WO2009069928A2 - Separator having porous coating layer, method for manufacturing the same and electrochemical device having the same - Google Patents
Separator having porous coating layer, method for manufacturing the same and electrochemical device having the same Download PDFInfo
- Publication number
- WO2009069928A2 WO2009069928A2 PCT/KR2008/006944 KR2008006944W WO2009069928A2 WO 2009069928 A2 WO2009069928 A2 WO 2009069928A2 KR 2008006944 W KR2008006944 W KR 2008006944W WO 2009069928 A2 WO2009069928 A2 WO 2009069928A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- separator
- binder
- coating layer
- crosslinked
- reactive groups
- Prior art date
Abstract
Description
Claims