WO2017105937A1 - Photo-imageable thin films with high dielectric constants - Google Patents
Photo-imageable thin films with high dielectric constants Download PDFInfo
- Publication number
- WO2017105937A1 WO2017105937A1 PCT/US2016/065226 US2016065226W WO2017105937A1 WO 2017105937 A1 WO2017105937 A1 WO 2017105937A1 US 2016065226 W US2016065226 W US 2016065226W WO 2017105937 A1 WO2017105937 A1 WO 2017105937A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formulation
- nanoparticles
- thin films
- photo
- functionalized
- Prior art date
Links
Classifications
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/022—Quinonediazides
- G03F7/023—Macromolecular quinonediazides; Macromolecular additives, e.g. binders
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/039—Macromolecular compounds which are photodegradable, e.g. positive electron resists
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/0047—Photosensitive materials characterised by additives for obtaining a metallic or ceramic pattern, e.g. by firing
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/022—Quinonediazides
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/039—Macromolecular compounds which are photodegradable, e.g. positive electron resists
- G03F7/0392—Macromolecular compounds which are photodegradable, e.g. positive electron resists the macromolecular compound being present in a chemically amplified positive photoresist composition
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/075—Silicon-containing compounds
- G03F7/0752—Silicon-containing compounds in non photosensitive layers or as additives, e.g. for dry lithography
Definitions
- the present invention relates to a photo-imageable thin film with a high dielectric constant.
- High dielectric constant thin films are of high interest for applications such as embedded capacitors, TFT passivation layers and gate dielectrics, in order to further miniaturize microelectronic components.
- One approach for obtaining a photo-imageable high dielectric constant thin film is to incorporate high dielectric constant nanoparticles in a photoresist.
- US7630043 discloses composite thin films based on a positive photoresist containing an acrylic polymer having alkali soluble units such as a carboxylic acid, and fine particles having a dielectric constant higher than 4. However, this reference does not disclose the binder used in the present invention.
- the present invention provides a formulation for preparing a photo-imageable film; said formulation comprising: (a) a positive photoresist comprising a cresol novolac resin and a
- Nanoparticles refers to particles having a diameter from 1 to 100 nm; i.e., at least 90% of the particles are in the indicated size range and the maximum peak height of the particle size distribution is within the range.
- nanoparticles have an average diameter 75 nm or less; preferably 50 nm or less; preferably 25 nm or less; preferably 10 nm or less; preferably 7 nm or less.
- the average diameter of the nanoparticles is 0.3 nm or more; preferably 1 nm or more.
- Particle sizes are determined by Dynamic Light Scattering (DLS).
- the breadth of the distribution of diameters of zirconia particles is 4 nm or less; more preferably 3 nm or less; more preferably 2 nm or less.
- the breadth of the distribution of diameters of zirconia particles, as characterized by BP (N75 - N25), is 0.01 or more. It is useful to consider the quotient W as follows:
- W is 1.0 or less; more preferably 0.8 or less; more preferably 0.6 or less; more preferably 0.5 or less; more preferably 0.4 or less.
- W is 0.05 or more.
- the functionalized nanoparticles comprise zirconium oxide and one or more ligands, preferably ligands which have alkyl, heteroalkyl (e.g., poly(ethylene oxide)) or aryl groups having polar functionality; preferably carboxylic acid, alcohol, trichlorosilane, trialkoxysilane or mixed chloro/alkoxy silanes; preferably carboxylic acid. It is believed that the polar functionality bonds to the surface of the nanoparticle.
- ligands have from one to twenty-five non-hydrogen atoms, preferably one to twenty, preferably three to twelve.
- ligands comprise carbon, hydrogen and additional elements selected from the group consisting of oxygen, sulfur, nitrogen and silicon.
- alkyl groups are from C1-C18, preferably C2-C12, preferably C3-C8.
- aryl groups are from C6- C 12.
- Alkyl or aryl groups may be further functionalized with isocyanate, mercapto, glycidoxy or (meth)acryloyloxy groups.
- alkoxy groups are from C 1-C4, preferably methyl or ethyl.
- organosilanes some suitable compounds are alkyltrialkoxysilanes, alkoxy(polyalkyleneoxy)alkyltrialkoxysilanes, substituted-alky alkoxysUanes, phenyltrialkoxysilanes, and mixtures thereof.
- some suitable oranosilanes are n-propyltrimethoxysilane, n- propyltriethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, phenyltrimethoxysilane,
- organoalcohols preferred are alcohols or mixtures of alcohols of the formula R10OH, where RIO is an aliphatic group, an aromatic-substituted alkyl group, an aromatic group, or an alkylalkoxy group. More preferred organoalcohols are ethanol, propanol, butanol, hexanol, heptanol, octanol, dodecyl alcohol, octadecanol, benzyl alcohol, phenol, oleyl alcohol, Methylene glycol monomethyl ether, and mixtures thereof.
- organocarboxyhc acids preferred are carboxylic acids of formula Rl 1COOH, where Rl 1 is an a phatic group, an aromatic group, a polyalkoxy group, or a mixture thereof.
- organocarboxyhc acids in which Rl 1 is an ahphatic group preferred ahphatic groups are methyl, propyl, octyl, oleyl, and mixtures thereof.
- organocarboxyhc acids in which Rl 1 is an aromatic group the preferred aromatic group is C6H5.
- Rl 1 is a polyalkoxy group.
- Rl 1 is a polyalkoxy group
- Rl 1 is a linear string of alkoxy units, where the alkyl group in each unit may be the same or different from the alkyl groups in other units.
- organocarboxyhc acids in which Rl 1 is a polyalkoxy group preferred alkoxy units are methoxy, ethoxy, and combinations thereof. Functionalized nanoparticles are described, e.g., in US2013/0221279.
- the amount of functionalized nanoparticles in the formulation (calculated on a solids basis for the entire formulation) is from 50 to 95 wt%; preferably at least 60 wt%, preferably at least 70 wt%, preferably at least 80 wt%, preferably at least 90 wt%; preferably no greater than 90 wt%.
- a diazonaphthoquinone inhibitor provides sensitivity to ultraviolet light. After exposure to ultraviolet light, diazonaphthoquinone inhibitor inhibits dissolution of the photoresist film.
- the diazonaphthoquinone inhibitor may be made from a diazonaphthoquinone having one or more sulfonyl chloride substituent groups and which is allowed to react with an aromatic alcohol species, e.g., cumylphenol, 1,2,3-trihydroxybenzophenone, p-cresol trimer or the cresol novolak resin itself.
- the cresol novolac resin has epoxy functionality from 2 to 10, preferably at least 3; preferably no greater than 8, preferably no greater than 6.
- the cresol novolac resin comprises polymerized units of cresols, formaldehyde and epichlorohydrin.
- the film thickness is at least 50 nm, preferably at least 100 nm, preferably at least 500 nm, preferably at least 1000 nm; preferably no greater than 3000 nm, preferably no greater than 2000 nm, preferably no greater than 1500 nm.
- the formulation is coated onto standard silicon wafers or Indium-Tin Oxide ( ⁇ ) coated glass slides.
- Pixelligent PN zirconium oxide (Zr02) functionalized nanoparticles with a particle size distribution ranging from 2 to 13 nm were purchased from Pixelligent Inc. These nanoparticles were synthesized via solvo-thermal synthesis, with a zirconium alkoxide based precursor.
- the potential zirconium alkoxide based precursor used may include zirconium (IV) isopropoxide isopropanol, zirconium (IV) ethoxide, zirconium (IV) n-propoxide, and zirconium (IV) n-butoxide.
- Different potential capping agents described in the text of this invention can be added to the nanoparticles via a cap exchange process.
- the positive broadband g-line and i-line capable SPR-220 photoresist was purchased from MicroChem.
- the developer MF-26A (2.38wt% tetramethyl ammonium hydroxoide) was provided by the Dow
- Photoimageability conditions are summarized in Table 2 as times to achieve less than 10% retained film.
- the films were subjected to a soft bake at 115°C for 5min. They were subsequently exposed to UV radiation via the use of an Oriel Research arc lamp source housing a 1000W mercury lamp fitted with a dichroic beam turning mirror designed for high reflectance and polarization insensitivity over a 350 to 450 primary spectral range.
- the developer used was MF-26A based on tetramethyl ammonium hydroxide.
- the coated wafers were dipped into a petri dish containing MF-26A for 6 min. Thickness of the films after each dipping time was determined via an M-2000 Woollam spectroscopic ellipsometer.
- Table 3 lists the permittivities measured at 1.15MHz of several thin films made of different amounts of Pixelligent PA (Pix-PA) and Pixelligent PN (Pix-PN) type nanoparticles mixed with the SPR- 220 positive photoresist, as a function of weight percent of nanoparticles incorporated in the photoresist.
- the permittivity obtained for the Pixelligent PA type nanoparticle based thin films was as high as 8.88 for 89.1 wt% of nanoparticles present in the given thin film, while it was as high as 8.46 for the Pixelligent PN type nanoparticle based thin films for 81.23 wt% of nanoparticles present the given thin film. Both results are significantly higher than the permittivity of the base SPR-220 photoresist, as well as the dielectric constant CTQ required by Dow customers.
- Table 4 shows the thicknesses of the SPR-220-nanoparticle thin films before and after experiencing the exposure conditions detailed in Table 3, and a 6min soak time in the developer MF-26A (2.38wt% TMAH).
- the films containing the Pix PN type nanoparticles were completely removed after 6 min, regardless of the concentration of nanoparticles present in the films.
- the thin films containing the Pix-PA nanoparticles only the thin film containing the largest amount of nanoparticles was almost completely removed. This could be assigned to the lower thickness of this film ( ⁇ 1615nm) when compared to the thicknesses of the other films containing this type of nanoparticles (>3000nm).
Landscapes
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Spectroscopy & Molecular Physics (AREA)
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Materials For Photolithography (AREA)
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP16820410.5A EP3391146A1 (en) | 2015-12-17 | 2016-12-07 | Photo-imageable thin films with high dielectric constants |
JP2018527084A JP2019502151A (ja) | 2015-12-17 | 2016-12-07 | 高誘電率を有する光画像化可能薄フィルム |
CN201680070732.5A CN108292095A (zh) | 2015-12-17 | 2016-12-07 | 具有高介电常数的光可成像薄膜 |
KR1020187018077A KR20180095543A (ko) | 2015-12-17 | 2016-12-07 | 높은 유전 상수를 갖는 광-이미지 형성 가능한 박막 |
US15/781,722 US20180356726A1 (en) | 2015-12-17 | 2016-12-07 | Photo-imageable thin films with high dielectric constants |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201562268539P | 2015-12-17 | 2015-12-17 | |
US62/268,539 | 2015-12-17 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017105937A1 true WO2017105937A1 (en) | 2017-06-22 |
Family
ID=57708747
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2016/065226 WO2017105937A1 (en) | 2015-12-17 | 2016-12-07 | Photo-imageable thin films with high dielectric constants |
Country Status (7)
Country | Link |
---|---|
US (1) | US20180356726A1 (ko) |
EP (1) | EP3391146A1 (ko) |
JP (1) | JP2019502151A (ko) |
KR (1) | KR20180095543A (ko) |
CN (1) | CN108292095A (ko) |
TW (1) | TW201741765A (ko) |
WO (1) | WO2017105937A1 (ko) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TW201802587A (zh) * | 2016-03-24 | 2018-01-16 | 陶氏全球科技責任有限公司 | 具有高介電常數之光可成像薄膜 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1331517A1 (en) * | 2000-10-31 | 2003-07-30 | Sumitomo Bakelite Co., Ltd. | Positive photosensitive resin composition, process for its preparation, and semiconductor devices |
EP1724640A1 (en) * | 2004-03-12 | 2006-11-22 | Toray Industries, Inc. | Positive light-sensitive resin composition, relief pattern using the same, and solid imaging element |
US7630043B2 (en) | 2006-07-19 | 2009-12-08 | Hitachi Displays, Ltd. | Liquid display device and fabrication method thereof |
EP2485091A1 (en) * | 2009-09-29 | 2012-08-08 | Toray Industries, Inc. | Positive photosensitive resin composition, cured film obtained using same, and optical device |
US20130221279A1 (en) | 2010-10-27 | 2013-08-29 | Pixelligent Technologies, Llc | Synthesis, capping and dispersion of nanocrystals |
Family Cites Families (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2576762B2 (ja) * | 1993-06-30 | 1997-01-29 | 日本電気株式会社 | リング網のノード間情報収集方式 |
US5641608A (en) * | 1995-10-23 | 1997-06-24 | Macdermid, Incorporated | Direct imaging process for forming resist pattern on a surface and use thereof in fabricating printing plates |
WO2002046841A1 (fr) * | 2000-12-05 | 2002-06-13 | Kansai Research Institute. Inc. | Constituants actifs et compositions de resine photosensible les contenant |
US8179622B2 (en) * | 2005-12-22 | 2012-05-15 | Fujifilm Corporation | Photosensitive transfer material, member for display device, process for producing the member, black matrix, color filter, process for producing the color filter, substrate for display device, and display device |
-
2016
- 2016-11-21 TW TW105138147A patent/TW201741765A/zh unknown
- 2016-12-07 JP JP2018527084A patent/JP2019502151A/ja active Pending
- 2016-12-07 KR KR1020187018077A patent/KR20180095543A/ko unknown
- 2016-12-07 EP EP16820410.5A patent/EP3391146A1/en not_active Withdrawn
- 2016-12-07 WO PCT/US2016/065226 patent/WO2017105937A1/en active Application Filing
- 2016-12-07 US US15/781,722 patent/US20180356726A1/en not_active Abandoned
- 2016-12-07 CN CN201680070732.5A patent/CN108292095A/zh not_active Withdrawn
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1331517A1 (en) * | 2000-10-31 | 2003-07-30 | Sumitomo Bakelite Co., Ltd. | Positive photosensitive resin composition, process for its preparation, and semiconductor devices |
EP1724640A1 (en) * | 2004-03-12 | 2006-11-22 | Toray Industries, Inc. | Positive light-sensitive resin composition, relief pattern using the same, and solid imaging element |
US7630043B2 (en) | 2006-07-19 | 2009-12-08 | Hitachi Displays, Ltd. | Liquid display device and fabrication method thereof |
EP2485091A1 (en) * | 2009-09-29 | 2012-08-08 | Toray Industries, Inc. | Positive photosensitive resin composition, cured film obtained using same, and optical device |
US20130221279A1 (en) | 2010-10-27 | 2013-08-29 | Pixelligent Technologies, Llc | Synthesis, capping and dispersion of nanocrystals |
Also Published As
Publication number | Publication date |
---|---|
KR20180095543A (ko) | 2018-08-27 |
CN108292095A (zh) | 2018-07-17 |
US20180356726A1 (en) | 2018-12-13 |
JP2019502151A (ja) | 2019-01-24 |
TW201741765A (zh) | 2017-12-01 |
EP3391146A1 (en) | 2018-10-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TWI337616B (ko) | ||
KR101118750B1 (ko) | 콜로이드 세라믹졸과 유기수지가 하이브리드화된 코팅제의 제조방법 및 이를 이용한 코팅막 | |
KR102266587B1 (ko) | 수지 조성물, 그 경화막과 그 제조방법, 및 고체촬상소자 | |
KR100929547B1 (ko) | 올리고실록산 하이브리드 코팅을 이용한 가스 차단막 | |
EP3391146A1 (en) | Photo-imageable thin films with high dielectric constants | |
JP2006137932A (ja) | コーティング用組成物およびそれを用いた表示装置 | |
WO2017165161A1 (en) | Photo-imageable thin films with high dielectric constants | |
JP2010144136A (ja) | 熱硬化性シリコーン樹脂組成物 | |
EP3433674A1 (en) | Photo-imageable thin films with high dielectric strength | |
WO2017105914A1 (en) | Photo-imageable thin films with high dielectric constants | |
JP6530644B2 (ja) | Ito導電膜形成用組成物及びito導電膜 | |
KR20180095544A (ko) | 높은 유전 상수를 갖는 광-이미지형성가능 박막 | |
TWI789893B (zh) | 阻障材及其製備方法 | |
CN116041709A (zh) | 一种光固化苯基氟硅改性环氧涂料、涂层的制备方法及应用 | |
JP2015017194A (ja) | アルコキシシランを含有する固体撮像素子用高屈折率膜形成組成物 | |
CN113527916A (zh) | 一种常温固化型低VOCs无机涂料及其制备方法 | |
JP2022029415A (ja) | 積層体 | |
JP2022029284A (ja) | 積層体 | |
TW201938656A (zh) | 有機改質之金屬氧化物或類金屬氧化物聚合物膜 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16820410 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2018527084 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 20187018077 Country of ref document: KR Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2016820410 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 2016820410 Country of ref document: EP Effective date: 20180717 |