WO2008041801A1 - Catalyseur pour inhiber la production de no2 - Google Patents

Catalyseur pour inhiber la production de no2 Download PDF

Info

Publication number
WO2008041801A1
WO2008041801A1 PCT/KR2007/004515 KR2007004515W WO2008041801A1 WO 2008041801 A1 WO2008041801 A1 WO 2008041801A1 KR 2007004515 W KR2007004515 W KR 2007004515W WO 2008041801 A1 WO2008041801 A1 WO 2008041801A1
Authority
WO
WIPO (PCT)
Prior art keywords
generation
inhibiting
catalyst
catalyst composition
module
Prior art date
Application number
PCT/KR2007/004515
Other languages
English (en)
Inventor
Hyun-Sik Han
Tae-Woo Lee
Original Assignee
Heesung Catalysts Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heesung Catalysts Corporation filed Critical Heesung Catalysts Corporation
Priority to EP07808305A priority Critical patent/EP2073929A4/fr
Publication of WO2008041801A1 publication Critical patent/WO2008041801A1/fr

Abstract

La présente invention concerne une composition catalytique pour inhiber la production de NO2, comprenant une composition catalytique d'oxyde métallique de base combinée à un oxyde de cérium-cobalt, une alumine active ou une zéolite, la composition catalytique d'oxyde métallique de base étant supportée par un métal précieux tel que le platine et/ou le palladium, et un métal non précieux tel que le baryum ou le strontium. L'invention concerne également un module destiné à inhiber la production de NO2 au moyen de ladite composition catalytique. Dans le système de post-traitement de gaz d'échappement dans lequel un catalyseur d'oxydation de diesel (DOC) et un filtre à suie catalysée (CSF) sont disposés en série, le module est disposé à l'extrémité arrière du CSF de sorte qu'on évite la production de NO2, et donc qu'on évite l'émission de gaz d'échappement visible, ce qui contribue à préserver l'environnement.
PCT/KR2007/004515 2006-10-04 2007-09-18 Catalyseur pour inhiber la production de no2 WO2008041801A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP07808305A EP2073929A4 (fr) 2006-10-04 2007-09-18 Catalyseur pour inhiber la production de no2

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020060097585A KR100809661B1 (ko) 2006-10-04 2006-10-04 Ｎｏ２ 생성 억제 촉매
KR10-2006-0097585 2006-10-04

Publications (1)

Publication Number Publication Date
WO2008041801A1 true WO2008041801A1 (fr) 2008-04-10

Family

ID=39268639

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2007/004515 WO2008041801A1 (fr) 2006-10-04 2007-09-18 Catalyseur pour inhiber la production de no2

Country Status (3)

Country Link
EP (1) EP2073929A4 (fr)
KR (1) KR100809661B1 (fr)
WO (1) WO2008041801A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5733837A (en) * 1993-05-10 1998-03-31 Sakai Chemical Industry Co., Ltd. Catalyst for catalytic reduction of nitrogen oxides
US6221804B1 (en) * 1998-01-27 2001-04-24 Mazda Motor Corporation Catalyst for purifying exhaust gas and manufacturing method thereof
KR100416735B1 (ko) * 1995-10-09 2004-03-26 삼성전기주식회사 자동차 배기가스 정화용 촉매 및 그 제조방법
KR20040044947A (ko) * 2001-09-19 2004-05-31 존슨 맛쎄이 퍼블릭 리미티드 컴파니 희박 ＮＯｘ 트랩／전환 촉매
KR20050118762A (ko) * 2004-06-15 2005-12-20 현대자동차주식회사 디젤 개질기를 이용한 자동차 배기가스 정화 시스템
US7030055B2 (en) * 2003-08-18 2006-04-18 W.R. Grace & Co.-Conn. NOx reduction compositions for use in FCC processes

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2064977C (fr) * 1991-04-05 1998-09-22 Eiichi Shiraishi Catalyseur purificateur de gaz d'echappement
KR200150138Y1 (en) 1994-02-23 1999-07-01 Cataler Ind Co Catalyst for purifying exhaust gases
FR2730175B1 (fr) * 1995-02-03 1997-04-04 Inst Francais Du Petrole Catalyseurs de reduction des oxydes d'azote en azote moleculaire dans un milieu surstoechiometrique en composes oxydants, procede de preparation et utilisations
JP3799651B2 (ja) * 1995-04-28 2006-07-19 マツダ株式会社 排気ガス浄化用触媒
KR100279938B1 (ko) 1998-09-11 2001-03-02 임의신 No 산화촉매 조성물

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5733837A (en) * 1993-05-10 1998-03-31 Sakai Chemical Industry Co., Ltd. Catalyst for catalytic reduction of nitrogen oxides
KR100416735B1 (ko) * 1995-10-09 2004-03-26 삼성전기주식회사 자동차 배기가스 정화용 촉매 및 그 제조방법
US6221804B1 (en) * 1998-01-27 2001-04-24 Mazda Motor Corporation Catalyst for purifying exhaust gas and manufacturing method thereof
KR20040044947A (ko) * 2001-09-19 2004-05-31 존슨 맛쎄이 퍼블릭 리미티드 컴파니 희박 ＮＯｘ 트랩／전환 촉매
US7030055B2 (en) * 2003-08-18 2006-04-18 W.R. Grace & Co.-Conn. NOx reduction compositions for use in FCC processes
KR20050118762A (ko) * 2004-06-15 2005-12-20 현대자동차주식회사 디젤 개질기를 이용한 자동차 배기가스 정화 시스템

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP2073929A4 *

Also Published As

Publication number Publication date
EP2073929A4 (fr) 2011-10-05
EP2073929A1 (fr) 2009-07-01
KR100809661B1 (ko) 2008-03-05

Similar Documents

Publication Publication Date Title
EP2922630B2 (fr) Catalyseur d'oxydation pour le traitement de gaz d'échappement d'un moteur à allumage par compression
EP2539040B1 (fr) Filtre à suie catalytique amélioré
KR101172020B1 (ko) 내연기관 배기가스의 정화 방법
JP4982241B2 (ja) 自動車用排気ガス浄化触媒、排気ガス浄化触媒系、および排気ガスの浄化方法
JP4681922B2 (ja) 排気ガス浄化用酸化触媒、及びそれを用いた排気ガス浄化システム
CZ2005148A3 (cs) Vznětový motor, motorové vozidlo, způsob provozování vznětového motoru a způsob zvyšování rychlosti katalyzované reakce
JP4012320B2 (ja) 希薄燃焼エンジン用排気ガス浄化用触媒
JP2007534467A (ja) リーンバーンエンジンからの排気ガスから汚染物質を除去するための酸化鉄で安定化された貴金属触媒
US6191061B1 (en) Method of purifying exhaust gas and catalyst for purifying exhaust gas
JP2016517342A (ja) Ｎｏ酸化用触媒材料
WO2007136148A1 (fr) Dispositif de purification de gaz d'échappement destiné à un moteur diesel présentant une ligne de recirculation de gaz d'échappement
AU615721B2 (en) Catalyst for purification of exhaust gas and process for production thereof
US20220395814A1 (en) Particulate filter
EP3468710A1 (fr) CATALYSEUR ADSORBEUR DE NOx
WO2018178681A1 (fr) Catalyseur absorbeur de nox
WO2018235752A1 (fr) Système de purification de gaz d'échappement
JPH0884911A (ja) 窒素酸化物分解用触媒およびこれを用いたディーゼルエンジン排ガスの浄化方法
JPH11123331A (ja) 排気ガス浄化用触媒
WO2008041801A1 (fr) Catalyseur pour inhiber la production de no2
JP2016500331A (ja) ゾーン化ディーゼル酸化触媒
KR100680324B1 (ko) 자동차 배기가스의 질소 산화물 저감용 촉매 조성물
JP2008215359A (ja) 希薄燃焼エンジン排気ガスの浄化方法
KR20240064639A (ko) 부분적으로 코팅된 촉매층을 갖는 미립자 필터
WO2024115790A1 (fr) Catalyseur pour le traitement d'un flux de gaz d'échappement contenant un ou plusieurs éléments parmi le formaldéhyde, l'oxyde d'azote (no), et les hydrocarbures comprenant du mn supporté sur un oxyde mixte cuo-al2o3
WO2024115789A1 (fr) Catalyseur contenant du cuivre et du manganèse pour le traitement d'un flux de gaz d'échappement contenant un ou plusieurs constituants parmi le formaldéhyde, l'oxyde d'azote (no) et des hydrocarbures

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07808305

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2007808305

Country of ref document: EP

NENP Non-entry into the national phase