Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K3/00—Materials not provided for elsewhere
  • C09K3/18—Materials not provided for elsewhere for application to surfaces to minimize adherence of ice, mist or water thereto; Thawing or antifreeze materials for application to surfaces
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05C—APPARATUS FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05C1/00—Apparatus in which liquid or other fluent material is applied to the surface of the work by contact with a member carrying the liquid or other fluent material, e.g. a porous member loaded with a liquid to be applied as a coating
  • B05C1/02—Apparatus in which liquid or other fluent material is applied to the surface of the work by contact with a member carrying the liquid or other fluent material, e.g. a porous member loaded with a liquid to be applied as a coating for applying liquid or other fluent material to separate articles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
  • B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
  • B05D7/02—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials to macromolecular substances, e.g. rubber
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60S—SERVICING, CLEANING, REPAIRING, SUPPORTING, LIFTING, OR MANOEUVRING OF VEHICLES, NOT OTHERWISE PROVIDED FOR
  • B60S1/00—Cleaning of vehicles
  • B60S1/02—Cleaning windscreens, windows or optical devices
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60S—SERVICING, CLEANING, REPAIRING, SUPPORTING, LIFTING, OR MANOEUVRING OF VEHICLES, NOT OTHERWISE PROVIDED FOR
  • B60S1/00—Cleaning of vehicles
  • B60S1/02—Cleaning windscreens, windows or optical devices
  • B60S1/04—Wipers or the like, e.g. scrapers
  • B60S1/32—Wipers or the like, e.g. scrapers characterised by constructional features of wiper blade arms or blades
  • B60S1/38—Wiper blades
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
  • C03C17/28—Surface treatment of glass, not in the form of fibres or filaments, by coating with organic material
  • C03C17/30—Surface treatment of glass, not in the form of fibres or filaments, by coating with organic material with silicon-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M169/00—Lubricating compositions characterised by containing as components a mixture of at least two types of ingredient selected from base-materials, thickeners or additives, covered by the preceding groups, each of these compounds being essential
  • C10M169/04—Mixtures of base-materials and additives
  • C10M169/044—Mixtures of base-materials and additives the additives being a mixture of non-macromolecular and macromolecular compounds
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60S—SERVICING, CLEANING, REPAIRING, SUPPORTING, LIFTING, OR MANOEUVRING OF VEHICLES, NOT OTHERWISE PROVIDED FOR
  • B60S1/00—Cleaning of vehicles
  • B60S1/02—Cleaning windscreens, windows or optical devices
  • B60S1/04—Wipers or the like, e.g. scrapers
  • B60S1/32—Wipers or the like, e.g. scrapers characterised by constructional features of wiper blade arms or blades
  • B60S1/38—Wiper blades
  • B60S2001/3827—Wiper blades characterised by the squeegee or blade rubber or wiping element
  • B60S2001/3829—Wiper blades characterised by the squeegee or blade rubber or wiping element characterised by the material of the squeegee or coating thereof
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2217/00—Coatings on glass
  • C03C2217/70—Properties of coatings
  • C03C2217/76—Hydrophobic and oleophobic coatings
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2218/00—Methods for coating glass
  • C03C2218/10—Deposition methods
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
  • C10M2201/04—Elements
  • C10M2201/041—Carbon; Graphite; Carbon black
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
  • C10M2201/06—Metal compounds
  • C10M2201/061—Carbides; Hydrides; Nitrides
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
  • C10M2201/06—Metal compounds
  • C10M2201/065—Sulfides; Selenides; Tellurides
  • C10M2201/066—Molybdenum sulfide
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
  • C10M2201/087—Boron oxides, acids or salts
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2213/00—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2213/00—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions
  • C10M2213/003—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions used as base material
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2213/00—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions
  • C10M2213/06—Perfluoro polymers
  • C10M2213/062—Polytetrafluoroethylene [PTFE]
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2229/00—Organic macromolecular compounds containing atoms of elements not provided for in groups C10M2205/00, C10M2209/00, C10M2213/00, C10M2217/00, C10M2221/00 or C10M2225/00 as ingredients in lubricant compositions
  • C10M2229/02—Unspecified siloxanes; Silicones
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2229/00—Organic macromolecular compounds containing atoms of elements not provided for in groups C10M2205/00, C10M2209/00, C10M2213/00, C10M2217/00, C10M2221/00 or C10M2225/00 as ingredients in lubricant compositions
  • C10M2229/04—Siloxanes with specific structure
  • C10M2229/041—Siloxanes with specific structure containing aliphatic substituents
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2229/00—Organic macromolecular compounds containing atoms of elements not provided for in groups C10M2205/00, C10M2209/00, C10M2213/00, C10M2217/00, C10M2221/00 or C10M2225/00 as ingredients in lubricant compositions
  • C10M2229/04—Siloxanes with specific structure
  • C10M2229/041—Siloxanes with specific structure containing aliphatic substituents
  • C10M2229/0415—Siloxanes with specific structure containing aliphatic substituents used as base material
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2229/00—Organic macromolecular compounds containing atoms of elements not provided for in groups C10M2205/00, C10M2209/00, C10M2213/00, C10M2217/00, C10M2221/00 or C10M2225/00 as ingredients in lubricant compositions
  • C10M2229/04—Siloxanes with specific structure
  • C10M2229/047—Siloxanes with specific structure containing alkylene oxide groups
  • C10M2229/0475—Siloxanes with specific structure containing alkylene oxide groups used as base material
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2020/00—Specified physical or chemical properties or characteristics, i.e. function, of component of lubricating compositions
  • C10N2020/01—Physico-chemical properties
  • C10N2020/02—Viscosity; Viscosity index
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2020/00—Specified physical or chemical properties or characteristics, i.e. function, of component of lubricating compositions
  • C10N2020/01—Physico-chemical properties
  • C10N2020/055—Particles related characteristics
  • C10N2020/06—Particles of special shape or size
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
  • C10N2030/26—Waterproofing or water resistance
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
  • C10N2030/40—Low content or no content compositions
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2050/00—Form in which the lubricant is applied to the material being lubricated
  • C10N2050/015—Dispersions of solid lubricants
  • C10N2050/02—Dispersions of solid lubricants dissolved or suspended in a carrier which subsequently evaporates to leave a lubricant coating

Definitions

• the present invention in general relates to a hydrophobic coating composition and in particular to a wiper blade imparting a hydrophobic film to a contacted window through wiper usage.
• hydrophobic glass treatment solutions have been applied to automotive windshields to improve driver vision under high humidity conditions of rain, sleet, or snow.
• Representative of such glass treatments are those detailed in U.S. Patents 3,579,540, 5,688,864, 6,432,181. While such glass treatments are effective in rendering the windshield hydrophobic so as to cause water to bead and not form windshield water film, these products have met with limited acceptance owing to the labor-intensive application, and somewhat toxic chemicals needed to be handled to create a hydrophobic windshield surface. Additionally, the application of such hydrophobic glass treatments while a windshield is being subjected to rain or other precipitation is impractical.
• coating compositions have been developed for a wiper blade that include a silicone wax, a silicone oil in a solid lubricant such that the wax dissolves in the silicone oil such that during operation of the wiper blade, components of the coating layer are transferred onto a contacting windshield through the friction of the wiper blade against the windshield.
• a composition is detailed in U.S. 2010/0234489. While such a coated wiper blade is effective in delivering a hydrophobic coating to a windshield upon wiper blade installation, the ability of the coating to be transferred to the windshield is rapidly degraded to the point where the ability to transfer coating components to a windshield significantly diminish in the time between wiper production and the actual installation of the blade on a vehicle. Additionally, the coatings imparted to a windshield tend to be irregular and create a mottled hydrophobicity.
• a coating composition suitable for application to an applicator, such as a wiper blade includes a silicone oil or mixture of silicone oils having an overall viscosity ranging from 2 square millimeters per second (mm 2 /s) to one million (mm 2 /s) at 25° C, a silicone resin, and a dry lubricant with a particle size of smaller than 100 microns.
• a solvent distinct from the silicone oil is present to help dissolve the silicone oil and the silicone resin to form a solution.
• a dry lubricant or mixture of dry solid lubricants is added to the solution to form a wiper blade coating composition, a hydrophobic film to a contacted windshield.
• the coating composition is stable and a wiper blade squeegee coated with such a composition is able to impart a hydrophobic film to the windshield even after storage for several weeks or months at elevated temperature.
• the coating composition is also provided that excludes silicone waxes and agents for crosslinking of the silicone oil.
• An improved coating composition for the application of a hydrophobic film to the contacted target surface is provided with the coating composition suitable for application to a wiper blade, the improved coating composition includes a silicone oil, a silicone resin and a dry lubricant wherein the improvement lies in being dissolved in the case of the silicone oil and the silicone resin, and suspended in the case of the dry lubricant in a solvent. It is appreciated that a more environmentally friendly option is to limit the use of, or even exclude a solvent with the silicone oil also functioning as a carrier.
• a kit is also provided that includes an applicator, the above coating composition, along with instructions for imparting a hydrophobic film to a target substrate such as windshield of a vehicle contacted by a wiper blade applicator.
• a process of activating a windshield includes contacting the windshield with a wiper blade coated with the coating composition.
• a water repellency of more than 60 degrees of water contact angle is achieved within 2000 wipe cycles.
• Fig. 1 is a plot of water contact angle in degrees as a function of wiper blade wipe cycles on automotive windshield glass for inventive compositions under various storage and application conditions;
• Fig. 2 is a plot of water contact angle in degrees as a function of wipe cycles for various commercially available water repellency wiper blades where reduced contact angle is consistently noted relative to the inventive compositions of Fig. 1.
• the present invention has utility as a vehicle windshield wiper having a coating that imparts a hydrophobic film to the contacted glass surface. While the present invention is largely detailed with respect to windshields, it is appreciated that other suitable target surfaces of usage for the present invention illustratively include manual squeegees, vehicle rear windows, aircraft exterior surfaces, and other exterior surfaces where water repellency is desired.
• the present invention has the attribute of long term storage stability coupled with the ability to even after storage, impart a hydrophobic film to a contacted surface.
• inventive coating composition is readily applied to a surface on which a hydrophobic film is desired with resort to other applicators illustratively including a buffing pad or cloth.
• An inventive coating composition includes a silicone oil that is liquid at 20°C. It is appreciated that a silicone oil operative herein readily includes a mixture of oils that vary in molecular weight, monomer subunits, or a combination thereof.
• a silicone oil operative in the present invention is a polydialkylsiloxane having a formula:
• R 1 and R 2 are in each occurrence independently H, C Qo alkyl, a substituent containing Q-Cio alkyl, C6-C 12 aryl, or a substituent containing C 6 -C 12 aryl; and M is an integer value of from 2 to 2230.
• a substituent is an alkyl or aryl in which a proton thereon is replaced with a moiety illustratively including hydroxyl, amino, fluorine, or vinyl,.
• Perfluoro silicone oils are also explicitly noted as being operative in an inventive coating composition.
• a silicone oil component is chosen to have a viscosity of from between 2 and 1,000,000 mm /s at 25°C and a surface tension of less than 30 dynes per centimeter (dynes/cm).
• a silicone oil is typically present in certain embodiments from 1 to 95 total weight percent of a coating composition and in still other embodiments from 10 to 60 total weight percent of an inventive coating composition.
• An exemplary oil component of an inventive coating composition includes a silicone oil.
• silicone oils operative herein illustratively include polydimethylsiloxane, decamethylcyclopentasiloxane, methylphenylpolysiloxane, methylhydrogenpolysiloxane, amino-functional polydimethylsiloxane, octamethyltrisiloxane, decamethyltetrasiloxane, carboxyl-functional polydimethylsiloxane, carbinol-functional polydimethylsiloxane, phenol-functional polydimethylsiloxane, fluoro-functional polydimethylsiloxane, epoxy-functional polydimethylsiloxane, alkyl-functional polydimethylsiloxane, polyether-functional polydimethylsiloxane, and combinations thereof.
• An inventive coating composition also includes a silicone resin soluble in a solvent along with the oil component or in the silicone oil component alone.
• a silicone resin is chosen such that upon being applied to a substrate promotes formation of a hydrophobic film thereon.
• Resins operative herein illustratively include a resin component of an inventive coating composition illustratively includes a , silicone-modified urethane resin, , silicone-modified epoxy resin, silicone resin, perfluoro- silicone resin, a partially fluorinated silicone resin, C -C alkyl- modified silicone resin, phenyl-modified silicone resin, , silicone-modified acrylic resin, and combinations thereoflt is appreciated that high lubricity and hydrophobicity are desirable characteristics of a resin or resin combination in an inventive coating composition. Equally important, the chosen resin is highly soluble in the silicone oil.
• the resin is a silicone resin. It should be appreciated that a combination of resins that vary in molecular weight, chemical structure, or a combination thereof are also operative herein.
• a resin is typically present in an inventive composition in an amount of from 0 to 80 total weight percent while in other embodiments of the present invention, the resin is present from 2 to 40 total weight percent.
• An inventive coating composition includes a solvent or a combination of solvents capable of forming a solution with a silicone oil and resin components of an inventive coating composition.
• the solvents operative herein illustratively include solvents suitable for dissolution of the silicone oil and resin operative illustratively include methylethylketone C Cg alkyl lactates, toluene, xylene, Q-Cg alkyl benzenes, Q-Cg alkyl acetates, C 2 -Cg alcohols, as well as combinations thereof.
• alkyl is used herein is intended to include linear, branched, and cyclic forms thereof.
• the nature of the solvent as operative herein is largely limited only to the ability to dissolve the silicone oil and the resin components.
• solvent evaporation to form a nonvolatile form as a layer adhered to the applicator in such embodiments the solvent is amenable to capture and in specific embodiments to recycle.
• Still another embodiment of an inventive coating composition contains no solvent; and thhe silicone oil alone is capable of forming a solution with the silicone resin component.
• An inventive coating composition also includes a particulate lubricant.
• a particulate lubricant according to the present invention is either applied separately to an applicator or as a colloidal dispersion in the solvent along with the resin and silicone oil components or in the silicone oil-silicone resin mixture without a solvent.
• the particulate lubricant in certain embodiments of the present invention has greater than 90 particle number percent of the particulate having a particle size smaller than 100 microns as determined by size guide number (SGN). In still other embodiments of the present invention, 100 particle number percent are smaller than 100 microns. In still other embodiments of the present invention, the particulate has a mean particle size smaller than 50 microns.
• a coating composition in solvated form is 0.5 to 30 total weight percent particulate lubricant and from 1 to 60 weight percent after the composition is dried to a nonvolatile form on an applicator or if no solvent is used.
• a particulate lubricant operative in the present invention illustratively includes graphite, turbostratic carbon, boron nitride, boric acid, polytetrafluoroethylene (PTFE), molybdenum disulfide (MoS 2 ), synthetic polymeric materials, and combinations thereof.
• An inventive coating composition has superior storage stability as a nonvolatile layer on an applicator such as a wiper blade through the exclusion of silicone waxes, as well as curing agents and/or curing catalysts operative to cross link the oil component.
• An inventive coating composition is applied to an applicator such as a wiper blade, cloth, or buffing pad and allowed to dry to a nonvolatile layer on the applicator.
• the layer coated applicator according to the present invention is amenable to storage for weeks or months even at extreme temperatures within the range of -50 to 120°C yet is still able to impart a hydrophobic film to a contacted surface. The resultant film imparts to the surface a water contact angle of more than 80° through simply rubbing the applicator against the target surface.
• nonvolatile coating composition layer is readily applied to an applicator such as a wiper blade, buffing pad, sponge, or cloth, through conventional techniques such as spray application, dip coating, or brush coating.
• the typical thickness of a nonvolatile layer of inventing coating composition on an applicator is between 2 and 500 microns although it should be appreciated that thicknesses of coating composition layer absent volatile solvent and other components are readily formed through repeated dosing of the applicator to achieve greater thickness layers or greater dilution of nonvolatile components within a solvent so as to achieve reduced thickness layers.
• the present invention also provides a kit for producing a hydrophobic film on a surface.
• the kit includes an applicator having a nonvolatile layer of the coating composition adhered to the applicator, or the coating composition in a separate bottle for user application to the applicator; along with instructions for contacting the coated applicator with the target surface to produce a hydrophobic film on the surface with a water droplet contact angle of greater than or equal to 80° with the contact angle being measured by ASTM C813.
• the kit in order to have a storage stability of greater than one month, and in certain embodiments more than three months, at an average temperature of between -50° and 120°C and lacks silicone waxes, as well as curing agents and/or curing catalysts operative to cross link the oil component that precluded the storage stabilities of the present invention.
• the kit includes a protective cover to limit physical contact between the applicator surface on which the nonvolatile layer of the coating composition is present from undesired transfer of the layer during handling, assembly, installation, shipping, storage, prior to contact with the target surface.
• a process for activating a windshield with a wiper blade applicator is achieved by wiping the windshield under wet, dry, or a combination of wet and dry conditions to a water repellency of more than 60 degrees of water contact angle within 2000 wipe cycles. In still other embodiments, this degree of water repellency is achieved while maintaining a wipe quality that is within 90% or greater of that for an uncoated wipe blade otherwise identical to said wiper blade while the water repellency on the wiped windshield surface remains. Wipe quality is typically graded from a scale of 1 to 10, as defined, for example, by Akron Rubber Development Laboratory (ARDL), Inc. [0024] An inventive composition formulation and nonvolatile layer formed therefrom are summarized in Table 1.
• Table 2 shows several exemplary inventive coating compositions with amounts in total solvated form weight percent.
• Example 2 65.0 10.0 10.0 5.0 5.0
• Example 3 70.0 20.0 5.0 5.0
• Example 4 65.0 10.0 10.0 5.0 5.0 5.0 2.0
• the coating compositions of the given examples are spray-coated on chloroprene rubber-natural rubber (CR-NR) blended squeegees and the coated squeegees are aged at various temperatures for various periods of time before WR activation test.
• the test results are shown in FIG. 1, where Curve 1 through Curve 5 are obtained for Example 1, Curve 6 for Example 2, Curve 7 for Example 3, and Curve 8 for Example 4.
• Curve 1 The coated squeegee is aged at room temperature for 37 days and at 50°C for 21 days.
• the windshield WR activation test is run under dry condition on a 2003 Honda Accord test buck.
• the average water CA on the windshield increased from below 30 degrees before activation to more than 80 degrees after 175 wipe cycles. There are 10 CA measurements across the wiped areas for each average CA data point.
• Curve 2 The coated squeegee is aged at room temperature for 37 days and at 50°C for 42 days.
• the windshield WR activation test is run under wet condition on a 2000 Ford Taurus test buck. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 3 The coated squeegee is aged at room temperature for 41 days and at 50°C for 180 days. The windshield WR activation test is run for 20 cycles under wet condition and then for 155 cycles under dry condition on a 2000 Ford Taurus test buck. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 4 The coated squeegee is aged at room temperature for 34 days and then is placed in a sedan's trunk for 244 days. The trunk's temperature during these 244 days fluctuated between no lower than -5 to about 60°C. The windshield WR activation test is run for 20 cycles under wet condition and then for 155 cycles under dry condition on a 2000 Ford Taurus test buck. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 5 The coated squeegee is aged at room temperature for 34 days and then is placed in a sedan's trunk for 244 days. The trunk's temperature during these 244 days fluctuated between no lower than -5 to about 60°C.
• the windshield WR activation test is run for 20 cycles under wet condition and then for 155 cycles under dry condition on a 2004 Toyota Camry test buck. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 6 The coated squeegee is aged at room temperature for 38 days and at 50°C for 144 days.
• the windshield WR activation test is run for 20 cycles under wet condition and then for 155 cycles under dry condition on a 2006 Nissan Altima test buck. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 7 The coated squeegee is aged at room temperature for 36 days and at 50°C for 132 days. Using a 2006 Nissan Altima test buck, the windshield WR activation test is run for 10 wet cycles followed by 10 dry cycles and this alternating wet-dry step is repeated 9 times. Similarly, the blade is able to activate the windshield quickly and fully.
• Curve 8 The coated squeegee is aged at room temperature for 13 days and at 50°C for 26 days. The windshield WR activation test is run for 20 cycles under wet condition and then followed by 155 cycles under dry condition on a 2003 Honda Accord test buck. Similarly, the blade is able to activate the windshield quickly and fully. [0037] COMPARATIVE EXAMPLES
• Patents and publications mention the specification are indicative of the levels of those skilled in the art to which the invention pertains. These patents and publications are incorporated herein by reference to the same extent as if each individual patent or publication is specifically and individually incorporated herein by reference.
• Numerical ranges cited herein are intended to recite not only the end values of such ranges but the individual values encompassed within the range and varying in single units of the last significant figure.
• a range of from 0.1 to 1.0 in arbitrary units according to the present invention also encompasses 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, and 0.9; each independently as lower and upper bounding values for the range.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Chemical & Material Sciences (AREA)
• Mechanical Engineering (AREA)
• Materials Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• Geochemistry & Mineralogy (AREA)
• Combustion & Propulsion (AREA)
• Wood Science & Technology (AREA)
• Paints Or Removers (AREA)
• Materials Applied To Surfaces To Minimize Adherence Of Mist Or Water (AREA)
• Application Of Or Painting With Fluid Materials (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (2)

Family

ID=49486674

Family Applications (1)

Country Status (7)

Families Citing this family (11)

Citations (4)

Family Cites Families (20)

• 2012
  • 2012-10-29 US US13/662,970 patent/US9540552B2/en active Active
• 2013
  • 2013-10-08 ES ES13783150T patent/ES2908973T3/es active Active
  • 2013-10-08 WO PCT/US2013/063863 patent/WO2014070388A2/en not_active Ceased
  • 2013-10-08 EP EP13783150.9A patent/EP2912152B1/en active Active
  • 2013-10-08 JP JP2015539626A patent/JP6329161B2/ja not_active Expired - Fee Related
  • 2013-10-08 CN CN201380056636.1A patent/CN104769088B/zh active Active
  • 2013-10-08 KR KR1020157010886A patent/KR102105121B1/ko active Active
• 2014
  • 2014-03-10 US US14/202,741 patent/US9637670B2/en active Active

Patent Citations (5)

Also Published As

Similar Documents

Legal Events