WO2019090562A1 - Ultrasonic atomizing nozzle for mining - Google Patents
Ultrasonic atomizing nozzle for mining Download PDFInfo
- Publication number
- WO2019090562A1 WO2019090562A1 PCT/CN2017/110121 CN2017110121W WO2019090562A1 WO 2019090562 A1 WO2019090562 A1 WO 2019090562A1 CN 2017110121 W CN2017110121 W CN 2017110121W WO 2019090562 A1 WO2019090562 A1 WO 2019090562A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- parts
- atomizing nozzle
- protective lacquer
- ultrasonic atomizing
- Prior art date
Abstract
An ultrasonic atomizing nozzle for mining. The surface of a metal housing of the nozzle is coated with a protective paint. The protective paint is prepared by the following steps: 1) sequentially adding 1-2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of oleoyl methylamine sodium ethanesulfonate, 2.2 parts by weight of gamma-methacryloxypropyltrimethoxysilane, and 8 parts by weight of phenolic resin into 24 parts by weight of deionized water, and stirring the mixture uniformly; and (2) then sequentially adding 14 parts by weight of polyvinyl acetate emulsion, 2.1 parts by weight of polycaprolactone, 1.2 parts by weight of alkyl naphthalene sulphonate, 0.5 weight part of ethylene diamine tetracetate, and 2.1 parts by weight of polyacrylate, and continuing stirring till the materials are fully and uniformly mixed so as to obtain a protective paint.
Description
本发明涉及一种矿用超声雾化喷嘴。The invention relates to a mine ultrasonic atomizing nozzle.
现有矿用超声雾化喷嘴,其金属壳体的耐腐蚀、防锈、防静电、耐热、抗氧化性能有待改进,影响矿用超声雾化喷嘴的长期使用。The existing mine ultrasonic atomizing nozzle has the corrosion resistance, rust prevention, antistatic, heat resistance and oxidation resistance of the metal casing to be improved, and affects the long-term use of the mineral ultrasonic atomizing nozzle.
发明内容Summary of the invention
本发明的目的在于提供一种矿用超声雾化喷嘴,其金属壳体表面涂覆有防护漆,使金属壳体具有优异的耐腐蚀、防锈、防静电、耐热、抗氧化性能,从而保障矿用超声雾化喷嘴能长期使用。The object of the present invention is to provide a mine ultrasonic atomizing nozzle, wherein the metal shell surface is coated with a protective lacquer, so that the metal shell has excellent corrosion resistance, rust prevention, antistatic, heat resistance and oxidation resistance, thereby The mine ultrasonic atomizing nozzle can be used for a long time.
为实现上述目的,本发明的技术方案是设计一种矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:In order to achieve the above object, the technical solution of the present invention is to design a mine ultrasonic atomizing nozzle, which comprises a metal casing, the metal casing surface is coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1~2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 to 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium methacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyl Trimethoxysilane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
优选的,矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:Preferably, the mining ultrasonic atomizing nozzle comprises a metal casing, the metal casing surface is coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 part by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
优选的,矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:Preferably, the mining ultrasonic atomizing nozzle comprises a metal casing, the metal casing surface is coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;
1) 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
优选的,矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:Preferably, the mining ultrasonic atomizing nozzle comprises a metal casing, the metal casing surface is coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1.2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1.2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
本发明的优点和有益效果在于:提供一种矿用超声雾化喷嘴,其金属壳体表面涂覆有防护漆,使金属壳体具有优异的耐腐蚀、防锈、防静电、耐热、抗氧化性能,从而保障矿用超声雾化喷嘴能长期使用。The invention has the advantages and beneficial effects of providing a mine ultrasonic atomizing nozzle, wherein the metal shell surface is coated with a protective paint, so that the metal shell has excellent corrosion resistance, rust prevention, antistatic, heat resistance and resistance. Oxidation properties, thus ensuring long-term use of mine ultrasonic atomizing nozzles.
“防护漆”的性能和用途是由其组分及配比所决定的,且“防护漆”中的不同组分会相互影响,组分及其配比会决定“防护漆”的最终性能,如果组分及其配比不相互协调,单个组分所带来的有益效果,会被其他组分消减甚至消除,严重的时候,不同组分相互抵触,起不到整体综合作用,产生负作用和次品。本发明通过大量创造性劳动、反复验证,得到“防护漆”的最优组分及配比,使得多个组分综合在一起、相互协调、并产生正向综合效应。The performance and use of "protective paint" is determined by its composition and proportion, and the different components of the "protective paint" will affect each other. The composition and its ratio will determine the final performance of the "protective paint". The components and their ratios are not coordinated with each other. The beneficial effects brought by the individual components will be reduced or even eliminated by other components. In severe cases, the different components will conflict with each other and will not function as a whole, resulting in a negative effect. Defective. The invention obtains the optimal composition and proportion of the "protective paint" through a large amount of creative labor and repeated verification, so that the multiple components are integrated, coordinated, and have a positive comprehensive effect.
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。The specific embodiments of the present invention are further described below in conjunction with the embodiments. The following examples are only intended to more clearly illustrate the technical solutions of the present invention, and are not intended to limit the scope of the present invention.
本发明具体实施的技术方案是:The technical solution specifically implemented by the present invention is:
实施例1Example 1
矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic ultrasonic atomizing nozzle comprises a metal shell coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1~2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 to 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium methacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyl Trimethoxysilane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。
2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
实施例2Example 2
矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic ultrasonic atomizing nozzle comprises a metal shell coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 part by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
实施例3Example 3
矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic ultrasonic atomizing nozzle comprises a metal shell coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
实施例4Example 4
矿用超声雾化喷嘴,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic ultrasonic atomizing nozzle comprises a metal shell coated with a protective lacquer, and the protective lacquer is prepared by the following steps:
1)将1.2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1.2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;
2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
上述各实施例的矿用超声雾化喷嘴,其金属壳体表面涂覆有防护漆,使金属壳体具有优异的耐腐蚀、防锈、防静电、耐热、抗氧化性能,从而保障矿用超声雾化喷嘴能长期使用。The mining ultrasonic atomizing nozzle of the above embodiments has a metal shell surface coated with a protective lacquer, so that the metal shell has excellent corrosion resistance, rust prevention, antistatic, heat resistance and oxidation resistance, thereby ensuring mining. Ultrasonic atomizing nozzles can be used for a long time.
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
The above description is only a preferred embodiment of the present invention, and it should be noted that those skilled in the art can make several improvements and retouchings without departing from the technical principles of the present invention. It should also be considered as the scope of protection of the present invention.
Claims (4)
- 一种矿用超声雾化喷嘴,其特征在于,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:A mine ultrasonic atomizing nozzle is characterized in that it comprises a metal shell coated with a protective lacquer, and the protective lacquer is prepared by the following steps:1)将1~2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 to 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium methacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyl Trimethoxysilane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
- 根据权利要求1所述的矿用超声雾化喷嘴,其特征在于,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic atomizing nozzle for mine according to claim 1, comprising a metal casing coated with a protective lacquer, the protective lacquer being prepared by the following steps:1)将1重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1 part by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
- 根据权利要求1所述的矿用超声雾化喷嘴,其特征在于,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic atomizing nozzle for mine according to claim 1, comprising a metal casing coated with a protective lacquer, the protective lacquer being prepared by the following steps:1)将2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。 2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.
- 根据权利要求1所述的矿用超声雾化喷嘴,其特征在于,包括金属壳体,该金属壳体表面凃覆有防护漆,所述防护漆通过如下步骤制备:The ultrasonic atomizing nozzle for mine according to claim 1, comprising a metal casing coated with a protective lacquer, the protective lacquer being prepared by the following steps:1)将1.2重量份乙二醇丁醚、1.5重量份聚甲基丙烯酸钾盐、1.9重量份油酰甲胺乙磺酸钠、2.2重量份γ-(甲基丙烯酰氧)丙基三甲氧基硅烷、8重量份酚醛树脂依次投入24重量份去离子水中,搅拌均匀;1) 1.2 parts by weight of ethylene glycol butyl ether, 1.5 parts by weight of potassium polymethacrylate, 1.9 parts by weight of sodium oleate, and 2.2 parts by weight of γ-(methacryloyloxy)propyltrimethoxy Base silane, 8 parts by weight of phenolic resin were sequentially put into 24 parts by weight of deionized water, and stirred uniformly;2)再依次投入14重量份白乳胶、2.1重量份聚己酸内醋、1.2重量份烷基萘磺酸盐、0.5重量份乙二胺四乙酸盐、2.1重量份聚丙烯酸酯,继续搅拌,至充分混合均匀,制得防护漆。 2) Further, 14 parts by weight of white latex, 2.1 parts by weight of polycaprolactone vinegar, 1.2 parts by weight of alkylnaphthalenesulfonate, 0.5 part by weight of ethylenediaminetetraacetate, 2.1 parts by weight of polyacrylate, and then stirring were continuously added. , to fully mix evenly, to obtain protective paint.