WO2008071690A2 - Feinteilige, kationische polymerdispersionen - Google Patents
Feinteilige, kationische polymerdispersionen Download PDFInfo
- Publication number
- WO2008071690A2 WO2008071690A2 PCT/EP2007/063684 EP2007063684W WO2008071690A2 WO 2008071690 A2 WO2008071690 A2 WO 2008071690A2 EP 2007063684 W EP2007063684 W EP 2007063684W WO 2008071690 A2 WO2008071690 A2 WO 2008071690A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- cationic
- acrylate
- monomers
- ethylenically unsaturated
- Prior art date
Abstract
Description
Claims