WO2011072110A1 - Article moulé pourvu d'une couche de décollage appliquée par le moule - Google Patents

Article moulé pourvu d'une couche de décollage appliquée par le moule Download PDF

Info

Publication number
WO2011072110A1
WO2011072110A1 PCT/US2010/059655 US2010059655W WO2011072110A1 WO 2011072110 A1 WO2011072110 A1 WO 2011072110A1 US 2010059655 W US2010059655 W US 2010059655W WO 2011072110 A1 WO2011072110 A1 WO 2011072110A1
Authority
WO
WIPO (PCT)
Prior art keywords
top coat
article
release coating
mold
polymer
Prior art date
Application number
PCT/US2010/059655
Other languages
English (en)
Inventor
Douglas E. Moon
Alan C. Kilbarger
Chad Michael Forsthoefel
Original Assignee
Illinois Tool Works, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Illinois Tool Works, Inc. filed Critical Illinois Tool Works, Inc.
Publication of WO2011072110A1 publication Critical patent/WO2011072110A1/fr

Abstract

La présente invention concerne un procédé de moulage d'article impliquant l'application d'une couche permanente de décollage sur la surface d'une cavité de moule. La couche de décollage permanente est recouverte d'une couche de finition lors du remplissage de la cavité de moule avec un polymère ou un précurseur de polymère dans des conditions permettant de former l'article, la couche de finition étant transférée sur l'article résultant de façon à former une peau de couche de finition sans enlever sensiblement la couche permanente de décollage de la surface de la cavité de moule. Les articles présentant des surfaces incurvées et des rapports d'aspect élevés sont particulièrement indiqués pour recevoir la peau de couche de finition selon ce procédé. On compose un matériau de couche de finition non saturé capable de réagir avec le polymère ou le précurseur de polymère pendant le moulage de façon à former une peau de couche de finition qui se lie par covalence au restant de l'article. Le procédé décrit en détail dans l'invention convient particulièrement bien à la formation de revêtements liés par covalence sur des articles élastomères. Cette peau de couche de finition se distingue par un coefficient de friction réduit, par une hydrophobicité modifiée, par une bonne résistance aux attaques par les solvants et autres agents chimiques, ainsi que par un blocage des modifications de résistance par rapport au même article de base non pourvu de la couche de finition. L'un des avantages de l'invention est d'éviter d'avoir à appliquer une couche de finition comparable après le moulage.
PCT/US2010/059655 2009-12-09 2010-12-09 Article moulé pourvu d'une couche de décollage appliquée par le moule WO2011072110A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US28505309P 2009-12-09 2009-12-09
US61/285,053 2009-12-09
US12/902,439 2010-10-12
US12/902,439 US20110136985A1 (en) 2009-12-09 2010-10-12 Molded article having a mold imparted release layer coating

Publications (1)

Publication Number Publication Date
WO2011072110A1 true WO2011072110A1 (fr) 2011-06-16

Family

ID=44082647

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/059655 WO2011072110A1 (fr) 2009-12-09 2010-12-09 Article moulé pourvu d'une couche de décollage appliquée par le moule

Country Status (2)

Country Link
US (1) US20110136985A1 (fr)
WO (1) WO2011072110A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015179311A1 (fr) * 2014-05-22 2015-11-26 Illinois Tool Works Inc. Agent de démoulage

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB201112447D0 (en) * 2011-07-20 2011-08-31 Surface Innovations Ltd Method
US8974218B2 (en) * 2012-04-26 2015-03-10 Nike, Inc. Mold plate and method of molding golf ball core
WO2023081342A1 (fr) * 2021-11-05 2023-05-11 Board Of Regents, The University Of Texas System Système, dispositif et procédé de détection tactile quadridimensionnelle
CN114474323A (zh) * 2022-01-06 2022-05-13 湖南临亚建材科技有限公司 一种装配式叠合板生产模具
CN114474325A (zh) * 2022-01-06 2022-05-13 湖南临亚建材科技有限公司 一种装配式墙板生产模具

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2604142A1 (de) * 1976-02-04 1977-08-11 Henkel & Cie Gmbh Vernetzte formkoerper mit lackierter oberflaeche aus vernetztem kunststoff und elastomeren
WO2002100928A1 (fr) * 2001-06-12 2002-12-19 North Carolina State University Revetements d'arret pour materiaux elastomeres
WO2008048565A1 (fr) * 2006-10-16 2008-04-24 E.I. Du Pont De Nemours And Company Composition de démoulage et procédé de production d'un article en polyuréthane prêt à peindre fabriqué par rotomoulage

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3231634A (en) * 1961-07-11 1966-01-25 Pittsburgh Plate Glass Co Mixture of unsaturated polyester resin and polymer of a conjugated diene
US4962178A (en) * 1988-11-03 1990-10-09 Ciba-Geigy Corporation Novel polysiloxane-polyurethanes and contact lens thereof
US5288560A (en) * 1991-01-30 1994-02-22 Daikyo Gomu Seiko, Ltd. Laminated sanitary rubber article
US5767185A (en) * 1993-11-08 1998-06-16 Specialty Silicone Products, Inc. Moldable and tintable silicone rubber composition for windshield wiper blade
IT1275972B1 (it) * 1995-03-24 1997-10-24 Ausimont Spa Dispersioni di politetrafluoroetilene in un solvente organico ed agenti disperdenti ivi impiegati
JPH106440A (ja) * 1996-06-19 1998-01-13 Toray Dow Corning Silicone Co Ltd シリコーンゲル成形物と剥離性フィルムからなる複合成形体およびその製造方法
US6040366A (en) * 1998-02-27 2000-03-21 General Electric Company Liquid injection molding silicone elastomers having primerless adhesion
US6294007B1 (en) * 1998-12-07 2001-09-25 Wacker Silicones Corporation Paintable organopolysiloxane mold release compositions and processes for their use
US6352609B1 (en) * 1999-07-12 2002-03-05 The Boeing Company Composite tooling process for curing materials at elevated temperatures
US6534184B2 (en) * 2001-02-26 2003-03-18 Kion Corporation Polysilazane/polysiloxane block copolymers
CN100402261C (zh) * 2002-08-01 2008-07-16 通用汽车公司 模具内涂饰加工用凝胶涂料组合物
US20080090060A1 (en) * 2003-06-20 2008-04-17 Gm Global Technology Operations, Inc. Low shrink low density laminate formulation
US20060147614A1 (en) * 2004-12-30 2006-07-06 3M Innovative Properties Company Transferable antireflection material for use on optical display

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2604142A1 (de) * 1976-02-04 1977-08-11 Henkel & Cie Gmbh Vernetzte formkoerper mit lackierter oberflaeche aus vernetztem kunststoff und elastomeren
WO2002100928A1 (fr) * 2001-06-12 2002-12-19 North Carolina State University Revetements d'arret pour materiaux elastomeres
WO2008048565A1 (fr) * 2006-10-16 2008-04-24 E.I. Du Pont De Nemours And Company Composition de démoulage et procédé de production d'un article en polyuréthane prêt à peindre fabriqué par rotomoulage

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015179311A1 (fr) * 2014-05-22 2015-11-26 Illinois Tool Works Inc. Agent de démoulage
US10113084B2 (en) 2014-05-22 2018-10-30 Illinois Tool Works, Inc. Mold release agent

Also Published As

Publication number Publication date
US20110136985A1 (en) 2011-06-09

Similar Documents

Publication Publication Date Title
US20110136985A1 (en) Molded article having a mold imparted release layer coating
Peng et al. Fabrication of microcavity-array superhydrophobic surfaces using an improved template method
US20190314838A1 (en) Spray application system components comprising a repellent surface and methods
AU760951B2 (en) Powder-free gloves with a silicone impregnated polyurethane inner coating
EP0146137B1 (fr) Procédé de moulage employant des revêtements en silicone cuisant à la température ambiante pour réaliser le démoulage multiple d'objets
US6887420B2 (en) Non-stick coated molds
US7517487B2 (en) Release agents comprising hydrophobic, nanoscalar particles, and the use of these mold release agents
AU2017257868B2 (en) Liquid reservoirs and articles comprising a repellent surface comprising a siloxane material
CA2372027A1 (fr) Composition de revetement aqueuse
US20050163951A1 (en) Device produced using an injection molding method and provided for storing liquids, and method for producing this device
EP0381209B1 (fr) Agent de démoulage pour moulage à poudre et procédé pour la préparation d'articles moulés avec utilisation de cet agent de démoulage
US20190002732A1 (en) Mold release agent
US20090030150A1 (en) Mold Release Agents Employing Polyvinyl Alcohol
Carreño et al. Synthesis and characterization of superhydrophobic surfaces prepared from silica and alumina nanoparticles on a polyurethane polymer matrix
US8092736B2 (en) Fluorotelomer/silane compositions
US20150045498A1 (en) Method for producing a surface - functionalised object
CN109622344A (zh) 医用功能涂层的涂装方法及应用
CN110802771A (zh) 一种注塑用脱模剂
WO2016060723A2 (fr) Surfaces durables superhydrophobes
CN111479860A (zh) 预处理由塑料制成的基材的方法
WO2017131682A1 (fr) Film composite auto-régénérant sur substrats
US20060258813A1 (en) Coating file forming method, coating material, releasing agent and rubber material
KR101426128B1 (ko) 아크릴 폴리올 수지 도료 조성물
DE2604142A1 (de) Vernetzte formkoerper mit lackierter oberflaeche aus vernetztem kunststoff und elastomeren
JP2010505634A5 (ja) 汚染した物体、汚染した物体をドライアイスで洗浄するための装置、汚染物を除去するための方法、及び機能皮膜の使用

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10793113

Country of ref document: EP

Kind code of ref document: A1

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10793113

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10793113

Country of ref document: EP

Kind code of ref document: A1