WO2014197993A1 - Marquages routiers résistant à l'abrasion et au gel/dégel - Google Patents

Marquages routiers résistant à l'abrasion et au gel/dégel Download PDF

Info

Publication number
WO2014197993A1
WO2014197993A1 PCT/CA2014/050550 CA2014050550W WO2014197993A1 WO 2014197993 A1 WO2014197993 A1 WO 2014197993A1 CA 2014050550 W CA2014050550 W CA 2014050550W WO 2014197993 A1 WO2014197993 A1 WO 2014197993A1
Authority
WO
WIPO (PCT)
Prior art keywords
road marking
retroreflective
armouring
marking according
road
Prior art date
Application number
PCT/CA2014/050550
Other languages
English (en)
Inventor
David G. JANEWAY
Jamie B. GORDY
Klaus H. Oehr
Original Assignee
Janeway David G
Gordy Jamie B
Oehr Klaus H
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Janeway David G, Gordy Jamie B, Oehr Klaus H filed Critical Janeway David G
Publication of WO2014197993A1 publication Critical patent/WO2014197993A1/fr

Abstract

Cette invention concerne un marquage routier, comprenant un matériau de renfort (22) rétro-réfléchissant ou semi-rétro-réfléchissant adhéré à une rainure renfoncée (10) d'une surface de roulement (12) au moyen d'un adhésif thermoplastique souple résistant au gel/dégel (14) tel qu'une composition copolymère à base d'époxy/uréthane. Les matériaux de renfort comprennent des particules de céramique, de quartz, de corindon, de perlite et des cristaux synthétiques, présentant une dureté Mohs supérieure ou égale à 7. Optionnellement, le marquage routier selon l'invention comprend un matériau de marquage rétro-réfléchissant supplémentaire tel que des billes de verre ou de la peinture réfléchissante, dont la rétro-réflexion est différente de celle du matériau de renfort. Ledit marquage routier peut être rénové quand il est usé.
PCT/CA2014/050550 2013-06-14 2014-06-12 Marquages routiers résistant à l'abrasion et au gel/dégel WO2014197993A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201361835186P 2013-06-14 2013-06-14
US61/835,186 2013-06-14

Publications (1)

Publication Number Publication Date
WO2014197993A1 true WO2014197993A1 (fr) 2014-12-18

Family

ID=52021531

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2014/050550 WO2014197993A1 (fr) 2013-06-14 2014-06-12 Marquages routiers résistant à l'abrasion et au gel/dégel

Country Status (1)

Country Link
WO (1) WO2014197993A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107513934A (zh) * 2017-09-20 2017-12-26 广东创科交通设施有限公司 一种撒播器及其道路划线机
CN108930209A (zh) * 2017-05-25 2018-12-04 钱宏毅 一种隧道反光渗水路面
CN109680597A (zh) * 2018-12-20 2019-04-26 安徽择正公路工程有限责任公司 道路标线装置及标线方法
CN110344342A (zh) * 2019-07-16 2019-10-18 安徽岩芯光电技术有限公司 玻璃珠施工方法、沉降度检测方法和装置及沉降度分析仪
CN111303722A (zh) * 2020-02-17 2020-06-19 南京路伸交通科技有限公司 一种耐久反光性自分层道路标线涂料及其制备方法
CZ309554B6 (cs) * 2022-05-10 2023-04-05 EternaLight s.r.o Způsob aplikace fotoluminiscenčního značení
CZ309598B6 (cs) * 2022-05-10 2023-05-03 EternaLight s.r.o. Způsob aplikace fotoluminiscenčního značení

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3782843A (en) * 1970-06-16 1974-01-01 Eigenmann Ludwig Road surface marking material and marked road
US5453320A (en) * 1990-10-31 1995-09-26 Minnesota Mining And Manufacturing Company Pavement marking material
US20120314290A1 (en) * 2011-06-09 2012-12-13 New York State Thruway Authority Method and apparatus for forming and applying retroreflective pavement markings

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3782843A (en) * 1970-06-16 1974-01-01 Eigenmann Ludwig Road surface marking material and marked road
US5453320A (en) * 1990-10-31 1995-09-26 Minnesota Mining And Manufacturing Company Pavement marking material
US20120314290A1 (en) * 2011-06-09 2012-12-13 New York State Thruway Authority Method and apparatus for forming and applying retroreflective pavement markings

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108930209A (zh) * 2017-05-25 2018-12-04 钱宏毅 一种隧道反光渗水路面
CN107513934A (zh) * 2017-09-20 2017-12-26 广东创科交通设施有限公司 一种撒播器及其道路划线机
CN109680597A (zh) * 2018-12-20 2019-04-26 安徽择正公路工程有限责任公司 道路标线装置及标线方法
CN109680597B (zh) * 2018-12-20 2021-03-05 安徽择正公路工程有限责任公司 道路标线装置及标线方法
CN110344342A (zh) * 2019-07-16 2019-10-18 安徽岩芯光电技术有限公司 玻璃珠施工方法、沉降度检测方法和装置及沉降度分析仪
CN111303722A (zh) * 2020-02-17 2020-06-19 南京路伸交通科技有限公司 一种耐久反光性自分层道路标线涂料及其制备方法
CZ309554B6 (cs) * 2022-05-10 2023-04-05 EternaLight s.r.o Způsob aplikace fotoluminiscenčního značení
CZ309598B6 (cs) * 2022-05-10 2023-05-03 EternaLight s.r.o. Způsob aplikace fotoluminiscenčního značení

Similar Documents

Publication Publication Date Title
WO2014197993A1 (fr) Marquages routiers résistant à l'abrasion et au gel/dégel
JP3597535B2 (ja) 模様付き耐チョーキング性舗装道路標示
DK2504492T3 (en) PREFORMED THERMOPLASTIC ROAD MARKING MARKETING AND PROCEDURE UNDER APPLICATION OF LARGE AGGREGATE FOR IMPROVED LONG TIME SAFETY AND REDUCED MARKET TREASURY
US2952192A (en) Marker stripe
GB2242144A (en) Anti-slip surfaces
KR101485488B1 (ko) 차선홈을 이용한 도로에서의 차선 설치 공법
CA2836558A1 (fr) Procede et appareil pour former et appliquer des marquages de revetement de route retroreflechissants
JPS6156727B2 (fr)
US20090291292A1 (en) Optically active elements including multiple bead layers
US2355430A (en) Delineated area
KR101336035B1 (ko) 미끄럼방지용 도로포장 조성물 및 이의 제조 방법
US20090196690A1 (en) Anti-slip composition and method of forming anti-slip layer using the same
US3106878A (en) Highway markers
KR101145816B1 (ko) 요철을 갖는 재귀반사형 포장재 및 그 시공방법
CA2955923C (fr) Methode de marquage de la chaussee et composition
JP3020579U (ja) 路面敷設ブロックおよびこれを用いた横断歩道路面構成体
Ellis et al. Evaluation of seal coating treatments to manage temporary pavement paint markings during highway construction
KR20200112366A (ko) 고휘도 반사 부재를 이용한 차선 시공방법
Rodin III et al. Evaluation of motorcyclists’ and bikers’ safety on wet pavement markings
KR102471614B1 (ko) 보차도용 재귀반사체
Nassiri Evaluation of Motorcyclists' and Bikers' Safety on Wet Pavement Markings
Lynch Pavement marking types and application
US20220098123A1 (en) Marking trafficked pavement substrates using a dry polymer modified cement
Anderson et al. Kwik Bond Polymers (R) high friction surface treatment.
Mohamed Evaluation and modeling of pavement marking characteristics based on laboratory and field data

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14811015

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14811015

Country of ref document: EP

Kind code of ref document: A1