WO2019008779A1 - 離型剤組成物、離型膜の形成方法、離型剤組成物の製造方法、及び製造装置 - Google Patents

離型剤組成物、離型膜の形成方法、離型剤組成物の製造方法、及び製造装置 Download PDF

Info

Publication number
WO2019008779A1
WO2019008779A1 PCT/JP2017/025935 JP2017025935W WO2019008779A1 WO 2019008779 A1 WO2019008779 A1 WO 2019008779A1 JP 2017025935 W JP2017025935 W JP 2017025935W WO 2019008779 A1 WO2019008779 A1 WO 2019008779A1
Authority
WO
WIPO (PCT)
Prior art keywords
release agent
solvent
wax
agent composition
liquid
Prior art date
Application number
PCT/JP2017/025935
Other languages
English (en)
French (fr)
Inventor
政敬 光本
宜晃 早坂
Original Assignee
長瀬産業株式会社
加美電子工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 長瀬産業株式会社, 加美電子工業株式会社 filed Critical 長瀬産業株式会社
Publication of WO2019008779A1 publication Critical patent/WO2019008779A1/ja

Abstract

本発明の離型剤組成物は、ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を含み、溶剤は２０℃、１気圧で液体であり、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む。かかる発明によれば、二酸化炭素を用いた噴霧塗装によっても、対象物に十分な離型性を付与することができる。

Description

離型剤組成物、離型膜の形成方法、離型剤組成物の製造方法、及び製造装置
　本発明は、二酸化炭素を含む離型剤組成物に関するものである。
　対象物に離型性を付与する方法として、ワックスなどの離型成分を液体二酸化炭素と混合し、得られた離型剤組成物を対象物に噴霧して、対象物の表面に離型成分の層をコーティングする方法が知られている（例えば、特許文献１）。この方法では、液体二酸化炭素が希釈剤として機能し、離型剤組成物の粘度が噴霧可能なレベルまで低下され、好適に噴霧が行える。
特表２００８－５４００７８号公報
　しかしながら、液体二酸化炭素を含む従来の離型剤組成物を対象物に噴霧しても、離型剤による離型性が十分に発揮されない場合があった。
　本発明は上記課題に鑑みてなされたものであり、二酸化炭素を用いた噴霧によっても、対象物に十分な離型性を付与することのできる離型剤組成物等を提供することを目的とする。
　本発明者らが鋭意検討したところ、ワックスと特定の溶剤とを含有する離型剤及び二酸化炭素を含む離型剤組成物であれば、二酸化炭素を用いた噴霧塗装によっても、対象物に十分な離型性を付与することができることを見出し、本発明を完成させるに至った。
　本発明の一形態に係る離型剤組成物は、ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を含み、溶剤は２０℃、１気圧で液体であり、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む。
　溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤は、脂肪族炭化水素、ガソリン、灯油、コールタールナフサ、石油エーテル、石油ナフサ、石油ベンジン、テレピン油、及びミネラルスピリットからなる群より選ばれる弱溶剤であってよい。
　ワックスの融点は３０～１４０℃であってよい。
　ワックスは、ポリエチレンワックス又は合成炭化水素ワックスであってよい。
　ワックスの配合量は、離型剤全量に対して、０．１～４０質量％であってよい。
　本発明の一形態に係る離型膜の形成方法は、上記離型剤組成物をノズルから噴霧して対象物に離型剤の液膜を形成する工程と、離型剤の液膜を乾燥して離型膜を形成する工程と、を備える。
　本発明の一形態に係る離型剤組成物の製造方法は、ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を混合して離型剤液組成物を得る工程を備え、溶剤は２０℃、１気圧で液体であり、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む。
　本発明の一形態に係る離型剤組成物の製造装置は、ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を混合して離型剤液組成物を得る混合部を備え、溶剤は２０℃、１気圧で液体であり、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む。
　本発明の一形態に係る二酸化炭素含有離型剤組成物調製用である離型剤は、ワックス及び溶剤を含有し、溶剤は２０℃、１気圧で液体であり、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む。
　本発明によれば、二酸化炭素を用いた噴霧塗装によっても、対象物に十分な離型性を付与することができる。
連続混合式二酸化炭素塗装装置の構成を示すブロック図である。
　以下、添付図面を参照して、本発明を実施するための形態を詳細に説明する。
　本発明の一実施形態に係る離型剤組成物は、ワックス及び溶剤を含有する離型剤と、液体二酸化炭素とを含む。
＜離型剤＞
　離型剤は、ワックス及び溶剤を含有する。ワックスは通常、溶剤には完全には溶解せず、溶剤中に分散されている。
＜ワックス＞
　ワックスは、通常３０～１４０℃の融点を有し、対象物に離型性を付与する作用がある離型成分である。ワックスとしては、パラフィンワックス、マイクロクリスタリンワックス、モンタンワックス、カルナバワックス等の天然ワックス、アマイドワックス等の半合成ワックス、及びポリエチレンワックス、ポリプロピレンワックス、ポリエチレンポリプロピレンコポリマーワックス、フィッシャートロップシュワックス、その他の炭化水素合成ワックス等の合成ワックスが挙げられる。ワックスは、１種を単独で使用してもよく、２種以上を併用してもよい。
　ワックスは、融点が３０℃以上、６０℃以上、又は７０℃以上であることができ、１４０℃以下、１２０℃以下、又は１００℃以下であることもできる。また、ワックスの重量平均分子量は、３００以上、６００以上、又は７００以上であってよく、３０００以下、９００以下、又は８００以下であってよい。ワックスの重量平均分子量は、ＧＰＣ法によって測定する。
　ワックスの配合量は、離型剤の全量に対して、０．１質量％以上、３質量％以上、５質量%以上、８質量％以上、１０質量％以上、又は１５質量％以上であってよく、４０質量％以下、３０質量％以下、又は２０質量％以下であってよい。
＜溶剤＞
　溶剤は２０℃、１気圧で液体である。溶剤は単一溶剤であってもよく、混合溶剤であってもよいが、溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を少なくとも１種含む。本明細書において、溶解度パラメータとは、Ｈｉｌｄｅｂｒａｎｄの溶解度パラメータである。溶解度パラメータ（以下、ＳＰ値とする。）とは、物質間の親和性の尺度を表す熱力学的なパラメータであり、類似したＳＰ値を有する物質同士は溶解しやすい傾向にあることが知られている。本明細書において、特に断りがない限り、ＳＰ値は、２０℃、１気圧におけるＳＰ値である。
　ＳＰ値が１７．５（ＭＰａ）０．５以下の溶剤の例は、脂肪族炭化水素、ガソリン（約１６）、灯油（約１６）、コールタールナフサ（約１６）、石油エーテル（約１６）、石油ナフサ（約１６）、石油ベンジン（約１６）、テレピン油（約１６）、及びミネラルスピリット（１６．０）である。括弧内の数値は各溶剤の典型的なＳＰ値であり、単位は（ＭＰａ）０．５である。これらの溶剤は溶解力が低く、「弱溶剤」と呼ばれることがある。ここで、石油ナフサ及びコールタールナフサは、それぞれ脂肪族系以外に芳香族系のソルベントナフサを含む。また、ミネラルスピリットは、ミネラルシンナー、ペトロリウムスピリット、ホワイトスピリット、及びミネラルターペンを含む。
　脂肪族炭化水素は、ペンタン若しくはヘキサンのように一般式ＣｎＨ２ｎ＋２で表すことのできるアルカン、二重結合を有するアルケン、三重結合を有するアルキン、又は環構造を有するシクロアルカン、シクロアルケン若しくはシクロアルキンのいずれであってもよい。脂肪族炭化水素は１７．５（ＭＰａ）０．５以下のＳＰ値を有する。脂肪族炭化水素の具体例は、ｎ－ペンタン（１４．３）、ｎ－ヘキサン（１４．９）、ｎ－オクタン（１５．５）、シクロヘキサン（１６．８）、ｎ－ペンテン（１４．５）、ｎ－ヘキセン（１５．０）、ｎ－オクテン（１５．５）、シクロペンテン（１７．２）、又はシクロヘキセン（１７．３）である。
　上記に列挙した弱溶剤は、作業者や環境に対する影響が少ないという点から、溶剤として好ましい。これら弱溶剤のうち、ガソリン、灯油、コールタールナフサ、石油エーテル、石油ナフサ、石油ベンジン、テレピン油、及びミネラルスピリットは、日本国の労働安全衛生法の有機溶剤中毒予防規則における「第三種有機溶剤」に分類される。第三種有機溶剤は、作業者に対する影響が特に少ないため、溶剤として好ましい。
　弱溶剤の市販品としては、例えば、「スワゾール１０００（石油ナフサ（ソルベントナフサ））」及び「スワゾール１５００（石油ナフサ（ソルベントナフサ））」（いずれも丸善石油株式会社製）、「ソルベッソ１５０（石油ナフサ（ソルベントナフサ））」、「ソルベッソ２００（石油ナフサ（ソルベントナフサ））」、「ＨＡＷＳ（ミネラルスピリット／石油エーテル）」及び「ＬＡＷＳ（ミネラルスピリット／石油エーテル）」（いずれもシェルジャパン社製）、「エッソナフサＮｏ．６（石油ナフサ）」、「エクソールＤ３０、Ｄ４０、Ｄ６０、Ｄ８０、Ｄ１１０（石油ナフサ）」及び「ペガゾール３０４０（灯油）」（いずれもエクソンモービル化学社製）、「Ａソルベント（ミネラルスピリット）」、「クレンゾル（ミネラルスピリット）」及び「イプゾール１００（石油ナフサ）」（いずれも出光興産株式会社製）、「ミネラルスピリットＡ（ミネラルスピリット）」及び「ハイアロム２Ｓ（石油ナフサ）」（いずれも新日本石油化学株式会社製）、「リニアレン１０（石油ナフサ）」及び「リニアレン１２（石油ナフサ）」（いずれも出光石油化学株式会社製）、並びに、「リカソルブ９００（水添石油ナフサ）」、「リカソルブ９１０Ｂ（水添石油ナフサ）」及び「リカソルブ１０００（水添石油ナフサ）」（いずれも新日本理化株式会社製）が挙げられる。
　ＳＰ値が１７．５（ＭＰａ）０．５以下の溶剤の他の例は、エチルエーテル（１４．９）、酢酸イソブチル（１７）、酢酸イソプロピル（１７．２）、酢酸イソペンチル（酢酸イソアミル、１６．０）、酢酸－ｎ－ブチル（１７．４）、酢酸－ｎ－ペンチル（１７．４）、１，１，１－トリクロルエタン（１７．５）、メチルイソブチルケトン（１７．２）、及びメチル－ｎ－ブチルケトン（１７．０）である。括弧内の数値は各溶剤の典型的なＳＰ値であり、単位は（ＭＰａ）０．５である。
　全溶剤に占める、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤の下限量は、特に制限されず、１質量％、２質量％、３質量％、４質量％、５質量％、又は６質量％であってよい。また、全溶剤に占める溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤の上限量は特に制限されず、１００質量％でもよく、９０質量％、８０質量％としてもよい。
　環境への配慮の観点から、溶解度パラメータが１７．５（ＭＰａ）０．５以下の全溶剤にしめる弱溶剤の量は多い方が好ましく、５０質量％以上、６０質量％以上、７０質量％以上、８０質量％以上、又は９０質量％以上とすることができる。全溶剤中の弱溶剤の割合が高いと、作業者や環境に対する影響をより軽減することができる。
＜ＳＰ値が１７．５（ＭＰａ）０．５を超える溶剤＞
　溶剤は、ＳＰ値が１７．５（ＭＰａ）０．５より大きい溶剤を１種以上さらに含むことができる。ＳＰ値が１７．５（ＭＰａ）０．５を超える溶剤の例は、アセトン（２０．３）、イソブチルアルコール（２２．７）、イソペンチルアルコール（イソアミルアルコール、２１．３）、エチレングリコールモノエチルエーテル（セロソルブ、２１．５）、エチレングリコールモノエチルエーテルアセテート（セロソルブアセテート、１９．３）、エチレングリコールモノ－ｎ－ブチルエーテル（ブチルセロソルブ、１９．４）、エチレングリコールモノメチルエーテル（メチルセロソルブ、２３．３）、オルト－ジクロルベンゼン（２０．５）、クレゾール（２０．９）、クロルベンゼン（１９．６）、酢酸エチル（１８．６）、酢酸メチル（１９．６）、シクロヘキサノール（２３．３）、シクロヘキサノン（２０．３）、１，４－ジオキサン（２０．５）、ジクロルメタン（１９．８）、Ｎ，Ｎ－ジメチルホルムアミド（２４．８）、スチレン（１９．０）、テトラクロルエチレン（１９．０）、テトラヒドロフラン（１８．６）、１－ブタノール（２３．３）、２－ブタノール（２２，１）、メタノール（２９．７）、メチルエチルケトン（１９．０）、メチルシクロヘキサノール（２１．３）、メチルシクロヘキサノン（１９．０）、クロロホルム（１９．０）、１，２－ジクロルエタン（２０．１）、１，２－ジクロルエチレン（１８．４～１８．６）、１，１，２，２－テトラクロルエタン（１９．８）、トリクロルエチレン（１８．８）、二硫化炭素（２０．５）、ジエチレングリコールモノメチルエーテル（エチルセロソルブ、２３．５）、プロピレングリコールモノブチルエーテル（１８．４）、イソプロピルアルコール（１８．０）、キシレン（１８．０）、酢酸－ｎ－プロピル（１８．０）、トルエン（１８．２）、四塩化炭素（１７．６）、エチルベンゼン（１８．０）、及びトリメチルベンゼン（１８．０）である。括弧内の数値は各溶剤の典型的なＳＰ値であり、単位は（ＭＰａ）０．５である。また、溶剤は、水（４７．９）を含んでいてもよい。
　全溶剤の合計の配合量は、離型剤全量に対して、９９．９質量％以下、９９質量％以下、９７質量％以下、９５質量%以下、９２質量％以下、９０質量％以下、又は８５質量％以下であってよく、６０質量％以上、７０質量％以上、又は８０質量％以上であってよい。
　離型剤組成物を噴霧した対象物に十分な離型性を付与する観点から、１７．５（ＭＰａ）０．５以下の溶剤のうちの少なくとも１種が、離型剤に含まれる全溶剤の中で最も高い沸点を有する溶剤であることが好ましい。
＜添加剤＞
　離型剤は、ワックス及び溶剤以外に、必要に応じて添加剤を含んでいてもよい。例えば、希釈剤、顔料、分散剤、シリコーン、変性シリコーン、アミン触媒、金属触媒、紫外線吸収剤、光安定剤、レベリング剤、密着性付与剤、レオロジーコントロール剤、又は重合開始剤等、離型剤に通常添加される添加剤を含有していてもよい。特に、離型剤に分散剤を配合することで、ワックスを溶剤中に、より安定的に分散させることができる。
＜液体二酸化炭素＞
　離型剤組成物中の二酸化炭素は液体状態である。離型剤組成物が噴霧されて加圧状態から解放されると、液体状態に圧縮されていた二酸化炭素が瞬時に気化して、その体積が大幅に膨張する。その際の力により、離型剤組成物は細かい霧状になる。
　液体二酸化炭素の配合量は、離型剤１００質量部に対して、２質量部以上、５質量部以上、１０質量部以上、又は２０質量部以上であることができる。液体二酸化炭素の配合量が２質量部以上であると、噴霧された離型剤組成物がより細かい霧状になるため、よりレベリング性の高い、離型剤の液膜及びそれを乾燥させた離型膜を形成することができる。
　このような離型剤組成物によれば、二酸化炭素を用いた噴霧塗装によっても、対象物に十分な離型性を付与することができる。
　続いて、このような離型剤組成物の製造方法を説明する。離型剤組成物は、上記離型剤と、液体二酸化炭素と、を混合する工程を備える方法により製造することができる。離型剤と液体二酸化炭素との混合は、例えば、インラインミキサーを使用したラインブレンド法により行うことができる。
　一実施形態において、離型剤組成物は、図１に示すような２液連続混合式二酸化炭素塗装装置を用いて製造することができる。図１において、離型剤タンク１に貯蔵された、ワックス及び溶剤を含有する離型剤は、離型剤高圧ポンプ２によって所定の圧力まで加圧され、離型剤加熱器３によって所定の温度まで加温されてから、混合器８へと供給される。一方、二酸化炭素ボンベ４に貯蔵された液体二酸化炭素は、二酸化炭素冷却器５によって冷却されて液化し、二酸化炭素高圧ポンプ６によって所定の圧力まで加圧され、二酸化炭素加熱器７によって所定の温度まで加温されてから、混合器８へと供給される。混合器８としては、例えば、インラインミキサーを使用できる。混合器８内で離型剤及び液体二酸化炭素が混合され、離型剤組成物となる。
　図１に示す塗装装置では、ワックスと溶剤とが、予め混合され、ワックスが溶剤に均一に分散された状態で貯蔵されているが、溶剤の一部を予め液体二酸化炭素と混合しておいてもよい。また、離型剤と液体二酸化炭素とを混合した後に、溶剤の一部をさらに混合してもよい。
　また、図１に示す塗装装置は、離型剤加熱器３、二酸化炭素冷却器５、及び二酸化炭素加熱器７を備えるが、これらはなくてもよい。また、図１に示す塗装装置において、離型剤組成物の温度を調整する熱交換器をさらに設けてもよい。また、二酸化炭素高圧ポンプ６もなくてよい。
　続いて、このように製造された離型剤組成物を対象物に噴霧して、対象物に離型性を付与する方法について説明する。対象物に離型性を付与する方法は、離型剤組成物をノズルから噴霧して対象物に離型剤の液膜を形成する工程と、離型剤の液膜を乾燥して離型膜を形成する工程と、を備える。
　例えば、図１において、混合器８により得られた離型剤組成物は加圧状態にあり、噴霧ガン９を通じて大気中に噴霧されることができる。離型剤組成物が噴霧されると、圧縮されていた二酸化炭素が瞬時に気化して、その体積が大幅に膨張する。その際の力により、離型剤組成物は細かい霧状（ミスト）になる。このミストを対象物に接触させることにより、対象物の表面に離型剤の液膜が形成される。その後、液膜を乾燥させることにより、対象物に離型性を付与する離型膜が形成される。ここで、離型剤がＳＰ値１７．５（ＭＰａ）０．５以下の溶剤を含むことで、離型剤の液膜の良好なレベリング性を維持しながら液膜を乾燥させることができる。これにより、形成される離型膜のレベリング性が良好となるためか、対象物に付与される離型性がより高いものとなると推察される。
　噴霧させる離型剤組成物の温度は、二酸化炭素が液体状態となる温度であればよく、０～３１℃であることができ、１０～３０℃であることができる。
　噴霧させる離型剤組成物の圧力は、二酸化炭素が液体状態となる圧力であればよく、０．５ＭＰａ以上であることでき、２～３０ＭＰａであることができる。
　本実施形態の方法によれば、噴霧する離型剤組成物がＳＰ値１７．５（ＭＰａ）０．５以下の溶剤を含むことにより対象物に良好なレベリング性で離型膜を形成することができるためか、対象物に十分な離型性を付与することできる。この理由としては、ＳＰ値１７．５（ＭＰａ）０．５以下の溶剤を含む溶剤はワックスとなじみが良いため、離型剤組成物を噴霧して二酸化炭素を気化した際又はその後に、ワックス同士が凝集しにくく、ワックスが溶剤中に分散された状態を良好に維持することができるためであると推察される。また、一般的に、ＳＰ値が低いほど溶剤の表面張力が低くなり、レベリング性が良くなる傾向がある。さらに、ＳＰ値が１７．５（ＭＰａ）０．５以下の溶剤のうちの少なくとも１種が、離型剤に含まれる全溶剤の中で最も高い沸点を有する溶剤であることが好ましい。これは、全溶剤の中で最後に蒸発する溶剤が、レベリング性を維持しながら液膜が乾燥することに作用していると考えられるため、ワックスとなじみの良い、ＳＰ値１７．５（ＭＰａ）０．５以下の溶剤が、最後に蒸発することが好ましいと考えられるためである。
　以下、実施例に基づき発明を具体的に説明するが、本発明は以下の実施例に限定されない。
(実施例１～１０)
　離型剤組成物をポリウレタンフォーム成型用金型の表面に噴霧し、これを用いて成型したポリウレタンフォーム（成型フォーム）の、金型からの離型性、及び、離型した成型フォームの外観を評価した。具体的な試験の内容を以下に示す。
　図１に示すような２液連続混合式二酸化炭素塗装装置において、離型剤タンク１に離型剤を仕込んだ。本実施例及び比較例で用いる離型剤を表１に示す。これらの離型剤はすべて中京油脂株式会社製である。表１において、「ＮＶ」は、離型剤中の非揮発成分（主成分はワックスである）の質量割合を意味する。また、「溶剤中の最低ＳＰ値」とは、溶剤に含まれる溶剤のうち、最もＳＰ値が低いもののＳＰ値を意味する。さらに、「石油系炭化水素」はソルベントナフサに含まれる。
Figure JPOXMLDOC01-appb-T000001
　離型剤と二酸化炭素との混合比が表２に示す値となるように、離型剤高圧ポンプ２及び二酸化炭素高圧ポンプ６の流量を設定した。混合器８内で、温度２０℃及び圧力１０ＭＰａの条件下、離型剤と二酸化炭素とを混合し、離型剤組成物を得た。６０℃に加温した鉄製箱形状金型（内寸法：縦１５ｃｍ、横２０ｃｍ、深さ５ｃｍで、取手のある蓋つき）に離型剤組成物を均一に噴霧（１ｍ２当たりの固形分換算で約５ｇ）し、１分間乾燥した。ポリウレタンフォームの成型原料としてポリオール（三井東圧製ＭＳ－３００）を４０質量部及びＴＤＩ／ＭＤＩ＝１／１を２０質量部、室温で２０００ｒｐｍにて５秒間撹拌混合し、これを直ちに金型に注入し、蓋をしめて、６０℃で１０分間発泡硬化させた。その後、成型フォームの金型からの離型性及び成型フォーム表面の仕上がりの外観を評価した。結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　成型フォーム表面の仕上がりの外観の評価は、成型フォームの表面の荒れを目視で観察することにより行った。評価基準：○はセル荒れなし；△はセル荒れあり；×はセル荒れが甚だしい。ここで、セルとは、ポリウレタンフォームを形成する気泡のことを指す。
　離型性の評価は、金型の蓋の取手にバネ秤をセットして蓋を開け、その時にかかった荷重を測定することにより行った。評価基準：○は１０ｋｇ未満；×は１０ｋｇ以上。
（比較例１～４）
　離型剤と二酸化炭素との混合比を表３に示す値とした以外は、実施例１～１０と同様にして、試験を行った。結果を表３に示す。
Figure JPOXMLDOC01-appb-T000003
　表２及び表３に示す結果より、実施例では、成型フォームの仕上がり外観及び離型性のいずれもが、比較例に比べて良好であった。これは、実施例における離型剤組成物によって、金型により良好な離型性を付与することができたことを示す。すなわち、実施例における離型剤組成物によれば、対象物（金型）に良好な離型性を付与することができる。
１…離型剤タンク、２…離型剤高圧ポンプ、３…離型剤加熱器、４…二酸化炭素ボンベ、５…二酸化炭素冷却器、６…二酸化炭素高圧ポンプ、７…二酸化炭素加熱器、８…混合器、９…噴霧ガン。

Claims (9)

  1. 　ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を含み、
    　前記溶剤は２０℃、１気圧で液体であり、
    　前記溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む、離型剤組成物。
  2. 　前記溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤が、脂肪族炭化水素、ガソリン、灯油、コールタールナフサ、石油エーテル、石油ナフサ、石油ベンジン、テレピン油、及びミネラルスピリットからなる群より選ばれる弱溶剤である、請求項１に記載の離型剤組成物。
  3. 　前記ワックスの融点が３０～１４０℃である、請求項１又は２に記載の離型剤組成物。
  4. 　前記ワックスが、ポリエチレンワックス又は合成炭化水素ワックスである、請求項１～３のいずれか一項に記載の離型剤組成物。
  5. 　前記ワックスの配合量が、離型剤全量に対して、０．１～４０質量％である、請求項１～４のいずれか一項に記載の離型剤組成物。
  6. 　請求項１～５のいずれか一項に記載の離型剤組成物をノズルから噴霧して対象物に離型剤の液膜を形成する工程と、
    　前記離型剤の液膜を乾燥して離型膜を形成する工程と、を備える、離型膜の形成方法。
  7. 　ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を混合して離型剤液組成物を得る工程を備え、
    　前記溶剤は２０℃、１気圧で液体であり、
    　前記溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む、離型剤組成物の製造方法。
  8. 　ワックス及び溶剤を含有する離型剤と、液体二酸化炭素と、を混合して離型剤液組成物を得る混合部を備え、
    　前記溶剤は２０℃、１気圧で液体であり、
    　前記溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む、離型剤組成物の製造装置。
  9. 　ワックス及び溶剤を含有し、
    　前記溶剤は２０℃、１気圧で液体であり、
    　前記溶剤は、溶解度パラメータが１７．５（ＭＰａ）０．５以下の溶剤を含む、二酸化炭素含有離型剤組成物調製用である離型剤。
PCT/JP2017/025935 2017-07-04 2017-07-18 離型剤組成物、離型膜の形成方法、離型剤組成物の製造方法、及び製造装置 WO2019008779A1 (ja)