WO2008060795A2 - Articles antimicrobiens et procédé de fabrication - Google Patents

Articles antimicrobiens et procédé de fabrication Download PDF

Info

Publication number
WO2008060795A2
WO2008060795A2 PCT/US2007/081477 US2007081477W WO2008060795A2 WO 2008060795 A2 WO2008060795 A2 WO 2008060795A2 US 2007081477 W US2007081477 W US 2007081477W WO 2008060795 A2 WO2008060795 A2 WO 2008060795A2
Authority
WO
WIPO (PCT)
Prior art keywords
silver
substrate
article
salt
group
Prior art date
Application number
PCT/US2007/081477
Other languages
English (en)
Other versions
WO2008060795A3 (fr
Inventor
David R. Holm
Scott A. Burton
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Priority to AU2007319586A priority Critical patent/AU2007319586A1/en
Priority to JP2009533475A priority patent/JP2010506945A/ja
Priority to EP07868453A priority patent/EP2081581A2/fr
Priority to BRPI0716001-1A2A priority patent/BRPI0716001A2/pt
Priority to US12/444,877 priority patent/US20100098949A1/en
Priority to MX2009004030A priority patent/MX2009004030A/es
Priority to CN2007800390994A priority patent/CN101528242B/zh
Priority to CA002666826A priority patent/CA2666826A1/fr
Publication of WO2008060795A2 publication Critical patent/WO2008060795A2/fr
Publication of WO2008060795A3 publication Critical patent/WO2008060795A3/fr

Abstract

L'invention concerne des articles antimicrobiens et des procédés de fabrication de tels articles.
PCT/US2007/081477 2006-10-18 2007-10-16 Articles antimicrobiens et procédé de fabrication WO2008060795A2 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
AU2007319586A AU2007319586A1 (en) 2006-10-18 2007-10-16 Antimicrobial articles and method of manufacture
JP2009533475A JP2010506945A (ja) 2006-10-18 2007-10-16 抗菌性物品及び製造方法
EP07868453A EP2081581A2 (fr) 2006-10-18 2007-10-16 Articles antimicrobiens et procédé de fabrication
BRPI0716001-1A2A BRPI0716001A2 (pt) 2006-10-18 2007-10-16 artigos microbicidas e mÉtodos e fabricaÇço dos mesmos
US12/444,877 US20100098949A1 (en) 2006-10-18 2007-10-16 Antimicrobial articles and method of manufacture
MX2009004030A MX2009004030A (es) 2006-10-18 2007-10-16 Articulos antimicrobianos y metodos de fabricacion.
CN2007800390994A CN101528242B (zh) 2006-10-18 2007-10-16 抗微生物制品及其制造方法
CA002666826A CA2666826A1 (fr) 2006-10-18 2007-10-16 Articles antimicrobiens et procede de fabrication

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US96653106P 2006-10-18 2006-10-18
US793106P 2006-10-18 2006-10-18
US61/007,931 2006-10-18
US60/966,531 2006-10-18

Publications (2)

Publication Number Publication Date
WO2008060795A2 true WO2008060795A2 (fr) 2008-05-22
WO2008060795A3 WO2008060795A3 (fr) 2008-08-28

Family

ID=39304830

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/081477 WO2008060795A2 (fr) 2006-10-18 2007-10-16 Articles antimicrobiens et procédé de fabrication

Country Status (9)

Country Link
EP (1) EP2081581A2 (fr)
JP (1) JP2010506945A (fr)
KR (1) KR20090066304A (fr)
CN (1) CN101528242B (fr)
AU (1) AU2007319586A1 (fr)
BR (1) BRPI0716001A2 (fr)
CA (1) CA2666826A1 (fr)
MX (1) MX2009004030A (fr)
WO (1) WO2008060795A2 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100190004A1 (en) * 2008-11-24 2010-07-29 Gibbins Bruce L Antimicrobial laminate constructs
US8192764B2 (en) 2006-01-13 2012-06-05 3M Innovative Properties Company Silver-containing antimicrobial articles and methods of manufacture
US8193267B2 (en) 2003-12-05 2012-06-05 3M Innovative Properties Company Polymer compositions with bioactive agent, medical articles, and methods
US20140171890A1 (en) * 2011-08-10 2014-06-19 R&T Fabric, Llc Antimicrobial Fabric and Method of Bactericidal Activation
WO2020094700A1 (fr) * 2018-11-07 2020-05-14 Universidade De Santiago De Compostela Composites polymères stables
CN115779131A (zh) * 2022-10-09 2023-03-14 湖南中腾湘岳生物科技有限公司 一种医用敷料的加工工艺及其医用敷料

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012246228A (ja) * 2011-05-25 2012-12-13 Atect Corp レジオネラ菌抗菌剤
EP2747572A4 (fr) * 2011-08-22 2015-04-29 Innovotech Inc Famille de composés de periodate d'argent (i) dotés de vastes propriétés antimicrobiennes
US9386772B2 (en) * 2012-02-14 2016-07-12 Allegiance Corporation Antimicrobial elastomeric articles
CN105062116A (zh) * 2015-07-27 2015-11-18 苏州天健竹业科技有限公司 瑜伽垫表层竹纤维复合材料及其制备方法
CN106751750A (zh) * 2016-11-21 2017-05-31 郑州源冉生物技术有限公司 一种鞋子用复合材料及其制备方法
JP2019199518A (ja) * 2018-05-16 2019-11-21 日本製紙株式会社 金属イオン含有セルロース繊維

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992018098A1 (fr) * 1991-04-10 1992-10-29 Capelli Christopher C Compositions antimicrobiennes utiles pour des applications medicales
US20060233889A1 (en) * 2005-04-14 2006-10-19 3M Innovative Properties Company Silver coatings and methods of manufacture

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2136455C (fr) * 1993-11-18 1999-06-29 Robert Edward Burrell Procede d'induction d'un effet anti-microbien avec des ions d'argent complexes
CN100382705C (zh) * 2003-06-10 2008-04-23 香港理工大学 纳米抗菌材料及其制备方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992018098A1 (fr) * 1991-04-10 1992-10-29 Capelli Christopher C Compositions antimicrobiennes utiles pour des applications medicales
US20060233889A1 (en) * 2005-04-14 2006-10-19 3M Innovative Properties Company Silver coatings and methods of manufacture

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8193267B2 (en) 2003-12-05 2012-06-05 3M Innovative Properties Company Polymer compositions with bioactive agent, medical articles, and methods
US8192764B2 (en) 2006-01-13 2012-06-05 3M Innovative Properties Company Silver-containing antimicrobial articles and methods of manufacture
US9289450B2 (en) 2006-01-13 2016-03-22 3M Innovative Properties Company Silver-containing antimicrobial articles and methods of manufacture
US20100190004A1 (en) * 2008-11-24 2010-07-29 Gibbins Bruce L Antimicrobial laminate constructs
US20140171890A1 (en) * 2011-08-10 2014-06-19 R&T Fabric, Llc Antimicrobial Fabric and Method of Bactericidal Activation
WO2020094700A1 (fr) * 2018-11-07 2020-05-14 Universidade De Santiago De Compostela Composites polymères stables
CN115779131A (zh) * 2022-10-09 2023-03-14 湖南中腾湘岳生物科技有限公司 一种医用敷料的加工工艺及其医用敷料
CN115779131B (zh) * 2022-10-09 2024-02-23 湖南中腾湘岳生物科技有限公司 一种医用敷料的加工工艺及其医用敷料

Also Published As

Publication number Publication date
MX2009004030A (es) 2009-04-27
CA2666826A1 (fr) 2008-05-22
AU2007319586A1 (en) 2008-05-22
KR20090066304A (ko) 2009-06-23
CN101528242B (zh) 2012-07-11
WO2008060795A3 (fr) 2008-08-28
BRPI0716001A2 (pt) 2013-07-30
CN101528242A (zh) 2009-09-09
EP2081581A2 (fr) 2009-07-29
JP2010506945A (ja) 2010-03-04

Similar Documents

Publication Publication Date Title
WO2008060795A2 (fr) Articles antimicrobiens et procédé de fabrication
US8399027B2 (en) Silver coatings and methods of manufacture
EP1979007B1 (fr) Articles antimicrobiens argentiferes et procedes de production
CN1889983B (zh) 银涂料和制造方法
US20100098949A1 (en) Antimicrobial articles and method of manufacture
CN101160146B (zh) 银涂料和制造方法
WO2006094098A2 (fr) Dispositif de soins de plaies
TW200826950A (en) Antimicrobial articles and method of manufacture
WO2005084436A1 (fr) Silicates et autres oxydes lies a des polymeres antimicrobiens

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780039099.4

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07868453

Country of ref document: EP

Kind code of ref document: A2

WWE Wipo information: entry into national phase

Ref document number: 12444877

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: MX/A/2009/004030

Country of ref document: MX

ENP Entry into the national phase

Ref document number: 2009533475

Country of ref document: JP

Kind code of ref document: A

Ref document number: 2666826

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 1020097007900

Country of ref document: KR

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2007319586

Country of ref document: AU

WWE Wipo information: entry into national phase

Ref document number: 2007868453

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2007319586

Country of ref document: AU

Date of ref document: 20071016

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: PI0716001

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20090417