WO2016098208A1 - Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau - Google Patents

Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau Download PDF

Info

Publication number
WO2016098208A1
WO2016098208A1 PCT/JP2014/083474 JP2014083474W WO2016098208A1 WO 2016098208 A1 WO2016098208 A1 WO 2016098208A1 JP 2014083474 W JP2014083474 W JP 2014083474W WO 2016098208 A1 WO2016098208 A1 WO 2016098208A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
active material
electrode active
silicon
containing alloy
Prior art date
Application number
PCT/JP2014/083474
Other languages
English (en)
Japanese (ja)
Inventor
智裕 蕪木
千葉　啓貴
渡邉　学
文博 三木
Original Assignee
日産自動車株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産自動車株式会社 filed Critical 日産自動車株式会社
Priority to PCT/JP2014/083474 priority Critical patent/WO2016098208A1/fr
Publication of WO2016098208A1 publication Critical patent/WO2016098208A1/fr

Abstract

[Problème] Obtenir un moyen permettant d'améliorer la durabilité de cycle d'un dispositif électrique tel qu'un accumulateur au lithium-ion. [Solution] Un matériau actif d'électrode négative comprenant un alliage contenant du silicium et ayant une teneur en oxygène de 0,5 à 20 % en masse est utilisé comme matériau actif d'électrode négative pour un dispositif électrique.
PCT/JP2014/083474 2014-12-17 2014-12-17 Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau WO2016098208A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP2014/083474 WO2016098208A1 (fr) 2014-12-17 2014-12-17 Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2014/083474 WO2016098208A1 (fr) 2014-12-17 2014-12-17 Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau

Publications (1)

Publication Number Publication Date
WO2016098208A1 true WO2016098208A1 (fr) 2016-06-23

Family

ID=56126131

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/083474 WO2016098208A1 (fr) 2014-12-17 2014-12-17 Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau

Country Status (1)

Country Link
WO (1) WO2016098208A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2017216939A1 (ja) * 2016-06-16 2019-05-23 日産自動車株式会社 電気デバイス用負極活物質、およびこれを用いた電気デバイス

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004105152A2 (fr) * 2003-05-22 2004-12-02 Matsushita Electric Industrial Co., Ltd. Accumulateur a electrolyte non aqueux et procede de production
JP2011249302A (ja) * 2010-04-28 2011-12-08 Hitachi Chem Co Ltd 複合粒子、複合粒子の製造方法、リチウムイオン二次電池用負極及びリチウムイオン二次電池
WO2012063762A1 (fr) * 2010-11-08 2012-05-18 古河電気工業株式会社 Nanoparticules utilisées dans une électrode négative pour batterie secondaire au lithium-ion et procédé de fabrication s'y rapportant
WO2013099441A1 (fr) * 2011-12-27 2013-07-04 日産自動車株式会社 Matière active d'électrode négative destinée à un dispositif électrique

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004105152A2 (fr) * 2003-05-22 2004-12-02 Matsushita Electric Industrial Co., Ltd. Accumulateur a electrolyte non aqueux et procede de production
JP2011249302A (ja) * 2010-04-28 2011-12-08 Hitachi Chem Co Ltd 複合粒子、複合粒子の製造方法、リチウムイオン二次電池用負極及びリチウムイオン二次電池
WO2012063762A1 (fr) * 2010-11-08 2012-05-18 古河電気工業株式会社 Nanoparticules utilisées dans une électrode négative pour batterie secondaire au lithium-ion et procédé de fabrication s'y rapportant
WO2013099441A1 (fr) * 2011-12-27 2013-07-04 日産自動車株式会社 Matière active d'électrode négative destinée à un dispositif électrique

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2017216939A1 (ja) * 2016-06-16 2019-05-23 日産自動車株式会社 電気デバイス用負極活物質、およびこれを用いた電気デバイス

Similar Documents

Publication Publication Date Title
JP6098719B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6493414B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6327362B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
WO2017081758A1 (fr) Matériau actif d'électrode négative pour dispositif électrique, et dispositif électrique utilisant ledit matériau
JP6112200B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6561461B2 (ja) 電気デバイス用負極、およびこれを用いた電気デバイス
JP6459479B2 (ja) 電気デバイス用負極、およびこれを用いた電気デバイス
JP6488690B2 (ja) 電気デバイス用負極、およびこれを用いた電気デバイス
WO2016098209A1 (fr) Matière active d'électrode négative pour dispositif électrique et dispositif électrique l'utilisant
JP6488689B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6485028B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6112199B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
WO2017216939A1 (fr) Substance active d'électrode négative pour dispositif électrique, et dispositif électrique utilisant celle-ci
JP6083471B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
WO2016098213A1 (fr) Matériau actif d'électrode négative pour un dispositif électrique et dispositif électrique utilisant ce dernier
JP6292317B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JP6736999B2 (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
WO2016098208A1 (fr) Matériau actif d'électrode négative destiné à être utilisé dans un dispositif électrique et dispositif électrique utilisant ledit matériau
JP6555278B2 (ja) リチウムイオン二次電池用負極活物質、およびこれを用いたリチウムイオン二次電池
JP2017224539A (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス
JPWO2019049239A1 (ja) 電気デバイス用負極活物質とその製造方法、およびこの活物質を用いた電気デバイス
JP2016115630A (ja) 電気デバイス用負極活物質、およびこれを用いた電気デバイス

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14908418

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14908418

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP