WO2015076573A1 - Batterie rechargeable - Google Patents

Batterie rechargeable Download PDF

Info

Publication number
WO2015076573A1
WO2015076573A1 PCT/KR2014/011178 KR2014011178W WO2015076573A1 WO 2015076573 A1 WO2015076573 A1 WO 2015076573A1 KR 2014011178 W KR2014011178 W KR 2014011178W WO 2015076573 A1 WO2015076573 A1 WO 2015076573A1
Authority
WO
WIPO (PCT)
Prior art keywords
separator
secondary battery
negative electrode
adhesive layer
active material
Prior art date
Application number
PCT/KR2014/011178
Other languages
English (en)
Korean (ko)
Inventor
천지현
김양섭
윤효상
Original Assignee
삼성에스디아이 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020140133337A external-priority patent/KR20150106808A/ko
Application filed by 삼성에스디아이 주식회사 filed Critical 삼성에스디아이 주식회사
Publication of WO2015076573A1 publication Critical patent/WO2015076573A1/fr

Abstract

La présente invention concerne une batterie rechargeable comprenant : une anode comprenant un matériau actif d'anode ; une cathode comprenant un matériau actif de cathode ; un électrolyte ; et un film de séparation agencé entre l'anode et la cathode, le film de séparation comprenant une couche adhésive poreuse comportant une pluralité de pores collée à l'anode ou à la cathode, l'électrolyte étant contenu dans les pores de la couche adhésive poreuse, et la couche adhésive poreuse comprenant un copolymère acrylate-acétate.
PCT/KR2014/011178 2013-11-21 2014-11-20 Batterie rechargeable WO2015076573A1 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
KR10-2013-0142324 2013-11-21
KR20130142324 2013-11-21
KR10-2014-0041124 2014-04-07
KR20140041124 2014-04-07
KR10-2014-0133337 2014-10-02
KR1020140133337A KR20150106808A (ko) 2013-11-21 2014-10-02 이차 전지 및 이의 제조 방법

Publications (1)

Publication Number Publication Date
WO2015076573A1 true WO2015076573A1 (fr) 2015-05-28

Family

ID=53179778

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2014/011178 WO2015076573A1 (fr) 2013-11-21 2014-11-20 Batterie rechargeable

Country Status (1)

Country Link
WO (1) WO2015076573A1 (fr)

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107316968A (zh) * 2017-05-11 2017-11-03 东莞市赛普克电子科技有限公司 一种粘性电池隔膜及使用该隔膜的锂离子电池
CN109565021A (zh) * 2016-09-21 2019-04-02 帝人株式会社 非水系二次电池用隔膜及非水系二次电池
CN109950464A (zh) * 2019-02-01 2019-06-28 湖北锂诺新能源科技有限公司 一种多孔硅碳负极极片及其制备方法
CN110982008A (zh) * 2019-12-30 2020-04-10 宣城研一新能源科技有限公司 锂离子电池负极水性粘结剂
CN111057184A (zh) * 2019-12-30 2020-04-24 宣城研一新能源科技有限公司 负极极片水性粘结剂的制备方法
CN112103558A (zh) * 2020-10-09 2020-12-18 昆山宝创新能源科技有限公司 自支撑固态电解质复合膜及其制备方法和应用
CN112103509A (zh) * 2020-08-20 2020-12-18 欣旺达电动汽车电池有限公司 正极集流体、正极片、锂离子电池及电池模组
WO2024113988A1 (fr) * 2022-11-28 2024-06-06 欣旺达动力科技股份有限公司 Batterie secondaire et dispositif électrique

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004063343A (ja) * 2002-07-30 2004-02-26 Toshiba Corp リチウムイオン二次電池
KR100727248B1 (ko) * 2007-02-05 2007-06-11 주식회사 엘지화학 다공성 활성층이 코팅된 유기/무기 복합 분리막 및 이를구비한 전기화학소자
KR20080101043A (ko) * 2007-05-15 2008-11-21 주식회사 엘지화학 다공성 코팅층이 형성된 세퍼레이터 및 이를 구비한전기화학소자
KR20110057079A (ko) * 2009-11-23 2011-05-31 주식회사 엘지화학 다공성 코팅층을 구비한 분리막의 제조방법, 이로부터 형성된 분리막 및 이를 구비한 전기화학소자
KR20130067684A (ko) * 2011-12-14 2013-06-25 주식회사 엘지화학 전기화학소자용 전극 및 이를 구비한 전기화학소자

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004063343A (ja) * 2002-07-30 2004-02-26 Toshiba Corp リチウムイオン二次電池
KR100727248B1 (ko) * 2007-02-05 2007-06-11 주식회사 엘지화학 다공성 활성층이 코팅된 유기/무기 복합 분리막 및 이를구비한 전기화학소자
KR20080101043A (ko) * 2007-05-15 2008-11-21 주식회사 엘지화학 다공성 코팅층이 형성된 세퍼레이터 및 이를 구비한전기화학소자
KR20110057079A (ko) * 2009-11-23 2011-05-31 주식회사 엘지화학 다공성 코팅층을 구비한 분리막의 제조방법, 이로부터 형성된 분리막 및 이를 구비한 전기화학소자
KR20130067684A (ko) * 2011-12-14 2013-06-25 주식회사 엘지화학 전기화학소자용 전극 및 이를 구비한 전기화학소자

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109565021A (zh) * 2016-09-21 2019-04-02 帝人株式会社 非水系二次电池用隔膜及非水系二次电池
CN107316968A (zh) * 2017-05-11 2017-11-03 东莞市赛普克电子科技有限公司 一种粘性电池隔膜及使用该隔膜的锂离子电池
CN107316968B (zh) * 2017-05-11 2020-07-14 东莞市赛普克电子科技有限公司 一种粘性电池隔膜及使用该隔膜的锂离子电池
CN109950464A (zh) * 2019-02-01 2019-06-28 湖北锂诺新能源科技有限公司 一种多孔硅碳负极极片及其制备方法
CN110982008A (zh) * 2019-12-30 2020-04-10 宣城研一新能源科技有限公司 锂离子电池负极水性粘结剂
CN111057184A (zh) * 2019-12-30 2020-04-24 宣城研一新能源科技有限公司 负极极片水性粘结剂的制备方法
CN110982008B (zh) * 2019-12-30 2022-01-07 浙江研一新能源科技有限公司 锂离子电池负极水性粘结剂
CN111057184B (zh) * 2019-12-30 2022-02-25 宣城研一新能源科技有限公司 负极极片水性粘结剂的制备方法
CN112103509A (zh) * 2020-08-20 2020-12-18 欣旺达电动汽车电池有限公司 正极集流体、正极片、锂离子电池及电池模组
CN112103509B (zh) * 2020-08-20 2023-06-06 欣旺达电动汽车电池有限公司 正极集流体、正极片、锂离子电池及电池模组
CN112103558A (zh) * 2020-10-09 2020-12-18 昆山宝创新能源科技有限公司 自支撑固态电解质复合膜及其制备方法和应用
WO2024113988A1 (fr) * 2022-11-28 2024-06-06 欣旺达动力科技股份有限公司 Batterie secondaire et dispositif électrique

Similar Documents

Publication Publication Date Title
WO2015076573A1 (fr) Batterie rechargeable
WO2017171524A1 (fr) Séparateur de dispositif électronique comprenant une couche adhésive, et ensemble d'électrodes comprenant un séparateur
WO2015076611A1 (fr) Séparateur comprenant une couche de revêtement, et batterie l'utilisant
WO2017039385A1 (fr) Membrane de séparation comprenant des parties de revêtement adhésif ayant différentes forces d'adhérence et ensemble électrode comprenant cette dernière
WO2014084681A1 (fr) Membrane de séparation de batterie secondaire contenant des couches de revêtement à double porosité en particules inorganiques ayant différentes propriétés de surface, batterie secondaire l'intégrant et procédé de fabrication d'une membrane de séparation
WO2017034353A1 (fr) Séparateur complexe pour élément électrochimique, comprenant une couche de liaison, et élément électrochimique le comprenant
WO2018038584A1 (fr) Séparateur pour dispositif électrochimique et dispositif électrochimique comprenant ledit séparateur
WO2020067778A1 (fr) Membrane de séparation destiné à un dispositif électrochimique et son procédé de fabrication
WO2017188537A1 (fr) Séparateur comprenant une couche adhésive poreuse et batterie rechargeable au lithium utilisant celui-ci
WO2012111956A2 (fr) Séparateur, son procédé de préparation et dispositif électrochimique le comprenant
WO2015076571A1 (fr) Composition d'agent de revêtement de séparateur, séparateur formé de la composition d'agent de revêtement, et batterie faisant appel à celui-ci
WO2011059154A1 (fr) Séparateur pour une batterie au lithium rechargeable et batterie au lithium rechargeable en comportant
WO2016171519A1 (fr) Séparateur pour batterie secondaire au lithium et son procédé de fabrication
WO2014208926A1 (fr) Séparateur comprenant une couche de revêtement et batterie utilisant ledit séparateur
WO2021075924A1 (fr) Membrane de séparation pour dispositif électrochimique, dispositif électrochimique comprenant ladite membrane de séparation, et procédé de fabrication de ladite membrane de séparation
WO2015076574A1 (fr) Séparateur et batterie rechargeable l'utilisant
WO2021034060A1 (fr) Séparateur ayant une couche résistante à la chaleur pour dispositif électrochimique et batterie secondaire le comprenant
WO2020226367A1 (fr) Composition de résine liante et séparateur la comprenant pour dispositif électrochimique
WO2020190101A1 (fr) Membrane de séparation destinée à un dispositif électrochimique et son procédé de fabrication
WO2020050559A1 (fr) Séparateur pour accumulateur n'ayant pas de substrat de séparateur
WO2021101222A1 (fr) Séparateur pour dispositif électrochimique, et dispositif électrochimique comprenant celui-ci
WO2022092679A1 (fr) Ensemble électrode et élément de batterie le comprenant
WO2018030810A1 (fr) Assemblage d'électrodes dans lequel une électrode et un film de séparation sont partiellement liés
WO2021080212A1 (fr) Dispositif et procédé de mesure de la résistance d'un séparateur sous pression
WO2015076602A1 (fr) Ensemble électrode ayant une rigidité à la flexion améliorée, son procédé de préparation et batterie électrochimique le comprenant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14864722

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14864722

Country of ref document: EP

Kind code of ref document: A1