Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B22—CASTING; POWDER METALLURGY
  • B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
  • B22D35/00—Equipment for conveying molten metal into beds or moulds
  • B22D35/06—Heating or cooling equipment
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J19/00—Chemical, physical or physico-chemical processes in general; Their relevant apparatus
  • B01J19/02—Apparatus characterised by being constructed of material selected for its chemically-resistant properties
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
  • C04B35/56—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides
  • C04B35/565—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on carbides or oxycarbides based on silicon carbide
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
  • C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/66—Monolithic refractories or refractory mortars, including those whether or not containing clay
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
  • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
  • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
  • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
  • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
  • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
  • C04B2235/3418—Silicon oxide, silicic acids, or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
  • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
  • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
  • C04B2235/3427—Silicates other than clay, e.g. water glass
  • C04B2235/3463—Alumino-silicates other than clay, e.g. mullite
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
  • C04B2235/74—Physical characteristics
  • C04B2235/77—Density
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
  • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
  • C04B2235/9607—Thermal properties, e.g. thermal expansion coefficient
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
  • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
  • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
  • C04B2235/9669—Resistance against chemicals, e.g. against molten glass or molten salts
  • C04B2235/9676—Resistance against chemicals, e.g. against molten glass or molten salts against molten metals such as steel or aluminium

Definitions

• This invention relates to apparatus used for conveying molten metals during casting operations and the like. More particularly, the invention relates to apparatus for and methods of providing heat to molten metals conveyed in such apparatus to prevent metal freeze-up, undue cooling, or similar effects, during the passage through such apparatus.
• a molten metal it is common practice during metal casting operations to cause a molten metal to flow through an elongated trough (sometimes called a launder), for example from a melting furnace to a casting mold.
• troughs are made of a material that can resist exposure to the molten metal for a reasonable period of time without undue damage, and the conditions must be such that the metal does not cool below its freezing temperature (solidus) before it reaches its destination.
• solidus freezing temperature
• troughs of this kind are fairly short, fast-flowing (e.g. relatively steeply inclined) or of relatively small metal-holding capacity, there is little risk of metal freezing.
• fast-flowing e.g. relatively steeply inclined
• metal-holding capacity there is little risk of metal freezing.
• various new practices have made it necessary to provide troughs of greater capacity, greater length and/or slower flow, particularly in the aluminum treatment arts.
• U.S. patent No. 5,527,381 to Peter D. Waite, et al. which issued on June 18, 1996, discloses a method of treating a molten metal with a gas to remove dissolved hydrogen and other impurities as the metal flows through a trough or launder.
• the treatment can be made more thorough if the trough is of large metal-holding capacity and the metal is caused to flow at a slow rate of throughput.
• molten metal used for a cladding layer of such an ingot is generally cast in much smaller amounts than the molten metal used for a core layer, so that the metal for the cladding layer must flow more slowly to the casting apparatus than the metal for the core.
• molten metal is sometimes filtered through ceramic foam filters to remove solid particles, and the use of such filters may slow the flow of molten metal through a trough. Consequently, in applications such as these and others, the risk of metal solidification (or undue cooling) in the trough is increased.
• One way of eliminating the risk of metal solidification is to heat the metal in the trough or the trough itself.
• Metal in the trough can be heated by directing a flame onto the upper surface of the metal as it flows through the trough, but this has the disadvantage that oxidation of the metal at the surface is thereby accelerated, particularly if the metal is aluminum or an aluminum alloy.
• Heating of the trough can be carried out by providing electrical heaters on or adjacent to the inner surface of the trough, but generally such heaters are slow to transfer heat to the metal and are therefore not always very effective in applications of this kind.
• Two patents illustrate the kind of approach taken in the past.
• a method and apparatus are provided for providing heat to a molten metal flowing through a metal conveying apparatus.
• Hot combustion gases generated by a burner or the like, are used to heat a heat-conductive material that comes into contact with the molten metal.
• the hot combustion gases are kept out of contact with the molten metal and are used to heat the metal solely by conduction through the refractory material.
• the heat-conductive material may be used to form a section of a trough, a channel element, or just a part of a trough or channel, or as an insert or body contacting the molten metal.
• the gases brought into contact with the heat-conductive material are confined within one or more enclosures that allow the gases to flow through the apparatus in the form of a stream while preventing contact of the combustion gases with isolated the molten metal (and preferably also the external atmosphere surrounding the apparatus).
• One exemplary embodiment provides a molten metal-conveying apparatus, comprising a molten metal-conveying channel, an enclosure for receiving and circulating combustion gases while preventing entry of said gases into said channel, a heat-conductive body of material separating at least part of said channel from said enclosure, and a combustion device for generating combustion gases and delivering said gases to said enclosure.
• a molten metal-conveying apparatus comprising a molten metal-conveying channel, an enclosure for receiving and circulating combustion gases while preventing entry of said gases into said channel, a heat-conductive body of material separating at least part of said channel from said enclosure, and a combustion device for generating combustion gases and delivering said gases to said enclosure.
• heat from said combustion gases is transferred to molten metal held in said channel through said body of heat conductive material.
• the molten metal is heated by the combustion gases, but the gases are kept out of direct contact with the molten metal in the channel.
• the heat-conductive body of material may form an elongated element (with a metal-contacting surface defining the channel and another surface contacting the combustion gases, e.g. an outside surface of the elongated element).
• the elongated element may be an open-topped trough section or an enclosed tube or tubes.
• the heat-conductive body of material may be separate from an element defining the channel, e.g. it may be a tubular member extending into the channel formed in an elongated element.
• the invention provides a molten metal conveying trough apparatus.
• the apparatus includes a molten metal conveying trough section having an upper end and an outer surface extending around the trough section from the upper end.
• An enclosure at least partially encloses the outer surface of the trough section, and the enclosure contains at least one chamber adjacent to the outer surface.
• An entrance into the chamber, or an entrance into each chamber when there is more than one, is provided through which hot combustion gases are introduced into the or each chamber.
• An exit from the or each chamber is also provided through which the hot combustion gases are removed after flowing as a stream through the chamber(s), thereby transferring heat into the trough section through the outer surface thereof.
• the apparatus preferably additionally comprises at least one generator of hot combustion gases, such as a fuel burner, positioned at the entrance of the or each chamber.
• Another exemplary embodiment provides a method of providing heat to a molten metal flowing through metal-conveying apparatus provided with at least one channel for conveying said molten metal, an enclosure for receiving and circulating combustion gases and a body of heat-conductive material separating at least part of said channel from said enclosure, said method comprising conveying molten metal through the channel, generating combustion gases, causing the combustion gases to enter and circulate through the enclosure while confining said combustion gases to prevent said gases entering said channel.
• Yet another exemplary embodiment provides a method of heating a section of a molten metal conveying trough having an upper end and an outer surface extending around the trough section from the upper end.
• the method comprises generating at least one stream of hot combustion gases, and directing the at least one stream to flow through an enclosed volume surrounding at least part of the outer surface of the molten metal conveying trough section.
• the outer surface of the trough is thereby exposed to the stream of hot combustion gases, thereby causing heat to transfer to the trough section and its contents through the outer surface.
• the hot combustion gases are generated by a burner that creates a stream of hot gases and a flame introduced into the enclosure.
• the combustion gases are normally used directly, i.e.
• the hot combustion gases are preferably confined to follow a winding path while in contact with the heat conductive refractory material and, ideally, substantially all of the surface of the heat conductive material opposite to the metal-contacting surface is exposed to the hot gases.
• the heat-conductive body may be made of any material that has sufficient heat conductivity to allow heat to pass at an effective rate from the hot combustion gases to the molten metal in the channel when used in thicknesses appropriate to provide good support for the molten metal and a robust apparatus.
• An "effective rate" of heat passage is, of course, a rate sufficient to achieve the desired effect (e.g. molten metal heating, metal temperature retention, or slowed cooling of the metal as it passes through the channel). While any effective thickness of material may be used, thinner cross-sections are better because they are less resistant to the passage of heat, provided adequate strength is retained. The thickness selected is generally no greater than that required for adequate strength of the trough section and good support of the molten metals.
• Suitable heat conductive materials include, for example, refractory metal compounds or solid metals. Many solid metals are attacked by flowing molten metal of the same or a different kind and are therefore not suitable, unless the metal-contacting surface is protected in some way. Cast iron has been found to have a good resistance to attack by molten metal (e.g.
• a refractory metal compound e.g. boron nitride.
• Refractory metal compounds may be used instead of metal, provided they have good thermal conductivity or can be used in thin sections. Such materials are generally strong at high temperatures, resistant to thermal shock, un reactive with molten metal, and have low coefficients of expansion.
• refractory metal oxides e.g. alumina, silica and calcium oxide, are generally regarded as heat insulators may not be suitable (unless mixed with more conductive materials or used in very thin sections) because they have low thermal conductivity (e.g. usually less than about 2 Watts/meter-Kelvin (W/mK).
• silicon carbide, boron nitride and silicon nitride are suitable materials (although boron nitride is extremely expensive, and is therefore unlikely to be used in practice while its price remains so high).
• heat-conductive refractories containing silicon carbide are particularly preferred, sometimes protected with a layer of silica to prevent oxidation at high temperatures.
• silicon carbide may be used in its pure form, it is generally mixed in granular form with binders and other refractory compounds in water, cast, dried and cured to form a dense solid. The larger the proportion of silicon carbide, the higher is the heat conductivity of the resulting refractory.
• FIG. 1 is a top plan view of an apparatus according to one embodiment of the present invention.
• Fig. 2 is a side view of the apparatus of Fig. 1 ;
• Fig. 3 is an end view of the apparatus of Fig. 1 ;
• Fig. 4 is a vertical transverse cross section of the apparatus of Fig. 1 taken on the line IV-IV shown in Fig. 2;
• Fig. 5 is a horizontal cross section of the apparatus of Fig. 1 taken on the line V-V shown in Fig. 2;
• Fig. 6 is a vertical longitudinal cross section of the apparatus of Fig.
• Fig. 7 is a central vertical longitudinal cross section of the apparatus of Fig. 1 taken on the line VII-VII shown in Fig. 1;
• Fig. 8 is a cross-section similar to Fig. 5 of an alternative embodiment of the present invention;
• Fig. 9 is a cross-section similar to that of Fig. 7, but showing a modified embodiment in which the trough has a constant depth throughout its length, and an insulating cover over the open top;
• Fig. 10 is a cross-section of an alternative exemplary embodiment.
• Fig. 11 is a cross-section of yet another alternative embodiment.
• FIG. 1 to 7 of the accompanying drawings A first exemplary embodiment of a molten metal conveying apparatus is shown in Figs. 1 to 7 of the accompanying drawings.
• This particular embodiment is intended for use with metal degasser nozzles intended for use with molten aluminum or aluminum alloys, thereby forming a compact in-line metal degasser unit which may, for example, be incorporated into a conventional trough or launder leading from a metal melting furnace to a casting apparatus.
• Other exemplary embodiments may be intended for use with other molten metals.
• the apparatus is indicated generally by reference numeral 10 and includes a section 11 of metal-conveying trough made up of two trough parts 12 and 13 abutting each other at a junction 14.
• the trough section is indicated generally by reference numeral 10 and includes a section 11 of metal-conveying trough made up of two trough parts 12 and 13 abutting each other at a junction 14.
• the trough section is indicated generally by reference numeral 10 and includes a section 11 of metal-conveying trough made up of two trough parts 12 and 13 abutting each other at a junction 14.
• I 1 acts as an elongated channel-forming element that conveys molten metal through the apparatus. Butting up to the trough section 11 at an upstream end is a trough inlet member 15, and butting up to the trough section 11 at a downstream end is a trough outlet member 16. All of these parts are of generally U-shaped cross-section and are made of a body of heat-conductive refractory ceramic material, the same material preferably being used for all these parts. While most molten metal-conveying troughs are made of insulating refractories, e.g. metal oxides, designed to prevent undue cooling of the molten metal as it is conveyed through the trough, the trough section 11 is instead heat conductive.
• insulating refractories e.g. metal oxides
• the preferred refractory material used for this purpose is a dense cast ceramic having a high thermal conductivity made of or containing silicon carbide (SiC). This material is resistant to high temperature and attack by aluminum and most aluminum alloys at their normal casting temperatures.
• the heat conductivity of such ceramics increases as the content of SiC increases and therefore it is desirable to use at least 25%, more preferably at least 50%, and even more preferably at least 65% of SiC in the composition.
• Pure cast SiC may be used, but is expensive and somewhat brittle.
• a particularly preferred material has the following composition:
• This material has a density of about 2.4 grams per cc and a heat conductivity in the range of 9.4 to 10.8 VWmK.
• inlet member 15, trough section 11 and outlet member 16 are firmly held together, possibly under resilient longitudinal compression provided by spring-loaded end plates (not shown), usually without any jointing or sealing compound, to form a continuous elongated open-topped channel 17 for conveying molten metal in the direction of arrow A from one side of the apparatus to the other.
• the inlet and outlet members are, in use, joined to other metal-conveying apparatus or trough parts using standard means of attachment.
• the inlet member 15 and outlet member 16 incorporate slight downward slopes from their respective outer ends to their inner ends, thereby making the channel 17 somewhat deeper within the trough section 11 than at the extreme inlet and outlet ends (see Fig. 7).
• a deep section of this kind in a trough may make it difficult to remove all of the metal between metal-conveying operations, so the trough section 11 and members 15 and 16 may alternatively be made of constant depth, if preferred.
• the trough section 11 has an upper end 23, an inner surface 18 defining part of the channel 17 and an outer surface 19 forming flat side walls 20 and flat bottom wall 21 delimiting the physical outer dimension of the trough section. Since the open channel 17 occupies most of the upper end 23, there is virtually no trough outer surface at the upper end of the trough. The thickness of the channel section between the inner surface 18 and the outer surface 19 is sufficient to confine and support the molten metal without yielding. It can be seen that the channel 17 formed within the trough section 11 is relatively broad and deep so that it can hold quite a large quantity of molten metal when sufficiently filled (e.g. up to the level 22 shown by broken line in Fig. 4).
• the channel section may be shaped and dimensioned differently to suit particular applications, and may be, for example, rectangular, V-shaped or semi-cylindrical.
• the apparatus of this exemplary embodiment is intended to be used with metal degassers (e.g. spinning gas injectors, one of which 25 is represented in broken lines in Fig.
• the deep and broad shape and dimension of the channel 17 allows sufficient room for the immersion and use of such degassers, a good head of metal above the gas insertion points (which improves metal degassing and cleaning operations), and optionally a relative slow rate of metal flow through the channel of about 3 meters/minute or less (in other applications where the channel section is used primarily for metal delivery, a higher flow rate of 4 to 9 meters/minute is more common and preferred).
• the particular cross-sectional shape and size of the channel 17 also means that the ratio of the molten metal surface 22 exposed to the atmosphere relative to the volume of contained molten metal is quite small, so surface oxidation does not present as much of a problem as would be the case for a shallower or wider trough.
• a cover (not shown in this embodiment, but see element 60 of Fig. 9) may be positioned over the channel 17 to reduce heat loss from the molten metal, although, in this embodiment, such a cover (if used) requires holes to allow the gas injectors 25 to pass through.
• the trough section 11 is surrounded on all sides, except at the open top 26 of the channel 17, by an enclosure in the form of a housing 30 comprising a metal-sided tank 31 lined with heat insulating refractory material 32 made, for example, of fire bricks stacked side-by-side or one on top of another, optionally without any jointing or sealing compounds, although a refractory mortar may be used between the bricks, if desired.
• the open top of the tank is wider than the trough section 11 and the gaps between the sides of the tank and the upper edges of the trough section are also bridged and closed off by refractory blocks 33, e.g.
• trough section 11 is supported by a short vertical wall 35 rising upwardly from the floor of the tank along the longitudinal centerline, and also by a vertical wall 36 extending transversely of the trough section (see Fig. 5 in particular).
• the junction 14 of the two parts 12 and 13 of the trough section is aligned with wall 36 to prevent slippage between the parts. Any tendency of the trough section 11 to sag or slip under the weight of the metal at the operating temperature is thus avoided by the underlying rigid and effective support provided by walls 35 and 36.
• the outlet member 16 of the trough is retained within an open-topped metal shell 37 held in place by an open-topped rectangular bracket 38 bolted to end wall 39 of the tank.
• a similar arrangement is provided for the inlet member 15 of the trough at the other end of the apparatus.
• the interior of the housing 30 incorporates two hollow chambers 40 forming enclosed spaces isolated from the outside atmosphere and mutually aligned with one following the other in the longitudinal direction of the apparatus.
• the chambers 40 are separated by transverse wall 36 which extends closely around the outer surface 19 of the trough section 1 1 (see Fig. 6) and thereby isolates the atmospheres within the two chambers from each other.
• Each chamber 40 is divided down the center by longitudinal wall 35 to form two hollow compartments 41 , but these compartments communicate with each other by virtue of the fact that the longitudinal walls 35 do not extend fully up to the transverse wall 36, leaving gaps 43 on each side.
• substantially all of the outer surface 19 of the trough section 1 1 should be encircled by the housing and chambers, i.e. at least those parts of the trough between end walls 39 and 45 of the housing. In some embodiments, however, it may be possible to enclose less of the outer surface of the trough, i.e. the upper end of the trough may stand clear of the housing, or the bottom wall of the trough may rest on the bottom of the tank and may not be exposed to the internal chambers 40.
• At least 50%, and more preferably at least 75%, and optionally at least 95% of the outer surface of the trough section is enclosed and encircled by the internal compartments and chambers, thereby ensuring (as will be explained) good and even heat delivery to the trough section and molten metal contained therein.
• Any parts of the trough that are not enclosed in this way may, if desired, be covered by a layer of heat insulating material to prevent undue heat loss from these parts.
• substantially the entire outer surface 19 of the trough section 1 1 is surrounded by and directly exposed to the internal compartments 41 of each chamber 40, i.e. not only at the sides 20 but also along the bottom 21.
• the only parts of the trough section not directly exposed to these hollow compartments are the parts supported by the walls 35 and 36, and the parts in contact with the refractory material 33 at the top edges. These parts of the trough section add up to only a small percentage of the outer wall of the trough section.
• Two openings 46 and 47 are formed in each of the end walls 39 and 45 of the tank 31 and pass through the adjacent refractory lining. Openings 46 are intended as inlets for hot combustion gases into the respective chambers 40, and openings 47 are intended as outlets for such gases (and are normally each connected to gas exhaust piping, not shown).
• Fuel burners 50 are positioned in or adjacent to the inlet openings 46 to generate streams of hot combustion gases, and optionally flames 51 , and to introduce them into the compartments 41 , as shown in Fig. 5.
• the hot gases circulate between the compartments 41 in each of the chambers 40 by virtue of the gaps 43 positioned at a distance from each of the inlets and outlets. This circulation of hot gases is represented by arrows B.
• the gases eventually leave the apparatus via the outlets 47, as represented by arrows C.
• the hot gases are free to ascend along the sides of the trough section 11 , as shown by arrows D, so that the substantially the entire outer surface 19 of the trough section 11 is exposed to and bathed in the hot circulating combustion gases during operation of the burners.
• the movements represented by arrows B, C and D form a steady stream of hot gases flowing through the chambers 40.
• the chambers are completely enclosed within the housing 30 and are sealed against loss of gases, except at inlets and outlets 46 and 47, so the streams of hot combustion gases are constrained to follow a winding or sinuous or serpentine path through each chamber, i.e. from compartment to compartment 41 via the distant gap 43 with the gases flowing in opposite directions in each compartment.
• the combustion gases are channeled and constrained in such a way that they are prevented from entering the channel 17 and coming into contact with the molten metal conveyed through the apparatus.
• trough section 11 is heated at its outer surface 19 by both radiant heat from the flames 51 and conduction/convection from direct contact with the hot combustion gases.
• the relatively good heat conductivity of the material of the trough section 11 allows the heat to penetrate through the trough section and into the channel 17 and molten metal held therein.
• the openings 46 and 47, and the burners 50, are preferably positioned and angled such that flames 51 and the stream of hot gases are not initially directed onto the outer surface 19 of the trough section 11 , nor onto the refractory lining 32, 33, thereby avoiding the formation of hot-spots and possible damage to the refractory surfaces.
• the flame and hot gases from the burners 50 are generally oriented horizontally in the longitudinal direction of the trough section into an open area of each chamber 40 beneath the level of the bottom wall of the trough section. This arrangement also ensures good heat distribution across the entire outer surface 19 of the trough section and thus prevents the formation of cool spots within the metal channel 17. It will be noted that the hot gases passing through the chambers 40 encounter only the refractory of the tank lining or the refractory of the trough section so that the high temperatures are accommodated without damage to the apparatus or undue heat loss.
• the burners 50 which may for example be gas-fired or oil-fired, are provided with suitable heating capacity to raise the temperature in the chambers quickly and to introduce sufficient heat into the trough section 11 to raise the temperature of the molten metal in channel 17, to keep the temperature of the molten metal constant, or to allow the molten metal to cool in a controlled manner, depending on the plans for the metal.
• suitable burners are so-called premix burners that are aspirated at the spud and the burner throat created by the velocity of gas moving through a nozzle.
• the mix of fuel and air may be controlled by a manual valve, or may be controlled automatically, e.g. by a computer following a pre-determined program.
• the combustion gases have a temperature in the range of 500 to 2000 0 C or more when introduced into the apparatus, and are thus capable of delivering heat rapidly and in unlimited quantities.
• the ceramic material of the trough section may be raised quickly to a suitable high temperature by the burners when the apparatus is first put into operation, and such temperature can be maintained indefinitely during normal metal flow.
• the apparatus may be heated by the combustion gases before metal is caused to flow through the trough, thereby avoiding rapid cooling of the metal as the first flow of the hot metal pours into the apparatus.
• thermocouples 55, 56 are provided to control the temperature of each chamber, one (55) for the control of the temperature of the trough and/or the metal within the trough, and the other (56) for control of over-temperature within the chamber.
• Trough temperature is taken outside the fire box near to the burner via thermocouple 55 positioned in direct contact with the trough.
• a thermocouple may be provided in contact with the molten metal and extending into the trough from the open upper end.
• thermocouple 56 is positioned in contact with the refractory 32 in the coolest part of the chamber.
• the burner 50 is then cycled between two control points, i.e. low metal temperature cycles the burner on, and high chamber temperature cycles the burner off.
• Backup thermocouples 57 are also provided in case of failure of the primary thermocouples.
• Thermocouples may be provided only on one long side of the housing 30, but may alternatively be positioned on both sides.
• the thermocouples are provided on the burner side of a chamber, but the burner of each chamber may be positioned differently in different installations due to such considerations as available space and exhaust facilities, etc., so it is prudent to provide thermocouples on each side during the production of the apparatus.
• the burners of one chamber may be positioned on the opposite transverse side from the burner of the other in contrast to the same-sided arrangement shown in the drawings. Indeed, this may be preferred for even distribution of heat along the trough section.
• Fig. 1 to 7 represent an exemplary embodiment in which there are two longitudinal heating chambers 40 within the housing, each divided into two lateral compartments 41 , which is an arrangement that is normally preferred.
• a relatively short trough section there may be just a single chamber with two compartments, one inlet, one outlet and one fuel burner (the inlet and outlet being positioned in the same side wall, and the chamber extending for the full length of the trough section).
• more than two chambers may be provided.
• Fig. 8 is a view similar to Fig. 5, but showing a three-chamber apparatus. In this case, an additional chamber 40' is positioned between two end chambers 40.
• the additional chamber has a divider wall 36' that divides the chamber into two compartments 41' and forces the hot combustion gases entering the chamber 40' through side inlet 46' from burner 50' to extend around the end of the divider wall as shown by arrows B' before emerging from the compartment at side outlet 47'.
• Additional similar chambers may be provided, if required. It is to be noted that the provision of more burners and chambers makes it possible to introduce greater amounts of heat into the apparatus and offers a more precise control of temperature or temperature profile along the channel.
• Figs. 1-7 (and also Fig. 8) is intended to provide a trough section suitable for use with metal degasser nozzles and is therefore quite deep.
• Fig. 9 shows an alternative embodiment having a shallower trough section 11 intended for more general use for conveying molten metal from one location to another.
• the floor of the trough section 11 is flat throughout its length and there are no trough inlet and outlet members as in the earlier apparatus.
• the overall height of the trough section 11 should preferably be approximately 100mm above the metal level 22 for safety.
• an insulating cover 60 may be positioned over the open upper end of the trough section to provide heat insulation for the molten metal.
• the length of the trough section is normally about 6.5 ft. and the two burners combined are capable of generating a maximum of at least 600,000 Btu/hr, or 92,000 Btu/hr/ft during apparatus heat-up (for a total of 600,000 Btu/hr).
• the output of the burners may be scaled back to about 360,000 Btu/hr, or 55,000 Btu/hr/ft.
• the burners may consume 12,000 liters per minute of gas at maximum output.
• the amount of air supplied to the burners should be an amount suitable for complete combustion of the gas to carbon dioxide (usually an excess of 3% over the stoichiometrical amount required for complete combustion), e.g. 120,000 liters per minute.
• This degree of heating ideally keeps the metal within a suitable temperature range, e.g. 20 0 C above the liquidus (or a minimum of 350 0 C) up to 1300 0 C (for aluminum and aluminum alloys), and up to about 850 0 C, or even up to about 1000 0 C.
• a particularly preferred range is 650-725 0 C. It is to be noted that a large amount of the heating effect may be brought about by radiant heating as well as convection heating.
• the metal movement through the trough section is generally expressed in terms of mass flow.
• the preferred rate is 86-550 lbs/minute, or about 2-5 cm/sec, although there is really no lower limit as the metal may be kept molten even when it is stationary.
• the flow should not be so fast that it becomes turbulent, which often occurs within the range of 15-20 cm/sec.
• those sections may also be heated, but by other means, e.g. by electrical heaters embedded in the trough walls or used to produce radiant heat from above.
• molten metal 22 is conveyed through six parallel tubes 111 made of a heat conductive material, preferably containing silicon carbide.
• the tubes have inner, metal-contacting, surfaces 118 and outer surfaces 119 that remain out of contact with the molten metal.
• the tubes are surrounded by an enclosure 132 made of an insulating refractory material, e.g. a material made of refractory metal oxides.
• the enclosed space between the exterior of the tubes 111 and the interior of the enclosure 132 forms a passage 141 through which hot combustion gases are caused to flow and circulate (e.g. a burner is provided at an inlet at one longitudinal end of the enclosure 132 and a vent for the gases is proved at an opposite longitudinal end).
• the metal within the tubes 111 is kept hot by heat from the combustion gases passing through the walls of the tubes 111 , whereas heat is retaining within the apparatus 110 by the insulation provided by the enclosure 132.
• the hot combustion gases in the channels formed by the tubes do not contact the molten metal as the gases are confined to follow a separate path and are vented before the molten metal exits the apparatus.
• molten metal 22 is conveyed through an elongated trough 250 made of a heat insulating material, e.g. a material made of refractory metal oxides.
• a body 211 of heat conductive material preferably a refractory substance made of or containing silicon carbide.
• the body is fabricated in the form of a hollow tubular element encircling an enclosed space 240.
• the body 211 has an outer surface 218 that contact the molten metal in the trough, and an inner surface 219 that is out of contact with the metal. Hot combustion gases are caused to flow through the enclosed space 240, e.g.
• the body 211 consequently confines and circulates the hot gases and keeps the gases out of contact with the molten metal in the trough 250.
• the molten metal is kept hot by heat from the combustion gases that passes through the conductive walls of the body 211.
• a removable cover 260 is provided to reduce heat losses from the surface of the molten metal.
• SiC are of very high thermal conductivity, and may thus be used in the illustrated embodiments when sufficiently strong and durable.
• a preferred range of thermal conductivity is at least about 2.5 W/mK, e.g. in the range of about 2.5 to 200 W/mK, with more preferred ranges being 5 to 80 W/mK and 7 to 25 W/mK.

Landscapes

• Engineering & Computer Science (AREA)
• Chemical & Material Sciences (AREA)
• Ceramic Engineering (AREA)
• Organic Chemistry (AREA)
• Materials Engineering (AREA)
• Structural Engineering (AREA)
• Manufacturing & Machinery (AREA)
• Mechanical Engineering (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Vertical, Hearth, Or Arc Furnaces (AREA)
• Waste-Gas Treatment And Other Accessory Devices For Furnaces (AREA)
• Furnace Charging Or Discharging (AREA)
• Furnace Details (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=39535932

Family Applications (1)

Country Status (10)

Cited By (5)

Families Citing this family (23)

Citations (5)

Family Cites Families (17)

• 2007
  • 2007-12-17 BR BRPI0720413-2A patent/BRPI0720413A2/pt not_active IP Right Cessation
  • 2007-12-17 WO PCT/CA2007/002275 patent/WO2008074134A1/en active Application Filing
  • 2007-12-17 KR KR1020097014999A patent/KR20090095651A/ko not_active Application Discontinuation
  • 2007-12-17 JP JP2009541706A patent/JP2010513029A/ja not_active Withdrawn
  • 2007-12-17 CN CNA2007800515133A patent/CN101610863A/zh active Pending
  • 2007-12-17 RU RU2009125202/02A patent/RU2009125202A/ru not_active Application Discontinuation
  • 2007-12-17 EP EP07855557A patent/EP2107956A1/de not_active Withdrawn
  • 2007-12-17 CA CA002673272A patent/CA2673272A1/en not_active Abandoned
  • 2007-12-18 US US12/002,989 patent/US20080163999A1/en not_active Abandoned
• 2009
  • 2009-07-13 NO NO20092643A patent/NO20092643L/no not_active Application Discontinuation

Patent Citations (5)

Also Published As

Similar Documents

Legal Events