WO2019098741A1 - 원단 일체형 차량용 시트백 프레임 및 그의 제조방법 - Google Patents

원단 일체형 차량용 시트백 프레임 및 그의 제조방법 Download PDF

Info

Publication number
WO2019098741A1
WO2019098741A1 PCT/KR2018/014081 KR2018014081W WO2019098741A1 WO 2019098741 A1 WO2019098741 A1 WO 2019098741A1 KR 2018014081 W KR2018014081 W KR 2018014081W WO 2019098741 A1 WO2019098741 A1 WO 2019098741A1
Authority
WO
WIPO (PCT)
Prior art keywords
fabric
composite material
seat back
back frame
thermoplastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2018/014081
Other languages
English (en)
French (fr)
Inventor
김동관
길용길
문형준
강용한
김희준
박상현
이은국
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LX Hausys Ltd
Original Assignee
LG Hausys Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LG Hausys Ltd filed Critical LG Hausys Ltd
Publication of WO2019098741A1 publication Critical patent/WO2019098741A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임은 원단과, 상기 원단의 일측면에 결합된 열가소성 섬유강화복합소재로 이루어진 원단 일체형 복합소재를 포함한다. 본 발명에 의하면 스틸 프레임과 같은 강성 및 강도를 유지하면서 경량으로 이루어지고 원단과 일체로 형성됨에 따라, 도장, 원단감싸기등의 후공정을 생략할 수 있고, 원단이 일체로 형성됨에 따라 시트백 프레임에 추가로 결합되는 보드를 생략할 수 있어 슬림화된 원단 일체형 차량용 시트백 프레임을 얻을 수 있고, 간소한 공정을 통해 원단과 열가소성 섬유강화복합재료를 합지시키고, 합지된 원단 일체형 복합재료를 이용하여 간단하게 제조할 수 있는 원단 일체형 차량용 시트백 프레임 제조방법을 얻을 수 있다.

Description

원단 일체형 차량용 시트백 프레임 및 그의 제조방법
본 발명은 원단 일체형 차량용 시트백 프레임 및 그의 제조방법에 관한 것이고, 보다 구체적으로 원단과 열가소성 섬유강화복합소재가 결합된 원단 일체형 복합재료로 이루어진 차량용 시트백 프레임 및 그의 제조방법에 관한 것이다.
일반적으로, 차량용 시트는 승차감이나 안전에 관련된 중요한데，차량 주행 시 전달되는 충격이나 진동을 적절하게 흡수하여 승객에게 안락감을 제공한다. 또한 이러한 여건을 만족시키면서，승객의 안전을 보장하기 위하여 충분한 강성 및 강도를 가질 수 있어야 한다.
그리고 시트백 프레임은 차량의 시트 내측에 구비되는 강성 구조물로서 사용자가 편안하고 안정된 자세를 취할 수 있도록 도움을 주는 시트백의 기본 골격이다.
또한, 승용차의 시트백 프레임(이하，간략히 '시트백 프레임'이라 함)은 자동차가 급정거하거나 충돌이 일어났을 경우 승객 거동에 의한 시트의 파단， 변형이 발생하여 시트에 착석한 승객에게 큰 피해를 줄 수 있다.
이에 따라, 시트백 프레임은 차량 충돌，추돌 및 급정거 등의 상황에서 시트백의 자중에 의한 관성 때문에 시트백의 파손이 없을 것，일정한 힘으로 당기거나 밀 때 시트백의 영구 변형 및 파손이 없을 것 등을 규정하는 법규를 만족해야 한다.
한편， 종래의 방식에 따른 시트백 프레임은 스틸 등의 단일의 소재를 사용하여 제작되었다. 하지만，스틸 등의 재질로 시트백 프레임을 제작할 경우, 시트백 프레임의 자체 중랑이 증가되는 단점이 있었다.
이러한 종래의 문제점을 해결하고자 경랑이면서 구조적인 강성을 만족시킬 수 있으며，스틸 등의 재질로 제작하는 경우에 비해 제조 단가를 상대적으로 낮출 수 있는 개선된 형태의 시트백 프레임의 개발이 요구되는 실정이다.
본 발명의 일 관점은 스틸 프레임과 같은 강성 및 강도를 유지하면서 경량으로 이루어지고, 원단과 일체로 형성됨에 따라, 도장, 원단감싸기등의 후공정을 생략할 수 있고, 슬림화로 구현가능한 원단 일체형 차량용 시트백 프레임을 제공하기 위한 것이다.
본 발명의 다른 관점은 원단이 일체로 형성됨에 따라 시트백 프레임에 추가로 결합되는 보드를 생략할 수 있어 슬림화된 원단 일체형 차량용 시트백 프레임을 제공하기 위한 것이다.
본 발명의 또 다른 관점은 간소한 공정을 통해 원단과 열가소성 섬유강화복합재료를 합지시키고, 합지된 원단 일체형 복합재료를 이용하여 차량용 시트백 프레임을 제조하는 방법을 제공하기 위한 것이다.
본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임은 원단과, 상기 원단의 일측면에 결합된 열가소성 섬유강화복합소재로 이루어진 원단 일체형 복합소재를 포함한다.
또한, 원단 일체형 차량용 시트백 프레임에 있어서, 상기 원단은 PET 부직포를 포함하여 이루어질 수 있다.
또한, 원단 일체형 차량용 시트백 프레임에 있어서, 상기 원단의 타측면에는 실리콘 코팅층이 형성될 수 있다.
또한, 원단 일체형 차량용 시트백 프레임에 있어서, 상기 열가소성 섬유강화 복합소재는 연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT)를 포함하는 복합수지로 이루어질 수 있다.
또한, 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임은 프레임 바디 및 보강제를 포함하고, 상기 프레임 바디는 원단과, 상기 원단이 일면에 결합된 열가소성 섬유강화복합소재로 이루어진 원단 일체형 복합소재를 포함하고, 상기 보강제는 상기 프레임 바디의 내측에 결합된다.
또한, 상기 원단 일체형 차량용 시트백 프레임에 있어서, 상기 보강제는 상기 프레임 바디의 내측인 열가소성 섬유강화복합소재에 사출성형되고, 장섬유 강화 열가소성 수지(LFT: Long Fiber reinforced Thermoplastic) 또는 단섬유강화 열가소성 수지(SFT) 또는 장섬유 강화 열가소성 수지(LFT)를 포함하는 복합수지로 이루어질 수 있다.
본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임의 제조방법은 열가소성 섬유강화복합소재의 일면에 원단을 적층하여 원단 일체형 복합소재로 성형하기 위한 재료를 마련하는 열가소성수지 적층단계와, 적층된 상기 원단과 상기 열가소성 섬유강화복합소재에 열을 가하고, 가압하여 상기 원단과 상기 열가소성 섬유강화복합소재를 결합시켜 원단 일체형 복합소재를 형성하는 가열 및 가압 합지단계와, 상기 원단 일체형 복합소재를 차량용 시트백 프레임 형상으로 형성시키는 성형단계를 포함한다.
또한, 원단 일체형 차량용 시트백 프레임의 제조방법에 있어서, 상기 가열 및 가압 합지단계는 상기 원단에 대향된 열가소성 섬유강화복합소재의 일면이 열에 의해 용융되고, 상기 원단은 상기 열가소성 섬유강화복합소재의 일면에 가압되어 결합된다.
또한, 원단 일체형 차량용 시트백 프레임의 제조방법에 있어서, 상기 가열 및 가압 합지단계에서 가열온도는 220°C ~ 240°C이고, 압력은 5~6Bar로 제공될 수 있다.
또한, 원단 일체형 차량용 시트백 프레임의 제조방법에 있어서, 상기 열가소성 섬유강화복합소재는 연속섬유 강화 열가소성수지(CFT) 또는 연속섬유 강화 열가소성수지(CFT)를 포함하는 복합수지로 이루어질 수 있다.
또한, 원단 일체형 차량용 시트백 프레임의 제조방법에 있어서, 상기 성형단계는 프레스 가압 성형단계이고, 상기 프레스 가압전에 원단 일체형 복합소재에 열을 가하는 예열단계를 포함할 수 있다.
또한, 원단 일체형 차량용 시트백 프레임의 제조방법에 있어서, 상기 예열단계는 상기 원단 측 보다 상기 열가소성 섬유강화복합소재 측에 높은 온도를 제공할 수 있다.
기타 실시 예들의 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.
본 발명에 의하면 스틸 프레임과 같은 강성 및 강도를 유지하면서 경량으로 이루어지고 원단과 일체로 형성됨에 따라, 도장, 원단감싸기등의 후공정을 생략할 수 있고, 원단이 일체로 형성됨에 따라 시트백 프레임에 추가로 결합되는 보드를 생략할 수 있어 슬림화된 원단 일체형 차량용 시트백 프레임을 얻을 수 있고, 간소한 공정을 통해 원단과 열가소성 섬유강화복합재료를 합지시키고, 합지된 원단 일체형 복합재료를 이용하여 간단하게 제조할 수 있는 원단 일체형 차량용 시트백 프레임 제조방법을 얻을 수 있다.
본 발명의 기술적 사상의 실시예는, 구체적으로 언급되지 않은 다양한 효과를 제공할 수 있다는 것이 충분히 이해될 수 있을 것이다.
도 1은 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임의 재료인 원단 일체형 복합소재를 개략적으로 도시한 구성도이다.
도 2는 도 1에 도시한 원단 일체형 복합소재를 이용한 일실시예에 따른 원단 일체형 차량용 시트백 프레임을 개략적으로 도시한 평면도이다.
도 3은 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임의 제조방법을 개략적으로 도시한 순서도이다.
도 4는 도 3에 도시한 성형단계의 일실시예를 개략적으로 도시한 세부공정도이다.
도 5는 보강제가 성형된 원단 일체형 차량용 시트백 프레임의 일시예를 개략적으로 도시한 사시도이다.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세하게 설명한다.
도 1은 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임의 재료인 원단 일체형 복합소재를 개략적으로 도시한 구성도이다.
도시한 바와 같이, 원단 일체형 복합소재(100)는 원단(110)과 열가소성 섬유강화복합소재(120)를 포함한다.
보다 구체적으로, 원단(110)은 PET 부직포를 포함하여 이루어질 수 있다.
또한, 원단(110)에는 외부에서 가해지는 열에 의해 원단의 패턴이 변형되지 않도록 실리콘 코팅층(111)이 형성될 수 있다.
또한, 실리콘 코팅층(111)은 패턴보호기능을 확보하기 위해 0.2mm 내지 2mm 두께로 형성될 수 있다.
그리고 열가소성 섬유강화복합소재(120)는 실리콘 코팅층(111)이 형성되지 않은 원단(110)의 일측면에 결합되고, 연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT )를 포함하는 복합수지로 이루어질 수 있다.
또한, 연속섬유 강화 열가소성수지(CFT)에 포함된 열가소성 수지는 폴리프로필렌 수지, 폴리에틸렌 수지, 폴리아미드 수지, 폴리에스테르 수지, 폴리페닐렌설파이드 수지 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
그리고 연속섬유 강화 열가소성수지(CFT)는 폴리프로필렌 수지와 연속 유리섬유(GF: continuous glass fiber)로 이루어질 수 있다.
그리고 연속섬유 강화 열가소성수지(CFT)는 외부충격을 효과적으로 흡수하고, 강성 및 충격 강도가 높아 차량용 시트백 프레임으로 매우 적합하다.
그러나 연속섬유 강화 열가소성수지(CFT)를 이용하여 시트백 프레임을 성형할 경우 유리섬유가 노출되어 사용시 분진 및 따가움을 느낄 수 있고, 이를 방지하기 위해 도장 또는 원단 감싸기의 후공정이 요구된다.
그러나 본 발명의 일실시예에 따른 원단 일체형 복합소재(100)는 원단(110)이 열가소성 섬유강화복합소재(120)의 일면을 커버하면서 일체로 형성됨에 따라 상기한 문제점이 미연에 방지된다.
이에 대한 일예로서, 도 2는 도 1에 도시한 원단 일체형 복합소재를 이용한 일실시예에 따른 원단 일체형 차량용 시트백 프레임을 개략적으로 도시한 평면도이다.
도시한 바와 같이, 시트백 프레임(1000)는 원단부(1100)와 프레임부(1200)가 일체화된 원단 일체형 복합소재를 성형하여 이루어진다.
또한 원단부(1100)는 PET 부직포를 포함하여 이루어지고, 프레임부(1200)는 연속섬유 강화 열가소성수지(CFT)로 이루어진다.
그리고 원단 일체형 복합소재는 프레스에 의해 가압성형되어 도 2에 도시한 시트백 프레임(1000)이 형성된다.
이하, 도 3 및 도 4를 참조하여 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임을 제조하는 방법에 대하여 보다 자세히 기술한다.
도 3은 본 발명의 일실시예에 따른 원단 일체형 차량용 시트백 프레임의 제조방법을 개략적으로 도시한 순서도이다.
도시한 바와 같이, 원단 일체형 차량용 시트백 프레임의 제조방법(S1000)은 원단 및 연속섬유 강화 열가소성수지 적층단계(S1100), 가열 및 가압 합지단계(S1200) 및 성형단계(S1300)를 포함한다.
보다 구체적으로, 원단 및 열가소성 섬유강화 복합소재 적층단계(S1100)는 열가소성 섬유강화복합소재의 일면에 원단을 적층하여 원단 일체형 복합소재로 성형하기 위한 재료를 마련하기 위한 단계이다.
그리고, 열가소성 섬유강화복합소재는 연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT )를 포함하는 복합소재로 이루어질 수 있다.
다음으로, 가열 및 가압 합지단계(S1200)는 적층된 원단과 연속섬유 강화 열가소성수지(CFT)에 열을 가하고, 가압하여 원단과 연속섬유 강화 열가소성수지(CFT)를 결합시켜 원단 일체형 복합소재를 형성하는 단계이다.
즉, 상기 원단에 대향된 연속섬유 강화 열가소성수지(CFT)의 일면은 열에 의해 용융된 상태가 되고, 원단은 연속섬유 강화 열가소성수지(CFT)의 일면에 가압되어 결합된다.
그리고 가열온도는 220°C ~ 240°C이고, 압력은 5~6Bar로 가해질 수 있다.
이때, 원단은 외부에서 가해지는 열에 의해 원단의 패턴이 변형되지 않도록 실리콘 코팅층이 형성된 원단이 채택될 수 있다.
다음으로, 성형단계(S1300)은 가열 및 가압 합지단계(S1200)를 통해 원단과 연속섬유 강화 열가소성수지가 일체화된 원단 일체형 복합수지를 시트백 프레임 형상으로 성형하는 단계이다.
이를 위해 성형단계(S1300)는 프레스 가압 성형단계로 이루어질 수 있다.
그리고, 효율적인 성형을 위해 프레스 가압전에 원단 일체형 복합소재에 열을 가하는 예열단계를 포함한다.
그리고 예열단계에서 원단의 패턴이 변형되지 않도록 원단 측 보다 연속섬유 강화 열가소성수지 측에 높은 온도를 제공할 수 있다.
그리고 프레스로 가압하여 차량용 시트백 프레임의 모양을 형성시킨다.
결국, 상기한 바와 같은 공정으로 구현될 경우, 원단 일체형 복합소재는 2번의 가열단계를 거치게 된다. 즉, 가열 및 가압 합지단계(S1200)에서 1차로 가열되고, 성형단계(S1300)에서 2차로 가열된다.
따라서, 1차 가열단계인 가열 및 가압 합지단계(S1200)에서 합지효율을 향상시키기 위해 원단의 손상발생할 정도의 열을 가할 필요가 없고, 성형단계(S1300)를 통해 추가로 가열되고 가압됨에 따라 원단과 연속섬유 강화 열가소성수지는 완벽하게 일체화된다.
도 4는 도 3에 도시한 성형단계의 일실시예를 개략적으로 도시한 세부공정도이다.
도시한 바와 같이, 프레스 가압성형을 위해 원단 일체형 복합소재(100)를 상부금형(10)와 하부금형(20) 사이에 위치시킨다. 그리고 상부금형(10)을 하부로 이동시키고, 하부금형(20)을 상부로 이동시켜 원단 일체형 복합소재(100)를 가압 성형시킨다.
그리고 프레스 가압성형 단계에서 원단 일체형 복합소재에 열을 가한 후 성형공정을 구현할 수 있고, 이때 원단(110) 측 보다 연속섬유 강화 복합수지(120) 측에 높은 온도를 제공하는 것이 바람직하다.
또한, 원단 일체형 차량용 시트백 프레임은 추가공정인 사출성형에 의해 원단 일체형 차량용 시트백 프레임의 내측으로 보강재를 추가로 결합시킬 수 있다.
즉, 도 5는 보강제가 성형된 원단 일체형 차량용 시트백 프레임의 일시예를 개략적으로 도시한 사시도이다.
보다 구체적으로, 원단 일체형 차량용 시트백 프레임(2000)은 프레임 바디(2100) 및 보강제(2200)을 포함한다.
그리고 프레임 바디(2100)는 원단(2110)과 열가소성 섬유강화복합소재(2120)가 일체화되어 이루어진다.
또한, 프레임 바디(2100)은 상기 열가소성 섬유강화 복합소재로 이루어지고, 연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT)를 포함하는 복합수지로 이루어질 수 있다.
그리고 보강제(2200)는 프레임 바디(2100)의 내측인 열가소성 섬유강화복합소재에 사출성형된다.
또한, 보강제(2200)는 프레임 바디(2100)에 강성과 강도를 제공하기 위한 것으로서, 장섬유 강화 열가소성 수지(LFT: Long Fiber reinforced Thermoplastic) 또는 단섬유강화 열가소성 수지(SFT) 또는 장섬유 강화 열가소성 수지(LFT)를 포함하는 소재로 이루어질 수 있다.
그리고 보강제는 장섬유 강화 열가소성 수지(LFT)에 포함된 열가소성 수지는 폴리프로필렌 수지, 폴리에틸렌 수지, 폴리아미드 수지, 폴리에스테르 수지, 폴리페닐렌설파이드 수지 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
이에 따라, 원단 일체형 차량용 시트백 프레임(2000)은 내측으로 보강제(2200)가 내재되고, 외측으로 원단(2110)이 결합된 상태가 된다.
이상, 첨부된 도면을 참조하여 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.

Claims (12)

  1. 원단과, 상기 원단의 일측면에 결합된 열가소성 섬유강화복합소재로 이루어진 원단 일체형 복합소재를 포함하는
    원단 일체형 차량용 시트백 프레임.
  2. 제 1 항에 있어서,
    상기 원단은 PET 부직포를 포함하는
    원단 일체형 차량용 시트백 프레임.
  3. 제 2 항에 있어서,
    상기 원단의 타측면에는 실리콘 코팅층이 형성된
    원단 일체형 차량용 시트백 프레임.
  4. 제 1 항에 있어서,
    상기 열가소성 섬유강화 복합소재는
    연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT)를 포함하는 복합수지로 이루어진
    원단 일체형 차량용 시트백 프레임.
  5. 프레임 바디 및 보강제를 포함하고,
    상기 프레임 바디는
    원단과, 상기 원단이 일면에 결합된 열가소성 섬유강화복합소재로 이루어진 원단 일체형 복합소재를 포함하고,
    상기 보강제는 상기 프레임 바디의 내측에 결합된
    원단 일체형 차량용 시트백 프레임.
  6. 제 5 항에 있어서,
    상기 보강제는 상기 프레임 바디의 내측인 열가소성 섬유강화복합소재에 사출성형되고,
    장섬유 강화 열가소성 수지(LFT: Long Fiber reinforced Thermoplastic) 또는 단섬유강화 열가소성 수지(SFT) 또는 장섬유 강화 열가소성 수지(LFT)를 포함하는 복합수지로 이루어진
    원단 일체형 차량용 시트백 프레임.
  7. 열가소성 섬유강화복합소재의 일면에 원단을 적층하여 원단 일체형 복합소재로 성형하기 위한 재료를 마련하는 열가소성수지 적층단계;
    적층된 상기 원단과 상기 열가소성 섬유강화복합소재에 열을 가하고, 가압하여 상기 원단과 상기 열가소성 섬유강화복합소재를 결합시켜 원단 일체형 복합소재를 형성하는 가열 및 가압 합지단계: 및
    상기 원단 일체형 복합소재를 차량용 시트백 프레임 형상으로 형성시키는 성형단계를 포함하는
    원단 일체형 차량용 시트백 프레임의 제조방법.
  8. 제 7 항에 있어서,
    상기 가열 및 가압 합지단계는
    상기 원단에 대향된 열가소성 섬유강화복합소재의 일면이 열에 의해 용융되고, 상기 원단은 상기 열가소성 섬유강화복합소재의 일면에 가압되어 결합된
    원단 일체형 차량용 시트백 프레임의 제조방법.
  9. 제 8 항에 있어서,
    상기 가열 및 가압 합지단계에서 가열온도는 220°C ~ 240°C이고, 압력은 5~6Bar인
    원단 일체형 차량용 시트백 프레임의 제조방법.
  10. 제 8 항에 있어서,
    상기 열가소성 섬유강화복합소재는
    연속섬유 강화 열가소성수지(CFT: Continuous Fiber reinforced Thermoplastic) 또는 연속섬유 강화 열가소성수지(CFT)를 포함하는 복합수지로 이루어진
    원단 일체형 차량용 시트백 프레임의 제조방법.
  11. 제 8 항에 있어서,
    상기 성형단계는
    프레스 가압 성형단계이고, 상기 프레스 가압전에 원단 일체형 복합소재에 열을 가하는 예열단계를 포함하는
    원단 일체형 차량용 시트백 프레임의 제조방법.
  12. 제 11 항에 있어서,
    상기 예열단계는
    상기 원단 측 보다 상기 열가소성 섬유강화복합소재 측에 높은 온도를 제공하는
    원단 일체형 차량용 시트백 프레임의 제조방법.
PCT/KR2018/014081 2017-11-16 2018-11-16 원단 일체형 차량용 시트백 프레임 및 그의 제조방법 Ceased WO2019098741A1 (ko)