WO2013107840A1 - Procédé de fabrication de grains microscopiques contenant du graphène et matériau pouvant ainsi être obtenu - Google Patents

Procédé de fabrication de grains microscopiques contenant du graphène et matériau pouvant ainsi être obtenu Download PDF

Info

Publication number
WO2013107840A1
WO2013107840A1 PCT/EP2013/050889 EP2013050889W WO2013107840A1 WO 2013107840 A1 WO2013107840 A1 WO 2013107840A1 EP 2013050889 W EP2013050889 W EP 2013050889W WO 2013107840 A1 WO2013107840 A1 WO 2013107840A1
Authority
WO
WIPO (PCT)
Prior art keywords
graphene
granular
vol
metal
copper
Prior art date
Application number
PCT/EP2013/050889
Other languages
English (en)
Inventor
Wlodzimierz Strupinski
Original Assignee
Isos Technologies Sarl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from PL397832A external-priority patent/PL397832A1/pl
Priority claimed from PL397831A external-priority patent/PL397831A1/pl
Application filed by Isos Technologies Sarl filed Critical Isos Technologies Sarl
Publication of WO2013107840A1 publication Critical patent/WO2013107840A1/fr

Abstract

Cette invention concerne un procédé de fabrication de grains microscopiques contenant du graphène, caractérisé en ce qu'il comprend les étapes suivantes : a) un granulat métallique ou de type alliage métallique, de préférence un cuivre granulaire, un nickel granulaire ou un aluminium granulaire, ayant une taille de grain entre 0,1 pm et 1 000 µm, de préférence entre 1 et 6 µm, est chauffé jusqu'à une température entre 600 et 1 040 °C, de préférence entre 920 et 1 040 °C, et est maintenu à cette température pendant 2 à 30 minutes, de préférence pendant 2 à 20 minutes, dans une atmosphère comprenant de l'argon et du propane, éventuellement avec ajout d'hydrogène et/ou d'azote, b) le matériau obtenu à l'issue de l'étape a) est refroidi jusqu'à la température ambiante, de préférence dans une atmosphère d'argon, de préférence à une vitesse de refroidissement optimisée. Cette invention concerne également des grains microscopiques contenant du graphène pouvant être obtenus selon le procédé de l'invention, en particulier, une poudre de graphène ou des granules métalliques recouvertes de graphène.
PCT/EP2013/050889 2012-01-18 2013-01-18 Procédé de fabrication de grains microscopiques contenant du graphène et matériau pouvant ainsi être obtenu WO2013107840A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
PL397832A PL397832A1 (pl) 2012-01-18 2012-01-18 Sposób wytwarzania proszku grafenowego
PLP-397831 2012-01-18
PL397831A PL397831A1 (pl) 2012-01-18 2012-01-18 Sposób wytwarzania granulatu grafenowego
PLP-397832 2012-01-18

Publications (1)

Publication Number Publication Date
WO2013107840A1 true WO2013107840A1 (fr) 2013-07-25

Family

ID=47710094

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2013/050889 WO2013107840A1 (fr) 2012-01-18 2013-01-18 Procédé de fabrication de grains microscopiques contenant du graphène et matériau pouvant ainsi être obtenu

Country Status (1)

Country Link
WO (1) WO2013107840A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017505748A (ja) * 2014-01-17 2017-02-23 シェンジェン カントンネット エナジー サービシーズ カンパニー リミテッド 還元型酸化グラフェンの修復方法
CN110225882A (zh) * 2016-12-06 2019-09-10 塔塔钢铁有限公司 一种制备石墨烯的工艺、一种石墨烯及其基材
CN110922742A (zh) * 2019-10-31 2020-03-27 深圳市超导新材料有限公司 一种新型透明导电膜及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2055673A1 (fr) * 2007-10-29 2009-05-06 Samsung Electronics Co., Ltd. Graphène et son procédé de préparation
US20090155161A1 (en) * 2007-12-17 2009-06-18 Samsung Electronics Co., Ltd. Method of preparing graphene shell and graphene shell prepared using the method
WO2009129194A2 (fr) * 2008-04-14 2009-10-22 Massachusetts Institute Of Technology Graphène à un plan et à nombre limité de plans de grande surface sur des substrats arbitraires
WO2011141486A1 (fr) * 2010-05-14 2011-11-17 Basf Se Procédé pour encapsuler des métaux et oxydes métalliques avec du graphène et l'utilisation de ces matériaux

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2055673A1 (fr) * 2007-10-29 2009-05-06 Samsung Electronics Co., Ltd. Graphène et son procédé de préparation
US20090155161A1 (en) * 2007-12-17 2009-06-18 Samsung Electronics Co., Ltd. Method of preparing graphene shell and graphene shell prepared using the method
WO2009129194A2 (fr) * 2008-04-14 2009-10-22 Massachusetts Institute Of Technology Graphène à un plan et à nombre limité de plans de grande surface sur des substrats arbitraires
WO2011141486A1 (fr) * 2010-05-14 2011-11-17 Basf Se Procédé pour encapsuler des métaux et oxydes métalliques avec du graphène et l'utilisation de ces matériaux

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
CHEN Z ET AL: "Bulk growth of mono- to few-layer graphene on nickel particles by chemical vapor deposition from methane", CARBON, ELSEVIER, OXFORD, GB, vol. 48, no. 12, 31 May 2010 (2010-05-31), pages 3543 - 3550, XP027142630, ISSN: 0008-6223, [retrieved on 20100714] *
SHILIANG WANG ET AL: "Synthesis, growth mechanism and thermal stability of copper nanoparticles encapsulated by multi-layer graphene", CARBON, ELSEVIER, OXFORD, GB, vol. 50, no. 6, 21 December 2011 (2011-12-21), pages 2119 - 2125, XP028403525, ISSN: 0008-6223, [retrieved on 20120112], DOI: 10.1016/J.CARBON.2011.12.063 *
SHUMIN WANG ET AL: "Controllable synthesis of a novel hedgehog-like core/shell structure", JOURNAL OF SOLID STATE CHEMISTRY, ORLANDO, FL, US, vol. 186, 14 December 2011 (2011-12-14), pages 235 - 239, XP028448032, ISSN: 0022-4596, [retrieved on 20111222], DOI: 10.1016/J.JSSC.2011.12.019 *
TOMO-O TERASAWA ET AL: "Growth of graphene on Cu by plasma enhanced chemical vapor deposition", CARBON, ELSEVIER, OXFORD, GB, vol. 50, no. 3, 24 September 2011 (2011-09-24), pages 869 - 874, XP028343562, ISSN: 0008-6223, [retrieved on 20111001], DOI: 10.1016/J.CARBON.2011.09.047 *
VIRENDRA SINGH ET AL: "Graphene based materials: Past, present and future", PROGRESS IN MATERIALS SCIENCE, PERGAMON PRESS, GB, vol. 56, no. 8, 30 March 2011 (2011-03-30), pages 1178 - 1271, XP028375493, ISSN: 0079-6425, [retrieved on 20110403], DOI: 10.1016/J.PMATSCI.2011.03.003 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017505748A (ja) * 2014-01-17 2017-02-23 シェンジェン カントンネット エナジー サービシーズ カンパニー リミテッド 還元型酸化グラフェンの修復方法
CN110225882A (zh) * 2016-12-06 2019-09-10 塔塔钢铁有限公司 一种制备石墨烯的工艺、一种石墨烯及其基材
CN110922742A (zh) * 2019-10-31 2020-03-27 深圳市超导新材料有限公司 一种新型透明导电膜及其制备方法

Similar Documents

Publication Publication Date Title
Vlassiouk et al. Large scale atmospheric pressure chemical vapor deposition of graphene
Wu et al. A review of graphene synthesis by indirect and direct deposition methods
Urade et al. Graphene properties, synthesis and applications: a review
Liu et al. 2D metals by repeated size reduction
Zheng et al. Plasma‐assisted approaches in inorganic nanostructure fabrication
Pingale et al. Facile synthesis of graphene by ultrasonic-assisted electrochemical exfoliation of graphite
JP5048873B2 (ja) 炭素質材料の製造方法及び薄片化黒鉛の製造方法
Kamali et al. Towards large scale preparation of carbon nanostructures in molten LiCl
Wang et al. Formation of CuO nanowires by thermal annealing copper film deposited on Ti/Si substrate
KR101701369B1 (ko) 탄소가 포함된 액체상의 전구체를 이용한 연속 롤투롤 방식의 고품질 그래핀 제조방법과 그 제조장치
KR101438027B1 (ko) 아크 방전을 이용한 고품질 그래핀 제조 방법 및 이를 이용한 고품질 그래핀
KR101294223B1 (ko) 대면적 그래핀 필름의 제조방법
Zhou et al. Low-temperature Ni particle-templated chemical vapor deposition growth of curved graphene for supercapacitor applications
Kahng et al. A study of graphene films synthesized on nickel substrates: existence and origin of small-base-area peaks
Okigawa et al. Electrical properties and domain sizes of graphene films synthesized by microwave plasma treatment under a low carbon concentration
WO2013107840A1 (fr) Procédé de fabrication de grains microscopiques contenant du graphène et matériau pouvant ainsi être obtenu
KR101573241B1 (ko) 3차원 그래핀 구조체 및 이를 이용한 전극 제조방법
Ali et al. Synthesis and characterization of high-quality multi layered graphene by electrochemical exfoliation of graphite
Xiaoli A review: the method for synthesis MoS 2 monolayer
CN111886200B (zh) 碳基复合材料
Huang et al. Growth of nanotwinned Cu nanowires in modified anodic aluminum oxide templates
An et al. A facile method for the synthesis of transfer-free graphene from co-deposited nickel–carbon layers
Dubosc et al. Impact of the Cu-based substrates and catalyst deposition techniques on carbon nanotube growth at low temperature by PECVD
KR20130024361A (ko) 자장여과 아크 소스 장치를 이용한 그래핀의 제조방법 및 이에 따라 제조되는 그래핀
Qian et al. Hybridization of conductive few-layer graphene with well-dispersed Pd nanocrystals

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13703740

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13703740

Country of ref document: EP

Kind code of ref document: A1