WO2016167289A1 - Composition de caoutchouc et pneumatique - Google Patents

Composition de caoutchouc et pneumatique Download PDF

Info

Publication number
WO2016167289A1
WO2016167289A1 PCT/JP2016/061919 JP2016061919W WO2016167289A1 WO 2016167289 A1 WO2016167289 A1 WO 2016167289A1 JP 2016061919 W JP2016061919 W JP 2016061919W WO 2016167289 A1 WO2016167289 A1 WO 2016167289A1
Authority
WO
WIPO (PCT)
Prior art keywords
rubber
silica
group
mass
parts
Prior art date
Application number
PCT/JP2016/061919
Other languages
English (en)
Japanese (ja)
Inventor
加藤　学
亮太 高橋
隆裕 岡松
美昭 桐野
Original Assignee
横浜ゴム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 横浜ゴム株式会社 filed Critical 横浜ゴム株式会社
Priority to JP2016553028A priority Critical patent/JPWO2016167289A1/ja
Publication of WO2016167289A1 publication Critical patent/WO2016167289A1/fr

Abstract

La présente invention concerne une composition de caoutchouc présentant une très faible génération de chaleur et une excellente résistance à l'usure. La présente invention concerne une composition de caoutchouc destinée à une bande de roulement de pneumatique et qui contient : un constituant de caoutchouc comprenant au moins un caoutchouc diène modifié où de 0,02 à 4 % en mole de double liaison totale d'un caoutchouc diène matériau source possède un groupe carboxy modifié ; une silice 1 qui présente une surface spécifique d'adsorption d'azote de 155 m2/g ou supérieure ; une silice 2 qui présente une surface spécifique d'adsorption d'azote de 125 m2/g ou inférieure ; et un agent de couplage au silane. La teneur en caoutchouc diène modifié est de 10 à 100 parties en masse pour 100 parties en masse du constituant de caoutchouc, la teneur totale de la silice 1 et de la silice 2 est de 55 à 200 parties en masse pour 100 parties en masse du constituant de caoutchouc, et la teneur de l'agent de couplage au silane est de 2 à 16 % en masse de ladite teneur totale. La présente invention concerne également un pneumatique présentant une bande de roulement de pneumatique qui utilise la composition de caoutchouc.
PCT/JP2016/061919 2015-04-14 2016-04-13 Composition de caoutchouc et pneumatique WO2016167289A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016553028A JPWO2016167289A1 (ja) 2015-04-14 2016-04-13 ゴム組成物及びタイヤ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015082443 2015-04-14
JP2015-082443 2015-04-14

Publications (1)

Publication Number Publication Date
WO2016167289A1 true WO2016167289A1 (fr) 2016-10-20

Family

ID=57126645

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/061919 WO2016167289A1 (fr) 2015-04-14 2016-04-13 Composition de caoutchouc et pneumatique

Country Status (2)

Country Link
JP (1) JPWO2016167289A1 (fr)
WO (1) WO2016167289A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018095701A (ja) * 2016-12-09 2018-06-21 住友ゴム工業株式会社 ゴム組成物及び空気入りタイヤ

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013036025A (ja) * 2011-07-14 2013-02-21 Yokohama Rubber Co Ltd:The タイヤ用ゴム組成物
WO2013157545A1 (fr) * 2012-04-16 2013-10-24 横浜ゴム株式会社 Composition de caoutchouc pour pneu et pneumatique
JP2013227375A (ja) * 2012-04-24 2013-11-07 Yokohama Rubber Co Ltd:The タイヤ用ゴム組成物
JP5700161B1 (ja) * 2014-05-16 2015-04-15 横浜ゴム株式会社 タイヤビードインシュレーション用ゴム組成物および空気入りタイヤ
JP5716850B1 (ja) * 2014-01-31 2015-05-13 横浜ゴム株式会社 変性ポリマー、これを用いるゴム組成物及びタイヤ

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013036025A (ja) * 2011-07-14 2013-02-21 Yokohama Rubber Co Ltd:The タイヤ用ゴム組成物
WO2013157545A1 (fr) * 2012-04-16 2013-10-24 横浜ゴム株式会社 Composition de caoutchouc pour pneu et pneumatique
JP2013227375A (ja) * 2012-04-24 2013-11-07 Yokohama Rubber Co Ltd:The タイヤ用ゴム組成物
JP5716850B1 (ja) * 2014-01-31 2015-05-13 横浜ゴム株式会社 変性ポリマー、これを用いるゴム組成物及びタイヤ
JP5700161B1 (ja) * 2014-05-16 2015-04-15 横浜ゴム株式会社 タイヤビードインシュレーション用ゴム組成物および空気入りタイヤ

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018095701A (ja) * 2016-12-09 2018-06-21 住友ゴム工業株式会社 ゴム組成物及び空気入りタイヤ

Also Published As

Publication number Publication date
JPWO2016167289A1 (ja) 2018-02-08

Similar Documents

Publication Publication Date Title
KR101644555B1 (ko) 타이어 트레드용 고무 조성물 및 공기입 타이어
JP2016037556A (ja) ゴム組成物および空気入りタイヤ
WO2015114998A1 (fr) Composition de caoutchouc et bandage pneumatique
WO2016167282A1 (fr) Composition de caoutchouc et pneu
JP5761442B1 (ja) 変性ポリマーおよびゴム組成物並びに空気入りタイヤ
WO2015114996A1 (fr) Composition de caoutchouc et pneu
US9803031B2 (en) Modified polymer, rubber composition and pneumatic tire
JP6024781B2 (ja) タイヤトレッド用ゴム組成物および空気入りタイヤ
JP6481693B2 (ja) ゴム組成物及びタイヤ
JP5812154B1 (ja) アンダートレッド用ゴム組成物および空気入りタイヤ
JP5716850B1 (ja) 変性ポリマー、これを用いるゴム組成物及びタイヤ
JP6686314B2 (ja) タイヤ用ゴム組成物
WO2016167289A1 (fr) Composition de caoutchouc et pneumatique
JP5761443B1 (ja) ゴム組成物及び空気入りタイヤ
JP5949987B1 (ja) タイヤトレッド用ゴム組成物および空気入りタイヤ
JP6112161B2 (ja) 変性ポリマーの製造方法、変性ポリマー、ゴム組成物および空気入りタイヤ
JP5812155B1 (ja) タイヤリムクッションまたはガムフィニッシング用ゴム組成物および空気入りタイヤ
JP5962809B1 (ja) タイヤトレッド用ゴム組成物およびそれを用いた空気入りタイヤ
WO2016148198A1 (fr) Composé, polymère modifié, composition de caoutchouc, pneu et bande transporteuse
WO2015173994A1 (fr) Composition de caoutchouc pour bourrage sur tringle, et pneumatique
JP5812157B1 (ja) タイヤリムクッションまたはガムフィニッシング用ゴム組成物および空気入りタイヤ
WO2015173989A1 (fr) Composition de caoutchouc pour coussin de jante de pneumatique ou finition de caoutchouc, et pneumatique
WO2016076269A1 (fr) Composition d'agent de modification de polymère, polymère modifié, composition de caoutchouc et pneu

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2016553028

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16780080

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16780080

Country of ref document: EP

Kind code of ref document: A1