WO2008017733A1 - Procédé de gravure par faisceau ionique et appareil de gravure par faisceau ionique - Google Patents
Procédé de gravure par faisceau ionique et appareil de gravure par faisceau ionique Download PDFInfo
- Publication number
- WO2008017733A1 WO2008017733A1 PCT/FI2007/050440 FI2007050440W WO2008017733A1 WO 2008017733 A1 WO2008017733 A1 WO 2008017733A1 FI 2007050440 W FI2007050440 W FI 2007050440W WO 2008017733 A1 WO2008017733 A1 WO 2008017733A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ion beam
- nanostructure
- substrate
- sample holder
- ions
- Prior art date
Abstract
La présente invention concerne un procédé de gravure par faisceau ionique servant à traiter des nanostructures tridimensionnelles. Une nanostructure préfabriquée (12) disposée sur un substrat (8) est gravée en trois dimensions en bombardant la nanostructure dans des conditions de vide avec un faisceau d'ions à faible énergie de masse moyenne (5) à un angle de Bragg incident (α) par rapport au substrat tout en faisant tourner la nanostructure autour d'un axe (N) normal au substrat. Selon l'invention, l'énergie massique des ions est comprise entre 0,0025 et 0,0225 keV/amu ; et l'angle incident (α) du faisceau ionique (5) par rapport au substrat (8) est compris entre 30 et 50 degrés, de préférence environ 40 degrés.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FI20060719 | 2006-08-09 | ||
FI20060719A FI122010B (fi) | 2006-08-09 | 2006-08-09 | Ionisuihkuetsausmenetelmä ja -laitteisto |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2008017733A1 true WO2008017733A1 (fr) | 2008-02-14 |
Family
ID=36950625
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/FI2007/050440 WO2008017733A1 (fr) | 2006-08-09 | 2007-08-09 | Procédé de gravure par faisceau ionique et appareil de gravure par faisceau ionique |
Country Status (2)
Country | Link |
---|---|
FI (1) | FI122010B (fr) |
WO (1) | WO2008017733A1 (fr) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2585010C1 (ru) * | 2014-12-12 | 2016-05-27 | Антон Борисович Архипов | Установка для двусторонней финишной обработки поверхности интраокулярных линз |
EP3809447A1 (fr) * | 2019-10-18 | 2021-04-21 | FEI Company | Procédé d'analyse tridimensionnelle d d'échantillons à grande surface utilisant le ponçage de fib par incidence rasante |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4503329A (en) * | 1981-09-30 | 1985-03-05 | Hitachi, Ltd. | Ion beam processing apparatus and method of correcting mask defects |
EP0708472A1 (fr) * | 1994-10-21 | 1996-04-24 | Yamaha Corporation | Fabrication d'un micro-émetteur d'électrons |
EP1104011A1 (fr) * | 1999-11-25 | 2001-05-30 | Sceptre Electronics Limited | Procédé de formation de nanostructures en silicium, matrice de fils quantiques et composants basés sur ladite matrice |
-
2006
- 2006-08-09 FI FI20060719A patent/FI122010B/fi not_active IP Right Cessation
-
2007
- 2007-08-09 WO PCT/FI2007/050440 patent/WO2008017733A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4503329A (en) * | 1981-09-30 | 1985-03-05 | Hitachi, Ltd. | Ion beam processing apparatus and method of correcting mask defects |
EP0708472A1 (fr) * | 1994-10-21 | 1996-04-24 | Yamaha Corporation | Fabrication d'un micro-émetteur d'électrons |
EP1104011A1 (fr) * | 1999-11-25 | 2001-05-30 | Sceptre Electronics Limited | Procédé de formation de nanostructures en silicium, matrice de fils quantiques et composants basés sur ladite matrice |
Non-Patent Citations (10)
Title |
---|
"Tectra Plasma Ion Source", 2 August 1998 (1998-08-02), Retrieved from the Internet <URL:http://www.web.archive.org/web/19980625194344> * |
FROST F. ET AL.: "Ion beam assisted smoothing of optical surfaces", APPL. PHYS. A, vol. 78, 2004, pages 651 - 654 * |
FROST F. ET AL.: "Large area smoothing of optical surfaces by low-energy ion beams", THIN SOLID FILMS, vol. 459, 2004, pages 100 - 105 * |
FROST F. ET AL.: "Smoothing of polycrystalline Cu(In,Ga)(Se,S)2 thin films by low-energy ion-beam etching", JOURNAL OF VACUUM SCIENCE & TECHOLOGY A, vol. 17, no. 3, May 1999 (1999-05-01) - June 1999 (1999-06-01), pages 793 * |
GRISOLIA J. ET AL.: "Co nanoelectrodes for the study of spin dependent transport through nano-objects", SUPERLATTICES AND MICROSTRUCTURES, vol. 36, 2004, pages 271 - 279 * |
Hyung Seok Kim et al., "Topography evolution of Si(001) substrate fabricated by Ar+ ion beam sputter etching". Kinetics-Driven Nanopatterning on Surfaces: Symposium Held November 28-December 2, 2004, Boston, Massachusetts U.S.A. Materials Research..... * |
SAVVIDES N.: "Correction masks for large-area ion beam etching and figuring of optics", JOURNAL OF APPLIED PHYSICS, vol. 99, 2006, pages 1 - 7 * |
SOLVOLAINEN M. ET AL.: "Ion beam sputering method for progressive reduction of nanostructures dimensions", APPL. PHYS. A, vol. 79, 2004, pages 1769 - 1773 * |
ZHAO G. ET AL.: "Fabrication of nanowires on Inp(100) by Ar+ irradiation", INDIUM PHOSPHIDE AND RELATED MATERIALS, 2005, INTERNATIONAL CONFERENCE ON GLASGOW, SCOTLAND, 8 May 2005 (2005-05-08) - 12 May 2005 (2005-05-12), PISCATAWAY, NJ, USA, IEEE, CONFERENCE PROCEEDINGS ARTICLE, pages 269 - 272 * |
ZIBERI B. ET AL.: "Importance of ion beam parameters on self-organized pattern formation on semiconductor surfaces by ion beam erosion", THIN SOLID FILMS, vol. 459, 2004, pages 106 - 110 * |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2585010C1 (ru) * | 2014-12-12 | 2016-05-27 | Антон Борисович Архипов | Установка для двусторонней финишной обработки поверхности интраокулярных линз |
EP3809447A1 (fr) * | 2019-10-18 | 2021-04-21 | FEI Company | Procédé d'analyse tridimensionnelle d d'échantillons à grande surface utilisant le ponçage de fib par incidence rasante |
Also Published As
Publication number | Publication date |
---|---|
FI122010B (fi) | 2011-07-15 |
FI20060719A (fi) | 2008-02-10 |
FI20060719A0 (fi) | 2006-08-09 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2079102B1 (fr) | Procédé d'aplanissement d'une surface solide avec un faisceau ionique d'agrégats gazeux | |
EP1918963B1 (fr) | Traitement à faisceau de particule chargé utilisant une source de agrégat | |
Tseng | Recent developments in micromilling using focused ion beam technology | |
Heller et al. | Defect Mediated Desorption of the KBr (001) Surface Induced<? format?> by Single Highly Charged Ion Impact | |
Xirouchaki et al. | Deposition of size-selected metal clusters generated by magnetron sputtering and gas condensation: a progress review | |
US8481981B2 (en) | Method of smoothing solid surface with gas cluster ion beam and solid surface smoothing apparatus | |
US8819861B2 (en) | Nanometer-scale sharpening of conductor tips | |
JP6752490B2 (ja) | 基板処理方法における欠陥削減 | |
JPS6130036A (ja) | マイクロ波プラズマ処理装置 | |
JPH09221309A (ja) | カーボンナノチューブを表面に有する炭素質物及びその製造方法 | |
JP2001028244A (ja) | ビーム源 | |
JP2003158099A5 (fr) | ||
WO2006123739A1 (fr) | Procédé et appareil d’aplatissement de surface solide | |
KR100445105B1 (ko) | 가스 클러스터 이온빔을 이용한 아이.티.오 박막 표면처리시스템 및 그 방법 | |
JP2639158B2 (ja) | エッチング方法およびエッチング装置 | |
WO2008017733A1 (fr) | Procédé de gravure par faisceau ionique et appareil de gravure par faisceau ionique | |
EP2263248B1 (fr) | Source ionique à effet de champ utilisant du gaz et comprenant un embout revêtu | |
JP2003522710A (ja) | ダイヤモンド表面の処理方法および対応するダイヤモンド表面 | |
US8460049B2 (en) | Fabrication of super ion—electron source and nanoprobe by local electron bombardment | |
Winter et al. | Interaction of slow HCI with solid surfaces: What do we know, what should we know? | |
Hoffrogge et al. | Nanostructuring of tips for scanning probe microscopy by ion sputtering: Control of the apex ratio and the tip radius | |
JP4636862B2 (ja) | ガスクラスターイオンビーム照射装置 | |
Ichiki | Study on size effect of cluster ion beam irradiation | |
TW201005786A (en) | Method for manufacturing workpieces with ion-etched surface | |
Ichiki et al. | The effects of cluster size on sputtering and surface smoothing of PMMA with gas cluster ion beams |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 07803703 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
NENP | Non-entry into the national phase |
Ref country code: RU |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 07803703 Country of ref document: EP Kind code of ref document: A1 |