WO2009059695A1 - Nanopartikelmodifizierte polyisocyanate - Google Patents
Nanopartikelmodifizierte polyisocyanate Download PDFInfo
- Publication number
- WO2009059695A1 WO2009059695A1 PCT/EP2008/009003 EP2008009003W WO2009059695A1 WO 2009059695 A1 WO2009059695 A1 WO 2009059695A1 EP 2008009003 W EP2008009003 W EP 2008009003W WO 2009059695 A1 WO2009059695 A1 WO 2009059695A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- formula
- modified
- group
- polyisocyanates
- groups
- Prior art date
Abstract
Description
Claims