WO2009146589A1 - A flakeboard surfaced with aluminium foil coated with uv-cured paint - Google Patents

A flakeboard surfaced with aluminium foil coated with uv-cured paint Download PDF

Info

Publication number
WO2009146589A1
WO2009146589A1 PCT/CN2008/071238 CN2008071238W WO2009146589A1 WO 2009146589 A1 WO2009146589 A1 WO 2009146589A1 CN 2008071238 W CN2008071238 W CN 2008071238W WO 2009146589 A1 WO2009146589 A1 WO 2009146589A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum foil
coated
paint
flakeboard
particle board
Prior art date
Application number
PCT/CN2008/071238
Other languages
French (fr)
Chinese (zh)
Inventor
丁乃今
Original Assignee
Ding Naijin
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ding Naijin filed Critical Ding Naijin
Priority to PCT/CN2008/071238 priority Critical patent/WO2009146589A1/en
Publication of WO2009146589A1 publication Critical patent/WO2009146589A1/en

Abstract

A flakeboard surfaced with aluminium foil coated with UV-cured paint includes a flakeboard (1) and aluminium foils (2) curtain-coated with UV-cured paint applied to both sides of said flakeboard. The manufacturing method includes these steps: 1) spreading metal adhesive on the back of the aluminium foil and curing said metal adhesive without pressure, then spreading phenolic resin adhesive on said flakeboard, and sticking the side of said aluminium foil with the cured metal adhesive to the flakeboard spread with adhesive; 2) applying with a roller a first layer of light-cured primer, then when half-dry, applying a second layer of light-cured primer, then applying a third surface coat of UV-cured paint, finally evening the painted surface with a heat finishing machine at 80°C.

Description

说明书 紫外线光固化漆铝箔饰面刨花板及其制作方法 技术领域  Ultraviolet light curing paint aluminum foil facing particleboard and manufacturing method thereof
[1] 本发明涉及一种 [1] The present invention relates to a
与淋涂紫外线光固化漆的铝箔复合的防火饰面板， 具体涉及一种紫外线光固化 漆铝箔饰面刨花板以及该刨花板的制作方法。  A fireproof veneer composited with an aluminum foil coated with an ultraviolet curable paint, specifically relates to an ultraviolet light-curing paint aluminum foil facing particleboard and a method of making the particle board.
背景技术  Background technique
[2] 现有市场上的各种装饰板存在很多问题， 如华丽板、 宝丽板防火性能差， 不坚 韧； 刨花板、 中密度纤维板表面粗糙、 甲醛释放量不符合室内环保要求， 各种 树脂和溶剂制作的装饰材料和涂饰材料有毒有害； 装饰材料的表面强度和硬度 左寸。  [2] There are many problems in various decorative boards on the market. For example, the gorgeous board and the Baoli board have poor fire resistance and are not tough; the surface of the particleboard and medium density fiberboard is rough, and the formaldehyde emission does not meet the indoor environmental requirements. Decorative materials and finishing materials made with solvents are toxic and harmful; the surface strength and hardness of decorative materials are left.
对发明的公开  Disclosure of invention
技术问题  technical problem
[3] 本发明的目的是提供一种 [3] The object of the present invention is to provide a
与淋涂紫外线光固化漆铝箔复合的紫外线光固化漆铝箔饰面刨花板， 防水、 防 潮、 无毒害， 同吋提供该刨花板的特种制作方法。  UV-curable lacquered aluminum foil facing particleboard composited with UV-curable lacquered aluminum foil. It is waterproof, moisture-proof and non-toxic. It also provides a special method for making this particleboard.
技术解决方案  Technical solution
[4] 紫外线光固化漆铝箔饰面刨花板， 其组成包括： 刨花板， 所述的刨花板上下面 复合经过光固化漆淋涂的铝箔。  [4] Ultraviolet light curing paint aluminum foil facing particleboard, the composition thereof comprises: particle board, and the aluminum foil coated with the light curing paint is laminated on the bottom of the particle board.
[5] 所述的紫外线光固化漆铝箔饰面刨花板， 所述的刨花板与铝箔之间具有夹层板 材。 [5] The ultraviolet light-curing lacquer aluminum foil facing particleboard, wherein the particle board and the aluminum foil have a sandwich board.
[6] 一种紫外线光固化漆铝箔饰面刨花板的制作方法，  [6] A method for preparing an ultraviolet light curing lacquer aluminum foil facing particleboard,
先把所述的铝箔背面涂上金属胶合剂， 待其无压固化后再把所述的刨花板涂上 酚醛树脂胶粘剂， 将铝箔背面已固化的涂胶面贴覆在已经涂上胶的刨花板基材 上， 然后用附着力极强的光固化辊涂第一道底漆， 光固化半分干后再辊涂上第 二道底漆， 最后淋第三层面漆， 最后用 80 c 的热流平机将漆面整平。  First, the back surface of the aluminum foil is coated with a metal glue, and after the pressureless curing, the particle board is coated with a phenolic resin adhesive, and the cured surface of the aluminum foil is pasted on the glued particle board base. On the material, then apply the first primer with a highly adhesive photocuring roller, lightly cure the semi-dried, then roll the second primer, finally the third layer of paint, and finally use the 80 c heat leveler. Level the paint.
有益效果 [7] 本发明的有益效果: Beneficial effect [7] Advantageous Effects of the Invention:
[8] [8]
本产品是用金属铝箔覆盖在刨花板表面， 使刨花板内的有毒有害物质无法释放 ， 并把金属的高强度、 高硬度和防火性能与刨花板的质轻、 坚挺结合起来， 同 吋釆用的光固化漆解决了釆用含苯、 甲醛或其它芳香烃溶剂油漆涂饰挥发固化 释放出的有毒物质对人体的毒害。  This product is covered with metal foil on the surface of the particle board, so that the toxic and harmful substances in the particle board can not be released, and the high strength, high hardness and fire resistance of the metal are combined with the light weight and firmness of the particle board. The lacquer solves the poisoning of toxic substances released by volatilization and curing with benzene, formaldehyde or other aromatic hydrocarbon solvents.
[9] 2. [9] 2.
解决了刨花板表面粗糙， 不防水、 易吸潮， 不环保的缺点， 使表面细腻、 平整 、 光洁， 且复合后板材强度高、 不变形， 扩大了刨花板的应用范围。  The invention solves the defects that the surface of the particle board is rough, not waterproof, easy to absorb moisture, and is not environmentally friendly, so that the surface is fine, smooth and smooth, and the strength of the sheet after the composite is high and does not deform, thereby expanding the application range of the particle board.
[10] 3. [10] 3.
铝箔可制成各种颜色和印刷逼真的珍贵天然树种木纹， 来替代昂贵薄木和浸渍 胶膜纸饰面材料， 具有防火、 强度高的特点， 并用紫外线光固化漆淋涂铝箔表 面， 提高了金属对人体皮肤的亲和力。  Aluminum foil can be made into various colors and printing realistic and precious natural tree wood grain to replace expensive thin wood and impregnated paper paper finishing materials. It has the characteristics of fireproof and high strength, and the surface of aluminum foil is coated with ultraviolet light curing paint. The affinity of metal for human skin.
[11] 4.传统漆面涂抹后， 在 24小吋内固化 90%， 在 3  [11] 4. After applying the traditional paint, it will cure 90% in 24 hours, at 3
个月至一年完全固化， 占用场地大， 要求条件高， 工人劳动环境差； 而本产品 可完全实现日班化连续生产， 无有害气体， 改善劳动环境和使用环境， 提高了 劳动生产率， 是无毒无害的绿色环保装饰板材。 由于本产品的加工工艺非常精 密， 使得板材的结构紧密， 不会出现板面起层等质量问题。  It is fully cured from month to year, occupying a large area, requiring high conditions, and poor working environment for workers. This product can fully realize daily production, no harmful gas, improve working environment and environment, and improve labor productivity. Non-toxic and harmless green decorative panels. Due to the very precise processing technology of this product, the structure of the sheet is tight, and there is no quality problem such as the delamination of the board.
[12] 5.  [12] 5.
本发明板材提供了一种新的完全绿色无污染装饰板材， 装饰后马上可以入住， 室内无任 1可异味， 有益于装璜工作者及居家人士身体健康。  The board of the invention provides a new completely green and pollution-free decorative board, which can be accommodated immediately after decoration, and has no odor in the room, which is beneficial to the health of the decoration workers and the home.
[13] 6.  [13] 6.
本发明板材饰面材料和漆膜阻燃， 装修的房屋可以阻止火势蔓延， 延长火苗进 入房间的吋间， 从而给人带来宝贵吋间。  The plate facing material and the paint film of the invention are flame retardant, and the decorated house can prevent the fire from spreading and prolong the flame into the room, thereby bringing valuable time.
[14] 7. [14] 7.
本发明板材外观坚韧靓丽， 硬度高耐磨性能好， 淋涂光固化漆后能使铝箔上的 色彩和花纹更加艳丽、 丰满、 逼真， 并彰显金属饰面材料的雍荣华贵。 本产品 的刨花板的两侧贴有等厚的夹层板材， 对称性好， 抗弯曲能力强， 而且不变形 ， 不会影响装饰的美观性， 适合于高档家具板材的工艺要求。 The appearance of the plate of the invention is tough and beautiful, and the hardness is high and the wear resistance is good. After the light-curing paint is applied, the color and pattern on the aluminum foil can be more vivid, full and realistic, and the metal veneer material is exaggerated. The chipboard of this product is affixed with equal thickness sandwich plates on both sides, which has good symmetry, strong bending resistance and no deformation. , will not affect the aesthetics of the decoration, suitable for the technical requirements of high-grade furniture panels.
附图说明 DRAWINGS
附图 1是本产品的结构示意图。  Figure 1 is a schematic view of the structure of the product.
本发明的最佳实施方式 BEST MODE FOR CARRYING OUT THE INVENTION
紫外线光固化漆铝箔饰面刨花板， 其组成包括： 刨花板 1  UV-curable lacquered aluminum foil facing particleboard, the composition of which includes: Particleboard 1
， 所述的刨花板上下面复合经过光固化漆淋涂的铝箔 2， 所述的铝箔为 素箔、 上色箔或印刷铝箔。 And the aluminum foil 2 coated with the light-curing paint is laminated on the bottom of the particle board, and the aluminum foil is a plain foil, a color foil or a printed aluminum foil.
所述的紫外线光固化漆铝箔饰面刨花板的制作方法， 该刨花板具有三层漆面， 使得漆面层平整饱满均匀， 保证漆面连续稳定不脱层。 先把铝箔背面涂上金属 胶合剂待其无压固化后再把刨花板涂上酚醛树脂胶粘剂， 再把铝箔已固化的涂 胶面贴覆在已经涂上胶的刨花板基材上， 然后用附着力极强的光固化一道底漆 辊涂， 光固化半分干后再辊涂上第二道底漆， 保证了漆面平整， 为淋面漆作好 了有效过渡， 能避免剥落掉漆， 最后淋第三层面漆， 通过前面涂层的稳固结合 ， 使第三层漆能具有坚固的附着力， 淋漆后通过 80 c  The method for preparing the ultraviolet light-curing lacquer aluminum foil facing particle board, the particle board has three layers of lacquer surface, so that the lacquer surface layer is flat and full, and the lacquer surface is continuously stable and does not delaminate. Firstly, the back side of the aluminum foil is coated with a metal glue to be pressurelessly cured, and then the particle board is coated with a phenolic resin adhesive, and the cured surface of the aluminum foil is pasted on the glued particle board substrate, and then the adhesion is applied. Extremely strong light curing with a primer roller coating, light curing and semi-drying, and then applying a second primer to ensure that the paint surface is smooth, making an effective transition for the topcoat, avoiding peeling off the paint, and finally dripping The third layer of paint, through the firm combination of the front coating, enables the third layer of paint to have a strong adhesion, after the lacquer passes 80 c
的热流平机使得漆面更加平整， 晶莹剔透， 提高其光感和强度， 经检验符合要 求后用紫外线光固化， 由此保证了在铝箔上形成稳定坚固而且美丽的漆面。 本发明的实施方式 The heat leveling machine makes the paint surface smoother, crystal clear, and enhances its light perception and strength. It is cured by ultraviolet light after it meets the requirements, thus ensuring a stable and beautiful paint surface on the aluminum foil. Embodiments of the invention
紫外线光固化漆铝箔饰面刨花板， 其组成包括： 刨花板 1  UV-curable lacquered aluminum foil facing particleboard, the composition of which includes: Particleboard 1
， 所述的刨花板上下面复合经过光固化漆淋涂的铝箔 2， 所述的铝箔为 素箔或者上色箔或者印刷铝箔。 The aluminum foil is coated on the underside of the particle board by a light-curing lacquer, and the aluminum foil is a plain foil or a colored foil or a printed aluminum foil.
所述的紫外线光固化漆铝箔饰面刨花板， 所述的刨花板与铝箔之间具有夹层板  The ultraviolet light curing lacquer aluminum foil facing particleboard, the sandwich board between the particle board and the aluminum foil

Claims

权利要求书 一种紫外线光固化漆铝箔饰面刨花板， 其组成包括： 刨花板， 其特征是： 所述的刨花板上下面复合经过光固化漆淋涂的铝箔。 Claims: An ultraviolet light-curing lacquer aluminum foil facing particleboard, comprising: a particle board, wherein: the particle board is coated with an aluminum foil coated with a light-curing paint.
2.根据权利要求 1  2. According to claim 1
所述的紫外线光固化漆铝箔饰面刨花板， 其特征是： 所述的刨花板与铝箔 之间具有夹层板材。 The ultraviolet light-curing lacquer aluminum foil facing particleboard is characterized in that: the particle board and the aluminum foil have a sandwich plate.
3.一种紫外线光固化漆铝箔饰面刨花板的制作方法， 其特征是： 先把所述的铝箔背面涂上金属胶合剂， 待其无压固化后再把所述的刨花板 涂上酚醛树脂胶粘剂， 将铝箔背面已固化的涂胶面贴覆在已经涂上胶的刨 花板基材上， 然后用附着力极强的光固化辊涂第一道底漆， 光固化半分干 后再辊涂上第二道底漆， 最后淋第三层面漆， 最后用 80 c  3. A method for preparing an ultraviolet light-curing lacquer aluminum foil facing particleboard, characterized in that: the back surface of the aluminum foil is coated with a metal glue, and after the pressureless curing, the particle board is coated with a phenolic resin adhesive. Applying the cured adhesive surface on the back side of the aluminum foil to the already coated particle board substrate, and then coating the first primer with a highly adhesive photocuring roller, photocuring the semi-dried and then roller coating Two primers, finally the third layer of paint, and finally 80 c
的热流平机将漆面整平。 The heat leveler flattens the paint.
PCT/CN2008/071238 2008-06-06 2008-06-06 A flakeboard surfaced with aluminium foil coated with uv-cured paint WO2009146589A1 (en)