WO2010086664A2 - Recyclage - Google Patents
Recyclage Download PDFInfo
- Publication number
- WO2010086664A2 WO2010086664A2 PCT/GB2010/050142 GB2010050142W WO2010086664A2 WO 2010086664 A2 WO2010086664 A2 WO 2010086664A2 GB 2010050142 W GB2010050142 W GB 2010050142W WO 2010086664 A2 WO2010086664 A2 WO 2010086664A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- article
- heating
- pressure
- contaminated
- temperature
- Prior art date
Abstract
L'invention concerne un procédé de recyclage d'un article contaminé comprenant : le hachage et/ou le broyage de l'article contaminé; le chauffage de l'article contaminé à une certaine température et à une certaine pression pour décontaminer au moins partiellement l'article contaminé broyé et/ou pour au moins altérer partiellement la forme physique de l'article contaminé broyé afin de produire un second article. Le second article peut être utilisé pour la fabrication d'un produit final tel qu'un sac.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB0901461A GB2467528A (en) | 2009-01-29 | 2009-01-29 | Recycling materials such as plastics |
GB0901461.4 | 2009-01-29 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2010086664A2 true WO2010086664A2 (fr) | 2010-08-05 |
WO2010086664A3 WO2010086664A3 (fr) | 2010-09-23 |
Family
ID=40469258
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/GB2010/050142 WO2010086664A2 (fr) | 2009-01-29 | 2010-01-29 | Recyclage |
Country Status (2)
Country | Link |
---|---|
GB (1) | GB2467528A (fr) |
WO (1) | WO2010086664A2 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107627487A (zh) * | 2017-09-28 | 2018-01-26 | 王占舟 | 一种减少塑料味的废旧塑料清洗方法 |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112888541B (zh) | 2018-08-01 | 2023-03-28 | 瑞派科创新有限公司 | 分离多层塑料层的方法 |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB292213A (en) * | 1927-03-10 | 1928-06-11 | Johannes Van Loon | An improved manufacture of activated carbons and decolorising charcoals |
GB1453851A (en) * | 1973-07-18 | 1976-10-27 | Boc International Ltd | Cover removal |
EP0631537B1 (fr) * | 1992-01-27 | 1996-06-26 | FLEISCHHAUER, Rosa Emilia | Procede et dispositif pour la collecte et la regranulation de dechets contenant des matieres plastiques etirees |
JPH0892411A (ja) * | 1994-09-19 | 1996-04-09 | Mitsubishi Chem Corp | ポリオレフィンの回収方法 |
AU2002324201A1 (en) * | 2001-09-19 | 2003-04-01 | Slane Environmental Limited | Waste treatment |
JP2003191237A (ja) * | 2001-12-26 | 2003-07-08 | Mitsui Sekitan Ekika Kk | 廃プラスチックの減容化方法 |
US20050261119A1 (en) * | 2004-05-18 | 2005-11-24 | Sabrina Pichee Chen | Tri-fold plastic bag roll, method and apparatus for making same |
GB0501864D0 (en) * | 2005-01-31 | 2005-03-09 | 3Dm Environmental Ltd | Treatment and recovery of waste |
-
2009
- 2009-01-29 GB GB0901461A patent/GB2467528A/en not_active Withdrawn
-
2010
- 2010-01-29 WO PCT/GB2010/050142 patent/WO2010086664A2/fr active Application Filing
Non-Patent Citations (1)
Title |
---|
None |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN107627487A (zh) * | 2017-09-28 | 2018-01-26 | 王占舟 | 一种减少塑料味的废旧塑料清洗方法 |
Also Published As
Publication number | Publication date |
---|---|
GB2467528A (en) | 2010-08-11 |
GB0901461D0 (en) | 2009-03-11 |
WO2010086664A3 (fr) | 2010-09-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8690090B2 (en) | Post consumer scrap film recycling system | |
CA2373452C (fr) | Procede de tri et de separation et installation de recyclage de plastiques | |
JP2965693B2 (ja) | 廃棄物を処理するための方法および装置 | |
EP2477762B1 (fr) | Matière plastique récupérée à partir de déchets médicaux infectieux et dispositifs médicaux fabriqués à partir de celle-ci | |
JPH04229210A (ja) | プラスチック成形品廃棄物の再生処理方法ならびにその装置 | |
JPH06173182A (ja) | 熱可塑性樹脂塗工包装材料の再処理方法及び二次処理に対する熱可塑性樹脂材料 | |
CZ2017446A3 (cs) | Způsob zpracování odpadu vznikajícího po recyklaci papíru z použitých nápojových kartónů | |
CN105903747B (zh) | 医用输液设备的回收处理工艺方法 | |
US5618003A (en) | Process and apparatus for reclaiming the components of used disposable sanitary articles | |
HUT76072A (en) | Method of treating solid waste and device for extrusion for mixed waste | |
KR100310406B1 (ko) | 폐기물 재자원화 처리 방법 및 그 장치 | |
US20230089544A1 (en) | Automated process and method for material separation and recycling | |
Chandara et al. | Plastic recyling in Indonesia by converting plastic wastes (Pet, Hdpe, Ldpe, And Pp) into plastic pellets | |
KR101583305B1 (ko) | 폐합성수지 재생방법 | |
CN103702774B (zh) | 处理废弃物品的方法 | |
WO2010086664A2 (fr) | Recyclage | |
EP2631051B1 (fr) | Procédé de recyclage de déchets de film post-consommation | |
GB2493600A (en) | Apparatus and methods for recovering polyolefin plastic | |
KR102562450B1 (ko) | 폐합성수지를 이용한 펠렛 제조 장치 및 공정 | |
US20100117267A1 (en) | Process for pelletizing pet | |
EP0574328B1 (fr) | Procédé de traitement et de neutralisation de déchets contenant des éléments pathogènes | |
WO2021260875A1 (fr) | Dispositif de recyclage de déchets organiques et procédé de recyclage associé | |
CZ294679B6 (cs) | Způsob zpracovávání odpadků a zařízení k jeho provádění | |
CN105478437A (zh) | 一种生活垃圾处理方法 | |
WO2023023830A1 (fr) | Procédé de recyclage d'emballages co-extrudés de produits phytosanitaires agricoles |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10704180 Country of ref document: EP Kind code of ref document: A2 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 10704180 Country of ref document: EP Kind code of ref document: A2 |