WO2013076032A1 - Chloridarme zusammensetzungen olefinisch funktionalisierter siloxanoligomere basierend auf alkoxysilanen - Google Patents
Chloridarme zusammensetzungen olefinisch funktionalisierter siloxanoligomere basierend auf alkoxysilanen Download PDFInfo
- Publication number
- WO2013076032A1 WO2013076032A1 PCT/EP2012/072964 EP2012072964W WO2013076032A1 WO 2013076032 A1 WO2013076032 A1 WO 2013076032A1 EP 2012072964 W EP2012072964 W EP 2012072964W WO 2013076032 A1 WO2013076032 A1 WO 2013076032A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- equal
- alcohol
- siloxane oligomers
- composition
- formula
- Prior art date
Abstract
Description
Claims