ガスを導入した。第1のガス導入口136から導入される混合ガスの流量を1.0とした際の金属導入口128から導入される混合ガスの流量を3.2に固定し、金属導入口128から導入される混合ガスの塩素濃度を43wt%に固定し、第1のガス導入口136から導入される混合ガス中の塩素ガス濃度を表3に示すように変化させた。表3における実験3は比較例であり、第1のガス導入口136から窒素のみが導入された実験である。反応時間は10時間とした。 Example 3
In this example, the influence of the chlorine concentration of the mixed gas introduced from the
Claims (15)
- 金属を導入するための金属導入口を有する第1の加熱炉、および前記第1の加熱炉と連結される第2の加熱炉を備える塩化炉、
前記第1の加熱炉を加熱する第1のヒータ、ならびに
前記第2の加熱炉を加熱する第2のヒータを有し、
前記第2の加熱炉は、前記金属の塩化物のガスを排出するための排出口を有し、
前記塩化炉は、塩素を含むガスを導入するための第1のガス導入口を有し、
前記第1のガス導入口は、前記第1のヒータと前記第2のヒータのいずれか一方に囲まれる、金属塩化物生成装置。 A chlorination furnace comprising a first heating furnace having a metal inlet for introducing metal, and a second heating furnace connected to the first heating furnace;
A first heater for heating the first heating furnace, and a second heater for heating the second heating furnace,
The second heating furnace has a discharge port for discharging the metal chloride gas,
The chlorination furnace has a first gas inlet for introducing a gas containing chlorine,
The first gas introduction port is a metal chloride generating device surrounded by one of the first heater and the second heater. - 前記第1のガス導入口は前記第2の加熱炉に設けられ、前記排出口と比較して前記第1の加熱炉から遠くに配置される、請求項1に記載の金属塩化物生成装置。 The metal chloride generator according to claim 1, wherein the first gas inlet is provided in the second heating furnace and is arranged farther from the first heating furnace than the outlet.
- 前記第1のガス導入口は前記第1の加熱炉に設けられ、
前記第1のガス導入口は、前記金属導入口よりも前記第1の加熱炉と前記第2の加熱炉の接続部に近い、請求項1に記載の金属塩化物生成装置。 The first gas inlet is provided in the first heating furnace;
2. The metal chloride generator according to claim 1, wherein the first gas introduction port is closer to a connection portion between the first heating furnace and the second heating furnace than the metal introduction port. - 前記第2の加熱炉は、塩素を含むガスを導入するための第2のガス導入口をさらに含み、
前記第2のガス導入口は、前記排出口と比較して前記第1の加熱炉により近く配置される、請求項2に記載の金属塩化物生成装置。 The second heating furnace further includes a second gas introduction port for introducing a gas containing chlorine,
The metal chloride generation device according to claim 2, wherein the second gas introduction port is disposed closer to the first heating furnace than the discharge port. - 前記第2のヒータは、前記第1の加熱炉の温度よりも高い温度で前記第2の加熱炉を加熱するように構成される、請求項1に記載の金属塩化物生成装置。 The metal chloride generator according to claim 1, wherein the second heater is configured to heat the second heating furnace at a temperature higher than a temperature of the first heating furnace.
- 前記第1の加熱炉は、塩素を含むガスを導入するための第3のガス導入口をさらに有し、
前記第3のガス導入口は、前記第1のヒータから露出される、請求項1に記載の金属塩化物生成装置。 The first heating furnace further has a third gas inlet for introducing a gas containing chlorine,
The metal chloride generator according to claim 1, wherein the third gas inlet is exposed from the first heater. - 前記第1の加熱炉は、
窒素を導入するための第4のガス導入口、および
前記窒素を加熱するための第3のヒータを有する、請求項1に記載の金属塩化物生成装置。 The first heating furnace includes:
The metal chloride generator according to claim 1, further comprising a fourth gas inlet for introducing nitrogen and a third heater for heating the nitrogen. - 前記第2の加熱炉の内径は、前記第1の加熱炉の内径より小さい、請求項1に記載の金属塩化物生成装置。 The metal chloride generator according to claim 1, wherein an inner diameter of the second heating furnace is smaller than an inner diameter of the first heating furnace.
- 第1のヒータと第2のヒータによって加熱されるように構成される塩化炉において金属を塩素ガスと反応させて前記金属の塩化物を生成すること、および
前記塩化炉に設けられる第1のガス導入口から塩素を含むガスを導入することで前記塩化物の蒸気を還元炉に輸送することを含み、
前記第1のガス導入口は、前記第1のヒータと前記第2のヒータのいずれか一方に囲まれる、金属粉体を製造する方法。 Reacting a metal with chlorine gas to produce a chloride of the metal in a chlorination furnace configured to be heated by a first heater and a second heater; and a first gas provided in the chlorination furnace Transporting the chloride vapor to a reduction furnace by introducing a gas containing chlorine from an inlet,
The method for producing metal powder, wherein the first gas inlet is surrounded by one of the first heater and the second heater. - 前記塩化炉は、
前記第1のヒータに囲まれる第1の加熱炉、および
前記第1の加熱炉に接続され、前記第2のヒータに囲まれる第2の加熱炉を有し、
前記方法は、前記第2の加熱炉において、前記塩化物を気化することをさらに含む、請求項9に記載の方法。 The chlorination furnace is
A first heating furnace surrounded by the first heater; and a second heating furnace connected to the first heating furnace and surrounded by the second heater;
The method of claim 9, further comprising vaporizing the chloride in the second furnace. - 前記第2の加熱炉において行われる前記塩化物の前記気化は、前記塩化物を生成する温度よりも高い温度で行う、請求項10に記載の方法。 The method according to claim 10, wherein the vaporization of the chloride performed in the second heating furnace is performed at a temperature higher than a temperature at which the chloride is generated.
- 前記第1のガス導入口は前記第1の加熱炉に設けられる、請求項10に記載の方法。 The method according to claim 10, wherein the first gas inlet is provided in the first heating furnace.
- 前記第1のガス導入口は前記第2の加熱炉に設けられる、請求項10に記載の方法。 The method according to claim 10, wherein the first gas inlet is provided in the second heating furnace.
- 前記塩化物の前記蒸気の前記還元炉への輸送は、前記第2の加熱炉に設けられる排出口を介して行われ、
塩素を含む前記ガスの導入は、前記第1のガス導入口、および前記第2の加熱炉に設けられる第2のガス導入口を用いて行われる、請求項13に記載の方法。 The transport of the vapor of the chloride to the reduction furnace is performed via an outlet provided in the second heating furnace,
The method according to claim 13, wherein the introduction of the gas containing chlorine is performed using the first gas introduction port and a second gas introduction port provided in the second heating furnace. - 前記第1の加熱炉に加熱された窒素を導入することをさらに含む、請求項10に記載の方法。
The method of claim 10, further comprising introducing heated nitrogen into the first furnace.