WO2019093474A1 - Plaque de polarisation circulaire et dispositif d'affichage - Google Patents

Plaque de polarisation circulaire et dispositif d'affichage Download PDF

Info

Publication number
WO2019093474A1
WO2019093474A1 PCT/JP2018/041654 JP2018041654W WO2019093474A1 WO 2019093474 A1 WO2019093474 A1 WO 2019093474A1 JP 2018041654 W JP2018041654 W JP 2018041654W WO 2019093474 A1 WO2019093474 A1 WO 2019093474A1
Authority
WO
WIPO (PCT)
Prior art keywords
circularly polarizing
polarizing plate
bending
polarizer
film
Prior art date
Application number
PCT/JP2018/041654
Other languages
English (en)
Japanese (ja)
Inventor
河村　真一
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2018201206A external-priority patent/JP2019091023A/ja
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to CN201880071779.2A priority Critical patent/CN111316144B/zh
Priority to KR1020207013006A priority patent/KR20200085755A/ko
Publication of WO2019093474A1 publication Critical patent/WO2019093474A1/fr

Abstract

La présente invention concerne une plaque de polarisation circulaire utilisée dans un dispositif d'affichage pliable pourvu d'un polariseur et d'au moins une couche de déphasage disposée sur un côté du polariseur, la teinte de la lumière réfléchie obtenue avant et après la courbure ne changeant pas de signe de part et d'autre de l'axe de coordonnées a* et de l'axe de coordonnées b* dans les coordonnées de chromaticité a*b* associées.
PCT/JP2018/041654 2017-11-10 2018-11-09 Plaque de polarisation circulaire et dispositif d'affichage WO2019093474A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201880071779.2A CN111316144B (zh) 2017-11-10 2018-11-09 圆偏振板及显示装置
KR1020207013006A KR20200085755A (ko) 2017-11-10 2018-11-09 원편광판 및 표시 장치

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2017217107 2017-11-10
JP2017-217107 2017-11-10
JP2018-201206 2018-10-25
JP2018201206A JP2019091023A (ja) 2017-11-10 2018-10-25 円偏光板

Publications (1)

Publication Number Publication Date
WO2019093474A1 true WO2019093474A1 (fr) 2019-05-16

Family

ID=66437889

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/041654 WO2019093474A1 (fr) 2017-11-10 2018-11-09 Plaque de polarisation circulaire et dispositif d'affichage

Country Status (1)

Country Link
WO (1) WO2019093474A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021026086A (ja) * 2019-08-02 2021-02-22 日東電工株式会社 位相差層付偏光板およびそれを用いた画像表示装置
JPWO2021039625A1 (fr) * 2019-08-28 2021-03-04
WO2021187098A1 (fr) * 2020-03-19 2021-09-23 住友化学株式会社 Feuille de polarisation circulaire et stratifié optique
WO2021187099A1 (fr) * 2020-03-19 2021-09-23 住友化学株式会社 Feuille de polarisation circulaire et stratifié optique
WO2022024469A1 (fr) * 2020-07-28 2022-02-03 日東電工株式会社 Corps stratifié optique et dispositif d'affichage d'image comprenant une plaque de polarisation avec une couche de déphasage de corps stratifié optique

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004258394A (ja) * 2003-02-26 2004-09-16 Dainippon Printing Co Ltd 光学機能性膜、反射防止フィルム、偏光板および表示装置
JP2008509433A (ja) * 2004-08-03 2008-03-27 スリーエム イノベイティブ プロパティズ カンパニー 固有偏光子、および固有偏光子を製造する方法
WO2016158300A1 (fr) * 2015-03-31 2016-10-06 富士フイルム株式会社 Plaque de polarisation circulaire et dispositif d'affichage pliable
JP2017502360A (ja) * 2013-12-06 2017-01-19 チャンカン・ケミカル・カンパニー・リミテッド 光学部材及びこれを備える表示装置
JP2017102443A (ja) * 2015-11-20 2017-06-08 日東電工株式会社 光学積層体および該光学積層体を用いた有機エレクトロルミネセンス表示装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004258394A (ja) * 2003-02-26 2004-09-16 Dainippon Printing Co Ltd 光学機能性膜、反射防止フィルム、偏光板および表示装置
JP2008509433A (ja) * 2004-08-03 2008-03-27 スリーエム イノベイティブ プロパティズ カンパニー 固有偏光子、および固有偏光子を製造する方法
JP2017502360A (ja) * 2013-12-06 2017-01-19 チャンカン・ケミカル・カンパニー・リミテッド 光学部材及びこれを備える表示装置
WO2016158300A1 (fr) * 2015-03-31 2016-10-06 富士フイルム株式会社 Plaque de polarisation circulaire et dispositif d'affichage pliable
JP2017102443A (ja) * 2015-11-20 2017-06-08 日東電工株式会社 光学積層体および該光学積層体を用いた有機エレクトロルミネセンス表示装置

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021026086A (ja) * 2019-08-02 2021-02-22 日東電工株式会社 位相差層付偏光板およびそれを用いた画像表示装置
CN114207484A (zh) * 2019-08-02 2022-03-18 日东电工株式会社 带相位差层的偏振片及使用其的图像显示装置
JPWO2021039625A1 (fr) * 2019-08-28 2021-03-04
WO2021039625A1 (fr) * 2019-08-28 2021-03-04 富士フイルム株式会社 Dispositif d'affichage à électroluminescence organique
JP7316363B2 (ja) 2019-08-28 2023-07-27 富士フイルム株式会社 有機エレクトロルミネッセンス表示装置
WO2021187098A1 (fr) * 2020-03-19 2021-09-23 住友化学株式会社 Feuille de polarisation circulaire et stratifié optique
WO2021187099A1 (fr) * 2020-03-19 2021-09-23 住友化学株式会社 Feuille de polarisation circulaire et stratifié optique
WO2022024469A1 (fr) * 2020-07-28 2022-02-03 日東電工株式会社 Corps stratifié optique et dispositif d'affichage d'image comprenant une plaque de polarisation avec une couche de déphasage de corps stratifié optique
JP2022024757A (ja) * 2020-07-28 2022-02-09 日東電工株式会社 光学積層体および該光学積層体の位相差層付偏光板を含む画像表示装置
JP7046127B2 (ja) 2020-07-28 2022-04-01 日東電工株式会社 光学積層体および該光学積層体の位相差層付偏光板を含む画像表示装置
JP7046127B6 (ja) 2020-07-28 2023-12-18 日東電工株式会社 光学積層体および該光学積層体の位相差層付偏光板を含む画像表示装置

Similar Documents

Publication Publication Date Title
JP6605682B2 (ja) 円偏光板
JP6589033B2 (ja) 表示装置
WO2019093474A1 (fr) Plaque de polarisation circulaire et dispositif d'affichage
JP2019091023A (ja) 円偏光板
JP2019098400A (ja) 積層フィルムの切断方法及び製造方法
JP2020086429A (ja) 光学積層体及びそれを備えた画像表示装置
WO2020121965A1 (fr) Stratifié et dispositif d'affichage d'image le comprenant
JP2021196575A (ja) 円偏光板、光学積層体、及びそれらを用いた画像表示パネル、画像表示装置
KR20220088414A (ko) 광학 적층체 및 표시 장치
JP2020118989A (ja) 光学フィルム
WO2019093501A1 (fr) Plaque de polarisation circulaire et dispositif d'affichage
WO2019093476A1 (fr) Plaque à polarisation circulaire et dispositif d'affichage
KR102668003B1 (ko) 원편광판 및 표시 장치
WO2020121964A1 (fr) Corps empilé et dispositif d'affichage d'image mettant en œuvre un tel corps empilé
JP7205202B2 (ja) 積層体およびそれを用いた画像表示装置
JP2021196576A (ja) 円偏光板、光学積層体、及びそれらを用いた画像表示パネル、画像表示装置
WO2020100468A1 (fr) Stratifié optique et dispositif d'affichage d'image le comprenant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18876188

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18876188

Country of ref document: EP

Kind code of ref document: A1