WO2010057800A1 - Bauteil mit einer katalytischen oberfläche, verfahren zu dessen herstellung und verwendung dieses bauteils - Google Patents
Bauteil mit einer katalytischen oberfläche, verfahren zu dessen herstellung und verwendung dieses bauteils Download PDFInfo
- Publication number
- WO2010057800A1 WO2010057800A1 PCT/EP2009/064828 EP2009064828W WO2010057800A1 WO 2010057800 A1 WO2010057800 A1 WO 2010057800A1 EP 2009064828 W EP2009064828 W EP 2009064828W WO 2010057800 A1 WO2010057800 A1 WO 2010057800A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- mno
- metallic
- component according
- particles
- Prior art date
Abstract
Description
Claims