WO2019078479A1 - Composition de résine thermoplastique et produit moulé formé à partir de celle-ci - Google Patents

Composition de résine thermoplastique et produit moulé formé à partir de celle-ci Download PDF

Info

Publication number
WO2019078479A1
WO2019078479A1 PCT/KR2018/010017 KR2018010017W WO2019078479A1 WO 2019078479 A1 WO2019078479 A1 WO 2019078479A1 KR 2018010017 W KR2018010017 W KR 2018010017W WO 2019078479 A1 WO2019078479 A1 WO 2019078479A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
thermoplastic resin
weight
vinyl
aromatic vinyl
Prior art date
Application number
PCT/KR2018/010017
Other languages
English (en)
Korean (ko)
Inventor
임성오
김은진
추동휘
권영철
Original Assignee
롯데첨단소재(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 롯데첨단소재(주) filed Critical 롯데첨단소재(주)
Priority to JP2020518696A priority Critical patent/JP7145941B2/ja
Priority to CN201880063130.6A priority patent/CN111201279A/zh
Publication of WO2019078479A1 publication Critical patent/WO2019078479A1/fr

Abstract

La présente invention concerne une composition de résine thermoplastique comprenant : (A) un copolymère greffé à base de vinyle modifié par du caoutchouc ; (B) un premier copolymère à base de vinyle-cyanovinyle aromatique ayant une masse moléculaire moyenne en poids d'environ 100 000 à 500 000 g/mol ; (C) un deuxième copolymère à base de vinyle-cyanovinyle aromatique ayant une masse moléculaire moyenne en poids d'environ 4 000 000 g/mol ou plus ; et (D) de l'oxyde de zinc, le rapport en masse de (C) et (D) étant d'environ 1 : environ 0,5 à environ 1 : environ 5.
PCT/KR2018/010017 2017-10-19 2018-08-30 Composition de résine thermoplastique et produit moulé formé à partir de celle-ci WO2019078479A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2020518696A JP7145941B2 (ja) 2017-10-19 2018-08-30 熱可塑性樹脂組成物及びこれから形成された成形品
CN201880063130.6A CN111201279A (zh) 2017-10-19 2018-08-30 热塑性树脂组合物和由其形成的模制品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2017-0135788 2017-10-19
KR1020170135788A KR101925728B1 (ko) 2017-10-19 2017-10-19 열가소성 수지 조성물 및 이로부터 형성된 성형품

Publications (1)

Publication Number Publication Date
WO2019078479A1 true WO2019078479A1 (fr) 2019-04-25

Family

ID=64744040

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2018/010017 WO2019078479A1 (fr) 2017-10-19 2018-08-30 Composition de résine thermoplastique et produit moulé formé à partir de celle-ci

Country Status (4)

Country Link
JP (1) JP7145941B2 (fr)
KR (1) KR101925728B1 (fr)
CN (1) CN111201279A (fr)
WO (1) WO2019078479A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20220049180A (ko) * 2020-10-14 2022-04-21 주식회사 엘지화학 열가소성 수지 조성물, 이의 제조방법 및 이를 포함하는 성형품

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1135787A (ja) * 1997-07-24 1999-02-09 Techno Polymer Kk 抗菌性熱可塑性樹脂組成物
KR20000046093A (ko) * 1998-12-31 2000-07-25 유현식 성형 및 압출안정성이 우수한 열가소성 수지조성물
KR20020054688A (ko) * 2000-12-28 2002-07-08 안복현 진공성형성이 우수한 스티렌계 열가소성 수지 조성물
KR20030010239A (ko) * 2001-07-26 2003-02-05 제일모직주식회사 압출 가공성이 우수한 열가소성 수지 조성물
JP2005239904A (ja) * 2004-02-26 2005-09-08 Techno Polymer Co Ltd 熱可塑性樹脂組成物及び成形品

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101469263B1 (ko) * 2011-12-22 2014-12-05 제일모직주식회사 열가소성 수지 조성물 및 그 성형품
KR101874160B1 (ko) * 2015-09-30 2018-07-04 롯데첨단소재(주) 투명 열가소성 수지 조성물 및 이로부터 형성된 성형품

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1135787A (ja) * 1997-07-24 1999-02-09 Techno Polymer Kk 抗菌性熱可塑性樹脂組成物
KR20000046093A (ko) * 1998-12-31 2000-07-25 유현식 성형 및 압출안정성이 우수한 열가소성 수지조성물
KR20020054688A (ko) * 2000-12-28 2002-07-08 안복현 진공성형성이 우수한 스티렌계 열가소성 수지 조성물
KR20030010239A (ko) * 2001-07-26 2003-02-05 제일모직주식회사 압출 가공성이 우수한 열가소성 수지 조성물
JP2005239904A (ja) * 2004-02-26 2005-09-08 Techno Polymer Co Ltd 熱可塑性樹脂組成物及び成形品

Also Published As

Publication number Publication date
JP2021500423A (ja) 2021-01-07
CN111201279A (zh) 2020-05-26
KR101925728B1 (ko) 2018-12-05
JP7145941B2 (ja) 2022-10-03

Similar Documents

Publication Publication Date Title
WO2018080013A1 (fr) Composition de résine thermoplastique et produit moulé fabriqué à partir de celle-ci
WO2018084484A2 (fr) Composition de résine thermoplastique et produit moulé fabriqué à partir de celle-ci
WO2018038573A1 (fr) Composition de résine thermoplastique et article moulé fabriqué à partir de celle-ci
WO2019031694A1 (fr) Composition de résine thermoplastique et produit moulé fabriqué à partir de ladite composition
WO2018124657A1 (fr) Composition de résine thermoplastique et article moulé fabriqué avec celle-ci
WO2012144781A2 (fr) Matériau composite de polymère biodégradable
WO2019078464A1 (fr) Composition de résine thermoplastique et article moulé formé à partir de celle-ci
WO2019066193A1 (fr) Composition de résine thermoplastique résistante aux rayonnements ionisants et article moulé comprenant celle-ci
WO2020067681A1 (fr) Composition de résine thermoplastique et produit moulé l'utilisant
WO2018124594A1 (fr) Composition de résine thermoplastique et article moulé fabriqué à partir de celle-ci
WO2019103519A2 (fr) Composition de résine
WO2017082661A1 (fr) Composition de résine thermoplastique et article moulé comprenant cette dernière
WO2019132371A1 (fr) Composition de résine thermoplastique et produit moulé formé à partir de celle-ci
WO2019132575A1 (fr) Composition de résine thermoplastique et article moulé fabriqué à partir de celle-ci
WO2019124855A1 (fr) Composition de résine thermoplastique et produit moulé fabriqué à partir de cette dernière
WO2017057904A1 (fr) Composition de résine thermoplastique et produit moulé la comprenant
WO2018124592A1 (fr) Composition de résine thermoplastique et article moulé produit à partir de celle-ci
WO2019078479A1 (fr) Composition de résine thermoplastique et produit moulé formé à partir de celle-ci
WO2020138785A1 (fr) Composition de résine thermoplastique et produit moulé formé à partir de celle-ci
WO2018043930A1 (fr) Copolymère à base de vinyle aromatique, son procédé de préparation et composition de résine thermoplastique comprenant celui-ci
WO2019093636A1 (fr) Composition de résine thermoplastique et article moulé produit à partir de celle-ci
WO2022211458A1 (fr) Composition de résine thermoplastique et article fabriqué à l'aide de celle-ci
WO2018124614A1 (fr) Composition de résine thermoplastique
WO2022114589A1 (fr) Composition de résine thermoplastique et produit moulé fabriqué à partir de celle-ci
EP1920003A1 (fr) Composition polymère comprenant une résine polymère styrénique modifiée par du caoutchouc et un polymère de caoutchouc éthylenique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18869378

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020518696

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18869378

Country of ref document: EP

Kind code of ref document: A1