WO2017116103A1 - Substrat de polyimide et module de substrat d'affichage comprenant celui-ci - Google Patents

Substrat de polyimide et module de substrat d'affichage comprenant celui-ci Download PDF

Info

Publication number
WO2017116103A1
WO2017116103A1 PCT/KR2016/015280 KR2016015280W WO2017116103A1 WO 2017116103 A1 WO2017116103 A1 WO 2017116103A1 KR 2016015280 W KR2016015280 W KR 2016015280W WO 2017116103 A1 WO2017116103 A1 WO 2017116103A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyimide substrate
formula
compound
polyimide
group
Prior art date
Application number
PCT/KR2016/015280
Other languages
English (en)
Korean (ko)
Inventor
우학용
정학기
Original Assignee
코오롱인더스트리 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코오롱인더스트리 주식회사 filed Critical 코오롱인더스트리 주식회사
Publication of WO2017116103A1 publication Critical patent/WO2017116103A1/fr

Abstract

La présente invention concerne un substrat de polyimide comprenant une couche de polyimide et une couche d'apprêt optique sous la couche de polyimide, et un module de substrat d'affichage le comprenant, la couche d'apprêt optique comprenant un composé de résine de silazane-siloxane, un composé de résine norbornène et un composé acrylique.
PCT/KR2016/015280 2015-12-31 2016-12-26 Substrat de polyimide et module de substrat d'affichage comprenant celui-ci WO2017116103A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR10-2015-0191068 2015-12-31
KR20150191068 2015-12-31
KR20160178134 2016-12-23
KR10-2016-0178134 2016-12-23

Publications (1)

Publication Number Publication Date
WO2017116103A1 true WO2017116103A1 (fr) 2017-07-06

Family

ID=59225340

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2016/015280 WO2017116103A1 (fr) 2015-12-31 2016-12-26 Substrat de polyimide et module de substrat d'affichage comprenant celui-ci

Country Status (2)

Country Link
TW (1) TW201727274A (fr)
WO (1) WO2017116103A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10985344B2 (en) 2017-10-27 2021-04-20 Applied Materials, Inc. Flexible cover lens films
EP3683047A4 (fr) * 2017-09-04 2021-08-04 Kolon Industries, Inc. Film de revêtement dur à structure multicouche, et film de polyimide comprenant celui-ci
US11260638B2 (en) 2019-08-29 2022-03-01 Shpp Global Technologies B.V. Transparent, flexible, impact resistant, multilayer film comprising polycarbonate copolymers
US11571881B2 (en) 2020-03-03 2023-02-07 Kolon Industries, Inc. Hard coating film having multilayer-structure, and polyimide film comprising same
US11579339B2 (en) 2018-05-10 2023-02-14 Applied Materials, Inc. Replaceable cover lens for flexible display
US11789300B2 (en) 2019-06-26 2023-10-17 Applied Materials, Inc. Flexible multi-layered cover lens stacks for foldable displays
US11988810B2 (en) 2018-08-14 2024-05-21 Applied Materials, Inc. Multi-layer wet-dry hardcoats for flexible cover lens

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0543834A (ja) * 1991-08-13 1993-02-23 Nippon Zeon Co Ltd 熱可塑性ノルボルネン系樹脂コーテイング剤及びコート層形成方法
KR20130003339A (ko) * 2011-06-30 2013-01-09 코오롱인더스트리 주식회사 플렉서블 디스플레이 기판
KR20140014209A (ko) * 2011-03-01 2014-02-05 에이제토 엘렉토로닉 마티리알즈 아이피 (재팬) 가부시키가이샤 저굴절율 막 형성용 조성물, 저굴절율 막의 형성 방법, 및 당해 형성 방법에 의해 형성된 저굴절율 막 및 반사 방지 막
KR20140093632A (ko) * 2013-01-18 2014-07-28 신에쓰 가가꾸 고교 가부시끼가이샤 프라이머 조성물 및 이것을 이용한 광반도체 장치
KR20140128638A (ko) * 2013-04-29 2014-11-06 이근수 개질된 폴리실라잔계 중합체, 이 중합체를 포함하는 코팅 조성물, 이를 이용하여 얻을 수 있는 코팅 플라스틱 기판과 이의 제조 방법, 및 상기 개질된 폴리실라잔계 중합체의 제조 방법

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0543834A (ja) * 1991-08-13 1993-02-23 Nippon Zeon Co Ltd 熱可塑性ノルボルネン系樹脂コーテイング剤及びコート層形成方法
KR20140014209A (ko) * 2011-03-01 2014-02-05 에이제토 엘렉토로닉 마티리알즈 아이피 (재팬) 가부시키가이샤 저굴절율 막 형성용 조성물, 저굴절율 막의 형성 방법, 및 당해 형성 방법에 의해 형성된 저굴절율 막 및 반사 방지 막
KR20130003339A (ko) * 2011-06-30 2013-01-09 코오롱인더스트리 주식회사 플렉서블 디스플레이 기판
KR20140093632A (ko) * 2013-01-18 2014-07-28 신에쓰 가가꾸 고교 가부시끼가이샤 프라이머 조성물 및 이것을 이용한 광반도체 장치
KR20140128638A (ko) * 2013-04-29 2014-11-06 이근수 개질된 폴리실라잔계 중합체, 이 중합체를 포함하는 코팅 조성물, 이를 이용하여 얻을 수 있는 코팅 플라스틱 기판과 이의 제조 방법, 및 상기 개질된 폴리실라잔계 중합체의 제조 방법

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3683047A4 (fr) * 2017-09-04 2021-08-04 Kolon Industries, Inc. Film de revêtement dur à structure multicouche, et film de polyimide comprenant celui-ci
US11117355B2 (en) 2017-09-04 2021-09-14 Kolon Industries, Inc. Hard coating film having multilayer-structure, and polyimide film comprising same
US10985344B2 (en) 2017-10-27 2021-04-20 Applied Materials, Inc. Flexible cover lens films
US11758757B2 (en) 2017-10-27 2023-09-12 Applied Materials, Inc. Flexible cover lens films
US11579339B2 (en) 2018-05-10 2023-02-14 Applied Materials, Inc. Replaceable cover lens for flexible display
US11988810B2 (en) 2018-08-14 2024-05-21 Applied Materials, Inc. Multi-layer wet-dry hardcoats for flexible cover lens
US11789300B2 (en) 2019-06-26 2023-10-17 Applied Materials, Inc. Flexible multi-layered cover lens stacks for foldable displays
US11934056B2 (en) 2019-06-26 2024-03-19 Applied Materials, Inc. Flexible multi-layered cover lens stacks for foldable displays
US11940683B2 (en) 2019-06-26 2024-03-26 Applied Materials, Inc. Flexible multi-layered cover lens stacks for foldable displays
US11940682B2 (en) 2019-06-26 2024-03-26 Applied Materials, Inc. Flexible multi-layered cover lens stacks for foldable displays
US11260638B2 (en) 2019-08-29 2022-03-01 Shpp Global Technologies B.V. Transparent, flexible, impact resistant, multilayer film comprising polycarbonate copolymers
US11571881B2 (en) 2020-03-03 2023-02-07 Kolon Industries, Inc. Hard coating film having multilayer-structure, and polyimide film comprising same

Also Published As

Publication number Publication date
TW201727274A (zh) 2017-08-01

Similar Documents

Publication Publication Date Title
WO2017116103A1 (fr) Substrat de polyimide et module de substrat d'affichage comprenant celui-ci
WO2014092422A1 (fr) Substrat polyimide transparent et son procédé de fabrication
KR101874616B1 (ko) 수지 필름, 적층체, 광학 부재, 가스 배리어재 및 터치 센서 기재
WO2014163352A1 (fr) Substrat de capot en polyimide
US10431753B2 (en) Substrate for display, color filter using the same and method for the production thereof, organic EL element and method for the production thereof, and flexible organic EL display
WO2017111289A1 (fr) Composition de poly(acide amique) à laquelle sont appliqués des monomères alicycliques et film de polyimide transparent l'utilisant
KR20180001175A (ko) 대전 방지된 폴리이미드 기판 및 이를 포함하는 표시 기판 모듈
WO2013002614A2 (fr) Acide polyamique, solution d'acide polyamique, couche protectrice de polyimide, et film de polyimide
WO2018212545A1 (fr) Film de revêtement dur et dispositif d'affichage d'image le comprenant
US11805616B2 (en) Polyimide-based composite film and display device comprising same
US20210047485A1 (en) Polyimide-based composite film and display device comprising same
TW201940570A (zh) 混合樹脂組成物
KR20180072268A (ko) 하드 코팅용 수지 조성물 및 이의 경화물을 하드 코팅층으로 포함하는 폴리이미드 기판
WO2021054513A1 (fr) Procédé de production d'une poudre de polyimide et poudre de polyimide ainsi produite
WO2023054866A1 (fr) Film optique ayant une structure multicouche et dispositif d'affichage le comprenant
WO2012153966A2 (fr) Feuille composite et substrat d'affichage l'utilisant
WO2018124769A1 (fr) Composition de revêtement et film préparé à partir de celle-ci
KR20160082478A (ko) 폴리이미드 기판 및 이를 포함하는 표시 기판 모듈
WO2018212547A1 (fr) Film de revêtement dur et appareil d'affichage d'image le comprenant
WO2016108629A1 (fr) Substrat de polyimide et module de substrat d'affichage comportant un tel substrat
US20210002440A1 (en) Polyimide-Based Film, Film for Cover Window, and Display Device Including the Same
WO2021117961A1 (fr) Film de polyimide présentant une excellente résistance aux intempéries
TWI757319B (zh) 剝離層形成用組成物
WO2013019040A2 (fr) Composition de résine hybride organique-inorganique photodurcissable
EP3045490A1 (fr) Panneau de protection pour dispositif d'affichage et dispositif d'affichage comprenant celui-ci

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16882055

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16882055

Country of ref document: EP

Kind code of ref document: A1