WO2014084725A1 - Stratifié en verre, couche adhésive et véhicule comprenant un tel stratifié en verre - Google Patents

Stratifié en verre, couche adhésive et véhicule comprenant un tel stratifié en verre Download PDF

Info

Publication number
WO2014084725A1
WO2014084725A1 PCT/NL2013/050757 NL2013050757W WO2014084725A1 WO 2014084725 A1 WO2014084725 A1 WO 2014084725A1 NL 2013050757 W NL2013050757 W NL 2013050757W WO 2014084725 A1 WO2014084725 A1 WO 2014084725A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass laminate
glass
adhesive layer
laminate
glass sheet
Prior art date
Application number
PCT/NL2013/050757
Other languages
English (en)
Inventor
Jacob WIERSEMA
Joseph Gerardus Maria VAN BUSSEL
Original Assignee
Aviation Glass & Technology B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Aviation Glass & Technology B.V. filed Critical Aviation Glass & Technology B.V.
Publication of WO2014084725A1 publication Critical patent/WO2014084725A1/fr

Abstract

Les stratifiés en verre comprenant des feuilles de verre ultra-minces durcies par voie chimique sont connus et ont l'avantage d'être relativement légers et de présenter des propriétés de résistance aux chocs et d'atténuation du bruit élevées. L'invention se rapporte à un stratifié en verre. L'invention se rapporte également à une couche adhésive à utiliser dans un tel stratifié en verre selon l'invention. L'invention se rapporte en outre à un véhicule comprenant un tel stratifié en verre.
PCT/NL2013/050757 2012-10-26 2013-10-28 Stratifié en verre, couche adhésive et véhicule comprenant un tel stratifié en verre WO2014084725A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
NL2009706 2012-10-26
NL2009706A NL2009706C2 (nl) 2012-10-26 2012-10-26 Glaslaminaat, hechtlaag, en voertuig omvattende een dergelijk glaslaminaat.

Publications (1)

Publication Number Publication Date
WO2014084725A1 true WO2014084725A1 (fr) 2014-06-05

Family

ID=47722495

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/NL2013/050757 WO2014084725A1 (fr) 2012-10-26 2013-10-28 Stratifié en verre, couche adhésive et véhicule comprenant un tel stratifié en verre

Country Status (2)

Country Link
NL (1) NL2009706C2 (fr)
WO (1) WO2014084725A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014168481A1 (fr) * 2013-04-11 2014-10-16 Aviation Glass & Technology B.V. Miroir de véhicule, et procédé de fabrication d'un tel miroir
WO2016113669A1 (fr) * 2015-01-13 2016-07-21 Driessen Aerospace Group N.V. Surfaces en verre pour utilisation dans des avions et autres véhicules
WO2017196171A1 (fr) * 2016-05-10 2017-11-16 Aviation Glass & Technology Holding B.V. Panneau d'aéronef, en particulier une fenêtre de cabine, et procédé de fabrication d'un tel panneau d'aéronef
JP2017214749A (ja) * 2016-05-31 2017-12-07 三和シヤッター工業株式会社 ドア装置
EP3235636A4 (fr) * 2014-12-19 2018-08-22 Nippon Electric Glass Co., Ltd. Stratifié de verre et de résine
CN112616312A (zh) * 2019-07-26 2021-04-06 法国圣戈班玻璃厂 低阻力轻质飞行器窗

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2223275A1 (de) * 1971-05-21 1972-12-07 Glaverbel Verfahren zum Schuetzen von Gegenstaenden aus Glas
US20080199690A1 (en) * 2007-02-15 2008-08-21 E. I. Du Pont De Nemours And Company Articles comprising high melt flow ionomeric compositions
WO2010036219A1 (fr) * 2008-09-25 2010-04-01 Agp Plastics, Inc. Fenêtres anti-écaillage
DE102009058136A1 (de) * 2009-12-12 2011-06-16 Daimler Ag Abgedichtete Substratschichtverbundscheibe
WO2011142441A1 (fr) * 2010-05-13 2011-11-17 三井・デュポンポリケミカル株式会社 Matériau multicouche, matériau d'étanchéité pour cellule solaire, couche intermédiaire pour verre (stratifié) de sécurité, module de cellule solaire, et verre de sécurité (stratifié)

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2223275A1 (de) * 1971-05-21 1972-12-07 Glaverbel Verfahren zum Schuetzen von Gegenstaenden aus Glas
US20080199690A1 (en) * 2007-02-15 2008-08-21 E. I. Du Pont De Nemours And Company Articles comprising high melt flow ionomeric compositions
WO2010036219A1 (fr) * 2008-09-25 2010-04-01 Agp Plastics, Inc. Fenêtres anti-écaillage
DE102009058136A1 (de) * 2009-12-12 2011-06-16 Daimler Ag Abgedichtete Substratschichtverbundscheibe
WO2011142441A1 (fr) * 2010-05-13 2011-11-17 三井・デュポンポリケミカル株式会社 Matériau multicouche, matériau d'étanchéité pour cellule solaire, couche intermédiaire pour verre (stratifié) de sécurité, module de cellule solaire, et verre de sécurité (stratifié)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014168481A1 (fr) * 2013-04-11 2014-10-16 Aviation Glass & Technology B.V. Miroir de véhicule, et procédé de fabrication d'un tel miroir
EP3235636A4 (fr) * 2014-12-19 2018-08-22 Nippon Electric Glass Co., Ltd. Stratifié de verre et de résine
WO2016113669A1 (fr) * 2015-01-13 2016-07-21 Driessen Aerospace Group N.V. Surfaces en verre pour utilisation dans des avions et autres véhicules
US20160221307A1 (en) * 2015-01-13 2016-08-04 Driessen Aerospace Group N.V. Glass surfaces for use in aircraft and other vehicles
WO2017196171A1 (fr) * 2016-05-10 2017-11-16 Aviation Glass & Technology Holding B.V. Panneau d'aéronef, en particulier une fenêtre de cabine, et procédé de fabrication d'un tel panneau d'aéronef
JP2017214749A (ja) * 2016-05-31 2017-12-07 三和シヤッター工業株式会社 ドア装置
CN112616312A (zh) * 2019-07-26 2021-04-06 法国圣戈班玻璃厂 低阻力轻质飞行器窗

Also Published As

Publication number Publication date
NL2009706C2 (nl) 2014-04-29

Similar Documents

Publication Publication Date Title
WO2014084725A1 (fr) Stratifié en verre, couche adhésive et véhicule comprenant un tel stratifié en verre
KR101870545B1 (ko) 하나 이상의 화학적으로 템퍼링된 판유리를 갖는 적층된 유리
JP5809132B2 (ja) 透明積層ガラスおよびその使用法
JP6186675B2 (ja) ガラス樹脂積層体
JP6337898B2 (ja) 複層ガラス
NL2010625C2 (nl) Spiegel, en werkwijze ter vervaardiging van een dergelijke spiegel.
JP6720984B2 (ja) 合わせガラス
MX2010014208A (es) Cristales de seguridad transparentes livianos.
EP2988931A1 (fr) Structures en verre stratifié présentant une forte adhérence entre le verre et la couche intermédiaire de polymère
WO1999058334A3 (fr) Lamines de verre pour systemes de fenetres de protection
KR20150022989A (ko) 높은 유리 대 중합체 중간층 접착력을 갖는 적층 유리 구조
JP6874764B2 (ja) 合わせガラス
CN112105500B (zh) 层叠玻璃件
WO2017094884A1 (fr) Verre feuilleté pour véhicules
WO2018084041A1 (fr) Verre feuilleté
KR20160060114A (ko) 중합체 판유리 및 유리 판유리로 구성된 복합 판유리
EP2743080B1 (fr) Film transparent multicouche et son procédé de fabrication
JP2017114029A (ja) 透明樹脂積層体
IL293150A (en) Laminated glazing for light aircraft, heating over part of its surface
WO2017196171A1 (fr) Panneau d'aéronef, en particulier une fenêtre de cabine, et procédé de fabrication d'un tel panneau d'aéronef
NL2009705C2 (nl) Glaslaminaat en voertuig omvattende een dergelijk glaslaminaat.
WO2020083669A1 (fr) Ensemble stratifié

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13786550

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13786550

Country of ref document: EP

Kind code of ref document: A1