WO2018031157A1 - Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution - Google Patents

Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution Download PDF

Info

Publication number
WO2018031157A1
WO2018031157A1 PCT/US2017/041337 US2017041337W WO2018031157A1 WO 2018031157 A1 WO2018031157 A1 WO 2018031157A1 US 2017041337 W US2017041337 W US 2017041337W WO 2018031157 A1 WO2018031157 A1 WO 2018031157A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
aliphatic hydrocarbon
homogeneous single
site catalyst
hydrocarbon solvent
Prior art date
Application number
PCT/US2017/041337
Other languages
English (en)
Inventor
Peijun Jiang
Robert T. Li
Jay L. Reimers
Original Assignee
Exxonmobil Chemical Patents Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Exxonmobil Chemical Patents Inc. filed Critical Exxonmobil Chemical Patents Inc.
Priority to CN201780047308.3A priority Critical patent/CN109563189B/zh
Priority to EP17742357.1A priority patent/EP3497135A1/fr
Priority to SG11201811503SA priority patent/SG11201811503SA/en
Publication of WO2018031157A1 publication Critical patent/WO2018031157A1/fr

Abstract

L'invention concerne un procédé de polymérisation en solution, ou, en variante, un procédé d'introduction de catalyseurs en poudre dans un réacteur de polymérisation en solution, comprenant la combinaison d'un précurseur de catalyseur monosite homogène avec des monomères d'alpha-oléfine pour former une polyoléfine, le précurseur de catalyseur monosite homogène se présentant sous la forme : (i) d'une poudre sèche, (ii) en suspension dans un solvant hydrocarboné aliphatique, ou (iii) en suspension dans une huile ou une cire, le précurseur de catalyseur monosite homogène étant présent à une concentration supérieure à 0,8 mmole/litre lorsqu'il est en suspension dans le solvant hydrocarboné aliphatique avant son introduction dans le réacteur de polymérisation en solution.
PCT/US2017/041337 2016-08-10 2017-07-10 Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution WO2018031157A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201780047308.3A CN109563189B (zh) 2016-08-10 2017-07-10 向溶液聚合反应器供应固体催化剂的方法
EP17742357.1A EP3497135A1 (fr) 2016-08-10 2017-07-10 Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution
SG11201811503SA SG11201811503SA (en) 2016-08-10 2017-07-10 Methods for supplying solid catalysts to a solution polymerization reactor

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201662373120P 2016-08-10 2016-08-10
US62/373,120 2016-08-10
EP16189476.1 2016-09-19
EP16189476 2016-09-19

Publications (1)

Publication Number Publication Date
WO2018031157A1 true WO2018031157A1 (fr) 2018-02-15

Family

ID=56985473

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/041337 WO2018031157A1 (fr) 2016-08-10 2017-07-10 Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution

Country Status (1)

Country Link
WO (1) WO2018031157A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020081202A1 (fr) * 2018-10-16 2020-04-23 Exxonmobil Chemical Patents Inc. Procédés de stabilisation de catalyseurs d'hydrogénation

Citations (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3012024A (en) 1957-11-25 1961-12-05 Celanese Corp Dry feed in forming slurry in olefin polymerization
US3790036A (en) 1969-11-21 1974-02-05 Union Carbide Corp Fluid bed polymerization catalyst injection system
US3876602A (en) 1971-11-26 1975-04-08 Union Carbide Corp Particulate catalyst injection method in polyolefin production
US4610574A (en) 1984-05-30 1986-09-09 Amoco Corporation Catalyst feeding system
US4774299A (en) 1984-03-30 1988-09-27 Bp Chemicals Limited Process for introducing a powder with catalytic activity into a fluidized-bed polymerization reactor
EP0428054A1 (fr) 1989-11-14 1991-05-22 Neste Oy Dispositif pour introduire un mélange de catalyseurs en forme de boue dans un réacteur de polymérisation
EP0428056A1 (fr) 1989-11-14 1991-05-22 Neste Oy Procédé et dispositif pour introduire des catalyseurs dilués en forme de boue dans un réacteur de polymérisation
WO1992016747A1 (fr) 1991-03-21 1992-10-01 Neste Oy Procede de dosage d'un catalyseur fluidise de polymerisation lors du remplissage d'un reacteur de polymerisation
US5312938A (en) * 1990-09-20 1994-05-17 The Dow Chemical Company Homogeneous catalysts and olefin polymerization process
WO1996021684A1 (fr) 1995-01-09 1996-07-18 W.R. Grace & Co.-Conn. Catalyseurs de polyolefine a composantes multiples
EP0878483A1 (fr) 1997-03-27 1998-11-18 Council of Scientific and Industrial Research Procédé pour la polymérisation et copolymérisation des oléfines
US20020034464A1 (en) 1999-08-30 2002-03-21 Equistar Chemicals, L.P. Dry catalyst feeder for polymerization reactors
WO2004005354A1 (fr) * 2002-07-03 2004-01-15 Basf Aktiengesellschaft Procede de production d'une dispersion de polymere aqueuse
WO2007029986A1 (fr) * 2005-09-09 2007-03-15 Sk Energy Co., Ltd. Systeme de catalyseur homogene permettant de produire un homopolymere ou des copolymeres d'ethylene alpha-olefines
EP2045273A1 (fr) * 2007-10-01 2009-04-08 Total Petrochemicals Research Feluy Patent Dept. Procédé pour fournir un matériel granulé à un réacteur de polymérisation
EP2192133A1 (fr) * 2008-11-07 2010-06-02 Borealis AG Procédé de préparation de polyoléfine doté d'un encrassement du réacteur réduit
US20130245344A1 (en) 2011-10-10 2013-09-19 Craig J. Emett Poly Alpha Olefin Compositions
US20150094434A1 (en) 2012-04-26 2015-04-02 Mitsui Chemicals, Inc. Process for producing olefin polymer
US20150141601A1 (en) 2013-11-15 2015-05-21 Exxonmobil Chemical Patents Inc. Pyridyldiamido Transition Metal Complexes, Production and Use Thereof

Patent Citations (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3012024A (en) 1957-11-25 1961-12-05 Celanese Corp Dry feed in forming slurry in olefin polymerization
US3790036A (en) 1969-11-21 1974-02-05 Union Carbide Corp Fluid bed polymerization catalyst injection system
US3876602A (en) 1971-11-26 1975-04-08 Union Carbide Corp Particulate catalyst injection method in polyolefin production
US4774299A (en) 1984-03-30 1988-09-27 Bp Chemicals Limited Process for introducing a powder with catalytic activity into a fluidized-bed polymerization reactor
US4610574A (en) 1984-05-30 1986-09-09 Amoco Corporation Catalyst feeding system
EP0428054A1 (fr) 1989-11-14 1991-05-22 Neste Oy Dispositif pour introduire un mélange de catalyseurs en forme de boue dans un réacteur de polymérisation
EP0428056A1 (fr) 1989-11-14 1991-05-22 Neste Oy Procédé et dispositif pour introduire des catalyseurs dilués en forme de boue dans un réacteur de polymérisation
US5312938A (en) * 1990-09-20 1994-05-17 The Dow Chemical Company Homogeneous catalysts and olefin polymerization process
WO1992016747A1 (fr) 1991-03-21 1992-10-01 Neste Oy Procede de dosage d'un catalyseur fluidise de polymerisation lors du remplissage d'un reacteur de polymerisation
US5385992A (en) * 1991-03-21 1995-01-31 Borealis Holding A/S Method for the dosage of a fluidized polymerization catalyst into a polymerization reactor
WO1996021684A1 (fr) 1995-01-09 1996-07-18 W.R. Grace & Co.-Conn. Catalyseurs de polyolefine a composantes multiples
US5714424A (en) 1995-01-09 1998-02-03 W. R. Grace & Co.-Conn. Multi-component polyolefin catalysts
EP0878483A1 (fr) 1997-03-27 1998-11-18 Council of Scientific and Industrial Research Procédé pour la polymérisation et copolymérisation des oléfines
US5955554A (en) 1997-03-27 1999-09-21 Council Of Scientific Industrial Research Process for polymerization and copolymerization of olefins
US20020034464A1 (en) 1999-08-30 2002-03-21 Equistar Chemicals, L.P. Dry catalyst feeder for polymerization reactors
WO2004005354A1 (fr) * 2002-07-03 2004-01-15 Basf Aktiengesellschaft Procede de production d'une dispersion de polymere aqueuse
WO2007029986A1 (fr) * 2005-09-09 2007-03-15 Sk Energy Co., Ltd. Systeme de catalyseur homogene permettant de produire un homopolymere ou des copolymeres d'ethylene alpha-olefines
EP2045273A1 (fr) * 2007-10-01 2009-04-08 Total Petrochemicals Research Feluy Patent Dept. Procédé pour fournir un matériel granulé à un réacteur de polymérisation
EP2192133A1 (fr) * 2008-11-07 2010-06-02 Borealis AG Procédé de préparation de polyoléfine doté d'un encrassement du réacteur réduit
US20130245344A1 (en) 2011-10-10 2013-09-19 Craig J. Emett Poly Alpha Olefin Compositions
US20150094434A1 (en) 2012-04-26 2015-04-02 Mitsui Chemicals, Inc. Process for producing olefin polymer
US20150141601A1 (en) 2013-11-15 2015-05-21 Exxonmobil Chemical Patents Inc. Pyridyldiamido Transition Metal Complexes, Production and Use Thereof

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020081202A1 (fr) * 2018-10-16 2020-04-23 Exxonmobil Chemical Patents Inc. Procédés de stabilisation de catalyseurs d'hydrogénation

Similar Documents

Publication Publication Date Title
US11130828B2 (en) Methods for supplying solid catalysts to a solution polymerization reactor
JP6970161B2 (ja) ポリオレフィン生成物の生成
CN1054859C (zh) 使用可溶性无载体催化剂进行气相聚合反应
CN100358922C (zh) 聚合催化剂组分的合成方法
EP3519450B1 (fr) Catalyseurs de polymérisation bimodaux
WO1994000500A1 (fr) Procede de polymerisation en solution utilisant un catalyseur metallocene pour la production de polymeres olefiniques
KR20100126666A (ko) 프로펜 첨가에 따른 폴리알파올레핀의 브랜치 레벨 및 점도 제어
JP2001507069A (ja) 高活性メタロセン重合法
CN101466742A (zh) 担载的抗静电聚合催化剂
CN103402636A (zh) 制造改性金属茂催化剂的方法、制成的催化剂及其用途
CN1042159A (zh) 用金属茂-铝烷催化体系生产高分子量epdm弹性体的方法
CN107488242B (zh) 使用微通道反应器和茂金属催化体系聚合线性α-烯烃方法
JP2009536673A (ja) オレフィン重合用帯電防止剤及び当該帯電防止剤の製造法
CN1169123A (zh) 防止反应器结垢的方法和催化剂
CN104093749A (zh) 催化剂组合物及其制备方法
JP2019065290A (ja) シンジオタクチックプロピレンポリマーおよび同を含む潤滑油
EP3519468A2 (fr) Catalyseurs de polymérisation ayant un meilleur enchaînement des unités éthylène
JP2019511601A (ja) オレフィン重合触媒系及びその使用方法
JP6488307B2 (ja) ポリオレフィン重合用の架橋メタロセン錯体
TW475933B (en) Propylene//propylene/olefin block copolymer and process for producing the same
WO2018031157A1 (fr) Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution
CN105308059A (zh) 催化剂组合物、其制备方法及使用其制备聚烯烃的方法
EP3497135A1 (fr) Procédés d'alimentation en catalyseurs solides d'un réacteur de polymérisation en solution
WO2006117983A1 (fr) CATALYSEUR DE POLYMERISATION ET PROCEDE DE FABRICATION DE POLY-α-OLEFINES UTILISANT CE CATALYSEUR
CN109641986A (zh) 烯烃聚合方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17742357

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2017742357

Country of ref document: EP

Effective date: 20190311