WO2017203312A1 - Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts - Google Patents

Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts Download PDF

Info

Publication number
WO2017203312A1
WO2017203312A1 PCT/IB2016/000697 IB2016000697W WO2017203312A1 WO 2017203312 A1 WO2017203312 A1 WO 2017203312A1 IB 2016000697 W IB2016000697 W IB 2016000697W WO 2017203312 A1 WO2017203312 A1 WO 2017203312A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
comprised
anyone
temperature
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2016/000697
Other languages
French (fr)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal SA
Original Assignee
ArcelorMittal SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ArcelorMittal SA filed Critical ArcelorMittal SA
Priority to PCT/IB2016/000697 priority Critical patent/WO2017203312A1/en
Priority to JP2018561533A priority patent/JP6811788B2/en
Priority to PL17730258.5T priority patent/PL3464668T3/en
Priority to HUE17730258A priority patent/HUE070727T2/en
Priority to ES17730258T priority patent/ES3017532T3/en
Priority to US16/302,997 priority patent/US20190300978A1/en
Priority to UAA201812130A priority patent/UA121286C2/en
Priority to RU2018142996A priority patent/RU2732713C2/en
Priority to FIEP17730258.5T priority patent/FI3464668T3/en
Priority to CA3025449A priority patent/CA3025449C/en
Priority to PCT/IB2017/000619 priority patent/WO2017203347A1/en
Priority to MA45147A priority patent/MA45147B1/en
Priority to BR112018072334-7A priority patent/BR112018072334B1/en
Priority to KR1020187034111A priority patent/KR102246751B1/en
Priority to EP17730258.5A priority patent/EP3464668B1/en
Priority to CN201780030522.8A priority patent/CN109154052B/en
Priority to MX2018014318A priority patent/MX2018014318A/en
Publication of WO2017203312A1 publication Critical patent/WO2017203312A1/en
Priority to ZA2018/07065A priority patent/ZA201807065B/en
Anticipated expiration legal-status Critical
Priority to US18/124,997 priority patent/US12509741B2/en
Priority to US19/400,064 priority patent/US20260078460A1/en
Ceased legal-status Critical Current

Abstract

The invention deals with a cold rolled and annealed steel sheet comprising by weight : 0.6 ≤C≤ 1.3%, 15.0≤ Mn ≤35%, 5≤ Al ≤15%, Si ≤2.40 % S ≤ 0.03%, P ≤0.1 %, N ≤0.1 %, possibly one or more optional elements chosen among Ni, Cr and Cu in an respective amount of up to 4.0%, up to 3.0% and up to 3.0% and possibly one or more elements chosen among B, Ta, Zr, Nb, V, Ti, Mo, and W in a cumulated amount of up to 2.0%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, the microstructure of said sheet comprising optionally up to 3% of kappa carbides, optionally up to 10.0% of granular ferrite, the remainder being made of austenite, the average grain size and average aspect ratio of the austenite being respectively below 6 Mm and comprised between 1.5 and 6 and the average grain size and average aspect ratio of the ferrite, when present, being respectively below 5 pm and below 3.0. It also deals with a manufacturing method and with use of such grade for making vehicle parts.

Description

Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
The present invention deals with a low density steel sheet presenting a microstructure mainly comprising austenite. The steel sheet according to the invention is particularly well suited for the manufacture of safety or structural parts for vehicles such as land motor vehicles.
Environmental restrictions are forcing automakers to continuously reduce the C02 emissions of their vehicles. To do that, automakers have several options, whereby their principal options are to reduce the weight of the vehicles or to improve the efficiency of their engine systems. Advances are frequently achieved by a combination of the two approaches. This invention relates to the first option , namely the red uction of the weight of the motor vehicles. I n this very specific field , there is a two-track alternative:
The first track consists of reducing the thicknesses of the steels while increasing their levels of mechanical strength . Unfortunately, this solution has its limits on account of a prohibitive decrease in the rigidity of certain automotive parts and the appearance of acoustical problems that create uncomfortable conditions for the passenger, not to mention the unavoidable loss of ductility associated with the increase in mechanical strength .
The second track consists of reducing the density of the steels by alloying them with other, lighter metals. Among these alloys, the low-density ones have attractive mechanical and physical properties while making it possible to significantly reduce the weight.
I n particular, US 2003/014591 1 discloses a Fe-AI-Mn-Si light steel having good formability and high strength. However, the ultimate tensile strength of such steels does not go beyond 800 MPa which does not allow taking full advantage of their low density for parts of all kinds of geometry.
The purpose of the invention therefore is to provide a steel sheet presenting a density below 7.4, an ultimate tensile strength of at least 900 MPa, a yield strength of at least 700 MPa and a uniform elongation of at least 28% .
In a preferred embodiment, the steel sheet according to the invention presents a density below 7.2, an ultimate tensile strength of at least 1 000 MPa, a yield strength of at least 800 MPa and a uniform elongation of at least 30%. This object is achieved by providing a steel sheet according to claim 1 . The steel sheet can also comprise characteristics of claims 2 to 7. Another object is achieved by providing the method according to claims 8 to 1 1 . Another aspect is achieved by providing parts or vehicles according to claims 12 to 14.
Other characteristics and advantages of the invention will become apparent from the following detailed description of the invention .
. Without willing to be bou nd by any theory it seems that the low density steel sheet according to the invention allows for an improvement of the mechanical properties thanks to this specific microstructure.
Regarding the chemical composition of the steel, carbon plays an important role in the formation of the microstructure and reaching of the targeted mechanical properties. Its main role is to stabilize austenite which is the main phase of the microstructure of the steel as well as to provide strengthening . Carbon content below 0.6% will decrease the proportion of austenite, which leads to the decrease of both ductility and strength of the alloy. However, since it is a main constituent element of the intragranular kappa carbide (Fe, Mn)3AICXi a carbon content above 1 .3% can promote the precipitation of such carbides in a coarse manner on the grain boundaries (intergranular kappa carbide (Fe, Mn)3AICx), what results in the decrease of the ductility of the alloy.
Preferably, the carbon content is between 0.80 and 1 .3% , more preferably between 0.8 and 1 .0% by weight so as to obtain sufficient strength .
Manganese is an important alloying element in this system , mainly d ue to the fact that alloying with very high amounts of manganese and carbon stabilizes the austenite down to room temperature, which can then tolerate high amounts of aluminium without being destabilized and transformed into ferrite or martensite. To enable the alloy to have a superior ductility, the manganese content has to be equal or higher to 1 5 %. However, when the manganese content is over 35%, the precipitation of β-Μη phase will deteriorate the ductility of the alloy. Therefore, the manganese content should be controlled to be equal or greater than 1 5.0%, but lower than equal to 35%. In a preferred embodiment, it is equal or greater than 1 5.5% or even than 16.0% . Its amount is more preferably between 1 8 and 25%.
Aluminium addition to high manganese austenitic steels effectively decreases the density of the alloy. In add ition, it considerably increases the stacking fault energy (SFE) of the austenite, leading in turn to a change in the strain hardening behavior of the alloy. Aluminium is also one of the primary elements of nanosized kappa carbide (Fe,Mn)3AICx and therefore its addition significantly enhances the formation of such carbides. The aluminium concentration of the present alloys should be adjusted , on one hand, to guarantee the austenite stability and the precipitation of kappa carbides, and on the other to control the formation of ferrite. Therefore, the aluminium content should be controlled to be equal or greater than 5% , but lower than equal to 1 5%. In a preferred embodiment, aluminium content is between 7 and 1 2% and preferably between 8 and 10%.
Silicon is a common alloying element for high manganese and aluminium steels. It has a very strong effect on the formation of ordered ferrite with a D03 structure. Besides, silicon was shown to enhance the activity of carbon in austenite and to increase the partitioning of carbon into the kappa carbides. I n addition , silicon has been described as an effective alloying element that can be used to delay or prevent the precipitation of brittle β-Μη phase. However, above a content of 2.40%, it reduces the elongation and tends to form undesirable oxides during certain assembly processes, and it must therefore be kept below this limit. Preferably, the content of silicon is below 2.0% and advantageously below 1 .0.
Sulfur and phosphorus are impurities that embrittle the grain boundaries.
Their respective contents must not exceed 0.03 and 0.1 % so as to maintain sufficient hot ductility.
Nitrogen content must be 0.1 % or less so as to prevent the precipitation of AIN and the formation of volume defects (blisters) during solidification .
Nickel has a positive effect on penetration of hydrogen into the steel and , therefore it can be used as a diffusion barrier to hydrogen . Nickel can also be used as an effective alloying element because it promotes the formation of ordered compounds in ferrite, such as the B2 component, leading to additional strengthening. However, it is desirable, among others for cost reasons, to limit the nickel addition to a maximum content of 4.0% or less and preferably between 0.1 and 2.0% or between 0.1 and 1 .0% . I n another embodiment, the nickel amount is below 0.1 %. Chromium may be used as optional element for increasing the strength of the steel by solution hardening. It also enhances the high temperature corrosion resistance of the steels according to the invention . However, since chromium red uces the stacking fault energy, its content must not exceed 3.0% and preferably between 0. 1 % and 2.0% or between 0. 1 and 1 .0% . In another embodiment, the chromium amount is below 0.1 %.
Likewise, optionally, an addition of copper with a content not exceeding 3.0% is one mean of hardening the steel by precipitation of copper rich precipitates. However, above this content, copper is responsible for the appearance of surface defects in hot-rolled sheet, Preferably, the amount of copper is between 0.1 and 2.0% or between 0.1 and 1 .0%. In another embod iment, the chromium amount is below 0.1 % .
Boron has a very low solid solubility and a strong tendency to segregate at the grain boundaries, interacting strongly with lattice imperfections. Therefore, boron can be used to limit the precipitation of intergranular kappa carbides. Preferably, the amount of boron is below 0.1 %.
Niobium can simultaneously increase strength and toughness in the steel since it is an effective grain refiner. In addition, tantalum, zirconium, niobium, vanadium , titanium, molybdenum and tungsten are also elements that may optionally be used to achieve hardening and strengthening by precipitation of nitrides, carbo-nitrides or carbides. However, when their cumulated amount is above 2.0%, preferably above 1 .0%, there is a risk that an excessive precipitation may cause a reduction in toughness, which has to be avoided . The microstructure of the steel sheet according to the invention comprises optionally up to 3% of kappa carbides, optionally up to 1 0% of g ranular ferrite, the remainder being made of austenite.
The austenitic matrix presents an average grain size below 6 pm and preferably below 4 μιτι, more preferably below 3 μηι and has an average aspect ratio between 1 .5 and 6, preferably between 2.0 and 4.0 and more preferably between 2.0 and 3.0.
During quenching , possible modulations in austenitic grains may ind icate the beginning of L' 12 ordering and thus, the presence of intragranular kappa carbides. Therefore, kappa carbides (Fe, Mn)3AICx can be present in the microstructure of the steel sheet according to the invention , up to an amount of 3% in area fraction. The presence of intergranular kappa carbides is not admitted as such intergranular coarse kappa carbides may cause a decrease in the ductility of the steel.
Ferrite can also be present in the microstructure of the sheet according to the invention up to an amount of 1 0.0% in, area fraction , preferably up to 5.0% or more preferably up to 3.0%. However, the ferrite morphology is limited to a granular geometry, excluding ferrite in form of bands, as they drastically degrade the ductility and formability of the steel. When present, the ferritic grains have an average grain size below 5 pm and preferably below 1 pm . The average aspect ratio of the ferrite, when present, is below 3.0 and preferably below 2.5, Such ferrite can be under the form of regular d isorded ferrite a or ordered as a B2 structure with a (Fe, Mn)AI composition or as a D03 structure with a (Fe, Mn)3AI composition, so that a, B2 and D03 structures can be observed in the steel according to the invention .
To protect the steel sheet according to the invention from corrosion, in a preferred embodiment, the steel sheet is covered by a metallic coating. The metallic coating can be an aluminum-based coating or a zinc-based coating.
Preferably, the aluminium-based coated comprises less than 1 5% Si, less than 5.0% Fe, optionally 0.1 to 8.0% Mg and optionally 0. 1 to 30.0% Zn , the remainder being Al.
Advantageously, the zinc-based coating comprises 0.01 -8.0% Al, optionally 0.2-8.0% Mg , the remainder being Zn.
The steel sheet according to the invention can be produced by any appropriate manufacturing method and the man skilled in the art can define one. It is however preferred to use the method according to the invention , which comprises the following steps:
- feeding a slab which composition is according to the invention
- reheating such slab at a temperature above 1 000°C and hot rolling it with a final rolling temperature of at least 800°C ,
- coiling the hot rolled steel sheet at a temperature above 350 °C, - cold-rolling such hot rolled steel sheet at a reduction comprised between 30 and 80%,
- annealing such cold rolled sheet by heating it up to an annealing temperature comprised between 700 and 1 000°C , hold ing it at such temperature during less than 5 minutes and cooling it at a rate of at least
30°C/s.
The steel sheets according to the present invention are preferably produced through a method in which an semi product, such as slabs, thin slabs, or strip made of a steel according to the present invention having the composition described above, is cast, the cast input stock is heated to a temperature above 1 000°C, preferably above 1 050°C and more preferably above 1 1 00°C or 1 1 50°C or used directly at such a temperature after casting , without intermediate cooling .
The final hot-rolling step is performed at a temperature above 800°C. To avoid any cracking problem through lack of ductility by the formation of ferrite in bands, the end-of-rolling temperature is preferably above or equal to 850° C.
After the hot-rolling , the strip has to be coiled at a temperature below 600°C and preferably above 350°C . In a preferred embodiment, the coiling is performed between 350 and 450°C to avoid excessive kappa carbide precipitation.
The hot-rolled product obtained by the process described above is cold- rolled after a possible prior pickling operation has been performed in the usual manner.
The cold-rolling step is performed with a reduction rate between 30 and 80%, preferably between 50 and 70% .
After this rolling step, a short annealing is performed by heating the sheet up to an annealing temperature comprised between 700 and 1 000°C , holding it at such temperature during less than 5 minutes and cooling it at a rate of at least 30°C/s, more preferably of at least 50°C/s and even more preferably of at least 70°C/s, Preferably, this annealing is carried out continuously. By controlling annealing temperature and time, either a fully austenitic or a two phase structure with the characteristics above can be obtained .
After this annealing step, the steel sheet may optionally be submitted to a metallic coating operation to improve its protection against corrosion . The coating process used can be any process adapted to the steel of the invention . Electrolytic or physical vapor deposition can be cited , with a particular emphasis on Jet Vapor Deposition . The metallic coating can be based on zinc or on aluminium , for example.
Examples
Seven grades, which compositions are gathered in table 1 , were cast in slabs and processed following the process parameters gathered in , table 2.
Table 1 - Compositions
Figure imgf000008_0001
Table 2 - Process parameters
Figure imgf000008_0002
The resulting samples were then analyzed and the corresponding microstructure elements and mechanical properties were respectively gathered in table 3 and 4. Table 3 - Microstructure
Figure imgf000009_0001
No samples showed any presence of intergranular kappa carbides nor of β-Μη phase.
Table 4 - Properties
Figure imgf000009_0002
The examples show that the steel sheets according to the invention are the only ones to show all the targeted properties thanks to their specific composition and microstructures.

Claims

A cold rolled and annealed steel sheet comprising by weight :
0.6 < C < 1 .3%,
1 5.0≤ Mn < 35%,
5 < A! < 1 5%,
Si < 2.40 %
S < 0.03%,
P < 0.1 %,
N < 0. 1 %,
possibly one or more optional elements chosen among Ni, Cr and Cu in an respective amount of up to 4.0%, up to 3.0% and up to 3.0% and possibly one or more elements chosen among B, Ta, Zr, Nb, V, Ti , Mo, and W in a cumulated amount of up to 2.0%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, the microstructure of said sheet comprising optionally up to 3% of kappa carbides, optionally up to 1 0% of granular ferrite, the remainder being made of austenite, the average grain size and average aspect ratio of the austenite being respectively below 6 pm and comprised between 1 .5 and 6 and the average grain size and average aspect ratio of the ferrite, when present, being respectively below 5 pm and below 3.0.
A steel sheet according to claim 1 , wherein the carbon content is comprised between 0.8 and 1 .0%.
A steel sheet according to claims 1 or 2 , wherein the manganese content is comprised between 20 and 30%.
A steel sheet according to anyone of claims 1 to 3, wherein the aluminum content is comprised between 8.5 and 1 0%.
A steel sheet according to anyone of claims 1 to 4, wherein the steel sheet has a ultimate tensile strength of at least 900 MPa, a yield strength of at least 700 MPa and a uniform elongation of at least 28%.
6. A steel sheet according to anyone of claims 1 to 5, wherein the steel sheet is covered by a metallic coating.
7. A steel sheet accord ing to claim 6 , wherein the steel sheet is covered by an aluminum-based coating or a zinc-based coating .
8. A method for producing a steel sheet comprising the following steps :
- feeding a slab which composition is according to claims 1 to 4
- reheating such slab at a temperature above 1 000°C and hot rolling it with a final rolling temperature of at least 800°C ,
- coiling the hot rolled steel sheet at a temperature below 600 °C,
- cold-rolling such hot rolled steel sheet at a reduction comprised between
30 and 80%,
- annealing such cold rolled sheet by heating it up to an annealing temperature comprised between 700 and 1 000°C, holding it at such temperature during less than 5 minutes and cooling it at a rate of at least 30°C/s.
9. Method according to claim 8, wherein the annealing temperature is comprised between 800 and 950°C .
1 0. Method according to anyone of claims 8 to 9, wherein the coiling temperature is comprised between 350 and 500°C.
1 1 . A method according to anyone of claims 8 to 1 0, comprising further a final coating step.
1 2. Use of a steel sheet according to anyone of claims 1 to 7 or obtainable according to the method of anyone of claims 8 to 1 1 for manufacturing a structural or safety part of a vehicle.
1 3. Part accord ing to claim 1 2, obtained by flexible rolling of said steel sheet.
14. Vehicle comprising a part according to anyone of claims 1 2 or 1 3.
PCT/IB2016/000697 2016-05-24 2016-05-24 Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts Ceased WO2017203312A1 (en)