WO2011069663A2 - Revêtements protecteurs qui respectent l'environnement et destinés à des substrats - Google Patents

Revêtements protecteurs qui respectent l'environnement et destinés à des substrats Download PDF

Info

Publication number
WO2011069663A2
WO2011069663A2 PCT/EP2010/007521 EP2010007521W WO2011069663A2 WO 2011069663 A2 WO2011069663 A2 WO 2011069663A2 EP 2010007521 W EP2010007521 W EP 2010007521W WO 2011069663 A2 WO2011069663 A2 WO 2011069663A2
Authority
WO
WIPO (PCT)
Prior art keywords
coating
metal
coated steel
coated
weight
Prior art date
Application number
PCT/EP2010/007521
Other languages
English (en)
Other versions
WO2011069663A3 (fr
Inventor
Douglas Jesus Figueroa Gordon
Tim Harding
Sivasambu BÖHM
Wu Li
Original Assignee
Tata Steel Uk Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Uk Limited filed Critical Tata Steel Uk Limited
Priority to EP10795940A priority Critical patent/EP2510061A2/fr
Priority to CN2010800559824A priority patent/CN102652157A/zh
Publication of WO2011069663A2 publication Critical patent/WO2011069663A2/fr
Publication of WO2011069663A3 publication Critical patent/WO2011069663A3/fr

Abstract

La présente invention concerne un substrat en acier laminé à froid et revêtu qui comprend une composition de revêtement réductible dans l'eau, ladite composition de revêtement comprenant de l'eau, un solvant organique, un silane en tant que lieur, un adjuvant de revêtement et un métal, le métal étant une particule de métal ou une particule d'alliage de métal ayant une teneur en aluminium supérieure à 50 % en poids et le reste représentant moins de 50 % en poids d'un métal différent de l'aluminium, et le revêtement ayant une épaisseur de film mouillé dans la plage de 6 µm à 90 µm.
PCT/EP2010/007521 2009-12-11 2010-12-10 Revêtements protecteurs qui respectent l'environnement et destinés à des substrats WO2011069663A2 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP10795940A EP2510061A2 (fr) 2009-12-11 2010-12-10 Revêtements protecteurs pour substrats
CN2010800559824A CN102652157A (zh) 2009-12-11 2010-12-10 用于基材的环境友好保护性涂层

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP09015364.4 2009-12-11
EP09015364 2009-12-11

Publications (2)

Publication Number Publication Date
WO2011069663A2 true WO2011069663A2 (fr) 2011-06-16
WO2011069663A3 WO2011069663A3 (fr) 2011-08-25

Family

ID=41668427

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2010/007521 WO2011069663A2 (fr) 2009-12-11 2010-12-10 Revêtements protecteurs qui respectent l'environnement et destinés à des substrats

Country Status (3)

Country Link
EP (1) EP2510061A2 (fr)
CN (1) CN102652157A (fr)
WO (1) WO2011069663A2 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013056848A1 (fr) * 2011-10-19 2013-04-25 Tata Steel Uk Limited Revêtements anti-incrustation et anticorrosion pour des substrats en acier
WO2013056847A1 (fr) * 2011-10-19 2013-04-25 Tata Steel Uk Limited Revêtements hybrides anti-tartre et anti-corrosion pour substrats en acier
WO2014079893A3 (fr) * 2012-11-21 2014-08-07 Epg (Engineered Nanoproducts Germany) Ag Couches anti-calcaire à forte résistance à l'abrasion et résistance chimique élevée
JP2015017311A (ja) * 2013-07-12 2015-01-29 日新製鋼株式会社 耐食性に優れた亜鉛系めっき鋼板の製造方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106460083A (zh) * 2014-03-25 2017-02-22 麦格纳动力系有限公司 使用热辅助校准过程形成动力传递部件的方法及使用该方法制造的动力传递部件
CN107876358B (zh) * 2017-09-28 2021-02-02 中国科学院金属研究所 一种用于镍基金属非渗镀表面的防护涂层及防护方法

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7078076B2 (en) * 2001-02-14 2006-07-18 Metal Coatings International Inc. Particulate metal alloy coating for providing corrosion protection
CA2501349C (fr) * 2002-10-07 2012-08-21 Coatings For Industry, Inc. Formation de revetement resistant a la corrosion
FR2866029B1 (fr) * 2004-02-11 2006-05-26 Dacral Composition de revetement anti-corrosion en dispersion aqueuse comprenant un titanate et/ou un zirconate organique
MXPA06010676A (es) * 2004-03-19 2007-02-21 Doerken Ewald Ag Microrevestimiento comprendiendo siloxanos.

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
None

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013056848A1 (fr) * 2011-10-19 2013-04-25 Tata Steel Uk Limited Revêtements anti-incrustation et anticorrosion pour des substrats en acier
WO2013056847A1 (fr) * 2011-10-19 2013-04-25 Tata Steel Uk Limited Revêtements hybrides anti-tartre et anti-corrosion pour substrats en acier
WO2014079893A3 (fr) * 2012-11-21 2014-08-07 Epg (Engineered Nanoproducts Germany) Ag Couches anti-calcaire à forte résistance à l'abrasion et résistance chimique élevée
US10196743B2 (en) 2012-11-21 2019-02-05 Epg (Engineered Nanoproducts Germany) Ag Highly abrasion-resistant anti-limescale layers with high chemical resistance
JP2015017311A (ja) * 2013-07-12 2015-01-29 日新製鋼株式会社 耐食性に優れた亜鉛系めっき鋼板の製造方法

Also Published As

Publication number Publication date
CN102652157A (zh) 2012-08-29
WO2011069663A3 (fr) 2011-08-25
EP2510061A2 (fr) 2012-10-17

Similar Documents

Publication Publication Date Title
JP5419457B2 (ja) 金属、特に鋼を腐食及び／又はスケーリングから保護するためのコーティング剤、並びに金属及び金属部品のコーティング方法
KR101006033B1 (ko) 절연 피막을 갖는 전자 강판 및 그 제조 방법
KR101884222B1 (ko) 부식 제어 코팅
EP3730672B1 (fr) Composition de solution de traitement de surface pour tôle d'acier plaquée d'alliage de zinc par immersion à chaud ternaire, fournissant une excellente résistance à la corrosion et au noircissement, tôle d'acier plaquée d'alliage de zinc par immersion à chaud ternaire traitée en surface l'utilisant, et son procédé de fabrication
WO2011069663A2 (fr) Revêtements protecteurs qui respectent l'environnement et destinés à des substrats
WO2013056848A1 (fr) Revêtements anti-incrustation et anticorrosion pour des substrats en acier
AU2013363910B2 (en) Multi-stage method for the coating of steel prior to hot forming
CN110168024B (zh) 可固化的保护涂料组合物
KR102314431B1 (ko) 우수한 내흑변성 및 내알칼리성을 부여하는 삼원계 용융아연합금 도금강판용 표면처리 용액 조성물, 이를 이용하여 표면처리된 삼원계 용융아연합금 도금강판 및 그 제조 방법
KR100687278B1 (ko) 방식용 코팅제 조성물
KR101586840B1 (ko) 내식성 및 내흑변성이 우수한 마그네슘 함유 합금 도금 강판용 코팅 조성물 및 이를 포함하는 강판
WO2013056847A1 (fr) Revêtements hybrides anti-tartre et anti-corrosion pour substrats en acier
KR20090107835A (ko) 향상된 내열성과 내스크래치성을 갖는 크롬프리 수지 용액조성물, 이의 제조 방법 및 이를 이용한 표면처리 강판
KR101069950B1 (ko) 전기전도성이 개선된 강판 및 이에 사용되는 수지 조성물
MXPA05001964A (es) Inhibidor de la herrumbre.
CN116057134B (zh) 表面处理组合物、经表面处理的三元系热浸镀锌合金钢板及其制造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080055982.4

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10795940

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
WWE Wipo information: entry into national phase

Ref document number: 2010795940

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 6016/CHENP/2012

Country of ref document: IN