WO2017039338A1 - 고내상 유중수형 화장료 조성물 - Google Patents

고내상 유중수형 화장료 조성물 Download PDF

Info

Publication number
WO2017039338A1
WO2017039338A1 PCT/KR2016/009754 KR2016009754W WO2017039338A1 WO 2017039338 A1 WO2017039338 A1 WO 2017039338A1 KR 2016009754 W KR2016009754 W KR 2016009754W WO 2017039338 A1 WO2017039338 A1 WO 2017039338A1
Authority
WO
WIPO (PCT)
Prior art keywords
oil
cosmetic composition
dimethicone
water
composition
Prior art date
Application number
PCT/KR2016/009754
Other languages
English (en)
French (fr)
Inventor
정춘복
강유진
김경남
최영진
Original Assignee
(주)아모레퍼시픽
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020160111368A external-priority patent/KR102506973B1/ko
Application filed by (주)아모레퍼시픽 filed Critical (주)아모레퍼시픽
Priority to MYPI2018700801A priority Critical patent/MY186442A/en
Priority to US15/756,429 priority patent/US10639267B2/en
Priority to CN201680063382.XA priority patent/CN108348410A/zh
Priority to SG11201801628YA priority patent/SG11201801628YA/en
Priority to JP2018511432A priority patent/JP6714075B2/ja
Publication of WO2017039338A1 publication Critical patent/WO2017039338A1/ko
Priority to HK18115073.8A priority patent/HK1256023A1/zh

Abstract

본 발명은 내상에 펄 입자 또는 수상 색소를 포함하여 색상을 나타내는 것을 특징으로 하는 고내상 유중수형 화장료 조성물을 제공한다. 본 발명은 상기 펄 또는 색소를 내상인 수상에 안정적으로 존재하게 하기 위하여 큰 유화 입자를 형성하는 특정 종류의 유화제를 사용하고, 에멀전 형성을 위한 유화력 보충과 제형의 분리 방지, 그리고 유동성을 개선하기 위하여 특정 종류의 분산제 및 방부제를 사용한다. 또한, 조성물의 표면 충진도를 높이기 위하여 외상인 유상 성분에 실리콘 오일 및 에스테르 오일을 포함하고, 적정 범위의 중량비로 배합한다. 본 발명의 화장료 조성물은 내상에 펄을 안정화함으로써 펄이 가지는 다양한 심미적, 기능적 효과를 제공한다.

Description

고내상 유중수형 화장료 조성물
본 출원은 2015년 09월 02일자 한국 특허 출원 제10-2015-0124174호 및 2016년 08월 31일자 한국 특허 출원 제10-2016-0111368호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된 모든 내용은 본 명세서의 일부로서 포함한다.
본 발명은 고내상 유중수형 화장료 조성물의 내상 파트에 색상을 나타내는 안료 또는 염료를 안정화하여 제품의 사용 시 내상의 색상을 나타내는 것을 특징으로 하는 고내상 유중수형 화장료 조성물에 관한 것으로서, 심미적, 기능적 효과를 겸비한 화장료 조성물의 제조 및 기타 유사 분야에서 활용될 수 있다.
건조한 피부는 주름이 생기기 쉽고 노화에 취약하다. 이에 따라 시중에는 피부에 수분을 공급할 수 있는 다양한 형태의 화장료 조성물들이 출시되어 있다. 특히, 최근에는 피부에 도포 시 물방울이 터져 나오는 것과 같은 시각적 효과를 제공하는 고내상의 유중수형 에멀전 제형의 화장 제품이 출시되어 보다 폭넓은 만족감을 제공할 수 있게 되었다. 상기 고내상의 유중수형 에멀전 제형은 조성물 입자의 내상인 수상의 함량을 현저하게 높여 제조하며, 손으로 문지르는 등의 외부 자극을 가하면 내상이 터져 나와 물방울 형태로 합일되는데, 이것이 마치 물이 터져 나와 맺히는 것처럼 보인다고 하여 일명 '물터짐 에멀전'으로 불리기도 한다. 이러한 형태의 에멀전은 시각적으로 수분 함유 상태를 확인할 수 있으므로 제품 사용에의 재미와 심리적인 만족감을 더해주는 새로운 형태의 보습형 화장료로서 각광받고 있다.
그러나 상기한 통상의 고내상 유중수형 에멀전 제형에서 터져 나오는 내상은 투명한 색으로, 물의 느낌을 제공하는 것 이외의 다양한 효과를 연출하기에는 상당한 제한이 있다. 이를테면, 사용 시에 터져 나오는 내상의 특성을 활용하여 수분감 이외에 영양감을 표현하고자 하는 경우나, 조성물 내에 함유된 각종 기능성 천연 물질의 특성을 표현하고자 하는 경우 등에 활용하는데 한계가 있다. 따라서 보다 개량된 형태의 고내상 유중수형 에멀전에 대한 개발이 필요한 실정이다.
이에 본 발명자들은 상기 에멀전 제형의 내상에 색상을 부여하면 심미적 효과는 물론 각종 기능성 효과 또한 겸비할 수 있음에 착안하였고, 오랜 연구와 노력을 통하여 본 발명을 완성하게 되었다.
[선행기술문헌]
[특허문헌]
(특허문헌 1) 유중 수형 유화 화장료 조성물 및 그 제조방법 (대한민국 등록특허 10-1453617)
(특허문헌 2) 피부 개선용 유중수형 메이크업 화장료 조성물 (대한민국 공개특허 10-2011-0059986)
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로,
고내상 유중수형 화장료 조성물의 내상에 색상을 구현하는 것을 목적으로 한다. 보다 구체적으로는 상기 내상에 색상을 나타내는 안료 또는 염료를 안정적으로 유지시키고 제품의 사용 시 이로부터 색상이 나타나도록 하는 것을 목적으로 한다.
또한, 내상에 색상이 구현된 고내상 유중수형 화장료 조성물이 분리 없이 안정적으로 유지되고, 표면 충진도가 우수하게 제공되도록 하는 것을 또 다른 목적으로 한다.
상기한 목적을 달성하기 위하여, 본 발명은 내상인 수상베이스의 제조 시 색상을 나타내는 안료 또는 염료를 포함시키는 것을 해결수단으로 한다.
특히 색상 구현을 위한 물질로서 '안료'를 포함시키는 경우, 본 발명의 화장료 조성물은 색상을 나타내는 안료가 내상인 수상에 안정적으로 존재하도록 큰 유화 입자를 형성하게 해주는 특정 종류의 유화제를 함유하고, 유화력을 보충하고 에멀전 제형의 분리를 방지하기 위하여 특정 종류의 분산제를 함유한다. 또한 내상의 색소를 보조적으로 안정화하기 위하여 점증제를 함유하고, 조성물의 표면 충진도를 높이기 위하여 실리콘 오일 및 에스테르 오일을 적정 비율로 배합하고 분산제의 함량을 조절하는 것이 바람직하다.
아울러, 색상 구현을 위한 물질로서 '염료'를 사용하는 경우에는 특별히 상기한 화장료 조성물의 조합 및 함량을 따르지 않아도 무방하며 통상의 고내상 유중수형 화장료 조성물의 조합 및 함량에 따라 자유롭게 활용 가능하다.
본 발명은 내상에 색상을 나타내는 안료 또는 염료 중 어느 하나 이상을 포함하고, 제품의 사용 시 내상의 색상을 나타내는 것을 특징으로 하는 고내상 유중수형 화장료 조성물을 제공한다.
이때, 상기 화장료 조성물은 피이지-10디메치콘(PEG-10 Dimethicone), 라우릴폴리글리세릴-3폴리디메칠실록시에칠디메치콘(Lauryl polyglyceryl-3 Polydimethylsiloxyethyl Dimethicone), 라우릴피이지-9폴리디메칠실록시에칠디메치콘(Lauryl PEG-9 Polydimethylsiloxyethyl Dimethicone), 폴리글리세릴-3폴리디메칠실록시에칠디메치콘(Polyglyceryl-3 Polydimethylsiloxyethyl Dimethicone), 카프릴릴 메치콘, 피이지-12 디메치콘/PPG-20 크로스폴리머(Caprylyl Methicone, PEG-12 Dimethicone/PPG-20 Crosspolymer), 디메치콘/피이지-10/15 크로스폴리머(Dimethicone/PEG-10/15 Crosspolymer), 디메치콘/폴리글리세린-3 크로스폴리머(Dimethicone/Polyglycerin-3 Crosspolymer), 세틸 피이지.피피지-10/1디메치콘(Cetyl PEG.PPG-10/1 Dimethicone), 세틸 디메치콘 코폴리올(Cetyl Dimethicone Copolyol) 및 디메치콘/비닐디메치콘 크로스폴리머(Dimethicone/Vinyl Dimethicone crosspolymer)로 이루어진 군 중에 선택되는 2종 이상의 유화제를 포함할 수 있다.
이때, 상기 화장료 조성물은 폴리하이드록시 스테아릭산(Polyhydroxystearic Acid), 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머(Acrylates/Ethylhexyl Acrylate/Dimethicone Methacrylate Copolymer) 및 비닐피롤리돈/헥사데센 코폴리머(Vinylpyrrolidone/Hexadecene Copolymer)로 이루어진 군 중에 선택되는 2종 이상의 분산제를 포함할 수 있다.
이때, 상기 화장료 조성물의 유상 성분은 실리콘 오일 및 에스테르 오일을 포함할 수 있다.
이때, 상기 실리콘 오일 대비 에스테르 오일의 중량비는 1:0.2 이상일 수 있다.
이때, 상기 색상을 나타내는 안료는 펄 입자 및 수상 분산 피그먼트 중 어느 하나 이상일 수 있다.
이때, 상기 펄 입자는 마이카, 합성 마이카, 알루미나, 보로실리케이트, 보론나이트라이드 분말, 탈크 및 세리사이트로 구성되는 군 중에 선택되는 1종 이상의 판상 분체일 수 있다.
이때, 상기 펄 입자는 티타늄 다이옥사이드, 틴옥사이드 및 아이언 옥사이드로 구성되는 군 중에 선택되는 1종 이상의 물질로 코팅된 것일 수 있다.
이때, 상기 펄 입자의 평균 입도는 6~15um일 수 있다.
이때, 상기 수상 분산 피그먼트는 티타늄 다이옥사이드를 알루미나 또는 실리카로 코팅한 것일 수 있다.
이때, 상기 화장료 조성물은 필름 포머를 포함할 수 있다.
이때, 상기 필름 포머는 하이드로제네이티드 폴리사이클로페타디엔(Hydrogenated Polycyclopentadiene)을 포함할 수 있다.
또한, 본 발명은 고내상 유중수형 화장료 조성물에 있어서,
유상 성분으로 실리콘 오일 및 에스테르 오일을 조성물의 총 중량 대비 각 3~7중량% 포함하고, 유화제로 디메치콘/피이지-10/15 크로스폴리머(Dimethicone/PEG-10/15 Crosspolymer), 디메치콘/폴리글리세린-3 크로스폴리머(Dimethicone/Polyglycerin-3 Crosspolyme) 및 세틸 피이지.피피지-10/1디메치콘(Cetyl PEG.PPG-10/1 Dimethicone)를 조성물의 총 중량 대비 각 0.1~3중량% 포함하고, 분산제로 폴리하이드록시 스테아릭 애씨드(Polyhydroxystearic Acid) 및 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머(Acrylates/Ethylhexyl Acrylate/Dimethicone Methacrylate Copolymer)를 조성물의 총 중량 대비 각 1~3중량% 포함하고, 수상 성분으로 색상을 나타내는 안료 및 염료 중 어느 하나 이상을 조성물의 총 중량 대비 1~2중량% 포함하고, 점증제로 하이드록시에틸 아크릴레이트/소듐 아크릴로일 디메틸 타우레이트 코폴리머(Hydroxyethyl Acrylate/Sodium Acryloyldimethyl Taurate Copolymer)를 조성물의 총 중량 대비 0.01~0.5중량% 포함하고, 필름 포머로 하이드로제네이티드 폴리사이클로페타디엔(Hydrogenated Polycyclopentadiene)을 조성물의 총 중량 대비 0.1~5중량%로 포함하는 것을 특징으로 하는 고내상 화장료 조성물을 제공한다.
본 발명은 상기한 과제 해결 수단을 이용하여, 사용 시 표면에서 물방울을 형성하는 내상에 색상을 구현하여 다양한 심미적, 기능적 효과를 나타내는 고내상 유중수형 화장료 조성물을 제공한다.
본 발명의 화장료 조성물은 제조 공정 중 및 제조 공정 후 제형의 분리 없이 내상에 포함된 색상 안료 또는 염료가 안정하게 유지되며, 용기에 충진 시 표면이 고르고 평편하게 충진된다.
이에 따라 본 발명의 화장료 조성물은 내상에 색상을 구현하는 물질로서 안료 또는 염료를 모두 포함할 수 있어서, 본 발명을 통하여 사용 가능한 색상 구현 물질의 범위를 보다 넓게 제공하는 것이 가능해진다.
도 1은 고내상 유중수형 화장료 조성물에 있어서, (a) 투명한 내상을 가지는 제형(종래의 에멀전) 및 (b) 본 발명에 따라 색상이 구현된 내상을 가지는 제형(본 발명의 에멀전)을 비교한 것이다.
도 2는 고내상 유중수형 화장료 조성물에 있어서, (a) 펄을 포함하고 있으나 내상에 색상을 구현하지 못하는 제형(펄 포함, 색상X) 및 (b) 본 발명에 따라 색상이 구현된 제형(펄 포함, 색상O)을 비교한 것이다.
도 3은 본 발명에 따른 고내상 유중수형 화장료 조성물의 구성 성분 중 분산제의 첨가를 생략한 제형이 제조 과정 중 가온 단계에서 분리되는 현상을 보여준다.
도 4는 고내상 유중수형 화장료 조성물에 있어서, 유상베이스를 구성하는 오일의 성분 중 실리콘 오일 및 에스테르 오일의 배합 중량비에 따른 표면 충진도의 차이를 보여준다.
도 5는 고내상 유중수형 화장료 조성물에 있어서, 유상베이스를 구성하는 오일로서 (a) 일반 제형, (b) 실리콘 오일만 포함한 제형 및 (c) 에스테르 오일만 포함한 제형의 에멀전 입자 크기를 현미경으로 관찰한 결과이다.
본 발명은 내상에 색상을 나타내는 고내상 유중수형 화장료 조성물을 제공한다.
고내상의 유중수형 화장료 조성물은 유중수형 에멀전의 통상 20~90%로 내상의 비율을 크게 형성하고 유화 입자의 크기를 증가시킴으로써 외부의 자극, 이를테면 손으로 문지르는 힘 등을 가할 때 내상을 구성하는 수상 성분이 밖으로 나오면서 합일되는 특성이 있다. 육안으로는 물방울이 터져 나와 맺히는 것과 같이 보인다고 하여 '물터짐' 제형이라고도 불리며, 사용자에게 심리적, 심미적 만족감을 높여줄 수 있는 제형이다.
본 발명은 상기 고내상 유중수형 화장료 조성물의 내상에 색상을 나타내는 안료 또는 염료를 안정화함으로써 보다 다양한 특성으로 연출하여 각 화장료 조성물의 기능 및 목적을 효과적으로 부각시킬 수 있다.
상기 색상을 나타내는 물질 중 염료는 모든 조성에서 자유롭게 활용 가능한 반면 안료의 경우에는 내상에서 단독으로 안정화된 상태로 존재하기 어렵고, 제조 공정 중 및 제조 공정 후 제형의 분리를 일으킬 수 있다. 따라서 본 발명은 이러한 안료를 포함하는 경우에도 안정적인 화장료 조성물의 제조가 가능하도록 가장 바람직한 조성물의 조합 및 함량을 제공한다.
그러나 이로부터 본 발명의 화장료 조성물을 특정 범위의 것으로만 제한하고자 하는 의미는 아니며 상기 특정 범위의 화장료 조성물은 본 발명을 보다 폭넓게 실시하기 하기 위한 하나의 실시 수단으로서 이해되어야 한다.
이하 본 발명을 보다 상세히 설명한다.
다만, 하기 내용은 본 발명에 대한 이해를 돕기 위하여 가장 대표적인 실시 형태만을 기재한 것으로서 본 발명의 권리 범위는 이에 한정되지 않으며 본 발명은 하기 내용과 균등한 모든 범위를 포괄하는 것으로 이해되어야 한다.
본 발명의 내상에 색상을 가지는 화장료 조성물은,
수상베이스와 유상베이스의 제조 및 가온 단계;
상기 수상 및 유상 베이스의 혼합, 유화를 통한 유중수(W/O)형 에멀전 제조 단계; 및
상기 유중수형 에멀전의 표면 충진을 위한 재가온 단계를 포함하여 제조된다.
본 발명의 화장료 조성물을 제조하기 위해서는 첫째, 상기 혼합 및 유화 단계에서 색상을 나타내는 안료 또는 염료가 내상인 수상 내에서 안정화되어야 하고, 둘째, 유화 에멀전의 입자가 안정적으로 형성되어야 하며, 셋째, 재가온 단계에서도 제형의 분리 없이 안정성이 유지되어야 하고, 넷째, 최종적인 표면 충진 상태가 고르고 평편해야 한다. 특히, 펄, 색상을 나타내는 안료 또는 염료 등을 포함하더라도 함유되는 기타 성분 물질에 따라 내상에 색상이 구현되지 않는 경우가 빈번한 바, 본 발명에서는 상기한 사항들을 동시에 만족시키면서도 내상에 색소를 안정하게 유지시킬 수 있는 성분 물질의 조합 및 함량을 제시한다.
구체적으로 본 발명의 화장료 조성물은 수상베이스의 제조 시 펄 및 점증제 등을 포함하고, 유상베이스의 제조 시 특정 종류의 유화제 및 분산제 등을 포함하며, 또한 유상베이스를 구성하는 오일의 종류 및 배합비를 한정함으로써 제조 단계에서 요구되는 상기 특성들을 만족시킬 수 있다.
이하 본 발명의 제조에 사용되는 각 핵심 성분에 대하여 보다 상세히 설명한다.
색상을 나타내는 안료 및 염료
본 발명은 고내상 유중수형 화장료 조성물의 사용 시 물방울을 형성하는 내상에 색상을 구현하기 위하여 수상 베이스의 제조 시 색상을 나타내는 안료 또는 염료를 첨가하고, 이를 안정화시키는 것을 핵심으로 한다. 본 명세서에서 '안료'는 무기물로서 색상을 나타내고, '염료'는 유기물로서 색상을 나타내는 물질을 의미한다.
상기 안료는 펄 입자 및 수상 분산 피그먼트 중 어느 하나 이상일 수 있다.
상기 펄 입자는 마이카, 합성 마이카, 알루미나, 보로실리케이트, 보론나이트라이드 분말, 탈크, 세리사이트 등의 판상 분체인 것이 바람직하고, 그 표면을 티타늄 다이옥사이드, 틴옥사이드, 아이언 옥사이드로 구성되는 군에서 선택된 1종 또는 2종 이상의 혼합물로 코팅하여 사용하는 것이 보다 바람직하다. 상기 코팅 비율은 펄 입자의 총 중량 대비 2~60중량%로 한다. 또한, 본 발명에 사용되는 펄은 미세간섭 펄인 것이 바람직하다. 미세간섭 펄은 외관 색상으로는 흰색을 띠고 있으나 피부상에서 반사광을 증가시키고 특유의 간섭색상을 가져 화사하고 독특한 색감을 나타낼 수 있다. 상기 미세간섭 펄 입자의 크기로 바람직하게는 직경 6~15um이고, 보다 바람직하게는 평균적으로 직경 7.19um이다. 상기 범위보다 펄 입자의 크기가 크면 유화 입자 안에 포집되기 어려우며, 상기 범위보다 펄 입자의 크기가 작으면 계면에 작용하여 제형의 안정도가 떨어질 수 있다. 즉, 펄 입자의 평균 입도는 제형의 안정도에 영향을 주므로, 지나치게 크거나 작은 펄 입자는 수상베이스 내에서 고르게 존재하지 못하고 분계(分界)하거나 계면에 작용하여 에멀전 안정도를 떨어뜨릴 수 있다.
종래에는 기타 안료 또는 염료에 비하여 특히 상기한 펄을 포함한 형태의 안료를 사용하는 경우에 이를 내상에 독립적으로 안정화시키기 어려운 한계가 있었다. 이는 통상 펄 입자 표면에 코팅되는 티타늄 다이옥사이드가 에멀전 생성 시 내상보다는 외상인 유상으로 끌려나가려는 특성이 컸기 때문이다. 그러나 본 발명에서는 조성물의 특정 조합과 함량을 한정함으로써 이러한 현상을 방지하고 내상에 펄 안료를 보다 안정적으로 분산시킬 수 있다.
한편, 본 명세서에서 '수상 분산 피그먼트'란 무기 물질에 친수성 입자가 코팅된 분체를 의미하며, 상기 무기 물질의 포함 범위에는 펄 입자를 반드시 배제하는 것은 아니나, 통상 펄 입자를 활용하는 형태는 전술한 바에 따르는 것이 보다 효과적이고, 상기한 수상 분산 피그먼트를 구성하는 무기 물질에는 펄 이외의 기타 무기 물질을 활용하는 것이 바람직하다. 이를테면 본 발명의 수상 분산 피그먼트는 티타늄 다이옥사이드(TiO2)에 알루미나(Alumina), 실리카(Silica) 중 어느 하나 이상을 코팅한 형태로 사용할 수 있다. 상기 수상 분산 피그먼트의 함량은 바람직하게는 조성물의 총 중량 대비 1~10중량%이고, 보다 바람직하게는 1.5중량% 이다.
한편, 상기 염료로는 유기 색소 등 수상에 분산 가능한 형태의 염료라면 어느 것이든 제한 없이 사용할 수 있다.
상기한 색상을 나타내는 안료 또는 염료는 선택적 또는 동시 사용 가능하고, 이로부터 구현되는 색상은 어느 색이나 한정 없이 제공하고자 하는 효과에 따라 다양하게 구현 가능하다. 이를테면, 우유 또는 에센스가 가지는 보습 및 영양감, 또는 미백효과 등을 표현하고자 할 때에는 흰색 펄을 사용할 수 있다.
유화제
에멀전이 유화될 때 유화 입자가 작게 형성되면 '물터짐' 현상이 약해지는 경향이 있다. 따라서 본 발명에서는 상기한 문제점을 방지하고 수상에 안정적으로 색상 안료를 함유시키기 위해 본 발명에서는 큰 유화 입자를 형성하게 해주는 유화제를 사용하고, 그 중에서도 특정 종류의 유화제를 조합하여 사용한다.
본 발명의 유화제로는, 피이지-10디메치콘(PEG-10 Dimethicone), 라우릴폴리글리세릴-3폴리디메칠실록시에칠디메치콘(Lauryl polyglyceryl-3 Polydimethylsiloxyethyl Dimethicone), 라우릴피이지-9폴리디메칠실록시에칠디메치콘(Lauryl PEG-9 Polydimethylsiloxyethyl Dimethicone), 폴리글리세릴-3폴리디메칠실록시에칠디메치콘(Polyglyceryl-3 Polydimethylsiloxyethyl Dimethicone), 카프릴릴 메치콘 (and) 피이지-12 디메치콘/피피지-20 크로스폴리머(Caprylyl Methicone (and) PEG-12 Dimethicone/ PPG-20 Crosspolymer), 디메치콘/피이지-10/15 크로스폴리머(Dimethicone/PEG-10/15 Crosspolymer), 디메치콘/폴리글리세린-3 크로스폴리머(Dimethicone/Polyglycerin-3 Crosspolymer), 세틸 피이지.피피지-10/1 디메치콘(Cetyl PEG.PPG-10/1 Dimethicone), 세틸 디메치콘 코폴리올(Cetyl Dimethicone Copolyol) 및 디메치콘/비닐 디메치콘 크로스폴리머(Dimethicone/Vinyl Dimethicone Crosspolymer)로 이루어진 군 중에 선택되는 2종 이상을 사용할 수 있다. 바람직하게는 디메치콘/피이지-10/15 크로스폴리머, 디메치콘/폴리글리세린-3 크로스폴리머 및 세틸 피이지.피피지-10/1 디메치콘을 사용할 수 있다.
상기 유화제의 함량은 조성물의 총 중량 대비 각 0.1~3중량%인 것이 바람직하나, 이에 제한되는 것은 아니다.
분산제
한편, 상기한 방법으로 수상에 펄을 안정화시킬 수는 있으나, 크게 형성된 유화 입자가 제형의 안정성을 저해하거나 수상에 포함된 색소가 계면의 안정성에 영향을 미쳐 공정 중 조성물이 분리되는 문제가 생기기 쉽다. 실제로 조성물의 충진 등을 위하여 재가온하는 과정에서 제형이 쉽게 분리되는 등의 문제가 발생한다.
이를 위하여 본 발명에서는 특정 종류의 분산제를 유상베이스에 첨가하고, 상기 분산제로부터 소정의 유화 유지력과 제형의 유동도를 보충한다. 그러나 모든 분산제가 유화에 도움을 주는 것은 아니며, 본 발명에 적합한 유화력을 가진 분산제로는 폴리하이드록시 스테아릭산(Polyhydroxystearic Acid), 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머(Acrylates/Ethylhexyl Acrylate/Dimethicone Methacrylate Copolymer) 및 비닐피롤리돈/헥사데센 코폴리머(Vinylpyrrolidone/Hexadecene Copolymer) 중에 선택되는 2종 이상을 사용할 수 있고, 바람직하게는 폴리하이드록시 스테아릭산 및 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머를 사용할 수 있다.
상기 분산제의 함량은 조성물의 총 중량 대비 각 1~3중량%인 것이 바람직하나, 이에 제한되는 것은 아니다.
점증제
점증제는 내상인 수상에 함유된 펄이 외상인 유상으로 끌려나가는 것을 보조적으로 방지하기 위하여 수상베이스에 첨가될 수 있다.
점증제가 첨가됨으로써 내부의 점도(thickness)가 증가하면 펄이 유상으로 끌려나가는 정도가 감소하고, 종래 대비 비교적 다량의 펄을 함유하는 것 또한 가능하다.
점증제의 종류에 있어서 특별한 제한은 없으나, 바람직하게는 잔탄검(Xanthan gum), 카보머(Carbomer), 하이드록시프로필 스타치 포스페이트(Hydroxypropyl Starch Phosphate), 소듐 마그네슘 실리케이트(Sodium Magnesium Silicate), 하이드록시에틸 셀룰로오스(Hydroxyethyl Cellulose) 및 하이드록시에틸 아크릴레이트/소듐 아크릴로디메틸 타우레이트 코폴리머(Hydroxyethyl Acrylate/Sodium Acryloyldimethyl Taurate Copolymer)로 이루어진 군 중에 선택되는 1종 이상을 사용할 수 있고, 그 함량은 조성물의 총 중량 대비 0.01~0.5중량%가 바람직하다.
필름 포머
피부 위에서의 밀착감 부여와 메이크업의 지속력 강화를 위하여 필름 포머(필름 형성제)가 첨가될 수 있다.
메이크업 제품에서 주로 사용되던 트리메틸실록시실리케이트 및 폴리프로필실세스퀴옥산 등의 MQ 또는 T 레진은 제형 내에서의 피그먼트 분산성을 높여 수상에 존재하는 컬러 구현 입자를 오일 파트로 분산시킨다. 본 발명에서는 하이드로제네이티드 폴리사이클로페타디엔(hydrogenated polycyclopentadiene)를 포함하는 필름 포머를 사용하여 물터짐 색상에 영향이 없으면서도 밀착성 및 지속성을 강화할 수 있다.
오일의 조합
최종적인 표면 충진 상태가 좋지 못하면 제품의 상용 가치가 떨어지므로 본 발명의 화장료 조성물은 우수한 충진도를 확보하기 위하여도 성분 물질의 조합을 한정하고 있다.
충진도는 유상 성분에 포함된 오일의 종류와 배합비 및 이에 따라 달라지는 분산제의 함량에 영향을 받는다. 구체적으로 본 발명의 유상 성분을 구성하는 오일은 실리콘 오일과 에스테르 오일을 포함하며, 실리콘 오일 대비 에스테르 오일의 배합 중량비가 높아질수록 표면 충진도가 우수하다. 이는, 실리콘 오일 대비 에스테르 오일이 증가할수록 에멀전입자 크기가 증가하여 고온 유동도가 증가하고, 고온 유동도가 증가할 수록 제형의 충진도가 좋아지기 때문이다.
본 발명에서는 실리콘 오일 대비 에스테르 오일의 배합 중량비가 1:0.2 이상일 때 바람직한 표면 충진도를 가진다.
상기한 내용을 종합하면, 본 발명의 바람직한 일 실시 형태로서, 유상 성분으로 실리콘 오일 및 에스테르 오일을 조성물의 총 중량 대비 각 3~7중량% 포함하고, 유화제로 디메치콘/피이지-10/15 크로스폴리머(Dimethicone/PEG-10/15 Crosspolymer), 디메치콘/폴리글리세린-3 크로스폴리머(Dimethicone/Polyglycerin-3 Crosspolyme) 및 세틸 피이지.피피지-10/1디메치콘(Cetyl PEG.PPG-10/1 Dimethicone)를 조성물의 총 중량 대비 각 0.1~3중량% 포함하고, 분산제로 폴리하이드록시 스테아릭 애씨드(Polyhydroxystearic Acid) 및 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머(Acrylates/Ethylhexyl Acrylate/Dimethicone Methacrylate Copolymer)를 조성물의 총 중량 대비 각 1~3중량% 포함하고, 수상 성분으로 색상을 나타내는 안료 및 염료 중 어느 하나 이상을 조성물의 총 중량 대비 1~2중량% 포함하고, 점증제로 하이드록시에틸 아크릴레이트/소듐 아크릴로일 디메틸 타우레이트 코폴리머(Hydroxyethyl Acrylate/Sodium Acryloyldimethyl Taurate Copolymer)를 조성물의 총 중량 대비 0.01~0.5중량% 포함하고, 필름 포머로 하이드로제네이티드 폴리사이클로페타디엔을 조성물의 총 중량 대비 0.1~5중량%로 포함하는 것을 특징으로 하는 고내상 화장료 조성물을 제조할 수 있다.
상기한 물질 외에도 본 발명의 효과를 저해하지 않는 한, 부수적인 성분 물질을 더 함유할 수 있다.
본 발명의 유중수형 화장료 조성물은 에멀전 제형이라면 어느 것이든 가능하지만, 특히 팩트, 파운데이션, 크림 등으로 제조될 때 보다 효과적이다.
이하, 본 발명에 대한 이해를 돕기 위하여 실험예를 기재한다. 다만 하기 실험예는 본 발명의 효과에 관한 일 예들에 해당할 뿐, 본 발명의 권리 범위 및 효과가 이에 한정되는 것은 아니다.
이하, 본 발명의 실시예 1 및 비교예 1 내지 2를 기재한다. 또한, 본 발명의 효과에 관한 실험예 1 내지 5를 기재한다. 실험에는 하기 실시예 1 및 비교예 1 또는 2를 이용하였다.
실시예 1
본 발명에 따라 내상에 색상을 구현한 제형에 대한 처방의 일 실시예를 하기 표 1로 제시한다.
구분 원료 함량 ( 중량% )
유화제 Dimethicone/PEG-10/15 Crosspolymer 1.7%
Dimethicone/Polyglycerin-3 Crosspolymer 1.5%
Cetyl PEG.PPG-10/1 Dimethicone 0.1%
유상 베이스 Phenyl Trimethicone 7%
Cyclopentasiloxane 3%
Neopentyl Glycol Diheptanoate 5.31%
Ethylhexyl Methoxycinnamate 6%
안료 Titanium Dioxide & Zinc Oxide & Iron Oxide 19%
Pearl Pigment (white) 1.5%
필름포머 Hydrogenated Polycyclopentadiene 1.5%
분산제 Acrylates/Ethylhexyl Acrylate/Dimethicone Methacrylate Copolymer 2%
Polyhydroxystearic Acid 1%
왁스 Polyethylene 3%
Ozokerite 2%
수상베이스 D.I water to 100
Polyol (Butylene glycol, Glycerine) 12%
Phenoxyethanol 0.4%
Ethylhexylglycerin 0.05%
Soduim Chloride 1%
Hydroxyethyl Acrylate/Sodium Acryloyldimethyl Taurate Copolymer 0.1%
비교예 1
투명한 내상을 가지는 제형의 처방은 하기 표 2로 제시한다.
하기 처방은 본 발명과 함께 새롭게 제안된 처방예로서 이에 따를 경우 종래에 비하여 보다 간편하고 효과적으로 투명 내상의 제형을 제조할 수 있다.
구분 원료 함량 ( 중량% )
유화제 Dimethicone/PEG-10/15 Crosspolymer 1%
Cetyl PEG.PPG-10/1 Dimethicone 0.1%
유상 베이스 Phenyl Trimethicone 8%
Cyclopentasiloxane 3%
Neopentyl Glycol Diheptanoate 5.41%
Ethylhexyl Methoxycinnamate 6%
안료 Titanium Dioxide & Zinc Oxide & Iron Oxide 19%
왁스 Polyethylene 3%
Ozokerite 2%
수상베이스 D.I water to 100
Polyol (Butylene glycol, Glycerine) 12%
Soduim chloride 1%
비교예 2
내상에 펄을 포함하고 있으나, 색상이 구현되지 않은 제형의 처방을 하기 표 3으로 제시한다.
구분 원료 함량 ( 중량% )
유화제 Dimethicone/PEG-10/15 Crosspolymer 1%
Cetyl PEG.PPG-10/1 Dimethicone 0.1%
유상 베이스 Phenyl Trimethicone 7%
Cyclopentasiloxane 3%
Neopentyl Glycol Diheptanoate 5.31%
Ethylhexyl Methoxycinnamate 6%
안료 Titanium Dioxide & Zinc Oxide & Iron Oxide 19%
Pearl Pigment (white) 1.5%
왁스 Polyethylene 3%
Ozokerite 2%
수상베이스 D.I water to 100
Polyol (Butylene glycol, Glycerine) 12%
Soduim Chloride 1%
< 실험예 1> - 내상에 대한 색상 구현 효과 확인
상기 실시예 1 및 비교예 1을 비교하여 내상에 색상이 구현된 효과를 확인할 수 있다.
도 1을 참조할 때, (a) 좌측은 상기 비교예 1에 따라 제조된 통상의 투명 내상을 가지는 제형이고, (b) 우측은 상기 실시예 1에 따라 제조된 내상에 색상이 구현된 제형이며, (b) 우측 도면으로부터 흰 색의 물방울 형태로 터져 나온 내상을 확인할 수 있다.
< 실험예 2> - 성분 조합에 따른 특이적 효과 확인
본 발명에서는 내상에 색상을 부여하기 위하여 수상에 펄 또는 수상 색소를 포함하지만 이에 따른 색상 구현 여부는 기타 함유된 성분 물질들의 조합에 따라 결정된다. 본 실험예 2에서는 처방 별 제형의 형태를 비교 관찰하여 이러한 사실 및 본 발명에 적합한 성분 조합을 함께 확인하였다.
도 2는 본 실험예 2의 관찰 결과 중 하나이다.
도 2를 참조하면, (a) 좌측은 상기 비교예 2에 따라 제조된 제형이고, (b) 우측은 상기 실시예 1에 따라 제조된 제형으로, (a) 및 (b) 제형은 모두 펄을 포함하고 있으나 우측 제형에서만 색상이 구현된 효과를 확인할 수 있다.
본 실험예 2를 통하여 본 발명의 실시를 위한 핵심은 유화제, 분산제, 점증제 및 방부제 등의 최적 조합에 있음을 확인할 수 있다.
< 실험예 3> - 분산제의 첨가 효과 확인
투명 내상의 제형과 비교하여 본 발명에서는 분산제의 첨가가 필수적이다.
본 실험예 3에서는 상기 분산제 첨가의 효과를 확인하였다.
도 3은 상기 실시예 1의 처방 중 분산제만을 생략하여 제조한 제형에 관한 것으로서, 공정 중 재가온 단계에서 제형의 분리가 일어난 상태를 보여준다.
< 실험예 4> - 오일 조합에 따른 표면 충진도 확인
본 실험예 4에서는 유상 성분 중 오일의 조합 및 조성물의 표면 충진도 간의 상관관계와 바람직한 표면 충진도를 가지도록 하는 오일의 적정 조합을 확인하였다.
도 4를 참조하면, 표면 충진도는 유상을 구성하는 오일 성분으로 실리콘 오일 및 에스테르 오일을 포함하되, 상기 두 오일의 배합 중량비를 조절함으로써 달리할 수 있음을 확인할 수 있다. 도 4의 (a) 좌측이 실리콘 오일 13%, 에스테르 오일 1.5%, (b) 중간이 실리콘 오일 13%, 에스테르 오일 2.56%, (c) 우측이 실리콘 오일 8%, 에스테르 오일 5.56% 일 때의 표면 충진도를 나타내며, 실리콘 오일 대비 에스테르 오일의 비율이 높아질수록, 즉 우측 제형으로 갈수록, 표면 충진도가 우수해짐을 알 수 있다.
한편, 표면 충진도는 고온에서 화장료 조성물의 유동도에 따라 결정된다. 또한 상기 고온 유동도는 조성물의 입자가 클수록 증가한다.
이와 관련하여 상기한 실리콘 오일 및 에스테르 오일의 조합이 조성물의 고온 유동도에 영향을 주는지 확인하기 위한 실험을 더 수행하였다.
도 5는 실리콘 오일 또는 에스테르 오일을 포함한 에멀전의 입자 크기를 현미경(Eclipse 80i, 니콘 인스트루먼트 코리아, X 100)으로 관찰한 결과이다. 도 5의 (a) 좌측은 일반 제형, (b) 중간은 실리콘 오일만 포함한 제형, (c) 우측은 에스테르 오일만 포함한 제형이다. 상기 일반 제형이라 함은 실리콘 오일 대비 에스테르 오일을 1:1로 포함하는 제형을 말한다.
상기 관찰 결과를 참조하면, 일반 제형 대비 실리콘 오일만 포함한 제형은 입자의 크기에 큰 차이가 없으나, 에스테르 오일만 포함한 제형은 입자의 크기가 매우 크게 형성됨을 확인할 수 있다. 즉, 에스테르 오일의 함유 비율이 높을수록 조성물의 입자의 크기가 커지고, 이에 따라 고온 유동도가 향상되며, 최종적으로는 표면의 충진도가 향상됨을 알 수 있다.
< 실험예 5> - 펄 입자의 평균 입도에 따른 특징 확인
본 실험예 5에서는 펄 입자의 입도가 제형 안정도 및 색감에 미치는 영향에 대해 알아보기 위하여 평균 입도가 상이한 펄 입자를 각각 포함하는 조성물의 특징을 하기 표 4에 나타내었다.
평균 입도 5um 8um 16um 20um
특징 제형 분리됨 색상 있음 제형 분리됨 색상 없음
상기 표 4에 나타난 바와 같이, 펄 입자의 평균 입도가 5um 및 16um에서는 제형 안정도가 떨어짐을 확인할 수 있으며, 20um에서는 색상이 나타나지 않았다. 따라서 펄 입자의 평균 입도는 6~15um가 적절함을 알 수 있다.

Claims (13)

  1. 내상에 색상을 나타내는 안료 또는 염료 중 어느 하나 이상을 포함하고, 제품의 사용 시 내상의 색상을 나타내는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  2. 제1항에 있어서,
    상기 화장료 조성물은 피이지-10디메치콘, 라우릴폴리글리세릴-3폴리디메칠실록시에칠디메치콘, 라우릴피이지-9폴리디메칠실록시에칠디메치콘, 폴리글리세릴-3폴리디메칠실록시에칠디메치콘, 카프릴릴 메치콘, 피이지-12 디메치콘/PPG-20 크로스폴리머, 디메치콘/피이지-10/15 크로스폴리머, 디메치콘/폴리글리세린-3 크로스폴리머, 세틸 피이지.피피지-10/1디메치콘, 세틸 디메치콘 코폴리올 및 디메치콘/비닐디메치콘 크로스폴리머로 이루어진 군 중에 선택되는 2종 이상의 유화제를 포함하는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  3. 제1항 또는 제2항에 있어서,
    상기 화장료 조성물은 폴리하이드록시 스테아릭산, 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머 및 비닐피롤리돈/헥사데센 코폴리머로 이루어진 군 중에 선택되는 2종 이상의 분산제를 포함하는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  4. 제3항에 있어서,
    상기 화장료 조성물의 유상 성분은 실리콘 오일 및 에스테르 오일을 포함하는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  5. 제4항에 있어서,
    상기 실리콘 오일 대비 에스테르 오일의 중량비는 1:0.2 이상인 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  6. 제1항에 있어서,
    상기 색상을 나타내는 안료는 펄 입자 및 수상 분산 피그먼트 중 어느 하나 이상인 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  7. 제6항에 있어서,
    상기 펄 입자는 마이카, 합성 마이카, 알루미나, 보로실리케이트, 보론나이트라이드 분말, 탈크 및 세리사이트로 구성되는 군 중에 선택되는 1종 이상의 판상 분체인 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  8. 제6항에 있어서,
    상기 펄 입자는 티타늄 다이옥사이드, 틴옥사이드 및 아이언 옥사이드로 구성되는 군 중에 선택되는 1종 이상의 물질로 코팅된 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  9. 제6항에 있어서,
    상기 펄 입자의 평균 입도는 6~15um인 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  10. 제6항에 있어서,
    상기 수상 분산 피그먼트는 티타늄 다이옥사이드를 알루미나 또는 실리카로 코팅한 것임을 특징으로 하는 고내상 유중수형 화장료 조성물.
  11. 제1항에 있어서,
    상기 화장료 조성물은 필름 포머를 포함하는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  12. 제11항에 있어서,
    상기 필름 포머는 하이드로제네이티드 폴리사이클로페타디엔을 포함하는 것을 특징으로 하는 고내상 유중수형 화장료 조성물.
  13. 고내상 유중수형 화장료 조성물에 있어서,
    유상 성분으로 실리콘 오일 및 에스테르 오일을 조성물의 총 중량 대비 각 3~7중량% 포함하고, 유화제로 디메치콘/피이지-10/15 크로스폴리머, 디메치콘/폴리글리세린-3 크로스폴리머 및 세틸 피이지.피피지-10/1디메치콘을 조성물의 총 중량 대비 각 0.1~3중량% 포함하고, 분산제로 폴리하이드록시 스테아릭 애씨드 및 아크릴레이트/에틸헥실 아크릴레이트/디메치콘 메타크릴레이트 코폴리머를 조성물의 총 중량 대비 각 1~3중량% 포함하고, 수상 성분으로 색상을 나타내는 안료 및 염료 중 어느 하나 이상을 조성물의 총 중량 대비 1~2중량% 포함하고, 점증제로 하이드록시에틸 아크릴레이트/소듐 아크릴로일 디메틸 타우레이트 코폴리머를 조성물의 총 중량 대비 0.01~0.5중량% 포함하고, 필름 포머로 하이드로제네이티드 폴리사이클로페타디엔을 조성물의 총 중량 대비 0.1~5중량%로 포함하는 것을 특징으로 하는 고내상 화장료 조성물.
PCT/KR2016/009754 2015-09-02 2016-09-01 고내상 유중수형 화장료 조성물 WO2017039338A1 (ko)