CN108296429A - A kind of Special Processes of Metal Castings new coating - Google Patents
A kind of Special Processes of Metal Castings new coating Download PDFInfo
- Publication number
- CN108296429A CN108296429A CN201810247538.0A CN201810247538A CN108296429A CN 108296429 A CN108296429 A CN 108296429A CN 201810247538 A CN201810247538 A CN 201810247538A CN 108296429 A CN108296429 A CN 108296429A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal castings
- special processes
- new coating
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of Special Processes of Metal Castings new coatings, it is characterised in that：It is prepared by following raw material in parts by weight：Vulcanize 12 ~ 23 parts of silicone elastomer；6 ~ 12 parts of adjacent benzoic acid dibutyl ester；20 ~ 26 parts of acrylic emulsion；5 ~ 8 parts of three silane of methyl；2 ~ 6 parts of antimony oxide；1 ~ 4 part of titanium dioxide；Six 2 ~ 8 parts of phosphorus meta-acid sodium；12 ~ 15 parts of foamed polystyrene；6 ~ 10 parts of Se deposit；4 ~ 10 parts of copper oxide, 3 ~ 7 parts of manganese oxide, 3 ~ 7 parts of iron oxide red；The Special Processes of Metal Castings new coating provided in the present invention, performance is stablized after paint film is solid, and the especially performances such as oil resistant, water-fast, resistance to oil-water mixture are more excellent；And adhesive force is good, flexibility, wearability, excellent impact resistance, it is not easy to cure blocking, suitable long-term construction operation.
Description
Technical field
The present invention relates to sapecial coating field more particularly to a kind of Special Processes of Metal Castings new coatings.
Background technology
Oil resistance anticorrosion coating property is stable, reliable, and the anti-corrosion phase imitates up to 10 years or more, is a kind of infant industry haveing excellent performance
Coating, while meeting the characteristic requirements of environmental protection coating material, it is environment-protecting and non-poisonous.Matching performance is good, as a result of Novel curing agent, no
Only small toxicity, and it is wide to construction temperature adaptability, you can it constructs, can also cure at low temperature at high temperature.But due to length
In phase storage or exposure air weight, then it is blocking to be easy solidification, it is difficult to use.
Invention content
That the technical problem to be solved in the present invention is to provide a kind of corrosion resistant performances is good, the Special Processes of Metal Castings of shelf life length are with novel
Coating.
In order to solve the above technical problems, the technical scheme is that：A kind of Special Processes of Metal Castings new coating, innovative point
It is：It is prepared by following raw material in parts by weight：Vulcanize 12 ~ 23 parts of silicone elastomer；6 ~ 12 parts of adjacent benzoic acid dibutyl ester；
20 ~ 26 parts of acrylic emulsion；5 ~ 8 parts of three silane of methyl；2 ~ 6 parts of antimony oxide；1 ~ 4 part of titanium dioxide；Six phosphorus meta-acid sodium 2
~ 8 parts；12 ~ 15 parts of foamed polystyrene；6 ~ 10 parts of Se deposit；4 ~ 10 parts of copper oxide, 3 ~ 7 parts of manganese oxide, iron oxide red 3 ~ 7
Part.
The advantage of the invention is that：
1）The Special Processes of Metal Castings new coating provided in the present invention, performance is stablized after paint film is solid, especially oil resistant, water-fast, oil resistant
The performances such as water mixed liquid are more excellent；And adhesive force is good, flexibility, wearability, excellent impact resistance, it is not easy to be solidified into
Block is suitble to long-term construction operation.
Specific implementation mode
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among the embodiment described range.
Embodiment 1：
A kind of Special Processes of Metal Castings new coating, is prepared by following raw material in parts by weight：Vulcanize 12 parts of silicone elastomer；
6 parts of adjacent benzoic acid dibutyl ester；20 parts of acrylic emulsion；5 parts of three silane of methyl；2 parts of antimony oxide；1 part of titanium dioxide；Six phosphorus
2 parts of meta-acid sodium；12 parts of foamed polystyrene；6 parts of Se deposit；4 parts of copper oxide, 3 parts of manganese oxide, 3 parts of iron oxide red.
Embodiment 2：
A kind of Special Processes of Metal Castings new coating, is prepared by following raw material in parts by weight：Vulcanize 17 parts of silicone elastomer；
9 parts of adjacent benzoic acid dibutyl ester；23 parts of acrylic emulsion；6.5 parts of three silane of methyl；4 parts of antimony oxide；2.5 parts of titanium dioxide；
Six 6 parts of phosphorus meta-acid sodium；13.5 parts of foamed polystyrene；8 parts of Se deposit；7 parts of copper oxide, 5 parts of manganese oxide, 5 parts of iron oxide red.
Embodiment 3：
A kind of Special Processes of Metal Castings new coating, is prepared by following raw material in parts by weight：Vulcanize 23 parts of silicone elastomer；
12 parts of adjacent benzoic acid dibutyl ester；26 parts of acrylic emulsion；8 parts of three silane of methyl；6 parts of antimony oxide；4 parts of titanium dioxide；Six
8 parts of phosphorus meta-acid sodium；15 parts of foamed polystyrene；10 parts of Se deposit；10 parts of copper oxide, 7 parts of manganese oxide, 7 parts of iron oxide red.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also has
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
It is defined by the appending claims and its equivalent thereof.
Claims (1)
1. a kind of Special Processes of Metal Castings new coating, it is characterised in that：It is prepared by following raw material in parts by weight：Vulcanize silica
12 ~ 23 parts of alkane elastomer；6 ~ 12 parts of adjacent benzoic acid dibutyl ester；20 ~ 26 parts of acrylic emulsion；5 ~ 8 parts of three silane of methyl；Three oxidations
Two 2 ~ 6 parts of antimony；1 ~ 4 part of titanium dioxide；Six 2 ~ 8 parts of phosphorus meta-acid sodium；12 ~ 15 parts of foamed polystyrene；6 ~ 10 parts of Se deposit；Oxygen
Change 4 ~ 10 parts of copper, 3 ~ 7 parts of manganese oxide, 3 ~ 7 parts of iron oxide red.