WO2011074307A1 - Module de cellule solaire à couches minces organique - Google Patents

Module de cellule solaire à couches minces organique Download PDF

Info

Publication number
WO2011074307A1
WO2011074307A1 PCT/JP2010/066804 JP2010066804W WO2011074307A1 WO 2011074307 A1 WO2011074307 A1 WO 2011074307A1 JP 2010066804 W JP2010066804 W JP 2010066804W WO 2011074307 A1 WO2011074307 A1 WO 2011074307A1
Authority
WO
WIPO (PCT)
Prior art keywords
photoelectric conversion
layer
electrode
conversion layer
electrode layer
Prior art date
Application number
PCT/JP2010/066804
Other languages
English (en)
Japanese (ja)
Inventor
鈴木　裕行
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大日本印刷株式会社 filed Critical 大日本印刷株式会社
Publication of WO2011074307A1 publication Critical patent/WO2011074307A1/fr

Abstract

L'invention concerne un module de cellule solaire à couches minces organique, dans lequel une pluralité de cellules unitaires aménagées sous une forme planaire sont reliées en série, ledit module présentant une configuration simple et pouvant être fabriqué à l'aide d'un procédé simple. L'invention concerne spécifiquement un module de cellule solaire à couches minces organique dans lequel une pluralité de cellules unitaires aménagées sous une forme planaire sont reliées en série, ledit module étant caractérisé en ce que la cellule unitaire comprend une première couche d'électrode formée sur un substrat transparent, une couche de conversion photoélectrique formée sur la première couche d'électrode, et une seconde couche d'électrode formée sur la couche de conversion photoélectrique ; la couche de conversion photoélectrique de la cellule unitaire et la couche de conversion photoélectrique de l'autre cellule unitaire sont formées comme un film continu ; et une couche de blocage de lumière servant à bloquer l'application de lumière sur la couche de conversion photoélectrique est formée sur le substrat transparent, entre la première couche d'électrode de la cellule unitaire et la première couche d'électrode de l'autre cellule unitaire.
PCT/JP2010/066804 2009-12-14 2010-09-28 Module de cellule solaire à couches minces organique WO2011074307A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009283140A JP5060541B2 (ja) 2009-12-14 2009-12-14 有機薄膜太陽電池モジュール
JP2009-283140 2009-12-14

Publications (1)

Publication Number Publication Date
WO2011074307A1 true WO2011074307A1 (fr) 2011-06-23

Family

ID=44167073

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/066804 WO2011074307A1 (fr) 2009-12-14 2010-09-28 Module de cellule solaire à couches minces organique

Country Status (2)

Country Link
JP (1) JP5060541B2 (fr)
WO (1) WO2011074307A1 (fr)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5609537B2 (ja) * 2010-10-26 2014-10-22 住友化学株式会社 発電装置
JP6418515B2 (ja) * 2014-03-31 2018-11-07 イムラ・ジャパン株式会社 電極
KR101567265B1 (ko) 2014-12-30 2015-11-06 현대자동차주식회사 색상 튜닝이 가능한 태양전지
KR102226532B1 (ko) * 2020-10-20 2021-03-11 코리아스펙트랄프로덕츠(주) 입자 계수용 광학계

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62232176A (ja) * 1986-03-31 1987-10-12 Kyocera Corp 光起電力装置
JPS63114053U (fr) * 1987-01-20 1988-07-22
JP2006511073A (ja) * 2002-12-20 2006-03-30 ケンブリッジ ディスプレイ テクノロジー リミテッド 光学装置の電気接続
JP2006237165A (ja) * 2005-02-23 2006-09-07 Sharp Corp 有機太陽電池モジュール及びその製造方法

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5955079A (ja) * 1982-09-22 1984-03-29 Fuji Electric Corp Res & Dev Ltd 薄膜太陽電池
JPS625672A (ja) * 1985-07-02 1987-01-12 Ricoh Co Ltd 画像読取等倍センサ−
JPH0682548B2 (ja) * 1986-10-31 1994-10-19 キヤノン株式会社 電子機器
JPH03109355A (ja) * 1989-09-21 1991-05-09 Kyowa Hakko Kogyo Co Ltd ２，２，５，５―テトラメチルシクロペンタンカルボン酸誘導体の製造方法およびその中間体
JPH03276768A (ja) * 1990-03-27 1991-12-06 Taiyo Yuden Co Ltd 光起電力素子
JP2008097269A (ja) * 2006-10-11 2008-04-24 U-Tec Kk Ｉｃタグ

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62232176A (ja) * 1986-03-31 1987-10-12 Kyocera Corp 光起電力装置
JPS63114053U (fr) * 1987-01-20 1988-07-22
JP2006511073A (ja) * 2002-12-20 2006-03-30 ケンブリッジ ディスプレイ テクノロジー リミテッド 光学装置の電気接続
JP2006237165A (ja) * 2005-02-23 2006-09-07 Sharp Corp 有機太陽電池モジュール及びその製造方法

Also Published As

Publication number Publication date
JP2011124507A (ja) 2011-06-23
JP5060541B2 (ja) 2012-10-31

Similar Documents

Publication Publication Date Title
JP4985717B2 (ja) 有機薄膜太陽電池およびその製造方法
US20170243698A1 (en) Photoelectric conversion element
US20150287873A1 (en) Electro-optic device having nanowires interconnected into a network of nanowires
US9082711B2 (en) Organic solar cell module and organic solar cell panel
JP5326731B2 (ja) 有機薄膜太陽電池
US11756743B2 (en) Photoelectric conversion element
WO2010148024A1 (fr) Dispositifs optoélectroniques enroulés et procédés pour leur fabrication
US9401442B2 (en) Textured micrometer scale templates as light managing fabrication platform for organic solar cells
JP5573372B2 (ja) 有機薄膜太陽電池およびその製造方法
JP2011142217A (ja) 有機薄膜太陽電池
JP5060541B2 (ja) 有機薄膜太陽電池モジュール
TWI624939B (zh) 包含金屬奈米結構複合層之串聯式有機光伏打裝置
JP2011151195A (ja) 有機薄膜太陽電池およびその製造方法
WO2011074306A1 (fr) Module de cellule solaire à couches minces organique
JP2012009561A (ja) 有機薄膜太陽電池モジュール
JP2013089807A (ja) 有機薄膜太陽電池、有機薄膜太陽電池モジュール、および有機薄膜太陽電池の製造方法
JP2012023407A (ja) 有機薄膜太陽電池
KR20120054643A (ko) 유기 감광성 광전자 소자
JP2011124582A (ja) 有機薄膜太陽電池モジュール
US20220005871A1 (en) Photoelectric conversion device
JP2010141250A (ja) 有機薄膜太陽電池およびその製造方法
Kareem et al. Fabrication and characterization of ZnSCubic: P3HT, ZnSHexa: P3HT and ZnSHexa: P3HT: PVA-Ag bulk heterojunction solar cells
CN115004380A (zh) 亚半透明光伏器件及其制造方法
JP7092970B2 (ja) 光電変換素子
KR101567923B1 (ko) 유기태양전지 및 그 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10837337

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10837337

Country of ref document: EP

Kind code of ref document: A1