WO2015167588A1 - Procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés - Google Patents

Procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés Download PDF

Info

Publication number
WO2015167588A1
WO2015167588A1 PCT/US2014/042449 US2014042449W WO2015167588A1 WO 2015167588 A1 WO2015167588 A1 WO 2015167588A1 US 2014042449 W US2014042449 W US 2014042449W WO 2015167588 A1 WO2015167588 A1 WO 2015167588A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
hydroforming
aluminum tube
bending
rack
Prior art date
Application number
PCT/US2014/042449
Other languages
English (en)
Inventor
S. George LUCKEY
David John Hill
Peter A. Friedman
Christopher John May
Stephen Kernosky
Andrey M. Ilinich
Original Assignee
Ford Global Technologies, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US14/266,065 external-priority patent/US20150315666A1/en
Priority claimed from US14/266,903 external-priority patent/US9709333B2/en
Priority claimed from US14/279,808 external-priority patent/US9925577B2/en
Priority claimed from US14/300,378 external-priority patent/US9545657B2/en
Application filed by Ford Global Technologies, Llc filed Critical Ford Global Technologies, Llc
Priority to GB1618102.6A priority Critical patent/GB2540306B/en
Priority to CN201480078630.9A priority patent/CN106794503B/zh
Priority to DE112014006624.9T priority patent/DE112014006624B4/de
Priority to RU2016145425A priority patent/RU2685318C2/ru
Priority to US14/428,051 priority patent/US10086422B2/en
Publication of WO2015167588A1 publication Critical patent/WO2015167588A1/fr

Abstract

La présente invention concerne un processus ou un procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés qui comprend les étapes consistant à extruder un tube en aluminium et transformer le tube d'aluminium extrudé en rail de véhicule par hydroformage. Plus spécifiquement, le procédé consiste à extruder le tube d'aluminium, cintrer le tube d'aluminium, préformer le tube d'aluminium, hydroformer le tube d'aluminium en rail de véhicule, couper le rail du véhicule à la longueur souhaitée puis vieillir artificiellement le rail et le soumettre à un prétraitement chimique discontinu. Dans un autre mode de réalisation, le vieillissement artificiel et les procédés de prétraitement chimique discontinus sont exécutés dans l'ordre inverse. Dans l'un comme l'autre des modes de réalisation, un recuit par induction localisé destiné à restaurer l'aptitude au formage peut être effectué entre le cintrage et le préformage, entre le préformage et l'hydroformage, ou les deux.
PCT/US2014/042449 2014-04-30 2014-06-16 Procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés WO2015167588A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
GB1618102.6A GB2540306B (en) 2014-04-30 2014-06-16 Value stream process for forming vehicle rails from extruded aluminum tubes
CN201480078630.9A CN106794503B (zh) 2014-04-30 2014-06-16 用于由挤出铝管形成车辆纵梁的价值流过程
DE112014006624.9T DE112014006624B4 (de) 2014-04-30 2014-06-16 Verfahren für das formen eines fahrzeuglängsträgers aus aluminium
RU2016145425A RU2685318C2 (ru) 2014-04-30 2014-06-16 Способ формования балки транспортного средства
US14/428,051 US10086422B2 (en) 2014-04-30 2014-06-16 Value stream process for forming vehicle rails from extruded aluminum tubes

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
US14/266,065 US20150315666A1 (en) 2014-04-30 2014-04-30 Induction annealing as a method for expanded hydroformed tube formability
US14/266,065 2014-04-30
US14/266,903 2014-05-01
US14/266,903 US9709333B2 (en) 2014-05-01 2014-05-01 Multipurpose rack for processing parts through multiple manufacturing processes
US14/279,808 2014-05-16
US14/279,808 US9925577B2 (en) 2014-05-16 2014-05-16 Rotary-draw bending mandrel with galling-resistive inserts
US14/300,378 US9545657B2 (en) 2014-06-10 2014-06-10 Method of hydroforming an extruded aluminum tube with a flat nose corner radius
US14/300,378 2014-06-10

Publications (1)

Publication Number Publication Date
WO2015167588A1 true WO2015167588A1 (fr) 2015-11-05

Family

ID=54359116

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/042449 WO2015167588A1 (fr) 2014-04-30 2014-06-16 Procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés

Country Status (5)

Country Link
CN (1) CN106794503B (fr)
DE (1) DE112014006624B4 (fr)
GB (1) GB2540306B (fr)
RU (1) RU2685318C2 (fr)
WO (1) WO2015167588A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20180230583A1 (en) * 2017-02-15 2018-08-16 S. George Luckey, Jr. Heat treatment and tube forming process for high strength aluminum tube body structure reinforcements

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109823405A (zh) * 2019-01-31 2019-05-31 重庆长安汽车股份有限公司 一种车身顶边梁的制造方法、车身顶边梁及汽车
CN114653806B (zh) * 2022-03-01 2023-12-22 哈尔滨工业大学（威海） 一种用于高强钢变径管状件的预成型方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020046505A1 (en) * 2000-07-25 2002-04-25 Seksaria Dinesh C. Ultra-lightweight thin sliding door for a vehicle
US20020125739A1 (en) * 2000-09-29 2002-09-12 L&L Products, Inc. Hydroform structural reinforcement system
US20110241385A1 (en) * 2010-03-30 2011-10-06 Ford Global Technologies Llc Vehicle Frame with Direction-Specific Deformation

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4766664A (en) * 1987-02-17 1988-08-30 Alumax Extrusions, Inc. Process for formation of high strength aluminum ladder structures
US5070717A (en) * 1991-01-22 1991-12-10 General Motors Corporation Method of forming a tubular member with flange
US5557961A (en) * 1995-11-13 1996-09-24 General Motors Corporation Hydroformed structural member with varied wall thickness
US6241310B1 (en) * 2000-05-17 2001-06-05 Asc Incorporated Vehicle structure with integral node
DE10312028B4 (de) * 2003-03-18 2005-07-28 Tower Automotive Hydroforming Gmbh & Co. Kg Verfahren zur Herstellung von Bauteilen
KR100552614B1 (ko) * 2003-07-22 2006-02-15 주식회사 성우하이텍 차체 멤버 제조 방법
KR100604634B1 (ko) * 2004-08-09 2006-07-28 주식회사 성우하이텍 차체 멤버 제조 방법
CN1824411A (zh) * 2005-08-08 2006-08-30 孙旭光 内加热金属管材高—中温超高水压一次成形技术、方法与设备
DE102005049050B4 (de) * 2005-10-13 2010-12-23 Saf-Holland Gmbh Verfahren zum Herstellen eines Achsenbauteils
JP5038819B2 (ja) * 2007-08-22 2012-10-03 有限会社東和工業 フレアー付き管体の曲げ加工方法
SE533223C2 (sv) * 2008-10-08 2010-07-27 Sapa Heat Transfer Ab Metod för formning av header-tank tillverkad i aluminium

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020046505A1 (en) * 2000-07-25 2002-04-25 Seksaria Dinesh C. Ultra-lightweight thin sliding door for a vehicle
US20020125739A1 (en) * 2000-09-29 2002-09-12 L&L Products, Inc. Hydroform structural reinforcement system
US20110241385A1 (en) * 2010-03-30 2011-10-06 Ford Global Technologies Llc Vehicle Frame with Direction-Specific Deformation

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20180230583A1 (en) * 2017-02-15 2018-08-16 S. George Luckey, Jr. Heat treatment and tube forming process for high strength aluminum tube body structure reinforcements
US10570489B2 (en) 2017-02-15 2020-02-25 Ford Global Technologies, Llc Heat treatment and tube forming process for high strength aluminum tube body structure reinforcements

Also Published As

Publication number Publication date
RU2016145425A3 (fr) 2018-05-30
RU2685318C2 (ru) 2019-04-17
RU2016145425A (ru) 2018-05-30
DE112014006624T5 (de) 2017-02-09
CN106794503A (zh) 2017-05-31
GB2540306A (en) 2017-01-11
GB201618102D0 (en) 2016-12-07
DE112014006624B4 (de) 2022-02-10
GB2540306B (en) 2020-07-15
CN106794503B (zh) 2019-07-19

Similar Documents

Publication Publication Date Title
US10086422B2 (en) Value stream process for forming vehicle rails from extruded aluminum tubes
AU2008249760B2 (en) Method for manufacturing tanks
WO2015167588A1 (fr) Procédé de chaîne de valeur pour former des rails de véhicule à partir de tubes en aluminium extrudés
CN105960294B (zh) 加工硬化合金板材的温成形
WO2014173703A1 (fr) Dispositif de trempe sous presse d'éléments structuraux
DE102012210976A1 (de) Heißprägeform und Herstellungsverfahren derselben
WO2006084321A1 (fr) Procede et appareil pour former une armature en metal
CN112008333A (zh) 用于形成车身构件的方法
EP2543453B1 (fr) Installation pour fabriquer un boulon en alliage de titane et procédé de fabrication d'un boulon en alliage de titane l'utilisant
WO2020011301A1 (fr) Procédé et dispositif de thermoformage de produits semi-finis métalliques
EP2176012B1 (fr) Procédé et système pour refouler des éléments creux
US20220371071A1 (en) Value stream process for roll forming and bobbin tool friction stir welding aluminum sheet to form vehicle structural rails
WO1991011541A1 (fr) Procede de galvanisation en ligne
US10040108B2 (en) Tubular structure support with variable dimensions and mechanical properties
EP3318647B1 (fr) Ligne de fabrication d'une pièce thermodurcie en forme de tôle
AU651960B2 (en) Inline galvanising process
US20240024940A1 (en) Roll forming system with heat treatment and associated methods
US11174542B2 (en) High volume manufacturing method for forming high strength aluminum parts
DE102018115052A1 (de) Verfahren zur Herstellung eines gebogenen, rohrförmigen Vorproduktes aus Metall für die Innenhochdruckumformung von Bauteilen und Werkzeug zur Herstellung eines solchen Vorproduktes
DE102008015169A1 (de) Verschlusselement für eine Platte eines Transportelements für einen Vorformling, Verfahren und Verwendung

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 14428051

Country of ref document: US

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14890467

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 201618102

Country of ref document: GB

Kind code of ref document: A

Free format text: PCT FILING DATE = 20140616

WWE Wipo information: entry into national phase

Ref document number: 1618102.6

Country of ref document: GB

WWE Wipo information: entry into national phase

Ref document number: 112014006624

Country of ref document: DE

ENP Entry into the national phase

Ref document number: 2016145425

Country of ref document: RU

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 14890467

Country of ref document: EP

Kind code of ref document: A1