WO2010041536A1 - ガラス基板の製造方法、および磁気記録媒体の製造方法 - Google Patents

ガラス基板の製造方法、および磁気記録媒体の製造方法 Download PDF

Info

Publication number
WO2010041536A1
WO2010041536A1 PCT/JP2009/065917 JP2009065917W WO2010041536A1 WO 2010041536 A1 WO2010041536 A1 WO 2010041536A1 JP 2009065917 W JP2009065917 W JP 2009065917W WO 2010041536 A1 WO2010041536 A1 WO 2010041536A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass substrate
polishing
glass
manufacturing
producing
Prior art date
Application number
PCT/JP2009/065917
Other languages
English (en)
French (fr)
Inventor
賢一 佐々木
秀樹 河合
Original Assignee
コニカミノルタオプト株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by コニカミノルタオプト株式会社 filed Critical コニカミノルタオプト株式会社
Publication of WO2010041536A1 publication Critical patent/WO2010041536A1/ja

Abstract

　研磨剤を含む研磨液を用いてガラス基板の表面を研磨する第１研磨工程と第２研磨工程とを有するガラス基板の製造方法において、ガラス基板を洗浄する洗浄工程と、ガラス基板を乾燥させる乾燥工程と、を有し、第１研磨工程を行った後、第２研磨工程を行う前に、洗浄工程と乾燥工程とをこの順に行うことを特徴とするガラス基板の製造方法。

Description

ガラス基板の製造方法、および磁気記録媒体の製造方法
　本発明は、ガラス基板の製造方法、および磁気記録媒体の製造方法に関する。
　従来、コンピュータ等に用いられる情報記録媒体として磁気ディスクがある。磁気ディスク用基板としては、アルミニウム基板が一般的に用いられてきた。しかし、近年、記録密度向上のための磁気ヘッド浮上量の低減の要請に伴い、アルミニウム基板よりも表面の平滑性に優れ、しかも表面欠陥が少ないことから磁気ヘッド浮上量の低減を図ることができるガラス基板を磁気ディスク用基板として用いる割合が増えてきている。
　このような磁気ディスク等のガラス基板は、ブランク材と呼ばれるガラス基板に研磨加工等を施すことによって製造される。ガラス基板（ブランク材）は、プレス成形によって製造する方法や、フロート法等によって作製された板ガラスを切断して製造する方法等が知られている。一定の形状に切り出されたガラス基板のままでは表面の凹凸が大きく、表面研磨を行う必要があり、また、高密度化の要請からより高精度に研磨する技術が求められている。
　従来、よく知られているように、ガラスの表面仕上げの工程は、大きく分けて、第１ラッピング工程、第２ラッピング工程、第１研磨工程、第２研磨工程の各工程からなる（例えば、特許文献１、特許文献２参照）。
　第１ラッピング工程は、ガラス基板の両表面を研磨加工し、ガラス基板の平行度、平坦度および厚みを予備調整する工程である。第２ラッピング工程は、ガラス基板の平行度、平坦度および厚みを微調整する工程である。
　第１研磨工程、第２研磨工程はいわゆる研磨工程であり、第１研磨工程でキズや欠陥を除去してガラス基板の表面を所定の面粗さにした後、第２研磨工程でガラス基板の表面をさらに精密に研磨する。近年、ガラス基板には非常に高いレベルの平滑性が要求されるため、第１研磨工程、第２研磨工程ではともに研磨剤を含む研磨液を用いて研磨する方法が用いられている。
特許第３１８４２６１号公報 特許第３１８４４９５号公報
　しかしながら、特許文献１、特許文献２に開示されている従来の研磨工程では、さらに高いレベルの平滑性を有するガラス基板を効率的に製造することが非常に困難になってきた。
　本発明は上記課題に鑑みてなされたものであり、平滑性の高いガラス基板を効率的に製造することができるガラス基板の製造方法、平滑性の高い磁気記録媒体を効率的に製造することができる磁気記録媒体の製造方法を提供することを目的とする。
　上記の課題を解決するために、本発明は以下の特徴を有するものである。
　１．研磨剤を含む研磨液を用いてガラス基板の表面を研磨する第１研磨工程と第２研磨工程とを有するガラス基板の製造方法において、
　前記ガラス基板を洗浄する洗浄工程と、
　前記ガラス基板を乾燥させる乾燥工程と、
　を有し、
　前記第１研磨工程を行った後、前記第２研磨工程を行う前に、前記洗浄工程と前記乾燥工程とをこの順に行うことを特徴とするガラス基板の製造方法。
　２．前記第１研磨工程に引き続いて前記洗浄工程を行うことを特徴とする前記１に記載のガラス基板の製造方法。
　３．前記洗浄工程では、純水を用いて前記ガラス基板に超音波洗浄を行うことを特徴とする前記１または２に記載のガラス基板の製造方法。
　４．前記乾燥工程では、前記ガラス基板に気体を吹き付けて乾燥させることを特徴とする前記１から３の何れか１項に記載のガラス基板の製造方法。
　５．前記気体の温度は、１５℃～２００℃であることを特徴とする前記４に記載のガラス基板の製造方法。
　６．前記１から５の何れか１項に記載のガラス基板の製造方法を用いてガラス基板を製造した後、前記ガラス基板の表面に磁性膜を形成する工程を有することを特徴とする磁気記録媒体の製造方法。
　本発明によれば、第１研磨工程を行った後、第２研磨工程を行う前に、洗浄工程と乾燥工程とをこの順に行うので、ガラス基板に付着した液体の皮膜を除去し表面状態を均質にするとともに、ガラス基板の表面の濡れ性を高めることができる。このことにより、第２研磨工程において研磨液がガラス基板の全面に均一に広がるので平滑度の高い研磨が可能になる。したがって、平滑性の高いガラス基板を効率的に製造することができるガラス基板の製造方法、平滑性の高い磁気記録媒体を効率的に製造することができる磁気記録媒体の製造方法を提供することができる。
ガラス基板の全体構成を示す図である。 ガラス基板の表主表面の上に磁性膜を備えている磁気記録媒体の例を示す図である。 ガラス基板の製造における工程を説明する製造工程図である。 ガラス基板表面のうねり及び微小うねりを説明するための基板の拡大断面図である。
　本発明を図示の実施の形態に基づいて説明するが、本発明は該実施の形態に限らない。
　図１は、本発明に係るガラス基板１の全体構成を示している。図１に示す様に、ガラス基板１は、中心に孔５が形成されたドーナツ状の円板形状をしている。１０ｔは外周端面、２０ｔは内周端面、７ａは表主表面、７ｂは裏主表面を示している。
　図２は、本発明に係る磁気記録媒体の一例である磁気ディスクの斜視図である。この磁気ディスクＤは、円形のガラス基板１の表面に磁性膜２が直接形成されている。なお、磁性膜２は裏主表面７ｂの上にも設けることができる。
　図３は、本発明に係るガラス基板の製造方法の一例の製造工程図である。
　本実施形態の製造工程では、第１研磨工程を行った後、第２研磨工程を行う前に、洗浄工程と乾燥工程とをこの順に行っている点が特徴である。図３を用いて、本実施形態のガラス基板の製造工程について詳しく説明する。
　なお、本発明のガラス基板は、磁気記録媒体に限定されるものではなく、光磁気ディスクや光ディスクなどにも用いることができる。
　＜ガラス基板の製造工程＞
　ガラス基板の大きさに特に限定はない。例えば、外径が２．５インチ、１．８インチ、１インチ、０．８インチなど種々の大きさのガラス基板がある。また、ガラス基板の厚みにも限定はなく、２ｍｍ、１ｍｍ、０．６３ｍｍなど種々の厚みのガラス基板がある。
　（ガラス溶融工程）
　最初に、ガラス素材を溶融する。
　ガラス基板の材料としては特に制限はない。例えば、ＳｉＯ２、Ｎａ２Ｏ、ＣａＯを主成分としたソーダライムガラス；ＳｉＯ２、Ａｌ２Ｏ３、Ｒ２Ｏ（Ｒ＝Ｋ、Ｎａ、Ｌｉ）を主成分としたアルミノシリケートガラス；ボロシリケートガラス；Ｌｉ２Ｏ－ＳｉＯ２系ガラス；Ｌｉ２Ｏ－Ａｌ２Ｏ３－ＳｉＯ２系ガラス；Ｒ’Ｏ－Ａｌ２Ｏ３－ＳｉＯ２系ガラス（Ｒ’＝Ｍｇ、Ｃａ、Ｓｒ、Ｂａ）などを使用することができる。中でも、アルミノシリケートガラスやボロシリケートガラスは、耐衝撃性や耐振動性に優れるため特に好ましい。
　（プレス成形工程）
　溶融ガラスを下型に流し込み、上型によってプレス成形して円板状のガラス基板前駆体を得る。なお、円板状のガラス基板前駆体は、プレス成形によらず、例えばダウンドロー法やフロート法で形成したシートガラスを研削砥石で切り出して作製してもよい。
　（コアリング加工工程）
　プレス成形したガラス基板前駆体は、カッター部にダイヤモンド砥石等を備えたコアドリル等で中心部に孔を開ける。
　（第１ラッピング工程）
　次に、ガラス基板の両表面をラッピング加工し、ガラス基板の全体形状、すなわちガラス基板の平行度、平坦度および厚みを予備調整する。
　（内・外径加工工程）
　次に、ガラス基板の外周端面および内周端面を、例えば鼓状のダイヤモンド等の研削砥石により研削することで内・外径加工する。この内・外径加工により、ガラス基板の外径寸法および真円度、孔の内径寸法、並びにガラス基板と孔との同心度を微調整し、また、ガラス基板の内・外周角部を、例えば、０．１ｍｍから０．２ｍｍ程度の４５°の面取りをする。
　（内周端面加工工程）
　この後、ガラス基板の内周端面を、研磨液を使用したブラシ研磨により面取り部の角部を曲面とし、また微細なキズ等を除去する。
　（第２ラッピング工程）
　次に、ガラス基板の両表面を再びラッピング加工して、ガラス基板の平行度、平坦度および厚みを微調整する。
　（外周端面加工工程）
　そして、ガラス基板の外周端面を、研磨液を使用したブラシ研磨により面取り部の角部を曲面とし、また微細なキズ等を除去する。
　なお、コアリング加工以降の第１ラッピング工程から外周端面加工工程までの順序は、図３に示したものに限定されず、状況に応じて適宜変更することができる。例えば、ラッピング工程を一つにして最初に行い、その後、内・外径加工工程、内周、外周端面加工工程を行っても良い。また、第１ラッピング工程、内・外径加工工程の後、第２ラッピング工程、内周、外周端面加工工程を行っても良い。
　第１及び第２ラッピング工程にてガラス基板をラッピングする研磨機について説明する。研磨機は、両面研磨機と呼ばれる公知の研磨機を使用できる。両面研磨機は、互いに平行になるように上下に配置された円盤状の上定盤と下定盤とを備えており、互いに逆方向に回転する。この上下の定盤の対向するそれぞれの面にガラス基板の主表面をラッピングするための複数のダイヤモンドペレットが貼り付けてある。上下の定盤の間には、下定盤の外周に円環状に設けてあるインターナルギアと下定盤の回転軸の周囲に設けてある太陽ギアとに結合して回転する複数のキャリアがある。このキャリアには、複数の穴が設けてあり、この穴にガラス基板をはめ込んで配置する。上下の定盤、インターナルギア及び太陽ギアは別駆動で動作することができる。
　研磨機のラッピング動作は、上下の定盤が互いに逆方向に回転し、ダイヤモンドペレットを介して定盤に挟まれているキャリアは、複数のガラス基板を保持した状態で、自転しながら定盤の回転中心に対して下定盤と同じ方向に公転する。このような動作している研磨機において、研削液を上定盤とガラス基板及び下定盤とガラス基板との間に供給することでガラス基板のラッピングを行うことができる。
　この両面研磨機を使用する際、ガラス基板に加わる定盤の加工圧力及び定盤の回転数を所望のラッピング状態に応じて適宜調整する。第１及び第２ラッピング工程における加工圧力は、５８８４Ｐａから１１７６８Ｐａとするのが好ましい。また、定盤の回転数は、１０ｒｐｍから３０ｒｐｍ程度とし、上の定盤の回転数を下の定盤回転数より３０％から４０％程度遅くするのが好ましい。定盤による加工圧力を大きくし、定盤の回転数を速くすると研磨量は多くなるが、加工圧力を大きくしすぎると面粗さが良好とならず、また、回転数が速すぎると平坦度が良好とならない。また加工圧力が小さく定盤の回転数が遅いと研磨量が少なく製造効率が低くなる。
　第２ラッピング工程を終えた時点で、大きなうねり、欠け、ひび等の欠陥は除去され、ガラス基板の主表面の面粗さは、Ｒｚ（最大高さ粗さ）が２μｍから４μｍ、Ｒａ（算術平均粗さ）が０．２μｍから０．４μｍ程度とするのが好ましい。このような面状態にしておくことで、次の化学強化工程を経て第１研磨工程で研磨を効率よく行うことができる。
　尚、第１ラッピング工程では、第２ラッピング工程を効率よく行うことができるように大まかに大きなうねり、欠け、ひびを効率よく除去する。このため、第２ラッピングで使用する粗さ＃１３００メッシュから＃１７００メッシュより粗い＃８００メッシュから＃１２００メッシュ程度のダイヤモンドペレットを使用するのが好ましい。第１ラッピング工程が完了した時点での面粗さは、Ｒｚが４μｍから８μｍで、Ｒａが０．４μｍから０．８μｍ程度とするのが好ましい。
　ガラス基板の内周、外周の端面は、内周及び外周端面加工工程でブラシ研磨によるポリッシング加工を行う。ブラシは、φ０．２からφ０．３ｍｍ程度のナイロン、ポリプロピレン等を使用するのが好ましい。また、研磨液は、粒径が数μｍ程度の酸化セリウムが好ましい。ブラシ研磨の結果、内周、外周の端面の面粗さは、Ｒｚが０．２μｍから０．４μｍで、Ｒａが０．０２μｍから０．０４μｍ程度とするのが好ましい。内・外径加工工程及び内周及び外周端面加工工程を経たガラス基板の端面の形状は、主表面と端面とが成す角部が取り除かれ、外周端面から０．２ｍｍから０．５ｍｍ程度の位置から主表面よりダレた状態となる。
　ここで、Ｒａ（算術平均粗さ）、Ｒｚ（最大高さ粗さ）は、ＪＩＳ　Ｂ０６０１：２００１で規定されている。これらは、原子間力顕微鏡（ＡＦＭ）等により測定することができる。これら規定及び測定方法は、以降で記述されるＲａ、Ｒｚについても同じく適用する。
　上記の例では、ガラス基板を研磨する際にダイヤモンドペレットと研削液を用いているが、上下の定盤の研磨面にパッドを貼り付け、研磨液を供給して研磨する方法とすることもできる。研磨剤としては、例えば、酸化セリウム、酸化ジルコニウム、酸化アルミニウム、酸化マンガン、コロイダルシリカ、ダイヤモンドなどが挙げられる。これらを水で分散化してスラリー状として使用する。パッドは硬質パッドと軟質パッドとに分けられるが、必要に応じて適宜選択して用いることができる。硬質パッドとしては、硬質ベロア、ウレタン発泡、ピッチ含有スウェード等を素材とするパッドが挙げられ、軟質パッドとしては、スウェードやベロア等を素材とするパッドが挙げられる。
　パッドと研磨剤を使用する研磨方法は、研磨剤の粒度やパッドの種類を変えて、粗研磨から精密研磨まで対応することができる。よって、第１ラッピング工程と第２ラッピング工程で、効率よく大きなうねり、欠け、ひび等を除去し上記の面粗さを得ることができる様に研磨剤、研磨剤の粒度、パッドを適宜組み合わせて対応することができる。
　また、第１及び第２ラッピング工程の後、ガラス基板の表面に残った研磨剤やガラス粉を除去するための洗浄工程を行うことが好ましい。
　尚、第１ラッピング工程及び第２ラッピング工程で使用する研磨機は、同一構成ではあるがそれぞれの工程専用に用意された別の研磨機を用いてラッピング加工を行うのが好ましい。これは、専用のダイヤモンドペレットを貼り付けているため交換が大掛かりな作業となり、また、ラッピング条件を再設定する等の煩雑な作業が必要となり、製造効率が低下するためである。
　（化学強化工程）
　第２ラッピング工程の次に、化学強化液にガラス基板を浸漬してガラス基板に化学強化層を形成する。化学強化層を形成することで耐衝撃性、耐振動性及び耐熱性等を向上させることができる。
　化学強化工程は、加熱された化学強化処理液にガラス基板を浸漬することによってガラス基板に含まれるリチウムイオン、ナトリウムイオン等のアルカリ金属イオンをそれよりイオン半径の大きなカリウムイオン等のアルカリ金属イオンによって置換するイオン交換法によって行われる。イオン半径の違いによって生じる歪みより、イオン交換された領域に圧縮応力が発生し、ガラス基板の表面が強化される。
　化学強化処理液に特に制限はなく、公知の化学強化処理液を用いることができる。通常、カリウムイオンを含む溶融塩又はカリウムイオンとナトリウムイオンをふくむ溶融塩を用いることが一般的である。カリウムイオンやナトリウムイオンを含む溶融塩としては、カリウムやナトリウムの硝酸塩、炭酸塩、硫酸塩やこれらの混合溶融塩が挙げられる。中でも、融点が低く、ガラス基板の変形を防止できるという観点からは、硝酸塩を用いることが好ましい。
　化学強化処理液は、上記の成分が融解する温度よりも高温になるよう加熱される。一方、化学強化処理液の加熱温度が高すぎると、ガラス基板の温度が上がりすぎ、ガラス基板の変形を招く恐れがある。このため、化学強化処理液の加熱温度はガラス基板のガラス転移点（Ｔｇ）よりも低い温度が好ましく、ガラス転移点－５０℃よりも低い温度とすることが更に好ましい。
　なお、加熱された化学強化処理液に浸漬される際の熱衝撃によるガラス基板の割れや微細なクラックの発生を防止するため、化学強化処理液への浸漬に先立って、予熱槽でガラス基板を所定温度に加熱する予熱工程を有していても良い。
　化学強化層の厚みとしては、ガラス基板の強度向上と研磨工程の時間の短縮との兼ね合いから、５μｍ～１５μｍ程度の範囲が好ましい。強化層の厚みがこの範囲の場合、平坦度、機械的強度である耐衝撃性が良好なガラス基板とすることができる。
　化学強化工程後の表主表面７ａの外周端部の形状は、化学強化工程前とほとんど変わらず、上記の５μｍ～１５μｍ程度の化学強化層がガラス基板の表面全体にほぼ一様に載った状態となる。
　（第１研磨工程）
　次に、研磨工程に関して説明する。研磨工程では、ガラス基板の表面を精密に仕上げるとともに主表面の外周端部の形状を研磨する。
　まず、第１研磨工程では、第２研磨工程で最終的に必要とされる面粗さを効率よく得ることができるように、面粗さを向上させるとともに所望の形状を効率よく得ることができる研磨を行う。
　研磨の方法は、ラッピング工程で使用したダイヤモンドペレットと研削液に代えて、パッドと研磨液を使用する以外は第１及び第２ラッピング工程で使用した研磨機と同一の構成の研磨機を使用する。
　パッドは硬度Ａで８０から９０程度の硬質パッドで例えば発泡ウレタンを使用するのが好ましい。パッドの硬度が研磨による発熱により柔らかくなると研磨面の形状変化が大きくなるため硬質パッドを用いるのが好ましい。研磨剤は、粒径が０．６μｍから２．５μｍの酸化セリウム、コロイダルシリカ、酸化ジルコニウム、酸化チタニウム、酸化マンガン等を水に分散させてスラリー状にして用いるのが好ましい。水と研磨剤との混合比率は、概ね１：９から３：７程度が好ましい。
　定盤によるガラス基板への加工圧力は、８８２６Ｐａから１０７８７Ｐａとするのが好ましい。定盤によるガラス基板への加工圧力は、外周端部の形状に大きく影響する。加工圧力を大きくしていくと、外周端部の内側が下がり外側に向かって上がる傾向を示す。また、加工圧力を小さくしていくと、外周端部は平面に近くなるとともに面ダレが大きくなる傾向を示す。こうした傾向を観察しながら加工圧力を決めることができる。
　また、化学強化工程までに得た平坦度を維持し、さらに面粗さを向上させるように定盤の回転数を２５ｒｐｍから５０ｒｐｍとし、上の定盤の回転数を下の定盤回転数より３０％から４０％遅くするのが好ましい。
　上記の研磨条件により研磨量を３０μｍから４０μｍとするのが好ましい。３０μｍ未満では、キズや欠陥を十分に除去ができない。また４０μｍを超える場合は、面粗さをＲｚが２ｎｍから６０ｎｍ、Ｒａが２ｎｍから４ｎｍの範囲とすることができるが、必要以上に研磨を行うことになり製造効率が低下する。
　（洗浄工程）
　公知の超音波洗浄機を用いてガラス基板を洗浄し、研磨剤等を除去する。洗浄液には純水などを用いることができる。
　（乾燥工程）
　洗浄後のガラス基板に、ゴミ、埃などが除去された乾燥した気体を吹き付けて乾燥させる。気体は、空気でも窒素ガスなどの不活性の高純度ガスでも良い。気体の温度は１５℃～２００℃にすることが好ましい。より好ましい気体の温度は２０℃～２００℃である。気体を吹き付ける時間は１分以上、好ましくは３分以上ガラス基板に付着した水分が完全に乾燥するまで気体を吹き付ける。
　なお、別法として、ガラス基板をオーブンに入れて乾燥させても良い。オーブンの内部温度は好ましくは２００℃以下である。
　洗浄工程と乾燥工程により、ガラス基板に付着した液体の皮膜を除去し、表面状態を均質にするので、ガラス基板の表面の濡れ性を高めることができる。
　（第２研磨工程）
　第２研磨工程は、第１研磨工程後のガラス基板の表面を更に精密に研磨する工程である。第２研磨工程で使用するパッドは、第１研磨工程で使用するパッドより柔らかい硬度６５から８０（Ａｓｋｅｒ－Ｃ）程度の軟質パッドで、例えば発泡ウレタンやスウェードを使用するのが好ましい。研磨剤としては、第１研磨工程と同様の酸化セリウム、コロイダルシリカ、酸化ジルコニウム、酸化チタニウム、酸化マンガン等を用いることができるが、ガラス基板の表面をより滑らかにするため、粒径がより細かくバラツキが少ない研磨剤を用いるのが好ましい。粒径の平均粒子径が４０ｎｍから７０ｎｍの研磨剤を水に分散させてスラリー状にして研磨液として用い、水と研磨剤との混合比率は、１：９から３：７程度が好ましい。
　本発明では第２研磨工程の前に、洗浄工程と乾燥工程とを行うことにより、ガラス基板の表面の濡れ性が高まっているので、研磨液がガラス基板の全面に均一に広がり平滑度の高い研磨が可能になる。
　定盤によるガラス基板への加工圧力は、８８２６Ｐａから１０７８７Ｐａが好ましい。定盤によるガラス基板への加工圧力は、第１研磨工程と同様に外周端部の形状に大きく影響するが、研磨速度が遅いため第１研磨工程ほど効率的に形状を変化させることはできない。加工圧力の加減による外周端部の形状の変化は、第１研磨工程と同様であり、加工圧力を大きくしていくと、外周端部の内側が下がり外側に向かって上がる傾向を示す。また、加工圧力を小さくしていくと、外周端部は平面に近くなるとともに面ダレが大きくなる傾向を示す。外周端部の形状を得るために、こうした傾向を観察しながら加工圧力を決めることができる。定盤の回転数を１５ｒｐｍから３５ｒｐｍとし、上定盤の回転数を下定盤の回転数より３０％から４０％遅くするのが好ましい。
　上記の様に第２研磨工程での研磨条件を調整して本発明の外周端部の形状を得るとともに、面粗さをＲｚが２ｎｍから６ｎｍ、Ｒａが０．２ｎｍから０．４ｎｍの範囲とすることができる。
　研磨量は２μｍから５μｍとするのが好ましい。研磨量をこの範囲とすると、表面に発生した微小な荒れやうねり、これまでの工程で生じた微小な傷痕といった微小な欠陥を効率良く除去することができる。
　第１及び第２研磨工程によって、ガラス基板の表面の化学強化された領域が減少する。第１及び第２研磨工程の後のガラス基板の表面に化学強化された領域が残っているか否か、あるいは残っている強化された領域の厚みについては制限はない。
　（第２洗浄工程）
　（検査工程）
　第２研磨工程の終了後、ガラス基板の洗浄及び検査を行い、ガラス基板が完成する。
　尚、情報記録媒体用ガラス基板の製造方法においては、上記以外の種々の工程を有していても良い。例えば、ガラス基板の内部歪みを緩和するためのアニール工程、ガラス基板の強度の信頼性確認のためのヒートショック工程、ガラス基板の表面に残った研磨剤や化学強化処理液等の異物を除去する洗浄工程、種々の検査・評価工程等を有していても良い。
　また、第２研磨工程では、第１研磨工程で使用した研磨機をそのまま用いるのではなく、同一構成ではあるがそれぞれの工程専用に用意された別の研磨機を用いて研磨を行うのが好ましい。これは、第１研磨工程で使用した研磨機をそのまま用いると第１研磨工程で残留した研磨剤等により第２研磨工程での研磨精度が低下したり、研磨条件を再設定する等の煩雑な作業が必要となり、製造効率が低下するためである。
　（磁性膜形成工程）
　次に、ガラス基板に設ける磁性膜２の製造工程について説明する。以下、図２に基づき磁性膜２を設けた磁気記録媒体Ｄについて説明する。
　磁性膜２の形成方法としては従来の公知の方法を用いることができ、例えば磁性粒子を分散させた熱硬化性樹脂をガラス基板上にスピンコートして形成する方法や、スパッタリング、無電解めっきにより形成する方法が挙げられる。スピンコート法での膜厚は約０．３μｍ～１．２μｍ程度、スパッタリング法での膜厚は０．０４μｍ～０．０８μｍ程度、無電解めっき法での膜厚は０．０５μｍ～０．１μｍ程度であり、薄膜化および高密度化の観点からはスパッタリング法および無電解めっき法による膜形成が好ましい。
　磁性膜に用いる磁性材料としては、特に限定はなく従来公知のものが使用できるが、高い保持力を得るために結晶異方性の高いＣｏを基本とし、残留磁束密度を調整する目的でＮｉやＣｒを加えたＣｏ系合金などが好適である。具体的には、Ｃｏを主成分とするＣｏＰｔ、ＣｏＣｒ、ＣｏＮｉ、ＣｏＮｉＣｒ、ＣｏＣｒＴａ、ＣｏＰｔＣｒ、ＣｏＮｉＰｔや、ＣｏＮｉＣｒＰｔ、ＣｏＮｉＣｒＴａ、ＣｏＣｒＰｔＴａ、ＣｏＣｒＰｔＢ、ＣｏＣｒＰｔＳｉＯなどが挙げられる。磁性膜は、非磁性膜（例えば、Ｃｒ、ＣｒＭｏ、ＣｒＶなど）で分割しノイズの低減を図った多層構成（例えば、ＣｏＰｔＣｒ／ＣｒＭｏ／ＣｏＰｔＣｒ、ＣｏＣｒＰｔＴａ／ＣｒＭｏ／ＣｏＣｒＰｔＴａなど）としてもよい。上記の磁性材料の他、フェライト系、鉄－希土類系や、ＳｉＯ２、ＢＮなどからなる非磁性膜中にＦｅ、Ｃｏ、ＦｅＣｏ、ＣｏＮｉＰｔ等の磁性粒子を分散された構造のグラニュラーなどであってもよい。また、磁性膜は、内面型および垂直型のいずれの記録形式であってもよい。
　また、磁気ヘッドの滑りをよくするために磁性膜の表面に潤滑剤を薄くコーティングしてもよい。潤滑剤としては、例えば液体潤滑剤であるパーフロロポリエーテル（ＰＦＰＥ）をフレオン系などの溶媒で希釈したものが挙げられる。
　さらに必要により下地層や保護層を設けてもよい。磁気ディスクにおける下地層は磁性膜に応じて選択される。下地層の材料としては、例えば、Ｃｒ、Ｍｏ、Ｔａ、Ｔｉ、Ｗ、Ｖ、Ｂ、Ａｌ、Ｎｉなどの非磁性金属から選ばれる少なくとも一種以上の材料が挙げられる。Ｃｏを主成分とする磁性膜の場合には、磁気特性向上等の観点からＣｒ単体やＣｒ合金であることが好ましい。また、下地層は単層とは限らず、同一又は異種の層を積層した複数層構造としても構わない。例えば、Ｃｒ／Ｃｒ、Ｃｒ／ＣｒＭｏ、Ｃｒ／ＣｒＶ、ＮｉＡｌ／Ｃｒ、ＮｉＡｌ／ＣｒＭｏ、ＮｉＡｌ／ＣｒＶ等の多層下地層としてもよい。
　磁性膜の摩耗や腐食を防止する保護層としては、例えば、Ｃｒ層、Ｃｒ合金層、カーボン層、水素化カーボン層、ジルコニア層、シリカ層などが挙げられる。これらの保護層は、下地層、磁性膜など共にインライン型スパッタ装置で連続して形成できる。また、これらの保護層は、単層としてもよく、あるいは、同一又は異種の層からなる多層構成としてもよい。なお、上記保護層上に、あるいは上記保護層に替えて、他の保護層を形成してもよい。例えば、上記保護層に替えて、Ｃｒ層の上にテトラアルコキシシランをアルコール系の溶媒で希釈した中に、コロイダルシリカ微粒子を分散して塗布し、さらに焼成して二酸化ケイ素（ＳｉＯ２）層を形成してもよい。
　［実施例］
　実施例のガラス基板を以下のように作製した。
　（ガラス基板の作製）
　図３で説明した製造工程図に従ってガラス基板を作製した。
　ガラス材料としてアルミノシリケートガラス（Ｔｇ：５００℃）を用い、溶融ガラスをプレス成形してブランク材を１００枚作製した。内外周加工工程、ラッピング工程を経て、外径６５ｍｍ、内径２０ｍｍのガラス基板とした。ガラス基板の厚みは０．６４ｍｍとした。
　（化学強化工程）
　予熱槽でガラス基板を所定温度に加熱した後、３００℃に加熱した化学強化処理液にガラス基板を浸漬した。化学強化処理液にはカリウムの硝酸塩を用いた。
　（第１研磨工程）
　ニッタ・ハース社製のウレタンパッドを用い、研磨剤としては、酸化セリウムを用いた。研磨条件は、パッドの硬度７６（硬度Ａ）、研磨剤の粒径０．６（μｍ）、回転数３０（ｒｐｍ）、加工圧力１０７８７（Ｐａ）とした。
　（洗浄工程）
　超音波洗浄機で１０分間洗浄を行った。
　（乾燥工程）
　２００℃に加熱した清浄な空気をガラス基板の両面に３０分間吹き付けて乾燥させた。
　（第２研磨工程）
　ＦＩＬＷＥＬ社製のスウェードパッドを用い、研磨剤としては、酸化セリウムおよびコロイダルシリカを用いた。研磨条件は、パッドの硬度８０（Ａｓｋｅｒ－Ｃ）、研磨剤の粒径３０（ｎｍ）、回転数３０（ｒｐｍ）、加工圧力１０７８７（Ｐａ）とした。
　（第２洗浄工程）
　第２洗浄工程として、ロールスクラブ機、カップスクラブ機でのブラシ洗浄を行い、その後超音波洗浄機で洗浄を行った。
　［比較例］
　比較例では、洗浄工程、乾燥工程を省略した以外は実施例と同じ条件でガラス基板を１００枚作製した。
　［測定方法］
　ガラス基板のうねり、微小うねりとこれらの測定方法について説明する。
　図４は、ガラス基板の断面の拡大図である。図４（ａ）の実線の１１がガラス基板の表面形状を示す測定断面曲線である。また、破線の１２はガラス基板の表面のうねりを表すうねり曲線である。図４（ｂ）は、図４（ａ）の一部を拡大した図であり、うねり曲線１２の上に発生している微小うねり１３を表している。
　図４（ａ）のうねり曲線１２のうねりの高さＷａは、多機能ディスク用干渉計（オプティフラット　Ｐｈａｓｅ　Ｓｈｉｆｔ　Ｔｅｃｈｎｏｌｏｇｙ．Ｉｎｃ．製）を用いて行い、ガラス基板表面の全面を測定する。測定原理は、ガラス基板の表面に白色光を照射し、位相の異なる参照光と測定光の干渉の強度変化を測定することで、表面の微妙な形状変化を測定する方法である。得られた測定データを５ｍｍ以上の周期をカットオフし、うねりＷａとした。
　図４（ｂ）のうねりの上に発生している微小うねりの高さμＷａは、３次元表面構造解析顕微鏡（ＺＹＧＯ社製；商品名ＮＥＷＶＩＥＷ５０００）によって測定する。波長は、３０～２００μｍ範囲で行い、１μｍ□を４カ所測定し、その平均値を微小うねりμＷａとした。
　［測定結果］
　実施例と比較例で作製した各１００枚のガラス基板表面のうねりＷａ、微小うねりμＷａをそれぞれ測定した測定結果の平均値を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　測定結果の判定は、うねりＷａが０．３３５ｎｍ以下、微小うねりμＷａが０．１４５ｎｍ以下の場合を良品とし、１００％良品の場合を○、不良が発生した場合を×としている。
　表１に示すように、実施例のうねりＷａの平均値は０．３３ｎｍ、微小うねりμＷａの平均値は０．１４ｎｍであった。また、ガラス基板は１００％良品であり判定は○であった。
　一方、比較例ではＷａの平均値は０．３４ｎｍ、微小うねりμＷａの平均値は０．１５ｎｍであった。また、不良品が４３％発生し判定は×であった。
　別途、乾燥工程までを終えた実施例のガラス基板１００枚に超純水を滴下し、接触角を測定する実験を行ったところ、接触角は０°～３０°の範囲であり実施例のガラス基板は濡れ性が良いことが確認できた。
　以上このように、本発明によれば、平滑性の高いガラス基板を効率的に製造することができるガラス基板の製造方法、磁気記録媒体の製造方法を提供することができる。
　１　ガラス基板
　２　磁性膜
　５　孔
　７ａ　表主表面
　７ｂ　裏主表面
　１０ｔ　外周端面
　１１　測定断面曲線
　１２　うねり曲線
　１３　微小うねり曲線
　２０ｔ　内周端面
　Ｄ　磁気ディスク

Claims (6)

  1. 　研磨剤を含む研磨液を用いてガラス基板の表面を研磨する第１研磨工程と第２研磨工程とを有するガラス基板の製造方法において、
    　前記ガラス基板を洗浄する洗浄工程と、
    　前記ガラス基板を乾燥させる乾燥工程と、
    　を有し、
    　前記第１研磨工程を行った後、前記第２研磨工程を行う前に、前記洗浄工程と前記乾燥工程とをこの順に行うことを特徴とするガラス基板の製造方法。
  2. 　前記第１研磨工程に引き続いて前記洗浄工程を行うことを特徴とする請求項１に記載のガラス基板の製造方法。
  3. 　前記洗浄工程では、純水を用いて前記ガラス基板に超音波洗浄を行うことを特徴とする請求項１または２に記載のガラス基板の製造方法。
  4. 　前記乾燥工程では、前記ガラス基板に気体を吹き付けて乾燥させることを特徴とする請求項１から３の何れか１項に記載のガラス基板の製造方法。
  5. 　前記気体の温度は、１５℃～２００℃であることを特徴とする請求項４に記載のガラス基板の製造方法。
  6. 　請求項１から５の何れか１項に記載のガラス基板の製造方法を用いてガラス基板を製造した後、前記ガラス基板の表面に磁性膜を形成する工程を有することを特徴とする磁気記録媒体の製造方法。
PCT/JP2009/065917 2008-10-07 2009-09-11 ガラス基板の製造方法、および磁気記録媒体の製造方法 WO2010041536A1 (ja)