CN113829702A - Preparation method of environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate - Google Patents
Preparation method of environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate Download PDFInfo
- Publication number
- CN113829702A CN113829702A CN202111142627.7A CN202111142627A CN113829702A CN 113829702 A CN113829702 A CN 113829702A CN 202111142627 A CN202111142627 A CN 202111142627A CN 113829702 A CN113829702 A CN 113829702A
- Authority
- CN
- China
- Prior art keywords
- cabinet body
- body plate
- treatment
- preparing
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of an environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate, which is characterized by comprising the following eight steps: s1, manufacturing an interlayer; s2, manufacturing a coating layer; s3 constant temperature pressing treatment; s4 cold pressing treatment at constant temperature; s5 glue rolling coating; s6 preparing a skin layer; s7, preparing a semi-finished product; s8 preparing the finished product. The cabinet body plate adopts the shaving board, the aluminum material and the veneer as the interlayer, the coating layer and the surface layer respectively, and the aluminum-wood combination product is used for sealing the edges of the shaving board, the aluminum material and the veneer, so that the manufacturing structure of the cabinet body plate is effectively simplified, the preparation process is simplified, the production cost is reduced, the release of toxic substances can be effectively inhibited, the environment is protected, and the phenomenon that the body health is influenced by the toxic substances inhaled by a human body is avoided; the cabinet body plate can have mildew-proof and flame-retardant performances without complex surface treatment, and the practicability of the cabinet body plate is effectively improved, so that the cabinet body plate can be suitable for different environments.
Description
Technical Field
The invention belongs to the technical field of cabinet body plates, and particularly relates to a preparation method of an environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate.
Background
The cabinet body board is used as a board for a cabinet supporting surface, and the traditional cabinet body board comprises a shaving board, a density board, a moisture-proof board, a large core board, a fir board, a multilayer solid board, a macaw board, an Europe pine board, a veneer board, a Mansix deck board and the like. Most of the boards contain toxic substances, and some of the boards even exceed the standard, and the cabinet boards containing the toxic substances can emit the toxic substances into a house when the house is decorated, so that the environment of the house is polluted, and meanwhile, the toxic substances can be inhaled by a human body to cause irreversible physical damage.
The cabinet body plate at the present stage is made of environment-friendly materials, so that the damage to human health and the environment can be reduced, the cost is higher, the post-treatment is more complex, and the cabinet body plate is easy to deform after long-time use. For example, chinese patent publication No. CN110525006A, published 2019, 12 and 03, discloses a surface treatment method for a moisture-proof heat-insulating cabinet board, and proposes "including: sequentially laminating and connecting the glass magnesium board, the wood bottom layer and the flame-retardant layer from outside to inside through adhesive hot pressing to obtain a cabinet body board to be treated; gluing the outer side of the glass magnesium board and the inner side of the flame retardant layer, and attaching the thermosetting resin impregnated paper high-pressure board which is pressed and attached with the impregnated bond paper to the outer side of the glass magnesium board and the inner side of the flame retardant layer; carrying out cold pressing treatment on the obtained semi-finished product, and then demoulding to carry out surface repairing treatment; the finished product is transported qualified through the conveyor belt after being detected, the cabinet body plate is made of environment-friendly and non-toxic raw materials in the prior art, harm to human bodies and environment is reduced, but the prior art is high in cost, the fireproof, flame-retardant, waterproof, moistureproof, wear-resistant and scratch-resistant performances of the plate can be achieved only through surface treatment, the treatment process is complex, and the cabinet body is easy to deform and attractive in appearance after long-term use. For this reason, a new technical solution is needed to solve the above technical problems.
Disclosure of Invention
The invention aims to provide a preparation method of an environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate, and aims to solve the problems that the existing cabinet body plate in the background art is made of a high-cost plate, the post-treatment process is complex, and the cabinet body plate is easy to deform after long-term use.
In order to achieve the purpose, the invention provides the following technical scheme: the preparation method of the environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate is characterized by comprising the following specific steps of:
s1 preparing an interlayer: selecting a flat shaving board as an interlayer, firstly carrying out double-sided fixed-thickness sand flattening, then carrying out electrostatic dust removal and infrared ray preheating treatment, and then coating glue on the front and back surfaces of the shaving board;
s2 manufacturing a coating layer: selecting an aluminum material as a coating layer, performing electrostatic precipitation treatment, soaking the aluminum material for 40-60 minutes by using a chemical component HJKV-205, drying the aluminum material for 20-25 minutes, flatly adhering the aluminum material to the front surface and the back surface of a shaving board by using glue, so that the aluminum material can be more tightly attached to the shaving board, and simultaneously reserving four sides of the aluminum material with a plurality of lengths;
s3 constant-temperature pressing treatment: firstly, carrying out constant temperature treatment on the aluminum material coated with the shaving board through an infrared constant temperature channel, and then carrying out pressing treatment through a pressing wheel, so that the aluminum material can be better bonded with the shaving board;
s4 constant-temperature cold pressing treatment: placing the pressed shaving board and aluminum material in a constant temperature space of 25-35 ℃ for constant temperature treatment for 40-50 minutes, and then performing cold pressing treatment at 10-15 ℃ for 6-8 hours, so that the aluminum material coated with the shaving board can be effectively prevented from deforming;
s5 glue rolling coating: coating glue on the front and back surfaces of the aluminum material subjected to constant-temperature cold pressing treatment by a glue coating wheel in a rolling manner;
s6 preparation of skin layer: selecting a veneer as a surface layer, firstly placing the veneer in a constant-temperature space of 25-35 ℃ for constant-temperature maintenance treatment, then controlling the water content of the veneer to be 8% -12%, then flatly attaching the veneer to the front surface and the back surface of the aluminum material coated with the shaving board through glue, simultaneously reserving four sides of the veneer with the same length as the aluminum material, and attaching the reserved four sides of the veneer and the reserved four sides of the aluminum material to form an aluminum-wood combined product;
s7 preparing a semi-finished product: repeating S3-S4, wherein the cold pressing treatment time in S4 is 8-12 hours, and performing UV coating through a UV coating production line to obtain a semi-finished cabinet body plate;
s8, preparing a finished product: the method comprises the steps of cutting a semi-finished cabinet body plate, adopting an aluminum-wood combination product to carry out edge sealing treatment on four sides of a shaving board, then finishing and flattening, then carrying out electrostatic dust removal, applying glue, and then carrying out finishing treatment to obtain a final finished product.
Compared with the prior art, the invention has the beneficial effects that:
1. the cabinet body plate adopts the shaving board, the aluminum material and the veneer as the interlayer, the coating layer and the surface layer respectively, and then the redundant aluminum-wood combination product is utilized to carry out edge sealing on the shaving board, so that the manufacturing structure of the cabinet body plate is effectively simplified, the manufacturing process is simplified, the production cost is reduced, the release of toxic substances can be effectively inhibited, the environment is protected, and the phenomenon that the body health is influenced by the toxic substances inhaled by a human body is avoided.
2. The cabinet body plate provided by the invention has the advantages that the cabinet body plate can have mildew-proof and flame-retardant performances without complex surface treatment, the practicability of the cabinet body plate is effectively improved, the cabinet body plate can be suitable for different environments, and the applicability of the cabinet body plate is effectively improved.
3. The cabinet body plate can effectively prevent deformation by using the stability of the aluminum material, thereby improving the stability of the cabinet body plate and avoiding the deformation of the cabinet body plate caused by long-time exposure in a humid environment.
Drawings
Fig. 1 is a schematic cross-sectional view of a cabinet body plate according to the present invention.
Wherein: 1. particle board; 2. aluminum material; 3. wood veneer; 4. an aluminum-wood combination product.
Detailed Description
The following examples are intended to further illustrate the invention and are not intended to limit the application of the invention.
Example 1:
referring to fig. 1, a 15mm flame-retardant shaving board 1, a 0.2mm aluminum material 2 and a 0.45mm wood veneer 3 are respectively selected as an interlayer, a coating layer and a surface layer of a cabinet body board, so that the manufacturing structure of the cabinet body board is effectively simplified, the preparation process is also effectively simplified, and the production cost is reduced.
Selecting a flame-retardant shaving board 1 as an interlayer, setting the thickness of the interlayer flame-retardant shaving board 1 to be 15mm, sanding the front and back surfaces of the flame-retardant shaving board 1 through a sanding machine, performing electrostatic dust collection and infrared ray preheating treatment, and then coating FP1069 glue on the front and back surfaces of the sanded flame-retardant shaving board 1;
selecting the aluminum material 2 as a coating layer, wherein the aluminum material 2 can be effectively prevented from deforming by using the stability of the aluminum material 2, so that the stability of a cabinet body plate is improved, and the cabinet body plate is prevented from deforming due to long-time exposure in a humid environment, the aluminum material 2 is firstly polished by a polishing machine, so that uniform pits are formed on the surface of the aluminum material 2, glue is favorably adhered, the aluminum material 2 is ensured to have viscosity, then electrostatic dust removal treatment is carried out, soaking is carried out for 50 minutes by using a chemical component HJKV-205, the toughness and the flame retardant property of the aluminum material 2 are effectively improved, then drying is carried out for 22 minutes, then the aluminum material 2 is flatly adhered to the front side and the back side of the flame-retardant shaving board 1 coated with FP1069 glue, and four sides of the aluminum material 2 with a plurality of lengths are reserved; then the aluminum material 2 coated with the flame-retardant shaving board 1 is subjected to constant temperature treatment through an infrared constant temperature channel, and then is subjected to pressing and pasting treatment through a pressing wheel, so that the aluminum material 2 can be better bonded with the flame-retardant shaving board 1, the difficulty of the preparation process is effectively reduced, then the flame-retardant shaving board 1 and the aluminum material 2 after pressing and pasting are placed in a constant temperature space of 30 ℃ for constant temperature treatment for 45 minutes, then cold pressing treatment is carried out at 12 ℃ for 7 hours, so that the aluminum material 2 coated with the shaving board 1 can effectively avoid deformation, and then FP1069 glue is coated on the front side and the back side of the aluminum material 2 coated with the flame-retardant shaving board 1 through glue coating wheels in a rolling manner;
selecting a veneer 3 as a surface layer, firstly placing the veneer 3 in a constant temperature space of 30 ℃ for constant temperature maintenance treatment, then carrying out control treatment on the water content to control the water content to be 8-12%, effectively improving the mildew resistance of the veneer 3, flatly attaching the veneer 3 to the front and back surfaces of an aluminum product 2 coated with a flame-retardant shaving board 1 through FP1069 glue, leaving four sides of the veneer 3 with the same thickness as that of the aluminum product 2, attaching the four sides and the four sides left by the aluminum product 2 to form an aluminum-wood combined product 4, cutting the aluminum product for edge sealing, effectively reducing the production cost, simultaneously saving the board resources, then carrying out constant temperature treatment on the aluminum product 2 which is externally attached with the veneer 3 and internally coated with the flame-retardant shaving board 1 through an infrared constant temperature channel, carrying out pressure attaching treatment through a pressure roller, and enabling the flame-retardant shaving board 1, the aluminum product 2 and the veneer 3 to be better pressed and attached together, then, the flame-retardant shaving board 1, the aluminum material 2 and the veneer 3 which are pressed together are placed in a constant-temperature space at 30 ℃ for constant-temperature treatment for 45 minutes, then cold-pressing treatment is carried out for 10 hours at 12 ℃, UV coating is carried out through a UV coating production line to obtain a semi-finished cabinet body board, then the semi-finished cabinet body board is cut, then the cut aluminum-wood combined product 4 is used for carrying out edge sealing treatment on four sides of the flame-retardant shaving board 1, then the edge sealing treatment is carried out, the decoration is carried out smoothly, sealing decoration glue is roll-coated after electrostatic dust removal, and finally the decoration treatment is carried out to obtain an 18mm cabinet body board, according to the national environmental protection grade standard of GB 18580 and 2001, the environmental protection grade of the 18mm cabinet body board reaches E0 grade, and according to the national flame-retardant standard of GB 8624 and 2012, the flame-retardant grade of the 18mm cabinet body board reaches B1 grade.
Example 2:
referring to fig. 1, a 10mm flame-retardant shaving board 1, a 0.45mm aluminum material 2 and a 0.5mm wood veneer 3 are respectively selected as an interlayer, a coating layer and a skin layer of a cabinet body board, the preparation method of the cabinet body board of the embodiment is the same as that of embodiment 1, a 13mm cabinet body board is obtained, the environment-friendly grade of the 13mm cabinet body board can also reach the E0 level according to the national environment-friendly grade standard of GB 18580-.
Example 3:
referring to fig. 1, a 17mm flame-retardant shaving board 1, a 0.65mm aluminum material 2 and a 1mm wood veneer 3 are selected as an interlayer, a coating layer and a skin layer of a cabinet body board respectively, the preparation method of the cabinet body board of the embodiment is the same as that of embodiment 1, a 22mm cabinet body board is obtained, the environmental protection grade of the 22mm cabinet body board reaches level E0 according to the national environmental protection grade standard of GB 18580-.
The data for the measurement of flame retardancy of examples 1 to 3 are shown below:
as can be seen from the above table, according to the above test methods, the items tested by the cabinet body panels obtained in examples 1-3 all meet the specified requirements of the flame performance C-s2, d0, t1, and the flame performance of the cabinet body panels in examples 1-3 also reaches the flame-retardant B level according to the national flame-retardant grade standard GB 8624-1(C-s2, do, t1) and comparing example 1 with example 3, the thicker the cabinet board the better the flame retardant performance.
Claims (10)
1. The preparation method of the environment-friendly flame-retardant mildew-proof deformation-proof cabinet body plate is characterized by comprising the following specific steps of:
s1 preparing an interlayer: selecting a flat shaving board as an interlayer, firstly performing double-sided fixed-thickness sand flattening, and then coating glue;
s2 manufacturing a coating layer: selecting an aluminum material as a coating layer, and flatly adhering the aluminum material to the front surface and the back surface of the shaving board through glue;
s3 constant temperature pressing treatment;
s4 cold pressing treatment at constant temperature;
s5 glue rolling coating;
s6 preparation of skin layer: selecting a veneer as a surface layer, and flatly attaching the veneer to the front surface and the back surface of the aluminum material coated with the shaving board through glue;
s7 preparing a semi-finished product: repeating S3-S4, and performing UV coating on the cabinet body plate through a UV coating production line to obtain a semi-finished cabinet body plate;
s8, preparing a finished product: and cutting the semi-finished cabinet body plate, and then performing edge sealing and modification treatment to obtain a final finished product.
2. The method for preparing the environment-friendly flame-retardant, mildew-proof and deformation-proof cabinet body board according to claim 1, wherein in S1, electrostatic precipitation and infrared preheating treatment are performed on a double-sided fixed-thickness sand flat particle board, and glue is coated on both the front and back surfaces of the particle board.
3. The method for preparing the environment-friendly flame-retardant, mildew-resistant and deformation-resistant cabinet plate as claimed in claim 1, wherein in S2, the aluminum material is subjected to electrostatic precipitation treatment before being adhered to the particle board, then is subjected to chemical treatment, and then is flatly adhered to the front and back surfaces of the particle board.
4. The method for preparing the environmentally friendly flame retardant, mold and deformation resistant cabinet plate as claimed in claim 1, wherein in S3, the constant temperature pressing treatment is performed by performing constant temperature treatment through an infrared constant temperature channel and then performing pressing treatment through a pressing wheel.
5. The method for preparing the environmentally friendly flame retardant, mildew resistant and deformation preventing cabinet body plate as claimed in claim 1, wherein in the step S4, the constant temperature cold pressing treatment is performed for 40-50 minutes in a constant temperature space at 25-35 ℃ and then for 6-8 hours at 10-15 ℃.
6. The method for preparing the environment-friendly flame-retardant, mildew-resistant and deformation-resistant cabinet body plate according to claim 1, wherein in S5, the glue is applied by rolling glue on the front and back surfaces of the aluminum material coated with the shaving board through glue application wheels.
7. The method for preparing the environmentally friendly flame retardant, mildew resistant and deformation resistant cabinet plate as claimed in claim 1, wherein in S6, before the veneer is attached to the front and back surfaces of the aluminum material, the veneer is subjected to constant temperature maintenance treatment in a constant temperature space at 25-35 ℃, and then the moisture content of the veneer is controlled to 8% -12%.
8. The method for preparing the environmentally friendly cabinet board with flame retardant, anti-mildew and anti-deformation functions as claimed in claim 1, wherein in S7, the cold pressing treatment time is 8-12 hours when repeating S4.
9. The method for preparing the environmentally friendly flame retardant, mildew resistant and deformation resistant cabinet body plate as claimed in claim 1, wherein in S8, the edge sealing and the modification treatment are performed by performing edge sealing treatment on an aluminum wood combination product, then performing modification and flattening, then performing electrostatic dust removal, applying glue, and then performing modification treatment.
10. The method for preparing the environment-friendly flame-retardant, mildew-resistant and deformation-resistant cabinet body plate as claimed in claim 1, wherein the thickness of the shaving plate is 9-15mm, the thickness of the aluminum material is 0.2-0.8 mm, and the thickness of the veneer is 0.04-1.5 mm.