WO2015095874A1 - Nickel plated zinc alloys for coinage - Google Patents
Nickel plated zinc alloys for coinage Download PDFInfo
- Publication number
- WO2015095874A1 WO2015095874A1 PCT/US2014/071945 US2014071945W WO2015095874A1 WO 2015095874 A1 WO2015095874 A1 WO 2015095874A1 US 2014071945 W US2014071945 W US 2014071945W WO 2015095874 A1 WO2015095874 A1 WO 2015095874A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- melting point
- zinc
- substrate
- copper
- Prior art date
Abstract
Description
Claims