WO2012057358A1 - Film optique, procédé de fabrication, plaque de polarisation et dispositif d'affichage d'image - Google Patents

Film optique, procédé de fabrication, plaque de polarisation et dispositif d'affichage d'image Download PDF

Info

Publication number
WO2012057358A1
WO2012057358A1 PCT/JP2011/075233 JP2011075233W WO2012057358A1 WO 2012057358 A1 WO2012057358 A1 WO 2012057358A1 JP 2011075233 W JP2011075233 W JP 2011075233W WO 2012057358 A1 WO2012057358 A1 WO 2012057358A1
Authority
WO
WIPO (PCT)
Prior art keywords
optical film
fine particle
containing layer
layer
fine
Prior art date
Application number
PCT/JP2011/075233
Other languages
English (en)
Japanese (ja)
Inventor
昌 神崎
篤志 金澤
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Publication of WO2012057358A1 publication Critical patent/WO2012057358A1/fr

Abstract

L'invention concerne un film optique qui comprend un film d'un matériau de base (101), et une couche contenant des particules fines (102) qui est formée sur le film de matériau de base et qui se compose d'un liquide à base de résine contenant des particules fines (104). Le rapport entre les particules fines (particules grossières), qui ont chacune un diamètre plus important que l'épaisseur moyenne (h) de la couche contenant des particules fines (102), et toutes les particules fines (104) contenues dans le liquide à base de résine est de 2% ou moins, et la surface de la couche contenant des particules fines (102) possède une forme obtenue en pressant la surface d'un moule contre celle-ci. L'invention concerne également une plaque de polarisation sur laquelle est appliqué le film optique, et un dispositif d'affichage d'image. La génération d'un défaut protubérant dû aux particules grossières peut être suffisamment supprimée ou éliminée sans augmenter l'épaisseur de la couche contenant des particules fines, et l'invention concerne également un film optique comprenant la couche contenant des particules fines, ayant une excellente uniformité de surface, ainsi qu'un procédé de fabrication du film optique de manière efficace et à faible coût.
PCT/JP2011/075233 2010-10-29 2011-10-26 Film optique, procédé de fabrication, plaque de polarisation et dispositif d'affichage d'image WO2012057358A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010-243980 2010-10-29
JP2010243980A JP2012098368A (ja) 2010-10-29 2010-10-29 光学フィルムおよびその製造方法、偏光板、ならびに画像表示装置

Publications (1)

Publication Number Publication Date
WO2012057358A1 true WO2012057358A1 (fr) 2012-05-03

Family

ID=45994058

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/075233 WO2012057358A1 (fr) 2010-10-29 2011-10-26 Film optique, procédé de fabrication, plaque de polarisation et dispositif d'affichage d'image

Country Status (3)

Country Link
JP (1) JP2012098368A (fr)
TW (1) TW201232055A (fr)
WO (1) WO2012057358A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200166677A1 (en) * 2017-08-04 2020-05-28 Daicel Corporation Antiglare film

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000258613A (ja) * 1999-03-10 2000-09-22 Dainippon Printing Co Ltd 防眩シート、表示装置及び防眩シートの製造方法
JP2002328615A (ja) * 2001-04-27 2002-11-15 Noritake Arai 表示機器の表面構造、情報表示機器の表示構造、および表示機器の表面構造の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000258613A (ja) * 1999-03-10 2000-09-22 Dainippon Printing Co Ltd 防眩シート、表示装置及び防眩シートの製造方法
JP2002328615A (ja) * 2001-04-27 2002-11-15 Noritake Arai 表示機器の表面構造、情報表示機器の表示構造、および表示機器の表面構造の製造方法

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200166677A1 (en) * 2017-08-04 2020-05-28 Daicel Corporation Antiglare film
US11976214B2 (en) * 2017-08-04 2024-05-07 Daicel Corporation Antiglare film

Also Published As

Publication number Publication date
JP2012098368A (ja) 2012-05-24
TW201232055A (en) 2012-08-01

Similar Documents

Publication Publication Date Title
JP5995412B2 (ja) 光学フィルムの製造方法、偏光板および画像表示装置の製造方法
JP5889067B2 (ja) 光学フィルムの製造方法
WO2011027905A1 (fr) Film diffuseur de lumière et son procédé de fabrication, plaque de polarisation diffuseuse de lumière, et dispositif d'affichage à cristaux liquides
WO2011027903A1 (fr) Film diffuseur de lumière et son procédé de fabrication, plaque de polarisation diffuseuse de lumière, et dispositif d'affichage à cristaux liquides
JP5539830B2 (ja) ハードコートフィルムの製造方法
WO2012046790A1 (fr) Film de diffusion de lumière, son procédé de production, plaque de polarisation de diffusion de lumière et dispositif d'affichage à cristaux liquides
JP2012048223A (ja) 光拡散フィルムおよびその製造方法、光拡散性偏光板、ならびに液晶表示装置
WO2012060457A1 (fr) Film de diffusion de lumière, procédé pour fabriquer le film de diffusion de lumière, plaque de polarisation diffusant la lumière et dispositif d'affichage à cristaux liquides
WO2012067046A1 (fr) Film de dispersion de la lumière, plaque de polarisation et dispositif d'affichage d'image
JP2012224735A (ja) 樹脂組成物、光学フィルムおよび液晶表示装置
KR20160015162A (ko) 방현 필름
KR20160015160A (ko) 방현 필름
KR20160015161A (ko) 방현 필름
WO2015050274A1 (fr) Film antiéblouissant
JP2012226038A (ja) 光学フィルムの製造方法、偏光板および画像表示装置
KR101875244B1 (ko) 광학 필름의 제조 방법, 편광판 및 화상 표시 장치
WO2012057358A1 (fr) Film optique, procédé de fabrication, plaque de polarisation et dispositif d'affichage d'image
WO2012074123A1 (fr) Film optique et dispositif d'affichage à cristaux liquides
JP6125749B2 (ja) 光学フィルム、偏光板および画像表示装置
JP2013174638A (ja) 光学フィルムの製造方法、偏光板および画像表示装置
KR20120122919A (ko) 광학 필름의 제조 방법, 편광판 및 화상 표시 장치
JP2013186456A (ja) 光学フィルムの製造方法、および光学フィルム
JP2014132291A (ja) 光学フィルムの製造方法、偏光板、画像表示装置
JP2012078742A (ja) 塗工装置および光学フィルムの製造方法
WO2015050273A1 (fr) Film antiéblouissant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11836490

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11836490

Country of ref document: EP

Kind code of ref document: A1