WO2007142742A1 - Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques - Google Patents

Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques Download PDF

Info

Publication number
WO2007142742A1
WO2007142742A1 PCT/US2007/009427 US2007009427W WO2007142742A1 WO 2007142742 A1 WO2007142742 A1 WO 2007142742A1 US 2007009427 W US2007009427 W US 2007009427W WO 2007142742 A1 WO2007142742 A1 WO 2007142742A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
thermoplastic
blend
cross
propylene
Prior art date
Application number
PCT/US2007/009427
Other languages
English (en)
Inventor
Weiqing Weng
Sunny Jacob
Peijun Jiang
Armenag H. Dekmezian
Aspy K. Mehta
James R. Ayers
David J. Lohse
Peter W. Manders
Palanisamy Arjunan
Original Assignee
Exxonmobil Chemical Patents Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Exxonmobil Chemical Patents Inc. filed Critical Exxonmobil Chemical Patents Inc.
Priority to EP07755628A priority Critical patent/EP2029643A1/fr
Publication of WO2007142742A1 publication Critical patent/WO2007142742A1/fr

Abstract

La présente invention concerne la préparation de vulcanisats thermoplastiques (TPV) présentant des caractéristiques morphologiques uniques. Cette invention porte plus particulièrement sur un procédé de préparation de compositions de TPV, au cours duquel le mélange de plastomères et d'élastomères est effectué dans un solvant contenant des agents de vulcanisation en vue d'induire une réticulation.
PCT/US2007/009427 2006-06-08 2007-04-18 Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques WO2007142742A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP07755628A EP2029643A1 (fr) 2006-06-08 2007-04-18 Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US81192306P 2006-06-08 2006-06-08
US60/811,923 2006-06-08

Publications (1)

Publication Number Publication Date
WO2007142742A1 true WO2007142742A1 (fr) 2007-12-13

Family

ID=37564040

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/009427 WO2007142742A1 (fr) 2006-06-08 2007-04-18 Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques

Country Status (3)

Country Link
EP (1) EP2029643A1 (fr)
CN (2) CN101460531A (fr)
WO (1) WO2007142742A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016154769A1 (fr) * 2015-03-27 2016-10-06 Exxonmobil Chemical Patents Inc. Compositions de polymère à base de propylène pour le moulage par injection
US10323140B2 (en) 2015-05-29 2019-06-18 Exxonmobil Chemical Patents Inc. Thermoplastic vulcanizates comprising broad molecular weight distribution polypropylene
US10344151B2 (en) 2015-03-27 2019-07-09 Exxonmobil Chemical Patents Inc. Propylene-based polymer compositions for grip applications

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8415431B2 (en) * 2010-08-05 2013-04-09 Exxonmobil Chemical Patents Inc. Thermoplastic elastomeric compositions
CN104059321A (zh) * 2013-03-19 2014-09-24 中纺投资发展股份有限公司 一种耐候环保阻燃柔性线缆用聚合物材料及其制备方法
EP3263640A1 (fr) * 2016-06-28 2018-01-03 Borealis AG Composition de polypropylène souple et transparent
CN107828178B (zh) * 2017-11-22 2020-10-16 东莞市华立实业股份有限公司 一种动态交联型耐候abs封边条材料及其制备方法
CN112135863A (zh) * 2018-04-06 2020-12-25 埃克森美孚化学专利公司 热塑性硫化橡胶组合物
CN116144120A (zh) * 2023-01-13 2023-05-23 赛轮集团股份有限公司 自密封胶料的制备方法、自密封胶料及其应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1599164A (en) * 1977-10-11 1981-09-30 Exxon Research Engineering Co Plastics-elastomer compositions
US6268438B1 (en) * 1996-12-17 2001-07-31 Exxonmobil Chemical Patents Inc. Thermoplastic elastomeric compositions
US20040260001A1 (en) * 2002-08-12 2004-12-23 Lin Chon-Yie Articles from plasticized polyolefin compositions
WO2005028556A1 (fr) * 2003-09-17 2005-03-31 Advanced Elastomer Systems Vulcanisats thermoplastiques et leur procede de production
EP1655332A1 (fr) * 2004-11-05 2006-05-10 Advanced Elastomer Systems, L.P. Vulcanisat thermoplastique à manufacturabilité amélioré
EP1688459A1 (fr) * 2005-02-04 2006-08-09 Advanced Elastomer Systems, L.P. vulcanisats thermoplastiques et leur utilisation
WO2006118674A1 (fr) * 2005-04-29 2006-11-09 Exxonmobil Chemical Patents Inc. Compositions de polyolefine plastifiee

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1599164A (en) * 1977-10-11 1981-09-30 Exxon Research Engineering Co Plastics-elastomer compositions
US6268438B1 (en) * 1996-12-17 2001-07-31 Exxonmobil Chemical Patents Inc. Thermoplastic elastomeric compositions
US20040260001A1 (en) * 2002-08-12 2004-12-23 Lin Chon-Yie Articles from plasticized polyolefin compositions
WO2005028556A1 (fr) * 2003-09-17 2005-03-31 Advanced Elastomer Systems Vulcanisats thermoplastiques et leur procede de production
EP1655332A1 (fr) * 2004-11-05 2006-05-10 Advanced Elastomer Systems, L.P. Vulcanisat thermoplastique à manufacturabilité amélioré
EP1688459A1 (fr) * 2005-02-04 2006-08-09 Advanced Elastomer Systems, L.P. vulcanisats thermoplastiques et leur utilisation
WO2006118674A1 (fr) * 2005-04-29 2006-11-09 Exxonmobil Chemical Patents Inc. Compositions de polyolefine plastifiee

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016154769A1 (fr) * 2015-03-27 2016-10-06 Exxonmobil Chemical Patents Inc. Compositions de polymère à base de propylène pour le moulage par injection
US10344151B2 (en) 2015-03-27 2019-07-09 Exxonmobil Chemical Patents Inc. Propylene-based polymer compositions for grip applications
US10344152B2 (en) 2015-03-27 2019-07-09 Exxonmobil Chemical Patents Inc. Propylene-based polymer compositions for injection molding
US10323140B2 (en) 2015-05-29 2019-06-18 Exxonmobil Chemical Patents Inc. Thermoplastic vulcanizates comprising broad molecular weight distribution polypropylene

Also Published As

Publication number Publication date
CN102627802A (zh) 2012-08-08
EP2029643A1 (fr) 2009-03-04
CN101460531A (zh) 2009-06-17

Similar Documents

Publication Publication Date Title
US8481646B2 (en) Solution blending process for preparing thermoplastic vulcanizates
US7935761B2 (en) Process for preparing articles
EP2029665B1 (fr) Procédé de préparation d'articles
EP2029643A1 (fr) Procédé de mélange de solution destiné à préparer des vulcanisats thermoplastiques
JP5806218B2 (ja) ブロック複合材及び耐衝撃性改質組成物
US8093335B2 (en) Thermoplastic polyolefin in-reactor blends and molded articles therefrom
US20060293461A1 (en) Process of making a heterogeneous polymer blend
US20060293455A1 (en) Heterogeneous polymer blend and process of making the same
JP5095080B2 (ja) 異相ポリマー組成物
US10364308B2 (en) Thermoplastic polyolefin compositions
JP2008546891A (ja) フィラー含有ｔｐｏ組成物から作製される自動車用品およびその製造方法
JP5340292B2 (ja) 良好な低温延性を有する充填材入りｔｐｏ組成物
WO2001042344A1 (fr) Composition polymere de propylene chargee
WO2010077881A2 (fr) Mélanges en réacteur de polyoléfines thermoplastiques et articles moulés à base de ceux-ci
WO2008020925A1 (fr) Mélanges de polyoléfine hétéro-phasique plastifiés
JP2005504160A (ja) ブロー成形可能なプロピレンポリマー組成物
WO2007067298A1 (fr) Formules vulcanisées thermoplastiques de copolymère aléatoire propylène-diène
US20020061976A1 (en) Propylene polymer composition
JP2004359877A (ja) プロピレン系樹脂組成物
JP2000309668A (ja) 熱可塑性樹脂組成物及びその射出成形体
EP1896533B1 (fr) Mélange hétérogène de polymères et son procédé de préparation
US10822481B2 (en) Thermoplastic polyolefin compositions with ethylene-propylene copolymers
JP2002012718A (ja) 熱可塑性樹脂組成物及びその射出成形体
JP2000344975A (ja) シンジオタクティックポリプロピレン組成物
US8962762B2 (en) Thermoplastic polymer compositions, methods for making the same, and articles made therefrom

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780020861.4

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07755628

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2007755628

Country of ref document: EP