Classifications

• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
  • C21D1/62—Quenching devices
  • C21D1/673—Quenching devices for die quenching
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
  • B21D22/02—Stamping using rigid devices or tools
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
  • B21D22/02—Stamping using rigid devices or tools
  • B21D22/022—Stamping using rigid devices or tools by heating the blank or stamping associated with heat treatment
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
  • B21D37/00—Tools as parts of machines covered by this subclass
  • B21D37/16—Heating or cooling
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
  • C21D1/18—Hardening; Quenching with or without subsequent tempering
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
  • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
  • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
• • C—CHEMISTRY; METALLURGY
  • C21—METALLURGY OF IRON
  • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
  • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
  • C21D9/50—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for welded joints
  • C21D9/505—Cooling thereof

Definitions

• the invention relates to a method of shaping and hardening a sheet-steel blank, composed of separate sheets welded together, to give a product by heating the blank to the austenitising range and hot-stamping the blank in a cooled tool pair, then hardening the formed product while it remains in the tool pair.
• a sheet-steel blank is hot-stamped in a cooled tool pair into shape, then the formed product is hardened while it remains in the tool pair.
• This is now the usual process for producing high-strength products for the vehicle industry.
• This method results in a tensile strenght of 1400 or 1500 MPa or more.
• the different sheets are usually laser-welded together to form a composite blank usually referred to as a TWB (Tailor- Welded Blank) and this composite blank is then formed and hardened by press hardening.
• TWB ilor- Welded Blank
• One aim of the invention is to improve the properties of a product of this kind.
• one aim is to reduce the risk of cracking around the weld in the event of a collision when the product is a high-strength product for vehicles and to reduce the risk of crack formation and other defects and indications of fracture during subsequent cutting across the joint.
• the weld between two sheets is cooled at a reduced cooling rate in relation to the areas on either side of the weld so that a narrow, soft area is formed along the weld.
• the weld and the area immediately around the weld then have a lower martensite content than the rest of the product, resulting in a narrow, soft area with lower yield point and tensile strength and an elongation at break which is considerably higher than it would have been had the weld been hardened in the same manner as the rest of the product.
• the weld is critical hi the event of a collision, and crack formation at the weld could be devastating to the desired deformation process and could reduce the energy absorption obtained by controlled deformation when the invention is not applied.
• the desired reduction of the cooling rate can be achieved by means of a gap between the tool pair and the finished product alongside the weld. It is also possible to have a narrow heated part of the tool pair alongside the weld.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Mechanical Engineering (AREA)
• Physics & Mathematics (AREA)
• Thermal Sciences (AREA)
• Crystallography & Structural Chemistry (AREA)
• Materials Engineering (AREA)
• Metallurgy (AREA)
• Organic Chemistry (AREA)
• Heat Treatment Of Articles (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=43356607

Family Applications (1)

Country Status (7)

Families Citing this family (7)

Citations (3)

Family Cites Families (4)

• 2009
  • 2009-06-15 SE SE0900805A patent/SE533825C2/sv not_active IP Right Cessation
• 2010
  • 2010-06-09 US US13/261,035 patent/US9127330B2/en active Active
  • 2010-06-09 JP JP2012516032A patent/JP5864414B2/ja active Active
  • 2010-06-09 ES ES10789809T patent/ES2731175T3/es active Active
  • 2010-06-09 KR KR20127001100A patent/KR20120037472A/ko not_active Ceased
  • 2010-06-09 WO PCT/SE2010/000157 patent/WO2010147531A1/en not_active Ceased
  • 2010-06-09 EP EP10789809.0A patent/EP2443263B1/en active Active

Patent Citations (3)

Also Published As

Similar Documents

Legal Events