WO2016028229A1 - Appareil de formage d'article métallique et procédés pour le formage d'un article métallique - Google Patents

Appareil de formage d'article métallique et procédés pour le formage d'un article métallique Download PDF

Info

Publication number
WO2016028229A1
WO2016028229A1 PCT/SG2015/050266 SG2015050266W WO2016028229A1 WO 2016028229 A1 WO2016028229 A1 WO 2016028229A1 SG 2015050266 W SG2015050266 W SG 2015050266W WO 2016028229 A1 WO2016028229 A1 WO 2016028229A1
Authority
WO
WIPO (PCT)
Prior art keywords
die
cavity
punch
forming
reservoir
Prior art date
Application number
PCT/SG2015/050266
Other languages
English (en)
Inventor
Beng Wah Chua
Meng Kwong Ho
Original Assignee
Agency For Science, Technology And Research
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Agency For Science, Technology And Research filed Critical Agency For Science, Technology And Research
Priority to CN201580056814.XA priority Critical patent/CN107405682A/zh
Publication of WO2016028229A1 publication Critical patent/WO2016028229A1/fr

Abstract

L'invention porte, selon divers modes de réalisation, sur un appareil de formage d'article métallique, l'appareil pouvant comprendre : une matrice comprenant une cavité de réservoir en creux dans une première partie d'une surface de la matrice et une cavité de formage en creux dans une seconde partie de la surface de la matrice adjacente à la première partie ; et un poinçon comprenant une saillie sur une surface du poinçon en regard de la surface de la matrice, le poinçon étant conçu pour se déplacer par rapport à la matrice pour déplacer la surface du poinçon par rapport à la surface de la matrice pour introduire la saillie du poinçon dans la cavité de réservoir de la matrice.
PCT/SG2015/050266 2014-08-20 2015-08-19 Appareil de formage d'article métallique et procédés pour le formage d'un article métallique WO2016028229A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN201580056814.XA CN107405682A (zh) 2014-08-20 2015-08-19 金属物品形成设备和用于形成金属物品的方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SG10201405077W 2014-08-20
SG10201405077W 2014-08-20

Publications (1)

Publication Number Publication Date
WO2016028229A1 true WO2016028229A1 (fr) 2016-02-25

Family

ID=55351047

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SG2015/050266 WO2016028229A1 (fr) 2014-08-20 2015-08-19 Appareil de formage d'article métallique et procédés pour le formage d'un article métallique

Country Status (2)

Country Link
CN (1) CN107405682A (fr)
WO (1) WO2016028229A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018103789A1 (fr) * 2016-12-05 2018-06-14 Schuler Pressen Gmbh Dispositif de coulée, presse et procédé de coulée d'une pièce et pièce

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114346210A (zh) * 2022-01-11 2022-04-15 松山湖材料实验室 铸造模具、铸造装置及铸造方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2500556A (en) * 1946-04-24 1950-03-14 Budds Aero Castings Inc Method of casting
US6267170B1 (en) * 1998-06-11 2001-07-31 Sumitomo Rubber Industries, Ltd. Manufacturing apparatus and method for amorphous alloy
JP2001259821A (ja) * 2000-03-24 2001-09-25 Akihisa Inoue 非晶質合金成型品の製造装置、製造用金型及び製法

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2582037B2 (ja) * 1993-11-29 1997-02-19 本田技研工業株式会社 鋳造方法
JP2002086258A (ja) * 2000-09-12 2002-03-26 Sumitomo Rubber Ind Ltd 非晶質合金の製造方法及び非晶質合金製造装置
JP2003126955A (ja) * 2001-10-23 2003-05-08 Ube Machinery Corporation Ltd 半凝固金属製品の成形方法と成形金型
JP4883403B2 (ja) * 2006-11-28 2012-02-22 新東工業株式会社 鋳物製品の鋳造方法
JP4378734B2 (ja) * 2007-12-05 2009-12-09 合志技研工業株式会社 半凝固金属製品の成形金型構造および半凝固金属製品の成形方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2500556A (en) * 1946-04-24 1950-03-14 Budds Aero Castings Inc Method of casting
US6267170B1 (en) * 1998-06-11 2001-07-31 Sumitomo Rubber Industries, Ltd. Manufacturing apparatus and method for amorphous alloy
JP2001259821A (ja) * 2000-03-24 2001-09-25 Akihisa Inoue 非晶質合金成型品の製造装置、製造用金型及び製法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018103789A1 (fr) * 2016-12-05 2018-06-14 Schuler Pressen Gmbh Dispositif de coulée, presse et procédé de coulée d'une pièce et pièce

Also Published As

Publication number Publication date
CN107405682A (zh) 2017-11-28

Similar Documents

Publication Publication Date Title
US8327914B2 (en) Feeding system for semi-solid metal injection
CN101274361B (zh) 低速真空压挤铸造工艺
US6123142A (en) Method of molding articles to minimize shrinkage and voids
CN104139169B (zh) 铸锻方法及铸锻装置
JP2017154175A (ja) 鋳造装置、及び鋳造方法
CN105705271A (zh) 生产高性能轴对称部件的方法和设备
TWI613018B (zh) 用以形成液態鍛造物品之方法與裝置
JP5339764B2 (ja) 鋳造方法
CN104493110A (zh) 一种金属层状复合锭的铸造装置及方法
CN106623856B (zh) 一种提高挤压铸造活塞铸件质量的方法和装置
WO2016028229A1 (fr) Appareil de formage d'article métallique et procédés pour le formage d'un article métallique
US20150052963A1 (en) Method and apparatus for forging
CN102717049A (zh) 一种闭模浇注直接挤压铸造的方法及其装置
KR102359579B1 (ko) 용탕 직접가압식 박육부품 주조 장치 및 방법
CN211661053U (zh) 一种铝合金压铸模具
CN114130989A (zh) 一种挤压铸造模具及工艺方法
KR20170002592U (ko) 히트싱크 불량저감을 위한 복수 런너 다이캐스팅 금형
KR20040100916A (ko) 3개의 챔버들을 이용한 수직 주입 기계
CN112658226B (zh) 一种不等厚深腔壳型铝合金构件挤压铸造装置及其使用方法
Murray et al. High pressure die casting of aluminium and its alloys
JP2004122146A (ja) 厚肉製品の高圧鋳造法
CN114160770A (zh) 一种间接挤压铸造冲头装置及挤压铸造方法
CN104815974B (zh) 一种液态金属模锻成型装置及其使用方法
JP2004202539A (ja) 金属鋳造品の穴加工法
WO1980001657A1 (fr) Procede de coulee sous pression

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15832997

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15832997

Country of ref document: EP

Kind code of ref document: A1