Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
  • C09D7/40—Additives
  • C09D7/47—Levelling agents
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J3/00—Processes of treating or compounding macromolecular substances
  • C08J3/12—Powdering or granulating
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
  • B29B9/00—Making granules
  • B29B9/12—Making granules characterised by structure or composition
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
  • B29B9/00—Making granules
  • B29B9/16—Auxiliary treatment of granules
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C64/00—Additive manufacturing, i.e. manufacturing of three-dimensional [3D] objects by additive deposition, additive agglomeration or additive layering, e.g. by 3D printing, stereolithography or selective laser sintering
  • B29C64/10—Processes of additive manufacturing
  • B29C64/141—Processes of additive manufacturing using only solid materials
  • B29C64/153—Processes of additive manufacturing using only solid materials using layers of powder being selectively joined, e.g. by selective laser sintering or melting
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C67/00—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00
  • B29C67/24—Shaping techniques not covered by groups B29C39/00 - B29C65/00, B29C70/00 or B29C73/00 characterised by the choice of material
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B27/00—Layered products comprising a layer of synthetic resin
  • B32B27/30—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers
  • B32B27/302—Layered products comprising a layer of synthetic resin comprising vinyl (co)polymers; comprising acrylic (co)polymers comprising aromatic vinyl (co)polymers, e.g. styrenic (co)polymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B33—ADDITIVE MANUFACTURING TECHNOLOGY
  • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
  • B33Y10/00—Processes of additive manufacturing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B33—ADDITIVE MANUFACTURING TECHNOLOGY
  • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
  • B33Y70/00—Materials specially adapted for additive manufacturing
  • B33Y70/10—Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B33—ADDITIVE MANUFACTURING TECHNOLOGY
  • B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
  • B33Y80/00—Products made by additive manufacturing
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J3/00—Processes of treating or compounding macromolecular substances
  • C08J3/12—Powdering or granulating
  • C08J3/124—Treatment for improving the free-flowing characteristics
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/20—Oxides; Hydroxides
  • C08K3/22—Oxides; Hydroxides of metals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
  • C08K3/24—Acids; Salts thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/32—Phosphorus-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/34—Silicon-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/34—Silicon-containing compounds
  • C08K3/346—Clay
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L79/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen with or without oxygen or carbon only, not provided for in groups C08L61/00 - C08L77/00
  • C08L79/04—Polycondensates having nitrogen-containing heterocyclic rings in the main chain; Polyhydrazides; Polyamide acids or similar polyimide precursors
  • C08L79/08—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D179/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen, with or without oxygen, or carbon only, not provided for in groups C09D161/00 - C09D177/00
  • C09D179/04—Polycondensates having nitrogen-containing heterocyclic rings in the main chain; Polyhydrazides; Polyamide acids or similar polyimide precursors
  • C09D179/08—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
  • C09D5/03—Powdery paints
  • C09D5/031—Powdery paints characterised by particle size or shape
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
  • C09D7/40—Additives
  • C09D7/60—Additives non-macromolecular
  • C09D7/61—Additives non-macromolecular inorganic
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
  • B29B9/00—Making granules
  • B29B9/12—Making granules characterised by structure or composition
  • B29B2009/125—Micropellets, microgranules, microparticles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29B—PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS
  • B29B9/00—Making granules
  • B29B9/16—Auxiliary treatment of granules
  • B29B2009/168—Removing undesirable residual components, e.g. solvents, unreacted monomers; Degassing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
  • B29K2105/25—Solid
  • B29K2105/251—Particles, powder or granules
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2379/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen with or without oxygen, or carbon only, not provided for in groups C08J2361/00 - C08J2377/00
  • C08J2379/04—Polycondensates having nitrogen-containing heterocyclic rings in the main chain; Polyhydrazides; Polyamide acids or similar polyimide precursors
  • C08J2379/08—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/34—Silicon-containing compounds
  • C08K3/36—Silica

Definitions

• AM additive Manufacturing
• 3D three-dimensional
• CAD computer-aided design
• AM has many advantages, including dramatically reducing the time from design to prototyping to commercial product. Running design changes are possible. Multiple parts can be built in a single assembly. No tooling is required. Minimal energy is needed to make these 3D solid objects. It also decreases the amount waste and raw materials.
• AM also facilitates production of extremely complex geometrical parts. AM also reduces the parts inventory for a business since parts can be quickly made on-demand and on-site.
• Laser sintering is a process by which a three dimensional article may be formed in a layer- wise fashion by selectively projecting a laser beam having the desired energy onto a bed of resin particles. Prototype or production parts may be efficiently and economically produced by this process, which is often times referred to as selective laser sintering.
• This process has been described in U.S. Pat. Nos. 4,944,817; 5,516,697 and 5,382,308 to Bourell, et al.; 5,304,329 and 5,342,919 to Dickens, Jr. et al. and 5,385,780 to Lee.
• a high power laser is used to fuse polymer powders of the required material type together into the desired three-dimensional shape.
• SLS processes require a polymer powder of well-defined shape, size and composition in order to make high quality part.
• the preferred size of the particles is usually below 100 um (Ref: Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications July 1, 2004 vol. 218 no. 3 247-252) and a narrow distribution of particle sizes is also preferred to get optimum precision and density of the sintered part.
• the preparation of such powders from thermoplastic resins on an economic, large scale is not straightforward.
• thermoplastic powders used for powder bed fusion processes such as laser sintering are made by (cryogenic) milling and subsequent sieving.
• This method has the disadvantage that the distribution in particle size is relatively high and that it is difficult to control the exact size of the powder. Also, fines are generated that cannot be used in the SLS process. Finally, the shape of the powder particles is very irregular.
• thermoplastic polyetherimide powder that can be used in powder bed fusion processes.
• the present invention offers a solution to that problem.
• Some embodiments is directed to a method comprising: providing a powder composition including at least one ultrafine, spherical thermoplastic powder having a glass transition temperature (Tg) of at least 150 degrees C; and powder bed fusing the powder composition to form a three-dimensional article.
• Tg glass transition temperature
• Another embodiment is directed to a method comprising: providing a powder composition including at least one ultrafine, spherical thermoplastic powder having a glass transition temperature (Tg) of at least 150 degrees C wherein the thermoplastic powder is chosen from polyetherimides, polysulfones, and polyarylsulfones and combinations thereof; and powder bed fusing the powder composition to form a three-dimensional article.
• Tg glass transition temperature
• Still another embodiment is directed to a method comprising providing a powder composition including at least one ultrafine, high Tg, spherical polyetherimide powder; and powder bed fusing the powder composition to form a three-dimensional article.
• Another embodiment is directed to the method of manufacturing a three dimensional article may comprise the steps of: (1) depositing a quantity of a powder composition including at least one ultrafine, high Tg, spherical thermoplastic powder on a support surface; (2) leveling the composition to form a smooth layer on the support surface; (3) then directing an energy beam over a predetermined target area on the support surface causing the composition to form an integral layer; and (d) repeating steps (1) to (3) to form additional layers that are integrally bonded to adjacent layers to form a three-dimensional article, wherein the thermoplastic composition includes at least one ultrafine, high Tg, spherical thermoplastic powder.
• the energy beam may be a laser.
• Still another embodiment is directed to the use of powders made with the emulsion process as described in US Patent Application Serial No. 13/841802, filed on 15- 03-2013, (Assignee Docket No. 12PLAS0295-US-NP) in powder bed fusing processes.
• Still another embodiment is directed to three dimensional articles of manufacture made be the powder bed fusing processes as described herein
• Figure 1 is two microphotographs showing the particle size morphology of two different Selective Laser Sintering (SLS) powders.
• SLS Selective Laser Sintering
• Figure 2 is two microphotographs showing the difference build platform surfaces using the two different SLS powders shown in Figure 1.
• Figure 3 is a microphotograph showing a 3D laser sintered part manufactured with powder B shown in Figures 1 and 2
• the present process has several advantages.
• This method employs spherical particles of well-defined particle size in the range that is optimum for powder bed fusing processes such as laser sintering and with a narrow size distribution.
• the powder compositions that contain additives like stabilizers, colorants and flow agents, or even specific additives that can help in the laser sintering process (e.g. specific absorbers for laser wavelength, curable resin to post crosslink, and the like.).
• Another advantage of the good particle size control with this method is that it gives the advantage of mixing 2 or more powders with different particle sizes. This may lead to better layer formation due to improved particle stacking, similar to the use of latexes with different particle sizes in waterborne emulsion paints.
• thermoplastic powder having a glass transition temperature (Tg) of at least 150 degrees C includes at least one thermoplastic polymer powder that have a glass transition temperature of at least 150 degrees C.
• these powders can include polyetherimides, polysulfones, and polyarylsulfones and combinations thereof. Suitable polyarylsulfones include polyphenylsulfones. Specific embodiments include ULTEM polyetherimide polymers (including such grades such as 1000 and 1040), SILTEM poly(siloxane-etherimide) polymers (including such grades such as STM1700, STM1500 as well as XH6050).
• the term "ultrafine” as used herein means thermoplastic powdered particles that a mean particle size of about 10 to about 100 microns wherein the amount of powder particles less than 10 microns is less than 2 percent by volume.
• the powder can be monomodal and have a mean particle of about 10 to about 100 microns.
• at least two powder compositions may employed wherein each powder composition has a different mean particle size from about 10 to about 100 microns, thereby forming a polymodal powder composition.
• the powder may also have a bulk density of greater than 0.5 grams per cubic centimeter (g/cc).
• thermoplastic powder particles are substantially spherical in shape. These spherical particles can be made by the emulsion process as described in US Patent Application, Serial No. 13/841802 filed on 15-03-2013
• polyetherimide is used herein to mean a compound comprising more than 1 for example 10 to 1000, or 10 to 500, structural units of formula (1)
• each R is the same or different, and is a substituted or unsubstituted divalent organic group, such as a C 6 -2o aromatic hydrocarbon group or a halogenated derivative thereof, a straight or branched chain C2-20 alkylene group or a halogenated derivative thereof, a C3-8 cycloalkylene group or halogenated derivative thereof, in particular a divalent group of formula (2)
• Q 1 is -0-, -S-, -C(0)-, -S0 2 -, -SO-, -C y H 2y - wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups), or -(C 6 H 1 o) z - wherein z is an integer from 1 to 4.
• R is m-phenylene, p-phenylene, or a diaryl sulfone.
• T is -O- or a group of the formula -0-Z-O- wherein the divalent bonds of the -O- or the -0-Z-O- group are in the 3,3', 3,4', 4,3', or the 4,4' positions.
• the group Z in -0-Z-O- of formula (1) is also a substituted or unsubstituted divalent organic group, and can be an aromatic C 6 - 2 4 monocyclic or polycyclic moiety optionally substituted with 1 to 6 Ci_8 alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded.
• Exemplary groups Z include groups derived from a dihydroxy compound of formula (3)
• R a and R b can be the same or different and are a halogen atom or a monovalent C 1-6 alkyl group, for example; p and q are each independently integers of 0 to 4; c is 0 to 4; and X : is a bridging group connecting the hydroxy-substituted aromatic groups, where the bridging group and the hydroxy substituent of each C 6 arylene group are disposed ortho, meta, or para (specifically para) to each other on the C 6 arylene group.
• the bridging group X a can be a single bond, -0-, -S-, -S(O)-, -S(0) 2 -, -C(O)-, or a C 1-18 organic bridging group.
• the C 1-18 organic bridging group can be cyclic or acyclic, aromatic or non-aromatic, and can further comprise heteroatoms such as halogens, oxygen, nitrogen, sulfur, silicon, or phosphorous.
• the Ci-18 organic group can be disposed such that the C 6 arylene groups connected thereto are each connected to a common alkylidene carbon or to different carbons of the C 1-18 organic bridging group.
• a specific example of a group Z is a divalent group of formula (3a) (3a)
• Q is -0-, -S-, -C(O)-, -S0 2 -, -SO-, or -C y H 2y - wherein y is an integer from 1 to 5 or a halogenated derivative thereof (including a perfluoroalkylene group).
• Z is a derived from bisphenol A, such that Q in formula (3a) is 2,2- isopropylidene.
• R is m-phenylene or p-phenylene and T is - 0-Z-O- wherein Z is a divalent group of formula (3a).
• R is m-phenylene or p- phenylene and T is -O-Z-0 wherein Z is a divalent group of formula (3a) and Q is 2,2- isopropylidene.
• the polyetherimide can be a copolymer, for example, a polyetherimide sulfone copolymer comprising structural units of formula (1) wherein at least 50 mole of the R groups are of formula (2) wherein Q 1 is -S0 2 - and the remaining R groups are independently p-phenylene or m-phenylene or a combination comprising at least one of the foregoing; and Z is 2,2'-(4-phenylene)isopropylidene.
• the polyetherimide optionally comprises additional structural imide units, for example imide units of formula (4)
• R is as described in formula (1) and W is a linker of the formulas
• additional structural imide units can be present in amounts from 0 to 10 mole % of the total number of units, specifically 0 to 5 mole , more specifically 0 to 2 mole %. In an embodiment no additional imide units are present in the polyetherimide.
• the polyetherimide can be prepared by any of the methods well known to those skilled in the art, including the reaction of an aromatic bis(ether anhydride) of formula (5)
• Copolymers of the polyetherimides can be manufactured using a combination of an aromatic bis(ether anhydride) of formula (5) and a different bis(anhydride), for example a bis(anhydride) wherein T does not contain an ether functionality, for example T is a sulfone.
• bis(anhydride)s include 3,3-bis[4-(3,4- dicarboxyphenoxy)phenyl]propane dianhydride; 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4'-bis(3,4- dicarboxyphenoxy)benzophenone dianhydride; 4,4'-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride; 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4'- bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4'-bis(2,3- dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4'-bis(2,3- dicarboxyphenoxy)diphen
• organic diamines examples include ethylenediamine, propylenediamine, trimethylenediamine, diethylenetriamine, triethylene tetramine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine,
• the organic diamine is m-phenylenediamine, p-phenylenediamine, sulfonyl dianiline, or a combination comprising one or more of the foregoing.
• the polyetherimides can have a melt index of 0.1 to 10 grams per minute (g/min), as measured by American Society for Testing Materials (ASTM) D1238 at 340 to 370 °C, using a 6.7 kilogram (kg) weight.
• the polyetherimide polymer has a weight average molecular weight (Mw) of 1,000 to 150,000 grams/mole (Dalton), as measured by gel permeation chromatography, using polystyrene standards.
• the polyetherimide has an Mw of 10,000 to 80,000 Daltons.
• polyetherimide polymers typically have an intrinsic viscosity greater than 0.2 deciliters per gram (dl/g), or, more specifically, 0.35 to 0.7 dl/g as measured in m-cresol at 25 °C.
• thermoplastic "polyetherimide” composition as used in the present specification and claims can also comprise a poly(siloxane-etherimide) copolymer comprisin polyetherimide units of formula (1) and siloxane blocks of formula (7).
• each R' is independently a Ci_i 3 monovalent hydrocarbyl group.
• each R' can independently be a Ci_i 3 alkyl group, Ci_i 3 alkoxy group, C 2 -i 3 alkenyl group, C 2 _i 3 alkenyloxy group, C 3 _ 6 cycloalkyl group, C 3 _ 6 cycloalkoxy group, C 6 -i4 aryl group, C 6 -io aryloxy group, C 7-13 arylalkyl group, C 7-13 arylalkoxy group, C 7-13 alkylaryl group, or C 7-13 alkylaryloxy group.
• the foregoing groups can be fully or partially halogenated with fluorine, chlorine, bromine, or iodine, or a combination comprising at least one of the foregoing. In an embodiment no halogens are present. Combinations of the foregoing R groups can be used in the same copolymer.
• the polysiloxane blocks comprises R' groups that have minimal hydrocarbon content.
• an R' group with a minimal hydrocarbon content is a methyl group
• the poly (siloxane-etherimide)s can be formed by polymerization of an aromatic bisanhydride (4) and a diamine component comprising an organic diamine (6) as described above or mixture of diamines, and a polysiloxane diamine of formula (7)
• R' and E are as described in formula (7), and R is each independently a C 2 -C 20 hydrocarbon, in particular a C 2 -C 20 arylene, alkylene, or arylenealkylene group.
• R 4 is a C 2 -C 20 alkyl group, specifically a C 2 -C 20 alkyl group such as propylene, and E has an average value of 5 to 100, 5 to 75, 5 to 60, 5 to 15, or 15 to 40.
• Procedures for making the polysiloxane diamines of formula (8) are well known in the art.
• the diamine component can contain 10 to 90 mole percent (mol ), or 20 to 50 mol , or 25 to 40 mol of polysiloxane diamine (8) and 10 to 90 mol , or 50 to 80 mol , or 60 to 75 mol of diamine (6), for example as described in US Patent 4,404,350.
• the diamine components can be physically mixed prior to reaction with the bisanhydride(s), thus forming a substantially random copolymer.
• block or alternating copolymers can be formed by selective reaction of (6) and (8) with aromatic bis(ether anhydrides (5), to make polyimide blocks that are subsequently reacted together.
• the poly(siloxane-imide) copolymer can be a block, random, or graft copolymer.
• poly(siloxane-etherimide) examples of specific poly(siloxane-etherimide) are described in US Pat. Nos. 4,404,350, 4,808,686 and 4,690,997.
• the poly(siloxane-etherimide) has units of formula (9)
• R' and E of the siloxane are as in formula (5), the R and Z of the imide are as in formula (1), R 4 is the same as R 4 as in formula (8), and n is an integer from 5 to 100.
• the R of the etherimide is a phenylene
• Z is a residue of bisphenol A
• R is n-propylene
• E is 2 to 50, 5, to 30, or 10 to 40
• n is 5 to 100
• each R' of the siloxane is methyl.
• the relative amount of polysiloxane units and etherimide units in the poly(siloxane-etherimide) depends on the desired properties, and are selected using the guidelines provided herein.
• poly(siloxane-etherimide) copolymer is selected to have a certain average value of E, and is selected and used in amount effective to provide the desired wt of polysiloxane units in the composition.
• the poly(siloxane-etherimide) comprises 10 to 50 wt , 10 to 40 wt , or 20 to 35 wt polysiloxane units, based on the total weight of the poly(siloxane- etherimide).
• alkyl includes branched or straight chain, unsaturated aliphatic Q_ 30 hydrocarbon groups e.g., methyl, ethyl, n-propyl, i-propyl, n-butyl, s-butyl, t-butyl, n- pentyl, s-pentyl, n- and s-hexyl, n-and s-heptyl, and, n- and s-octyl.
• Alkoxy means an alkyl group that is linked via an oxygen (i.e., alkyl-O-), for example methoxy, ethoxy, and sec-butyloxy groups.
• Alkylene means a straight or branched chain, saturated, divalent aliphatic hydrocarbon group (e.g., methylene (-CH 2 -) or, propylene (-(CH 2 ) 3 -)).
• Cycloalkylene means a divalent cyclic alkylene group, -C n H 2n _ x , wherein x represents the number of hydrogens replaced by cyclization(s).
• Cycloalkenyl means a monovalent group having one or more rings and one or more carbon-carbon double bond in the ring, wherein all ring members are carbon (e.g., cyclopentyl and cyclohexyl).
• aryl means an aromatic hydrocarbon group containing the specified number of carbon atoms, such as to phenyl, tropone, indanyl, or naphthyl.
• hetero means that the compound or group includes at least one ring member that is a heteroatom (e.g., 1, 2, or 3 heteroatom(s)), wherein the heteroatom(s) is each independently N, O, S, or P.
• the at least one ultrafine, high Tg, spherical polyetherimide powder used in the present processes can be made by the methods disclosed in US Patent Application Serial No. 13/841,802 filed on March 15, 2013, which is incorporated herein by reference in its entirety.
• the at least one ultrafine, high Tg, spherical thermoplastic powder such as polyetherimide powder is made by a process comprising (a) dissolving high Tg thermoplastic material such as polyetherimide polymer in an organic solvent capable of dissolving the thermoplastic material to form a solution; (b) emulsifying the solution by combining the solution with water and a surfactant to form an emulsion; (c) transferring the emulsion into a receiving water containing a surfactant to remove the organic solvent and form a slurry; and (d) recovering thermoplastic particles of less than 75 micron diameter.
• This process may further include heating the emulsion up to or below the boiling point of the emulsion before transferring the emulsion into the receiving water.
• this process may include heating the emulsion above the boiling point of the emulsion before transferring the emulsion into the receiving water.
• the solvent may be a member selected from the group of methylene chloride, chloroform, and combinations thereof.
• the surfactant may be an anionic surfactant including sodium dodecyl benzene sulfonate (SDBS), sodium lauryl sulfate, and combinations thereof.
• SDBS sodium dodecyl benzene sulfonate
• This process may further comprise filtering the slurry to form a wet cake. And, this process may further comprise drying the wet cake under heat and vacuum.
• thermoplastic powder such as polyetherimide polymer powder is made by the steps of: (a) dissolving a thermoplastic material such as polyetherimide polymer in a solvent to form a solution, wherein the thermoplastic material is soluble in the solvent, the solvent has a boiling point that is less than 100 C and the solvent is immiscible with water; (b) emulsifying the solution by combining the solution with de-ionized water and a surfactant under agitation conditions sufficient to form an emulsion; (c) transferring the emulsion into a de-ionized receiving water, the receiving water also containing a surfactant and removing the solvent and form a slurry; (d) pre-filtering the slurry to remove any macro particles or contaminates; (e) filtering the slurry to form a wet cake; (f) filtering the slurry to form a wet cake; (g) drying the washed wet cake under heat and vacuum; and (h) recovering particles of thermoplastic material
• the powder composition comprises between 50 to 100 weight percent of the at least one ultrafine, high Tg, spherical thermoplastic polymer powder such as polyetherimide powder, based on the weight of polymeric materials in the powder.
• the powder composition can contain a colorant or a process aid.
• the powder composition may optionally contain a flow agent.
• a thermoplastic composition of the present invention contains 0%, preferably 0.05%, to about 5%, and more preferably about 0.075% to about 1%, by weight of a particulate flow agent.
• the powder composition contains about 0.1% to about 0.25%, by weight, of the flow agent.
• This optional flow agent included in the powder composition is a particulate inorganic material having a median particle size of 10 microns or less, and is chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate.
• the flow agent preferably is present in an amount sufficient to allow the polyetherimide to flow and level on the build surface of the laser sintering device.
• One useful flow agent is a fumed silica.
• a powder composition also can contain other optional ingredients.
• These optional ingredients are particulate materials and include organic and inorganic materials, such as fillers and coloring agents.
• An optional ingredient is present in a sufficient amount to perform its intended function, without adversely affecting the thermoplastic composition or an article prepared therefrom.
• Optional ingredients have a particle size in the range of the particle sizes of the polyetherimide and/or optional flow agent. Each optional ingredient is milled, if necessary, to the desired median particle size and particle size distribution.
• each individual optional ingredient typically is present in the powder composition in an amount of about 0.1% to about 30%, by weight, of the
• the total amount of optional ingredients in the powder composition ranges from 0% up to about 30%, by weight.
• each optional ingredient it is not necessary for each optional ingredient to melt during the laser sintering process. However, each optional ingredient must be compatible with the
• polyetherimide in order to provide a strong and durable article of manufacture.
• the optional ingredient therefore, can be inorganic, filler that imparts additional strength to the article of manufacture.
• Another optional ingredient is a coloring agent, for example a pigment or a dye, like carbon black, to impart a desired color to the article of manufacture.
• the coloring agent is not limited, as long as the coloring agent does not adversely affect the composition or an article prepared therefrom, and is sufficiently stable to retain its color under conditions of the laser sintering process and during exposure to the laser.
• Still other additional optional ingredients may also include, for example, toners, extenders, fillers, colorants (e.g., pigments and dyes), lubricants, anticorrosion agents, thixotropic agents, dispersing agents, antioxidants, adhesion promoters, light stabilizers, organic solvents, surfactants, flame retardants, and mixtures thereof.
• Still another optional ingredient also can be a second polymer that modifies the properties of the polyetherimide.
• the spherical polyetherimide powder used herein may have certain
• the commercially available ULTEM polyether imide has a tg of 215 degrees C. It may have comprises at least 5 weight percent of one or more amorphous polyetherimide powder. It may have has a weight average molecular weight of between 1,000 and 150,000 Daltons. Each powder may be monomodal and have a mean particle of about 10 to about 75 microns. The powder may have a bulk density of greater than 0.5 grams per cubic centimeter (g/cc).
• the method of manufacturing a three dimensional article may comprise the steps of: (1) depositing a quantity of a powder composition including at least one ultrafine, high Tg, spherical polyetherimide powder on a support surface; (2) leveling the composition to form a smooth layer on the support surface; (3) then directing an energy beam over a predetermined target area on the support surface causing the composition to form an integral layer; and (d) repeating steps (1) to (3) to form additional layers that are integrally bonded to adjacent layers to form a three-dimensional article, wherein the thermoplastic composition includes at least one ultrafine, high Tg, spherical polyetherimide powder.
• the energy beam may be a laser.
• the term "powder bed fusing" is used herein to mean all laser sintering and all selective laser sintering processes as well as other powder bed fusion processes.
• sintering of the powder composition may be accomplished via application of electromagnetic radiation other than that produced by a laser, with the selectivity of the sintering achieved, for example, through selective application of inhibitors, absorbers, susceptors, or the electromagnetic radiation (e.g., through use of masks or directed laser beams).
• Any other suitable source of electromagnetic radiation may be used, including, for example, infrared radiation sources, microwave generators, lasers, radiative heaters, lamps, or a combination thereof.
• SMS selective mask sintering
• U.S. Pat. No. 6,531,086 which describes an SMS machine in which a shielding mask is used to selectively block infrared radiation, resulting in the selective irradiation of a portion of a powder layer.
• the powder composition may include one or more heat absorbers and/or dark-colored materials (e.g., carbon black, carbon nanotubes, or carbon fibers).
• the present invention also includes all three dimensional products made by powder bed fusing these powder compositions. After a layer-by-layer manufacture of an article of manufacture, the article may exhibit excellent resolution, durability, and strength. These articles of manufacture may have a wide variety of uses, including as prototypes and as end products as well as molds for end products.
• powder bed fused (e.g., laser sintered) articles may be produced from the powder compositions using any suitable powder bed fusing processes including laser sintering processes.
• These articles can include a plurality of overlying and adherent sintered layers that include a polymeric matrix which, in some embodiments, have reinforcement particles dispersed throughout the polymeric matrix.
• Laser sintering processes are sufficiently well known, and are based on the selective sintering of polymer particles, where layers of polymer particles are briefly exposed to laser light and the polymer particles exposed to the laser light are thus bonded to one another. Successive sintering of layers of polymer particles produces three-dimensional objects. Details concerning the selective laser sintering process are found, by way of example, in the specifications U.S.
• the powder described herein may also be used in other rapid prototyping or rapid manufacturing processing of the prior art, in particular in those described above.
• the inventive powder may in particular be used for producing moldings from powders via the SLS (selective laser sintering) process, as described in U.S. Pat. No. 6,136,948 or WO 96/06881, via the SIB process (selective inhibition of bonding of powder), as described in WO 01/38061, via 3D printing, as described in EP 0 431 924, or via a microwave process, as described in DE 103 11 438.
• SLS selective laser sintering
• SIB selective inhibition of bonding of powder
• the sintered layers of laser sintered articles of the present invention may be of any thickness suitable for laser sintered processing.
• the plurality of sintered layers may be each, on average, preferably at least about 50 microns thick, more preferably at least about 80 microns thick, and even more preferably at least about 100 microns thick.
• the plurality of sintered layers are each, on average, preferably less than about 200 microns thick, more preferably less than about 150 microns thick, and even more preferably less than about 120 microns thick.
• Three-dimensional articles produced from powder compositions of the invention using a layer-by-layer sintering other than laser sintering may have layer thicknesses that are the same or different from those described above.
• the invention may alternately comprise, consist of, or consist essentially of, any appropriate components herein disclosed.
• the invention may additionally, or alternatively, be formulated so as to be devoid, or substantially free, of any components, materials, ingredients, adjuvants or species used in the prior art compositions or that are otherwise not necessary to the achievement of the function and/or objectives of the present invention.
• Powder A has a rough, cracked surface and potato-like morphology while the powder B consists of dense spheres.
• the mean particle size for both powder A and B where between 10-15 micron.
• the particle size distribution for powder A was much narrower than that of powder B as can be seen from the tabulated data below.
• Powder B contains a larger percentage of submicron particles.
• Table 3 Powder flow behavior of polyetherimide made from jet milling process versus emulsion based process. The flow behavior was quantified from poor (ranked as 1) to good (ranked as 4). Sample
• Embodiment 1 A method comprising: providing a powder composition including at least one ultrafine, spherical thermoplastic polymer powder having a glass transition temperature (Tg) of at least 150 degrees C; and powder bed fusing the powder composition to form a three-dimensional article.
• Tg glass transition temperature
• Embodiment 2 The method of Embodiment 1, wherein the powder composition comprises between 50 to 100 weight percent of the at least one ultrafine, high Tg, spherical thermoplastic polymer powder, based on the weight of polymeric materials in the powder.
• Embodiment 3 The method of any of Embodiments 1-2, wherein the spherical thermoplastic polymer powder has a glass transition temperature of more than 150° C. and less than 350° C.
• Embodiment 4 The method of any of Embodiments 1-3, wherein the spherical thermoplastic polymer powder has a glass transition temperature of more than 200° C. and less than 300° C.
• Embodiment 5 The method of any of Embodiments 1-4, wherein the thermoplastic polymer powder has a weight average molecular weight of between 1,000 and 150,000 Daltons.
• Embodiment 6 The method of any of Embodiments 1-5, wherein each ultrafine, high Tg, spherical thermoplastic polymer powder is monomodal and has a mean particle of about 10 to about 75 microns and the amount of powder particles smaller than 10 microns is less than 2 percent by volume.
• Embodiment 7 The method of any of Embodiments 1-6, further comprising adding a flow agent or to the powder composition.
• Embodiment 8 The method of Embodiment 7, wherein the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• Embodiment 9 The method of any of Embodiments 7-8, wherein the amount of flow agent is from about 0.05% to about 5% of the powder composition.
• Embodiment 10 The method of any of Embodiments 1-9, wherein the polyetherimide powder has a bulk density of greater than 0.5 grams per cubic centimeter.
• Embodiment 11 The method of any of Embodiments 1-10, wherein at least two powder compositions are employed and each powder composition has a different mean particle size, thereby forming a polymodal powder composition.
• Embodiment 12 A method comprising: providing a powder composition including at least one ultrafine, spherical thermoplastic polymer powder having a glass transition temperature (Tg) of at least 150 degrees C wherein the thermoplastic polymer powder is chosen from polyetherimides, polysulfones, and polyarylsulfones and
• Embodiment 13 The method of Embodiment 12, wherein the powder composition comprises between 50 to 100 weight percent of the at least one ultrafine, high Tg, spherical thermoplastic polymer powder, based on the weight of polymeric materials in the powder.
• Embodiment 14 The method of any of Embodiments 12-13, wherein the spherical thermoplastic polymer powder has a glass transition temperature of more than 150° C. and less than 350° C.
• Embodiment 15 The method of any of Embodiments 12-14, wherein the spherical thermoplastic polymer powder has a glass transition temperature of more than 200° C. and less than 300° C.
• Embodiment 16 The method of any of Embodiments 12-15, wherein the thermoplastic polymer powder has a weight average molecular weight of between 1,000 and 150,000 Daltons.
• Embodiment 17 The method of any of Embodiments 12-16, wherein each ultrafine, high Tg, spherical thermoplastic polymer powder is monomodal and has a mean particle of about 10 to about 75 microns and the amount of powder particles smaller than 10 microns is less than 2 percent by volume.
• Embodiment 18 The method of any of Embodiments 12-17, further comprising adding a flow agent or to the powder composition.
• Embodiment 19 The method of Embodiment 18, wherein the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• Embodiment 20 The method of any of Embodiments 18-19, wherein the amount of flow agent is from about 0.05% to about 5% of the powder composition.
• Embodiment 21 The method of any of Embodiments 1-20, wherein the polyetherimide powder has a bulk density of greater than 0.5 grams per cubic centimeter.
• Embodiment 22 The method of any of Embodiments 1-21, wherein at least two powder compositions are employed and each powder composition has a different mean particle size, thereby forming a polymodal powder composition.
• Embodiment 23 A method comprising: providing a powder composition including at least one ultrafine, high Tg, spherical polyetherimide powder; and powder bed fusing the powder composition to form a three-dimensional article.
• Embodiment 24 The method of Embodiment 23, wherein the powder composition comprises between 50 to 100 weight percent of the at least one ultrafine, high Tg, spherical polyetherimide powder, based on the weight of polymeric materials in the powder.
• Embodiment 25 The method of any of Embodiments 23-24, wherein the spherical polyetherimide powder has a glass transition temperature of more than 150° C. and less than 350° C.
• Embodiment 26 The method of any of Embodiments 23-25, wherein the spherical polyetherimide powder has a glass transition temperature of more than 200° C. and less than 300° C.
• Embodiment 27 The method of any of Embodiments 23-26, wherein the powder composition comprises at least 5 weight percent of one or more amorphous polyetherimide powder.
• Embodiment 28 The method of any of Embodiments 23-27, wherein the polyetherimide powder has a weight average molecular weight of between 1,000 and 150,000 Daltons.
• Embodiment 29 The method of any of Embodiments 23-24, wherein each ultrafine, high Tg, spherical polyetherimide powder is monomodal and has a mean particle of about 10 to about 75 microns.
• Embodiment 30 The method of any of Embodiments 23-29, wherein at least one ultrafine, high Tg, spherical polyetherimide powder is made by a process comprising (a) dissolving polyetherimide in an organic solvent capable of dissolving the polyetherimide to form a solution; (b) emulsifying the solution by combining the solution with water and a surfactant to form an emulsion; (c) transferring the emulsion into a receiving water containing a surfactant to remove the organic solvent and form a slurry; and (d) recovering polyetherimide particles of less than 75 micron diameter.
• Embodiment 31 The method of Embodiment 30, further comprising heating the emulsion up to or below the boiling point of the emulsion before transferring the emulsion into the receiving water.
• Embodiment 32 The method of any of Embodiments 30-31, further comprising heating the emulsion above the boiling point of the emulsion before transferring the emulsion into the receiving water.
• Embodiment 33 The method of any of Embodiments 30-32, wherein the solvent is a member selected from the group of methylene chloride, chloroform, and combinations thereof.
• Embodiment 34 The method of any of Embodiments 30-33, wherein the surfactant is anionic, cationic or non-ionic surfactant or combinations thereof.
• Embodiment 35 The method of any of Embodiments 30-34, wherein the surfactant is a surfactant selected from the group of sodium dodecyl benzene sulfonate (SDBS), sodium lauryl sulfate, and combinations thereof.
• SDBS sodium dodecyl benzene sulfonate
• sodium lauryl sulfate sodium lauryl sulfate
• Embodiment 36 The method of any of Embodiments 30-35, further comprising filtering the slurry to form a wet cake.
• Embodiment 37 The method of any of Embodiments 30-36, further comprising drying the wet cake under heat and vacuum.
• Embodiment 38 The method of any of Embodiments 23-37, further comprising adding a flow agent or to the powder composition.
• Embodiment 39 The method of Embodiment 38, wherein the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• the flow agent chosen from the group consisting of a hydrated silica, amorphous alumina, a glassy silica, a glassy phosphate, a glassy borate, a glassy oxide, titania, talc, mica, a fumed silica, kaolin, attapulgite, calcium silicate, alumina, and magnesium silicate and combinations thereof.
• Embodiment 40 The method of any of Embodiments 38-39, wherein the amount of flow agent is from about 0.05% to about 5% of the powder composition.
• Embodiment 41 The method of any of Embodiments 23-40, wherein the polyetherimide powder has a bulk density of greater than 0.5 grams per cubic centimeter.
• Embodiment 42 The method of any of Embodiments 23-41, wherein at least two powder compositions are employed and each powder composition has a different mean particle size, thereby forming a polymodal powder composition.
• Embodiment 43 A method of manufacturing a three dimensional article comprising the steps of: (1) depositing a quantity of a powder composition including at least one ultrafine, high Tg, spherical thermoplastic polymer powder on a support surface; (2) leveling the composition to form a smooth layer on the support surface; (3) then directing an energy beam over a predetermined target area on the support surface causing the composition to form an integral layer; and (d) repeating steps (1) to (3) to form additional layers that are integrally bonded to adjacent layers to form a three-dimensional article, wherein the thermoplastic composition includes at least one ultrafine, high Tg, spherical thermoplastic powder.
• Embodiment 44 The method of claim of the Embodiment 43 wherein the energy beam is a laser.
• Embodiment 45 The method of any of the Embodiments 43-44, wherein the at least one ultrafine, high Tg, spherical thermoplastic powder is made by the steps of: (a) dissolving a thermoplastic polymer material in a solvent to form a solution, wherein the thermoplastic polymer is soluble in the solvent, the solvent has a boiling point that is less than 100 C and the solvent is immiscible with water; (b) emulsifying the solution by combining the solution with de-ionized water and a surfactant under agitation conditions sufficient to form an emulsion; (c) transferring the emulsion into a de-ionized receiving water, the receiving water also containing a surfactant and removing the solvent and form a slurry; (d) pre-filtering the slurry to remove any macro particles or contaminates; (e) filtering the slurry to form a wet cake; (f) filtering the slurry to form a wet cake
• Embodiment 46 The method of any of the Embodiments 43-45, wherein the thermoplastic polymer is chosen from polyetherimide, polysulfone, polyarylsulfones, and combinations thereof.
• Embodiment 47 A three-dimensional sintered article resulting from the method of any of the Embodiments 1-46.
• embodiment means that a particular element (e.g., feature, structure, and/or characteristic) described in connection with the embodiment is included in at least some embodiments described herein, and may or may not be present in other embodiments.
• element e.g., feature, structure, and/or characteristic
• the described elements may be combined in any suitable manner in the various embodiments.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Materials Engineering (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Polymers & Plastics (AREA)
• Medicinal Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Manufacturing & Machinery (AREA)
• Mechanical Engineering (AREA)
• Wood Science & Technology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• Structural Engineering (AREA)
• Composite Materials (AREA)
• Civil Engineering (AREA)
• Ceramic Engineering (AREA)
• Dispersion Chemistry (AREA)
• Inorganic Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=52988471

Family Applications (1)

Country Status (6)

Cited By (13)

Families Citing this family (37)

Citations (19)

Family Cites Families (12)

• 2015
  • 2015-04-06 KR KR1020167026459A patent/KR102322827B1/ko active Active
  • 2015-04-06 EP EP15717365.9A patent/EP3129210B1/en not_active Not-in-force
  • 2015-04-06 WO PCT/US2015/024452 patent/WO2015157148A1/en not_active Ceased
  • 2015-04-06 CN CN201580018653.5A patent/CN106170506A/zh active Pending
  • 2015-04-06 US US15/302,272 patent/US10669437B2/en active Active
  • 2015-04-06 JP JP2016561670A patent/JP2017516680A/ja active Pending

Patent Citations (19)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events